Measurement of Gibbs energy of formation of Ca2PbO4 using a solid-state cell with three electrodes

Phase relations in the system Ca-Pb-O at 1100 K have been determined by equilibrating 18 compositions in the ternary and identifying the phases present in quenched samples by X-ray diffraction and energy dispersive X-ray analysis (EDX). Only one ternary compound Ca2PbO4 was found to be present. The compound coexists with CaO and PbO. The intermetallic compounds Ca2Pb, Ca5Pb3 and CaPb and liquid alloys are in equilibrium with CaO. The standard Gibbs energies of formation of Ca2PbO4 (880 - 1100 K) and Pb3O4 (770 - 910 K) were determined using solid-state cells based on yttria-stabilized zirconia as the solid electrolyte. Pure oxygen gas at 0.1 MPa was used as the reference electrode. For measurements on Ca2PbO4, a novel cell design with three electrodes in series, separated by solid electrolyte membranes, was used to avoid polarization of the electrode containing three solid phases. Two three-phase electrodes were used. The first absorbs the electrochemical flux of oxygen from the reference electrode to the measuring electrode. The other three-phase electrode, which is unaffected by the oxygen flux through the solid electrolyte, is used for electromotive force (EMF) measurement. The results from EMF studies were cross-checked using thermogravimetry (TG) under controlled oxygen partial pressures. The stability of Pb3O4 was investigated using a conventional solid-state cell with RuO2 electrodes. The results can be summarized by the following equations: 2CaO + PbO +1/2O(2) --> Ca2PbO4 Delta(r)G degrees/J mol(-1) = (- 128340 + 93.21 T/K) +/- 200 3PbO + 1/2O(2) --> Pb3O4 Delta(r)G degrees/J mol(-1) = (- 70060 + 77.5 T/K) +/- 150

Microstructure evolution during solidification of DRMMCs (discontinuously reinforced metal matrix composites): State of art

Distribution of particle reinforcements in cast composites is determined by the morphology of the solidification front. Interestingly, during solidification, the morphology of the interface is intrinsically affected by the presence of dispersed reinforcements. Thus the dispersoid distribution and length scale of matrix microstructure is a result of the interplay between these two. A proper combination of material and process parameters can be used to obtain composites with tailored microstructures. This requires the generation of a broad data base and optimization of the complete solidification process. The length scale of soldification microtructure has a large influence on the mechanical properties of the composites. This presentation addresses the concept of a particle distribution map which can help in predicting particle distribution under different solidification conditions Future research directions have also been indicated.

New La2CuO4 derivatives La(2-2x)Sr(2x)Cu(1-x)M(x)O(4) (M=Ti, Mn, Fe, or Ru): A study of linear Cu-O-M electronic interaction in two dimensions

Oxides of the general formula La2-2xSr2xCu1-xII,M(x)(IV)O(4) (M = Ti, Mn, Fe, or Ru), crystallizing in the tetragonal K,NIF, structure, have been synthesized. For M=Ti, only the x=0,5 member could be prepared, while for M=Mn and Fe, the composition range is 0 Cu(III)-O-Fe(III) valence degeneracy. Increasing the strontium content at the expense of lanthanum in La2-2xSr2xCu1-xFexO4 for x less than or equal to 0.20 renders the samples metallic but not superconducting. (C) 1997 Academic Press.

