Critical investigation of high performance spin-coated high-kappa titania thin films based MOS capacitor

We report the tunable dielectric constant of titania films with low leakage current density. Titanium dioxide (TiO2) films of three different thicknesses (36, 63 and 91 nm) were deposited by the consecutive steps of solution preparation, spin-coating, drying, and firing at different temperatures. The problem of poor adhesion between Si substrate and TiO2 insulating layer was resolved by using the plasma activation process. The surface roughness was found to increase with increasing thickness and annealing temperature. The electrical investigation was carried out using metal-oxide-semiconductor structure. The flat band voltage (V-FB), oxide trapped charge (Q(ot)), dielectric constant (kappa) and equivalent oxide thicknesses are calculated from capacitance-voltage (C-V) curves. The C-V characteristics indicate a thickness dependent dielectric constant. The dielectric constant increases from 31 to 78 as thickness increases from 36 to 91 nm. In addition to that the dielectric constant was found to be annealing temperature and frequency dependent. The films having thickness 91 nm and annealed at 600 A degrees C shows the low leakage current density. Our study provides a broad insight of the processing parameters towards the use of titania as high-kappa insulating layer, which might be useful in Si and polymer based flexible devices.

Long-period modulated structure and electric-field-induced structural transformation in Na0.5Bi0.5TiO3-based lead-free piezoelectrics

Na0.5Bi0.5TiO3- based lead-free piezoelectrics exhibiting giant piezostrain are technologically interesting materials for actuator applications. The lack of clarity with regard to the structure of the nonpolar phase of this system has hindered the understanding of the structural mechanism associated with the giant piezostrain and other related phenomena. In this paper, we have investigated the structure and field-induced phase transformation behavior of a model system (0.94 - x) Na0.5Bi0.5TiO3-0.06BaTiO(3)-xK(0.5)Na(0.5)NbO(3) (0.0 <= x <= 0.025). A detailed structural analysis using neutron powder diffraction revealed that the nonpolar phase is neither cubic nor a mixture of rhombohedral (R3c) and tetragonal (P4bm) phases as commonly reported in literature but exhibits a long-period modulated structure, which is most probably of the type root 2 x root 2 x n with n = 16. Our results suggest that the giant piezoelectric strain is associated with a field-induced phase transformation of the long-period modulated structure to rhombohedral R3c structure above a critical field. We also demonstrate that the giant piezostrain is lost if the system retains a fraction of the field-induced R3c phase. A possible correlation among depolarization temperature, giant piezostrain, and its electrical fatigue behavior has also been indicated.

On the issues of resolving a low melting combination as a definite eutectic or an elusive cocrystal: A critical evaluation

Cocrystals and eutectics are different yet related crystalline multi-component adducts with diverse applications in pharmaceutical and materials fields. Recently, they were shown to be alternate products of cocrystallization experiments. Whereas a cocrystal shows distinct diffraction, spectroscopic and thermal signatures as compared to parent components, the hallmark of a eutectic is its low melting nature. However, in certain cases, there can be a problem when one resorts to design a cocrystal and assess its formation vis-A -vis a eutectic. In the absence of a gold standard method to make a cocrystal, it is often difficult to judge how exhaustive should the cocrystallization trials be to ensure the accomplishment of a desired/putative cocrystal. Further, a cocrystal can manifest with intermolecular interactions and/or crystal structure similar to that of its parent compounds such that the conventional diffraction and spectroscopic techniques will be of little help to conclusively infer the formation of cocrystal in the lack of single crystals. Such situations combined with low melting behavior of a combination brings the complication of resolving the combination as a cocrystal or eutectic since now both the adducts share common features. Based on the curious case of Caffeine-Benzoic acid combination, this study aims to unfold the intricate issues related to the design, formation and characterization of cocrystals and eutectics for a way forward. The utility of heteronuclear seeding methodology in establishing a given combination as a cocrystal-forming one or a eutectic-forming one in four known systems is appraised.