Refinement of the thermodynamic properties of ruthenium dioxide and osmium dioxide

The standard Gibbs energies of formation of RuO2 and OsO2 at high temperature have been determined with high precision, using a novel apparatus that incorporates a buffer electrode between the reference and working electrodes, The buffer electrode absorbs the electrochemical flux of oxygen through the solid electrolyte from the electrode with higher oxygen chemical potential to the electrode with lower oxygen potential, The buffer electrode prevents polarization of the measuring electrode and ensures accurate data, The standard Gibbs energies of formation (Delta(f)G degrees) of RuO2, in the temperature range of 900-1500 K, and OsO2, in the range of 900-1200 K, can be represented by the equations Delta(f)G degrees(RuO2)(J/mol) = -324 720 + 354.21T - 23.490T In T Delta(f)G degrees(OsO2)(J/mol) = -304 740 + 318.80T - 18.444T In T where the temperature T is given in Kelvin and the deviation of the measurement is +/- 80 J/mol, The high-temperature heat ;capacities of RuO2 and OsO2 are measured using differential scanning calorimetry. The information for both the low- and high-temperature heat rapacity of RuO2 is coupled with the Delta(f)G degrees data obtained in this study to evaluate the standard enthalpy of formation of RuO2 at 298.15 K (Delta(f)H degrees(298.15K)). The low-temperature heat capacity of OsO2 has not been measured: therefore, the standard enthalpy and entropy of formation of OsO2 at 298.15 K (Delta(f)H degrees(298.15K) and S degrees(298.15K), respectively) are derived simultaneously through an optimization procedure from the high-temperature heat capacity and the Gibbs energy of formation. Both Delta fH degrees(298.15K) and S degrees(298.15K) are treated as variables in the optimization routine, For RuO2, the standard enthalpy of formation at 298.15 K is Delta fH degrees(298.15K) (RuO2) -313.52 +/- 0.08 kJ/mol, and that for OsO2 is Delta(f)H degrees(298.15K) (OSO2) = -295.96 +/- 0.08 kJ/mol. The standard entropy of OsO2 at 298.15 K that has been obtained from the optimization is given as S degrees(298.15K) (OsO2) = 49.8 +/- 0.2 J (mol K)(-1).

Role of hydroxyl group on the mesomorphism of alkyl glycosides:synthesis and thermal behavior of alkyl 6-deoxy-beta-D-glucopyranosides

A homologous series of alkyl 6-deoxy-beta-D-glucopyranoside amphiphiles was prepared,in an effort to identify the role of hydroxyl group in the mesomorphic behavior of alkyl glycosides. Synthesis was performed by a chlorination of the sugar moiety in alkyl-beta-D-glucopyranosides with methylsulfonyl chloride in DMF, followed by a metal mediated dehalogenation to secure alkyl 6-deoxy-beta-D-glucopyranosides, wherein the alkyl chain length varied from C-9 to C-16. The mesomorphic behavior of these 6-deoxy alkyl glycosides was assessed using polarizing optical microscopy, differential scanning calorimetry and X-ray diffraction method. Whereas the lower homologues exhibited a monotropic SmA phase till sub-ambient temperatures, the higher homologues formed a plastic phase. A partial interdigitized bilaye structure of SmA phase is inferred from experimental d-spacing and computationally derived lengths of the molecules. The results were compared with those of normal alkyl glucopyranosides, retained with hydroxyl groups at C-2-C-6 carbons, and alkyl 2-deoxy-glucopyranosides, devoid of a hydroxyl group at C-2 and the comparison showed important differences in the mesomorphic behavior.(C)2010 Elsevier Ireland Ltd. All rights reserved.