Spin state and exchange in the quasi-one-dimensional antiferromagnet KFeS2

We report the optical spectra and single crystal magnetic susceptibility of the one-dimensional antiferromagnet KFeS2. Measurements have been carried out to ascertain the spin state of Fe3+ and the nature of the magnetic interactions in this compound. The optical spectra and magnetic susceptibility could be consistently interpreted using a S = 1/2 spin ground state for the Fe3+ ion. The features in the optical spectra have been assigned to transitions within the d-electron manifold of the Fe3+ ion, and analysed in the strong field limit of the ligand field theory. The high temperature isotropic magnetic susceptibility is typical of a low-dimensional system and exhibits a broad maximum at similar to 565 K. The susceptibility shows a well defined transition to a three dimensionally ordered antiferromagnetic state at T-N = 250 K. The intra and interchain exchange constants, J and J', have been evaluated from the experimental susceptibilities using the relationship between these quantities, and chi(max), T-max, and T-N for a spin 1/2 one-dimensional chain. The values are J = -440.71 K, and J' = 53.94 K. Using these values of J and J', the susceptibility of a spin 1/2 Heisenberg chain was calculated. A non-interacting spin wave model was used below T-N. The susceptibility in the paramagnetic region was calculated from the theoretical curves for an infinite S = 1/2 chain. The calculated susceptibility compares well with the experimental data of KFeS2. Further support for a one-dimensional spin 1/2 model comes from the fact that the calculated perpendicular susceptibility at 0K (2.75 x 10(-4) emu/mol) evaluated considering the zero point reduction in magnetization from spin wave theory is close to the projected value (2.7 x 10(-4) emu/mol) obtained from the experimental data.

Theoretical analysis of x-ray-absorption near-edge fine structure at the O and metal K edges of LaFeO3 and LaCoO3

We present experimental x-ray-absorption spectra at the oxygen and 3d transition-metal K edges of LaFeO3 and LaCoO3. We interpret the experimental results in terms of detailed theoretical calculations based on multiple-scattering theory. Along with providing an understanding of the origin of various experimental features, we investigate the effects of structural distortions and the core-hole potential in determining the experimental spectral shape. The results indicate that the core-hole potential as well as many-body effects within the valence electrons do not have any strong effect on the spectra suggesting that the spectral features can be directly interpreted in terms of the electronic structure of such compounds.

X-ray photoelectron spectroscopic investigations of Cu-Ni, Au-Ag, Ni-Pd, and Cu-Pd bimetallic clusters

Core-level binding energies of the component metals in bimetallic clusters of various compositions in the Ni-Cu, Au-Ag, Ni-Pd, and Cu-Pd systems have been measured as functions of coverage or cluster size, after having characterized the clusters with respect to sizes and compositions. The core-level binding energy shifts, relative to the bulk metals, at large coverages or cluster size, Delta E(a), are found to be identical to those of bulk alloys. By substracting the Delta E(a) values from the observed binding energy shifts, Delta E, we obtain the shifts, Delta E(c), due to cluster size. The Delta E(c) values in all the alloy systems increase with the decrease in cluster size. These results establish the additivity of the binding energy shifts due to alloying and cluster size effects in bimetallic clusters.

Magnetocaloric effect in La1-xSrxCoO3 (0.05 <= x <= 0.40)

We report studies of magnetocaloric effect in lanthanum cobaltate doped with different Sr-concentrations, La1-xSrxCoO3 (0.05 less than or equal to x less than or equal to 0.4). The study has revealed that La0.6Sr0.4CoO3, which exhibits a moderately large value of maximum entropy change of about 1.45 J/kg/K in 1.5 T DC-fieid around its Curie temperature (of 235 K), can be used as an active magnetic refrigerant (AMR) material at similar to 2.35 K. (C) 1999 Elsevier Science B.V. Al rights reserved.

Magneto-structural correlation in (mu-alkoxo/hydroxo)(mu-carboxylato)dicopper(II) systems: Synthesis, X-ray structure and magnetic properties of aquo(mu-hydroxo) (mu-arylcarboxylato)bis(N,N,N ',N '-tetramethylethane-1,2-diamine)dicopper(II) diperchlorate

