218 resultados para Lithium batteries
Resumo:
Total syntheses of (±)-1,4-dimethoxy-6,6-dimethyl-B-norestra-1,3,5(10)-trien-17?-ol(11a), (±)-2,3-dimethoxy-6,6-dimethyl-B-norestra-1,3,5(10)-trien-17?-ol (11b), and (±)-3-methoxy-6,6-dimethyl-B-norestra-1,3,5(10)trien-17?-ol (11c), have been carried out starting from 4,7-dimethoxy-3,3-dimethylindan-1-one (1), 5,6-dimethoxy-3,3-dimethylindan-1-one (2), and 4?-methoxy-3-methylbut-2-enophenone (4), respectively. Generally, it is found that the intermediate 6,6-dimethyl-B-norestra-1,3,5(10),8-tetraen-17?-ols (10), on lithium�liquid ammonia reduction, yield a mixture of 8?,9?- and 8?,9?-trienols, (11) and (12) respectively, in the ratio 1 : 1. This is due to the comparable stabilities of these two isomers. However, the reduction carried out in presence of aniline affords a higher percentage of the 8?,9?-trienol (11). The assignment of configurations is made by chemical and 1H n.m.r. analysis. Catalytic hydrogenation of the tetraenols (10) is shown to proceed via initial isomerisation to the corresponding 6,6-dimethyl-B-norestra-1,3,5(10),9(11)-tetraen-17?-ols (26), followed by hydrogenation from the ?-side to give, exclusively, the 8?,9?-trienols (12).
Resumo:
Solid acid polymer electrolytes (SAPE) were synthesised using polyvinyl alcohol, potassium iodide and sulphuric acid in different molar ratios by solution cast technique. The temperature dependent nature of electrical conductivity and the impedance of the polymer electrolytes were determined along with the associated activation energy. The electrical conductivity at room temperature was found to be strongly depended on the amorphous nature of the polymers and H2SO4 concentration. The ac (100 Hz to 10 MHz) and dc conductivities of the polymer electrolytes with different H2SO4 concentrations were analyzed. A maximum dc conductivity of 1.05 x 10(-3) S cm(-1) has been achieved at ambient temperature for electrolytes containing 5 M H2SO4. The frequency and temperature dependent dielectric and electrical modulus properties of the SAPE were studied. The charge transport in the present polymer electrolyte was obtained using Wagner's polarization technique, which demonstrated the charge transport to be mainly due to ions. Using these solid acid polymer electrolytes novel Zn/SAPE/MnO2 solid state batteries were fabricated and their discharge capacity was calculated. An open circuit voltage of 1.758V was obtained for 5 M H2SO4 based Zn/SAPE/MnO2 battery. (C) 2010 Elsevier Ltd. All rights reserved.
Resumo:
Alkali aluminosilicate glasses prepared by the gel and the melt routes have been investigated by Si-29 and Al-27 MAS NMR spectroscopy. It is found that Al has a tetrahedral coordination in the gel glasses modified with equivalent proportions of alkalis unlike in a pure aluminosilicate glass where Al has both four and six coordinations. Silicon is present as Q4 units in all the 5M2O 5Al2O3 9OSiO2 ( M = Li, Na and K) gel glasses studied whereas it is present in Q2 or Q3 species in the lithium aluminosilicate glasses of compositions 40Li2O x Al2O3 (1-x)SiO2 (1 less-than-or-equal-to x less-than-or-equal-to 15) and xLi2O 10Al2O3 (1-x)SiO2 (20 less-than-or-equal-to x less-than-or-equal-to 40). The combination of Q2 and Q3 is also found in certain sodium aluminosilicate glasses, but they change to Q2 and Q1 as the concentration of SiO2 decreases.
Resumo:
A small-cluster approximation has been used to calculate the activation barriers for the d.c. conductivity in ionic glasses. The main emphasis of this approach is on the importance of the hitherto ignored polarization energy contribution to the total activation energy. For the first time it has been demonstrated that the d.c. conductivity activation energy can be calculated by considering ionic migration to a neighbouring vacancy in a smali cluster of ions consisting of face-sharing anion polyhedra. The activation energies from the model calculations have been compared with the experimental values in the case of highly modified lithium thioborate glasses.
Resumo:
Raman spectroscopic measurements in borate glasses have been reviewe. The review shows that the technique is useful in identifying the structural groups present in the borate on the basis of the Krogh-Moe hypothesis. Vitreous B2O3 and alkali borates are extensvvely studied and a satisfactory assignment of bands is possible by a careful consideration of the literature. A cation effect on the borate netwoork is observed. Availaable measurements on binary borates other than alkali borates and on ternary borates are limited and more work is required to identify the structural modifications that take place with composition. Mixed alkali effect is reported only lithium-caesium borade and shows the formation of non-bridging oxygens, destroying the six-membered rings when Li2O is replaced by Cs2O. Fast ionic glasses (alkali borates containing alkali halides) yield the same Raman spectra as the alkali borates, except when the alkali is a fluoride.