Plasticity in the primary binding site of galactose/N-acetylgalactosamine-specific lectins - Implication of the C-H center dot center dot center dot O hydrogen bond at the specificity-determining C-4 locus of the saccharide in 4-methoxygalactose recognition by jacalin and winged bean (basic) agglutinin I

It is currently believed that an unsubstituted axial hydroxyl at the specificity-determining C-4 locus of galactose is indispensable for recognition by galactose/N-acetylgalactosamine-specific lectins. Titration calorimetry demonstrates that 4-methoxygalactose retains binding allegiance to the Moraceae lectin jacalin and the Leguminosae lectin, winged bean (basic) agglutinin (WBA I). The binding reactions were driven by dominant favorable enthalpic contributions and exhibited significant enthalpy-entropy compensation. Proton NMR titration of C-methoxygalactose with jacalin and WBA I resulted in broadening of the sugar resonances without any change in chemical shift. The alpha-and beta-anomers of 4-methoxygalactose were found to be in slow exchange with free and lectin-bound states. Both the anomers experience magnetically equivalent environments at the respective binding sites. The binding constants derived from the dependence of NMR line widths on 4-methoxygalactose concentration agreed well with those obtained from titration calorimetry. The results unequivocally demonstrate that the loci corresponding to the axially oriented C-4 hydroxyl group of galactose within the primary binding site of these lectins exhibit plasticity. These analyses suggest, for the first time, the existence of C-H ... O-type hydrogen-bond(s) in protein-carbohydrate interactions in general and between the C-4 locus of galactose derivative and the lectins jacalin and WBA I in particular.

Combined free and forced convection along a rotating vertical cylinder

The steady incompressible laminar mixed convection boundary layer flow along a rotating slender vertical cylinder with an isothermal wall has been studied. The transformed coupled nonlinear partial differential equations have been solved numerically using the Keller box method. In general, the rotation of the cylinder, the buoyancy forces and the curvature parameter are found to significantly affect the skin friction, heat transfer, velocity and temperature profiles as well as the pressure distribution. The buoyancy forces cause an overshoot in the axial velocity profile but the rotation and curvature parameters reduce it.

Formation and crystallization of hydrogen-induced amorphous SmFe2H3.6 alloy

On hydrogenation of the Laves phase SmFe2, an amorphous SmFe2H3.6 (a-SmFe2H3.6) alloy was formed between 400 K and 500 K. The amorphous nature of the alloy was confirmed by X-ray diffraction, transmission electron microscopy and thermal analysis. However, SmFe2 absorbed hydrogen in the crystal state below 350 K and decomposed into SmH2 and α-Fe above 550 K. The crystallization behaviour of a-SmFe2H3.6 was investigated by differential scanning calorimetry in combination with electron microscopy. Even after considerable hydrogen desorption (Image ) by an endothermic reaction on heating, the amorphous state was retained. Crystallization of a-SmFe2H3.6 took place in two stages. The first stage involved the precipitation of α-Fe in the amorphous matrix. The second stage involved the decomposition of the remaining amorphous phase into the equilibrium phases SmH2 and SmFe2.

Effect of network connectivity on thermal properties of As30Te70-xTlx glasses

Alternating differential scanning calorimetry (ADSC) studies were undertaken to investigate the effect of Tl addition on the thermal properties of As30Te70-xTlx ( 6 <= x <= 22 at%) glasses. These include parameters such as glass-transition temperature (T-g), changes in specific heat capacity (Delta C-p) and relaxation enthalpy (Delta H-NR) at the glass transition. It was found that T-g of the glasses decreased with the addition of Tl, which is in contrast to the dependence of T-g in As - Te glasses on the addition of Al and In. The change in heat capacity Delta C-p through the glass transition was also found to decrease with increasing Tl content. The addition of Tl to the As - Te matrix may lead to a breaking of As - Te chains and the formation of Tl+Te- AsTe2/2 dipoles. There was no significant dependence of the change of relaxation enthalpy, through the glass transition, with composition.

