Studies on the variations in compression strengths of graphite powders bearing glass-epoxy composites exposed to humid conditions

The moisture absorption and changes in compression strengths in glass-epoxy (G-E composites without and with discrete quantities of graphite powders introduced into the resin mix prior to its spreading on specific glass fabric (layers) during the lay-up (stacking) sequence forms the subject matter of this report. The results point to higher moisture absorption for graphite bearing specimens. The strengths of graphite-free coupons show a continuous decrease, while the filler bearing ones show an initial rise followed by a drop for larger exposure times. Scanning Fractographic features were examined for an understanding of the process. The observations were explained invoking the effect of matrix plasticizing and the role of interfacial regions.

Effect of porosity on the indentation behaviour of nanoporous alumina films

Anodising aluminium in an acid electrolyte results in a porous alumina film. The pores are uniformly distributed and their structure can be controlled by varying the anodising parameters. In this study, the pore structure of the anodic alumina films is varied systematically by varying the anodising time and a subsequent pore widening chemical etch. The indentation behaviour of the resulting film is studied using a depth sensing nanoindenter. The hardness of the films was found to be decreasing with decreasing solid area fraction. Understanding the deformation behaviour of nanoporous alumina would help tailoring the mechanical properties by tuning the geometry.

A template-free, combustion-chemical route to macroporous nickel monoliths displaying a hierarchy of pore sizes

Recently, we demonstrated a very general route to monolithic macroporous materials prepared without the use of templates (Rajamathi et al. J. Mater. Chem. 2001, 11, 2489). The route involves finding a precursor containing two metals, A and B, whose oxides are largely immiscible. Firing of the precursor followed by suitable sintering results in a monolith from which one of the oxide phases can be chemically leached out to yield a macroporous mass of the other oxide phase. The metals A and B that we employed in the demonstration were Ni and Zn. From the NiO-ZnO monolith that was obtained by decomposing the precursor, ZnO could be leached out at high pH to yield macroporous NiO. In the present work, we show that combustion-chemical (also called self-propagating) decomposition of a mixture of Ni and Zn nitrates with urea as a fuel yields an intimate mixture of the oxides that can be sintered and leached with alkali to form a macroporous NiO monolith. The new process that we present here thereby avoids the need for a crystalline single-source precursor. A novel and unanticipated aspect of the present work is that the combination of high temperatures and rapid quenching associated with combustion synthesis results in an intimate mixture of wurtzite ZnO and the metastable rock-salt Ni1-xZnxO where x is about 0.3. Leaching this monolith with alkali gives a macroporous mass of rock-salt Ni1-xZnxO, which upon reduction in H-2/Ar forms macroporous Ni and ZnO. There are thus two stages in the process that lead to two modes of pore formation. The first is associated with leaching of ZnO by alkali. The second is associated with the reduction of porous Ni1-xZnxO to give porous Ni and ZnO.

Embrittlement of a bulk metallic glass due to low-temperature annealing

Embrittlement of a bulk La-based metallic glass due to isothermal and isochronal annealing below the T-g was investigated. Results show that the impact toughness decreases with increasing annealing time or temperature, accompanied by a change in fracture morphology. Reasons for this are discussed in terms of structural relaxation. (C) 2002 Acta Materialia Inc. Published by Elsevier Science Ltd. All rights reserved.

Evolution of ferroelectric SrBi2Nb2O9 phase in the Li2B4O7-SrO-Bi2O3-Nb2O5 glass system

Glasses of various compositions in the system (100 - x)Li-2 B-4 O-7 - x (SrO-Bi2O3-Nb2O5) (10 less than or equal to x less than or equal to 60) (in molar ratio) were prepared via a conventional melt-quenching technique. The glassy nature of the as-quenched samples was established by Differential Thermal Analyses (DTA). X-ray powder diffraction (XRD) and Transmission Electron Microscopic (TEM) studies confirmed the amorphous nature of the as quenched and crystallinity in the heat-treated samples. The formation of nanocrystalline layered perovskite SrBi2Nb2O9 (SBN) phase, in the samples heat-treated at temperatures higher than 550degreesC, through an intermediate fluorite phase in the LBO glass matrix was confirmed by both the XRD and High Resolution Transmission Electron Microscopy (HRTEM). The samples that were heat-treated at two different temperatures, 550 and 625degreesC, (containing 0.35 and 0.47 mum sized SBN crystallites) exhibited broad dielectric anomalies in the vicinity of ferroelectric to paraelectric transition temperature of the parent SBN ceramics. A downward shift in the phase transition temperature was observed with decreasing crystallite size of SBN. The observation of pyroelectric and ferroelectric properties for the present samples confirmed their polar nature.

A chemical approach to understand fragilities of glass-forming liquids

Fragility is viewed as a measure of the loss of rigidity of a glass structure above its glass transition temperature. It is attributed to the weakness of directional bonding and to the presence of a high density of low-energy configurational states. An a priori fragility function of electronegativities and bond distances is proposed which quite remarkably reproduces the entire range of reported fragilities and demonstrates that the fragility of a melt is indeed encrypted in the chemistry of the parent material. It has also been shown that the use of fragility-modified activation barriers in the Arrhenius function account for the whole gamut of viscosity behavior of liquids. It is shown that fragility can be a universal scaling parameter to collapse all viscosity curves on to a master plot.