Resumo:
The details of the first total synthesis of a natural thapsane lg containing three contiguous quaternary carbon atoms, starting from cyclogeraniol (9) '5 described. The Claisen rearrangement of 9 with methoxypropene in the presence of a catalytic amount of propionic acid produced ketone 10. Rhodium acetate-catalyzed intramolecular cyclopropanation of a-diazo-&keto ester 12, obtained from 10 via 8-keto ester 8, furnished cyclopropyl keto ester 7. Lithium in liquid ammonia reductive cleavage of cyclopropyl compound 7 gave a 1:l mixture of hydrindanone 6 and keto1 13. Wittig methylenation of 6 furnished ester 21. Epoxidation of 21, followed by BF3-OEt2-catalyzed rearrangement of epoxide 23 afforded hemiacetal 25. Treatment of hemiacetal 25 with triethylsilane in trifluoroacetic acid furnished lactone 22, a degradation product of various thapsanes. Finally, DIBAH reduction of lactone 22 generated the thapsane
Resumo:
Influence of succinonitrile (SN) dynamics on ion transport in SN-lithium perchlorate (LiClO4) electrolytes is discussed here via dielectric relaxation spectroscopy. Dielectric relaxation spectroscopy (similar to 2 x 10(-3) Hz to 3 MHz) of SN and SN-LiClO4 was studied as a function of salt content (up to 7 mol % or 1 M) and temperature (-20 to +60 degrees C). Analyses of real and imaginary parts of permittivity convincingly reveal the influence Of trans gauche isomerism and solvent-salt association (solvation) effects on ion transport. The relaxation processes are highly dependent on the salt concentration and temperature. While pristine SN display only intrinsic dynamics (i.e., trans-gauche isomerism) which enhances with an increase in temperature, SN-LiClO4 electrolytes especially at high salt concentrations (similar to 0.04-1 M) show salt-induced relaxation processes. In the concentrated electrolytes, the intrinsic dynamics was observed to be a function of salt content, becoming faster with an increase in salt concentration. Deconvolution of the imaginary part of the permittivity spectra using Havriliak-Negami (HN) function show a relaxation process corresponding to the above phenomena. The permittivity data analyzed using HN and Kohlrausch-Williams-Watta (KWW) functions show non-Debye relaxation processes and enhancement in the trans phase (enhanced solvent dynamics) as a function of salt concentration and temperature.
Resumo:
Scheelite type solid electrolytes, Li(0.5)Ce(0.5-x)Ln(x)MoO(4) (x = 0 and 0.25, Ln = Pr, Sm) have been synthesized using a solid state method. Their structure and ionic conductivity (a) were obtained by single crystal X-ray diffraction and ac-impedance spectroscopy, respectively. X-ray diffraction studies reveal a space group of I4(1)/a for Li(0.5)Ce(0.5-x)Ln(x)MoO(4) (x = 0 and 0.25, Ln = Pr, Sm) scheelite compounds. The unsubstituted Li0.5Ce0.5MoO4 showed lithium ion conductivity similar to 10(-5)-10(-3) Omega(-1)cm(-1) in the temperature range of 300-700 degrees C (sigma = 2.5 x 10(-3) Omega(-1) cm(-1) at 700 degrees C). The substituted compounds show lower conductivity compared to the unsubstituted compound, with the magnitude of ionic conductivity being two (in the high temperature regime) to one order (in the low temperature regime) lower than the unsubstituted compound. Since these scheelite type structures show significant conductivity, the series of compounds could serve in high temperature lithium battery operations.
Resumo:
Birch reduction of 8,9-didehydroestradiol-17 beta 3-methyl ether 1 or 9(11)-didehydroestradiol-17 beta 3-methyl ether 2 followed by acid hydrolysis results in a mixture of 19-nortestosterone 8 and 19-nor-9 beta, 10 alpha-testosterone 9 in varying amounts. However, reduction of their acetates with sodium or lithium, tert-butyl alcohol in liquid ammonia and in the presence of aniline affords exclusively 19-nortestosterone. Similarly, 18a-homo-19-nortestosterone 12 is prepared from the acetate of 18a-homoestradiol-17 beta 3-methyl ether, 10.