Carbon nanotube reinforced supramolecular gels with electrically conducting, viscoelastic and near-infrared sensitive properties

Pristine and long-chain functionalized single-walled carbon nanotubes (SWNTs) were incorporated successfully in supramolecular organogels formed by an all-trans tri(p-phenylenevinylene) bis-aldoxime to give rise to new nanocomposites with interesting mechanical, thermal and electrical properties. Variable-temperature UV-vis and fluorescence spectra reveal both pristine and functionalized SWNTs promote aggregation of the gelator molecules and result in quenching of the UV-vis and fluorescence intensity. Electron microscopy and confocal microscopy show the existence of a densely packed and directionally aligned fibrous network in the resulting nanocomposites. Differential scanning calorimetry (DSC) of the composites shows that incorporation of SWNTs increases the gel formation temperature. The DSC of the xerogels of 1-SWNT composites indicates formation of different thermotropic mesophases which is also evident from polarized optical microscopy. The reinforced aggregation of the gelators on SWNT doping was reflected in the mechanical properties of the composites. Rheology of the composites demonstrates the formation of a rigid and viscoelastic solid-like assembly on SWNT incorporation. The composites from gel-SWNTs were found to be semiconducting in nature and showed enhanced electrical conductivity compared to that of the native organogel. Upon irradiation with a near IR laser at 1064 nm for 5 min it was possible to selectively induce a gel-to-sol phase transition of the nanocomposites, while irradiation for even 30 min of the native organogel under identical conditions did not cause any gel-to-sol conversion.

Vapor phase oxidation of p-xylene

The kinetics of the vapor phase oxidation of p-xylene over ferric molybdate catalyst were studied in an isothermal, differential, tubular flow reactor in the temperature range of 360 to 420° C. The major product obtained was p-tolualdehyde with small amounts of maleic anhydride and p-toluic acid. No terephthalic acid or CO2 were observed. The reaction rate data collected fit the redox model given by Equation 1. The values of activation energies Ex, Eo and frequency factors Ax, Ao obtained are 72, 63 kJ/mol and 0.64, 2.89 m3/kg catalyst s respectively. The reaction mechanism was established by studying the oxidation of p-tolualdehyde, toluic and terephthalic acids. It is concluded that the reaction follows a parallel-consecutive scheme. On a étudié la cinétique de l'oxydation, en phase gazeuse, du para-xylène sur un catalyseur consistant en molybdate ferrique; cette oxydation s'est faite dans un réacteur à écoulement tubulaire, isothermique et différentiel, dans une échelle de températures comprises entre 360°C et 420°C. Le produit principal obtenu a été le para-tolualdéhyde; on a aussi trouvé de faibles quantités d'anhydride maléique et d'acide para-toluique, mais on n'a pas noté la présence d'acide téréphtalique ni d'anhydride carbonique (CO2). Les résultats obtenus en ce qui a trait à la vitesse de réaction concordent bien avec les données du modèle redox indiquées par l'équation 1. Les valeurs des énergies d'activation Ex et Eo ainsi que des facteurs de fréquence Ax et Ao obtenus sont respectivement 72 et 63 kilojoules/mol. et 0.64 × 103 et 2.89 m3/kg de catalyseur. On a établi le mécanisme de la réaction en étudiant l'oxydation du para-tolualdéhyde et des acides toluique et téréphtalique. On conclut que la réaction se fait d'une manière parallèle et consécutive.

Kinetics and mechanism of thermal decomposition of tetramethylammonium nitrate

The mechanism of thermal decomposition of tetramethylammonium nitrate has been investigated by thermogravimetry and mass spectrometry. The activation energy for the decomposition has been determined by isothermal decomposition technique using thermogravimetry and by monitoring mass spectrometrically the formation of trimethylamine. The activation energies determined in both the cases compare well, suggesting that the decomposition proceeds via dissociation of tetramethylammonium nitrate into trimethylamine and methylnitrate.

Effect of Storage Temperatures on the Mechanical Properties of the Composite Solid Propellants

Accelerated ageing studies for three composite propellant formulations, namely polystyrene (PS)/ ammonium perchlorate (AP), polymethylmethacrylate (PMMA)/AP and poly phenol formaldehyde (PPF)/AP have been carried out in the temperature range of 55-125°C. Measurements of the ultimate compression strength (Uc) and isothermal decomposition rate (TD rate) were monitored as a function of storage time and temperature. The change in Uc was found to be linearly dependent on the change in TD rate irrespective of the propellant systems. Analysis of the results further revealed that the cause of ageing for both Uc and burning rate (r) is the thermal decomposition of the propellant. The safe-life for the change in mechanical properties was found to be higher compared to the change in r for PS and PMMA based propellants.