Asymmetrically dibridged dicopper(II) complexes, [Cu-2(OH)(O2CC6H4-p-Me)(tmen)(2)(H2O)](ClO4)(2) (1) and [Cu-2(OH)(O2CC6H4-p-OMe)(tmen)(2)(H2O)](ClO4)(2) (2) (tmen = N,N,N',N'-tetramethylethane-1,2-diamine), were prepared and structurally characterized. Complex 1 crystallizes in the monoclinic space group P2(1)/a with a = 17.718(2), b = 9.869(1), c = 19.677(2) Angstrom, beta = 115.16(1)degrees, V = 3114.3(6) Angstrom(3) and Z = 4. The structure was refined to R(wR(2)) = 0.067(0.178). Complex 2 crystallizes in the monoclinic space group P2(1)/a with a = 17.695(3), b = 9.574(4), c = 20.104(2) Angstrom, beta = 114.18(1)degrees, V = 3107(1) Angstrom(3) and Z = 4. The final residuals are R(wR(2)) = 0.067(0.182). The complexes have a [Cu-2(mu-OH)(mu-OH)(mu-O2CAr)](2+) core with tmen Ligands occupying the terminal sites of the core. In addition, one copper is axially bound to a water molecule. The Cu ... Cu distances and the Cu-OH Cu angles in the core are 3.394(1) Angstrom, 124.4(2)degrees for 1 and 3.374(1) Angstrom, 123.3(3)degrees for 2. The complexes show axial X-band EPR spectral features in methanol glass at 77 K giving g(perpendicular to) = 2.02, g(parallel to) = 2.3 (A(parallel to) = 165 x 10(-4) cm(-1)) and a visible band near similar to 630 nm in methanol. The complexes are weakly antiferromagnetic. A theoretical fit of the magnetic susceptibility data in the temperature range 40-295 K gives -J = 10 cm(-1), g = 2.05 for 1 and -J = 10 cm(-1), g = 2.0 for 2. Plots of -2J versus the Cu-OH-Cu angle (phi) in this class of asymmetrically dibridged dicopper(II) complexes having d(x2-y2)-d(x2-y2) magnetic orbitals show a linear magneto-structural correlation: -2J(cm(-1)) = 11.48 phi(deg) - 1373.

Role of Hetero-Halogen (F center dot center dot center dot X, X = Cl, Br, and I) or Homo-Halogen (X center dot center dot center dot X, X = F, Cl, Br, and I) Interactions in Substituted Benzanilides

A series of halogen-substituted benzanilides have been synthesized and characterized, and crystallization studies directed toward generation of polymorphs have been performed to delineate the importance of interactions involving halogens. The effect of halogen substitution on the molecular conformation and supramolecular packing has been investigated. The N-H center dot center dot center dot O H-bond is a key structure-directing element acting in conjunction with C-H center dot center dot center dot O and C-H center dot center dot center dot pi interactions. In addition, it is of importance to note that organic fluorine prefers Type I F center dot center dot center dot F contacts, whereas Cl, Br, and I prefer Type II contacts. Hetero-halogen center dot center dot center dot halogen interactions on the other hand are predominately of Type II geometry, and this is due to the greater polarizability of the electron density associated with the heavier halogens. It is of importance to evaluate the contributing role of these interactions in crystal structure packing and the co-operativity associated with such interactions in the solid state.

Structural phase transitions in Bi2V1-xGexO5.5-x/2 (x=0.2, 0.4, and 0.6) single crystals: X-ray crystallographic study

Single crystals of Bi2V1-xGexO5.5-x/2 (x = 0.2, 0.4, and 0.6) were grown by slow cooling of melts. Bismuth vanadate transforms from an orthorhombic to a tetragonal structure and subsequently to an orthorhombic system when the Ge4+ concentration was varied from x = 0.2 to x = 0.6. All of these compositions crystallized in polar space groups (Aba2, F4mm, and Fmm2 for x = 0.2, 0.4, and 0.6, respectively). The structures were fully determined by single crystal X-ray diffraction studies, (C) 1999 Elsevier Science Ltd.

X-Codes: A Low Complexity Full-Rate High-Diversity Achieving Precoder for TDD MIMO Systems

We consider a time division duplex multiple-input multiple-output (nt × nr MIMO). Using channel state information (CSI) at the transmitter, singular value decomposition (SVD) of the channel matrix is performed. This transforms the MIMO channel into parallel subchannels, but has a low overall diversity order. Hence, we propose X-Codes which achieve a higher diversity order by pairing the subchannels, prior to SVD preceding. In particular, each pair of information symbols is encoded by a fixed 2 × 2 real rotation matrix. X-Codes can be decoded using nr very low complexity two-dimensional real sphere decoders. Error probability analysis for X-Codes enables us to choose the optimal pairing and the optimal rotation angle for each pair. Finally, we show that our new scheme outperforms other low complexity precoding schemes.

