Kinetic decomposition of Ni2SiO4 in oxygen potential gradients

Nickel orthosilicate (Ni2SiO4) has been found to decompose into its component binary oxides in oxygen potential gradients at 1373 K. Nickel oxide was formed at the high oxygen potential boundary, while silica was detected at the low oxygen potential side. Significant porosity and fissures were observed near the Ni2SiO4/SiO2 interface and the SiO2 layer. The critical oxygen partial pressure ratio required for decomposition varied from 1.63 to 2.15 as the oxygen pressures were altered from 1.01 ⊠ 105 to 2.7X 10−4 Pa, well above the dissociation pressure of Ni2SiO4. Platinum markers placed at the boundaries of the Ni2SiO4 sample indicated growth of NiO at the higher oxygen potential boundary, without any apparent transport of material to the low oxygen potential side. However, significant movement of the bulk Ni2SiO4 crystal with respect to the marker was not observed. The decomposition of the silicate occurs due to the unequal rates of transport of Ni and Si. The critical oxygen partial pressure ratio required for decomposition is related both to the thermodynamic stability of Ni2SiO4 with respect to component oxides and the ratio of diffusivities of nickel and silicon. Kinetic decomposition of multicomponent oxides, first discovered by Schmalzried, Laqua, and co-workers [H. Schmalzried, W. Laqua, and P. L. Lin, Z. Natur Forsch. Teil A 34, 192 (1979); H. Schmalzried and W. Laqua, Oxid. Met. 15, 339 (1981); W. Laqua and H. Schmalzried, Chemical Metallurgy—A Tribute to Carl Wagner (Metallurgical Society of the AIME, New York, 1981), p. 29] has important consequences for their use at high temperatures and in geochemistry.

Standard Gibbs energy of formation of Pb2Ru2O6.5

Lead ruthenate is used as a bifunctional electrocatalyst for both oxygen evolution and reduction and as a conducting component in thick-film resistors. It also has potential applications in supercapacitors and solid oxide fuel cells. However, thermodynamic properties of the compound have not been reported in the literature. The standard Gibbs energy of formation has now been determined in the temperature range from 873 to 1123 K using a solid-state cell incorporating yttria-stabilized zirconia (YSZ) as the electrolyte, a mixture of PbO + Pb2Ru2O6.5 + Ru as the measuring electrode, and Ru + RuO2 as the reference. The design of the measuring electrode is based on a study of phase relations in the ternary system Pb–Ru–O at 1123 K. For the reaction,S0884291400095625_eqnU1 the standard enthalpy of formation and standard entropy at 298.15 K are estimated from the high-temperature measurements. An oxygen potential diagram for the system Pb–Ru–O is composed based on data obtained in this study and auxiliary information from the literature

Thermodynamic properties of SmFeO3(S) and SM3R5O12(S)

The enthalpy increments and the standard molar Gibbs energy (G) of formation of SmFeO3(S) and SM3Fe5O12(s) have been measured using a Calvet micro-calorimeter and a solid oxide galvanic cell, respectively. A X-type transition, related to magnetic order-disorder transformation (antiferromagnetic to paramagnetic), is apparent from the heat capacity data at similar to673 K for SmFeO3(s) and at similar to560 K for Sm3Fe5O12(S). Enthalpy increment data for SmFeO3(s) and SM3Fe5O12(s), except in the vicinity of X-transition, can be represented by the following polynomial expressions: {H-m(0)(T) - H-m(0)(298.15 K){/J mol-(1)(+/-1.2%) = -54 532.8 + 147.4 . (T/K) + 1.2 . 10(-4) . (T/K)(2) +3.154 . 10(6) . (T/K)(-1); (298.15 less than or equal to T/K less than or equal to 1000) for SmFeO3(s), and {H-m(0)(T) - H-m(0)(298.15 K)}/J mol(-1) (+/-1.4%) = -192 763 + 554.7 . (T/K) + 2.0 . 10(-6) . (T/K)(2) + 8.161 . 10(6) - (T/K)(-1); (298.15 less than or equal to T/K less than or equal to 1000) for Sm3Fe5O12(s). The reversible emf of the solid-state electrochemical cells, (-)Pt/{SmFeO3(s) + Sm2O3(S) + Fe(s)) // YDT / CSZ // {Fe(s) + Fe0.95O(s)} / Pt(+) and (-)Pt/{Fe(s) + Fe0.95O(S)} // CSZ // {SmFeO3(s) + Sm3Fe5O12(s) + Fe3O4(s) / Pt(+), were measured in the temperature ranges of 1005-1259 K and 1030-1252 K, respectively. The standard molar G of formation of solid SmFeO3 and Sm3Fe5O12 calculated by the least squares regression analysis of the data obtained in the current study, and data for Fe0.95O and Sm2O3 from the literature, are given by: Delta(f)G(m)(0)(SmFeO3, s)/kj . mol(-1)(+/-2.0) = -1355.2 + 0.2643 . ; (1005 less than or equal to T/K less than or equal to 1570) and Delta(f)G(m)(0)(Sm3Fe5O12, s)/kj . mol(-1) (+/- 3.1) = -4891.0 + 1.0312 . (T/K); (1030 less than or equal to T/K less than or equal to 1252) The uncertainty estimates for Delta(f)G(m)(0) include the standard deviation in the emf and uncertainty in the data taken from the literature. Based on these thermodynamic data, the oxygen potential diagram for the system Sm-Fe-O was constructed at 1250 K.