Experimental studies and phase field modeling of microstructure evolution during solidification with electromagnetic stirring

Thixocasting requires manufacturing of billets with non-dendritic microstructure. Aluminum alloy A356 billets were produced by rheocasting in a mould placed inside a linear electromagnetic stirrer. Subsequent heat treatment was used to produce a transition from rosette to globular microstructure. The current and the duration of stirring were explored as control parameters. Simultaneous induction heating of the billet during stirring was quantified using experimentally determined thermal profiles. The effect of processing parameters on the dendrite fragmentation was discussed. Corresponding computational modeling of the process was performed using phase-field modeling of alloy solidification in order to gain insight into the process of morphological changes of a solid during this process. A non-isothermal alloy solidification model was used for simulations. The morphological evolution under such imposed thermal cycles was simulated and compared with experimentally determined one. Suitable scaling using the thermosolutal diffusion distances was used to overcome computational difficulties in quantitative comparison at system scale. The results were interpreted in the light of existing theories of microstructure refinement and globularisation.

Chiral gels derived from secondary ammonium salts of (1R, 3S)-(+)-camphoric acid

In order to have access to chiral gels, a series of salts derived from (1R, 3S)-(+)-camphoric acid and various secondary amines were prepared based on supramolecular synthon rationale. Out of seven salts prepared, two showed moderate gelation abilities. The gels were characterized by differential scanning calorimetry, table top rheology, scanning electron microscopy, single crystal and powder X-ray diffraction. Structure property correlation based on X-ray diffraction techniques remain inconclusive indicating that some of the integrated part associated with the gelation phenomena requires a better understanding.

Crystallization characteristics of vitrovac 4040 (Fe39Ni39Mo4Si6B12)

The metallic glass Vitrovac 4040 with the composition Fe39Ni39Mo4Si6B12 crystallizes in the order alpha-Fe, hexagonal Ni5Si2 and gamma-(Fe,Ni,Mo) by primary, secondary and polymorphic modes, respectively. The activation energies determined from the non-isothermal kinetics using Kissinger method turn out to be 490, 550 and 449 kJ.mol-1 for the above crystallization reactions. It has been observed that alpha transforms to gamma during annealing. Further, the bct (Fe1-xNix)3B phase has been identified when the glass is annealed above 1023 K.

Flow And Heat-Transfer Over An Upstream Moving Wall With A Magnetic-Field And A Parallel Free Stream

The flow and heat transfer over an upstream moving non-isothermal wall with a parallel free stream have been considered. The magnetic field has been applied in the free stream parallel to the wall and the effect of induced magnetic field has been included in the analysis. The boundary layer equations governing the steady incompressible electrically conducting fluid flow have been solved numerically using a shooting method. This problem is interesting because a solution exists only when the ratio of the wall velocity does not exceed a certain critical value and this critical value depends on the magnetic field and magnetic Prandtl number. Also dual solutions exist for a certain range of wall velocity.

Studies in biogas technology. Part I. Performance of a conventional biogas plant

This paper gives an account of a conventional 5.66 m3/day (200 cubic ft/day) biogas plant which has been instrumented, operated and monitored for 2 1/2 years. The observations regarding input to the plant, sludge and biogas outputs, and conditions inside the digester, have been described. Three salient features stand out. First, the observed average daily gas yield is much less than the rated capacity of the plant. Secondly, the plants show ease of operation and a very slow response to reductions and cessations of dung supply. Thirdly, the unexpectedly marked uniformity of density and temperature inside the digester indicates the almost complete absence of the stratification which is widely believed to take place; hence, biogas plants may be treated as isothermal, ‘ uniform ’ density, most probably imperfectly mixed, fed-batch reactors operating at the mean ambient temperature and the density of water.