Crystal structure and thermal and electrical properties of the perovskite solid solution Nd1-xSrxFeO3-delta (0 <= x <= 0.4)

The crystal structure, thermal expansion and electrical conductivity of strontium-doped neodymium ferrite (Nd1-xSrxFeO3-delta where 0less than or equal toxless than or equal to0.4) were investigated. All compositions had the GdFeO3-type orthorhombic perovskite structure. The lattice parameters were determined at room temperature by X-ray powder diffraction. The orthorhombic distortion decreases with increasing Sr substitution. The pseudocubic lattice parameter shows a minimum at x=0.3. The thermal expansion curves for x=0.2-0.4 displayed rapid increase in slope at higher temperatures. The electrical conductivity increased with Sr content and temperature. The calculated activation energies for electrical conduction decreased with increasing x. The electrical conductivity can be described by the small polaron hopping mechanism. The charge compensation for divalent ion on the A-site is provided by the formation of Fe4+ ions on the B site and vacancies on the oxygen sublattice. The results indicate two defect domains: for low values of x, the predominant defect is Fe4+ ions, whereas for higher values of x, oxygen vacancies dominate. (C) 2002 Elsevier Science B.V. All rights reserved.

Difference in spin state and covalence between La1-xSrxCoO3 and La2-xSrxLi0.5Co0.5O4

We present a comparative study of the spin states and electronic properties of La1-xSrxCoO3 and La2-xSrxLi0.5Co0.5O4 using X-ray absorption near-edge structure spectroscopy at both the O-K and Co-L-2.3 thresholds. In the La2-xSrxLi0.5Co0.5O4 system the CoO6 octahedra are isolated, the holes induced by Sr doping are trapped in the isolated Co(IV)O-6 octahedra, and a low-spin state is found for the Co ions, which does not change upon Sr doping. In the La1-xSrxCoO3 system, the interconnected CoO6 octahedra, with a 180degrees Co-O-Co bond angle, give rise to a transition from low-spin to intermediate-spin state with a ferromagnetic alignment of the Co spins. The double-exchange, ferromagnetic coupling between Co ions mediated by the 180degrees bond angle is responsible for suppressing the low spin-state. We find that the branching ratio of spectral intensities at the L-2 and L-3 thresholds in the Co-L-2.3 X-ray absorption spectra is sensitive to the spin state of the Co ions allowing its direct spectroscopic determination. (C) 2002 Published by Elsevier Science B.V.

Magnetic ordering in La0.85Pb0.15Mn1-xTixO3 (0 <= x <= 0.15)

Powder-neutron diffraction study has been carried out at 300 and 10 K in La0.85Pb0.15Mn1-xTixO3 (0 less than or equal to x less than or equal to 0.15). The samples crystallize in the rhombohedral phase. The magnetic moment reduces nonlinearly with increase in Ti and correlates well with the reported behavior of T-C. The change in the moment and T-C could not be related to change in the one electron bandwidth, W. The reduction is attributed to the effect of dilution and thereby reducing the double exchange ferromagnetic interaction. (C) 2002 Elsevier Science B.V. All rights reserved.

Mossbauer study of La1-xCaxMn1-y (57)FeyO(3) with x = 0, 0.25; y=0.01

Temperature dependent Mossbauer measurements are done on the samples of La1- xCaxMn1-y (FeyO3)-Fe-57 with x=0 and 0.25, and y=0.01. With decreasing temperature, the specimen with x=0.25 shows a paramagnetic to ferromagnetic transition around 175 K. In the specimen x=0.0, the temperature dependence of both the center shift (delta) and the recoilless fraction (f) can be fitted very well with the Debye theory with a theta(D)=320+/-50 K. But for the specimens with x=0.25, f and delta show distinct deviations from the Debye behavior in the temperature range in which the resistivity shows a sharp decrease. Dips observed in both the f and delta around the transition temperature suggest that the Jahn-Teller distortion observed in these systems is dynamic in nature.