Resumo:
We describe three different families of metal oxides, viz., (i) protonated layered perovskites, (ii) framework phosphates of NASICON and KTiOPO4 (KTP) structures and (iii) layered and three-dimensional oxides in the H-V-W-O system, synthesized by 'soft-chemical' routes involving respectively ion-exchange, redox deinteracalation and acid-leaching from appropriate parent oxides. Oxides of the first family, HyA2B3O10(A = La/Ca; B = Ti/Nb), exhibit variable Bronsted acidity and intercalation behaviour that depend on the interlayer structure. V2(PO4)3 prepared by oxidative deintercalation from Na3V2(PO4)3 is a new host material exhibiting reductive insertion of lithium/hydrogen, while K0.5Nb0.5 M0.5OPO4(M = Ti, V) are novel KTP-like materials exhibiting second harmonic generation of 1064 nm radiation. HxVxW1-xO3 for x = 0.125 and 0.33 possessing alpha-MoO3 and hexagonal WO3 structures, prepared by acid-leaching of LiVWO6, represent functionalized oxide materials exhibiting redox and acid-base intercalation reactivity.
Resumo:
Lithium phosphorus oxynitride (LiPON), the widely used solid electrolyte for thin film microbatteries, is not compatible with the ambient humid temperatures. The reasons for reduction in ionic conductivity of LiPON thin films from 2.8 x 10(-6) Scm(-1) to 9.9 x 10(-10) Scm(-1) when exposed to air are analyzed with the aid of AC impedance measurements, SEM, XPS and stylus profilometry. Initially, particulate-free film surfaces obtained soon after rf sputter deposition in N-2 ambient conditions becomes covered with microstructures, forming pores in the film when exposed to air. LiPON films are deposited on Ti coated silicon in addition to bare silicon, ruling out the possibility of stress-related rupturing from the LiPON/Si interface. The reduction of nitrogen, phosphorus, and increased presence of lithium, oxygen and carbon over the film surface lowers the ionic conductivity of LiPON films when exposed to air. (c) 2011 Elsevier B.V. All rights reserved.
Resumo:
Influence of dispersion of uniformly sized mono-functional and bi-functional (''Janus'') particles on ionic conductivity of novel ``soggy sand'' electrolytes and its implications on mechanical strength and lithium-ion battery performance are discussed here.
Resumo:
Lithium phosphorus oxynitride (LiPON) thin films as solid electrolytes were prepared by reactive radio frequency (rf) magnetron sputtering from Li3PO4 powder compact target. High deposition rates and ease of manufacturing powder target compared with conventional ceramic Li3PO4 targets offer flexibility in handling and reduce the cost associated. Rf power density varied from 1.7 Wcm(-2) to 3 Wcm(-2) and N-2 flow from 10 to 30 sccm for a fixed substrate to target distance of 4 cm for best ionic conductivity. The surface chemical analysis done by X-ray photoelectron spectroscopy showed incorporation of nitrogen into the film as both triply, NE and doubly. Nd coordinated form. With increased presence of NE, ionic conductivity of LiPON was found to be increasing. The electrochemical impedance spectroscopy of LiPON films confirmed an ionic conductivity of 1.1 x 10(-6) Scm(-1) for optimum rf power and N-2 flow conditions. (C) 2011 Elsevier B.V. All rights reserved.
Resumo:
A previous B-11 nuclear magnetic resonance investigation of glasses belonging to the B2S3-Li2S-LiI system had allowed the authors to determine the variation of the number of three and four coordinated boron atoms with composition. These results, in addition to the observation that vitreous B2S3 quite easily forms fibres during casting, have led us to propose structural hypotheses for B2S3 based glasses, which are supported by the present Raman spectroscopy study. For vitreous B2S3 the spectra were accounted for on the basis of the various types of BS3/2 triangles proposed by the model. Molecular orbital considerations allowed us to assign the most significant lines for the binary glasses by assuming that BS3/2 triangles (with or without nonbridging sulphur atoms) and BS4 tetrahedra were present. In the ternary system, lithium iodide has been found to interact slightly on the structural entities, altering their vibrational characteristics without fundamentally modifying their nature.
Resumo:
The influence of pH on the corrosion behaviour of two aluminium-lithium-copper-magnesium-zirconium (8090 and 2091) alloys was studied and compared with a standard aircraft alloy, 2014 (Al-4.4% Cu) and 99.9% pure Al. In constant exposure and potentiodynamic polarization studies conducted in 3.5% NaCl solution having different pH values, all the alloys exhibited high corrosion rates in acidic and alkaline environments, with a minimum in less hostile environments close to neutral pH. The pitting potentials for aluminium-lithium alloys were slightly lower than those for 2014 and pure Al. The effect of pH on the passive current density was also less for aluminium-lithium alloys.