Pyroelectric, ferroelectric and optical properties of glass nanocomposite: Lithium borate-bismuth tungstate

Glass nanocomposites in the system (1-x)Li2B4O7-xBi(2)WO(6) (0 less than or equal to x less than or equal to 0.35, in molar ratio) were fabricated by splat quenching technique. The as-quenched samples were X-ray amorphous. Differential Thermal Analyses (DTA) confirmed their glassy nature. The composites on heat-treatment at 720 K yielded monophasic crystalline bismuth tungstate in lithium borate glass matrix. The average size and the spherical nature of the dispersed crystallites were assessed via High Resolution Transmission Electron Microscopy (HRTEM). The dielectric constants (epsilon(r)) of both the as-quenched and post heat-treated composites were found to increase with increase in x (bismuth tungstate content) at all the frequencies (100 Hz-40 MHz) in the temperature range 300 K-870 K. While the dielectric loss (D) decreased with increasing x. The pyroelectric coefficients of the as-quenched (consisting 20 nm sized crystallites) and 720 K heat-treated sample (x = 0.3) were determined as a function of temperature (300 K-873 K) and the values obtained at room temperature were 20 and 60 muC/m(2) K respectively. The as-quenched and heat-treated (720 K) glass nanocomposites exhibited ferroelectric (P Vs E) hysteresis loops. The remnant polarization and coercive field of the heat-treated glass nanocomposite at 300 K were respectively 2.597 muC/cm(2) and 543 V/cm. These glass nanocomposites were birefringent in the 300-873 K temperature range.

Reactivity ratios for the oxidative copolymerizations of indene with methyl methacrylate and methacrylonitrile

The copolyperoxides of indene with methyl methacrylate and methacrylonitrile have been synthesized by the free-radical-initiated oxidative copolymerization of indene and the monomers. The compositions of copolyperoxides, obtained from H-1 and C-13 NMR spectra, have been utilized to determine the reactivity ratios. The reactivity ratios indicate that the copolyperoxides contain a large proportion of the indene units in random placement. Thermal degradation studies of the copolyperoxides by differential scanning calorimetry and electron-impact mass spectroscopy support alternating peroxide units in the copolyperoxide chain. The energy of activation for thermal degradation suggests that the degradation is controlled by the dissociation of the peroxide (-O-O-) bonds in the copolyperoxide chain. The flexibility of copolyperoxide in terms of glass transition temperature (T-g) has also been examined. (C) 2002 Elsevier Science Ltd. All rights reserved.

Compressive behavior and fracture features of rubber bearing glass-epoxy composites exposed to aqueous media

Epoxy systems containing HTBN rubber material and reinforced with E-glass fibres, exposed to a fixed time duration in three separate media were subjected to compressive mode of deformation. The yield stress and fractographic features noted on the compression failed samples are reported in this work. The experiment reveals that the seawater exposed sample exhibits a drop in strength compared to dry (unexposed) sample. This kind of drop is maintained if the media is changed from seawater to distilled water. When HCl is included in seawater. the experiment shows a small rise in strength value. These changes have been attributed to various factors like medium ingress into samples assisting interface failure, the larger-sized Cl- influencing the extent of diffusion of medium into system and finally their participation in the deformation phenomena. The fractographic features reveal interface separations that show either scattered debris or a cleaner surface or display a whitish-coated matrix region depending on whether the tests are done on unexposed samples or on ones following the immersion in the media.

Dielectric anomaly in strontium borate-bismuth vanadate glass nanocomposite

Transparent glass nanocomposites in the pseudo binary system (100 - x) SrB4O7 (SBO)-x Bi2VO5.5 (BiV) (0 less than or equal to n less than or equal to 70) were prepared by the splat quenching technique. The nano-crystallization of bismuth vanadate (BiV) in 50 SBO-50 BiV (in mol%) glass composite has been demonstrated. These were characterized for their structural, thermal and dielectric properties. As-quenched composites under study have been confirmed to be amorphous by X-ray powder diffraction (XRD) studies. The glass transition temperature (T-g) and crystallization temperatures (T-er) were determined using differential thermal analyses (DTA), High resolution transmission electron microscopic (HRTEM) studies carried out on heat-treated samples reveal the presence of spherical nanosize crystallites of Bi2VO5.5 (BiV) dispersed in the glassy matrix of SrB4O7 (SSO). The dielectric constant (epsilon (r)) and the dielectric loss (D) measurements were carried out on the as-quenched and heat-treated glass nanocomposite samples in the frequency range 100 Hz-10 MHz. The as-quenched and the heat-treated at two different temperatures (720 and 820 K) samples exhibited broad dielectric anomalies in the vicinity of the ferroelectric-to-paraelectric transition temperature of the parent BiV ceramics. The Curie-Weiss law was found to be valid at a temperature above the transition temperature, establishing the diffused nature of the transition. (C) 2001 Elsevier Science Ltd. All rights reserved.

Effect of absorption in aqueous and hygrothermal media on the compressive properties of glass fiber reinforced syntactic foam

Absorption due to immersion in aqueous media consisting of either saline or seawater or due to exposure to water vapor conditions and the attendant effect on the compressive properties of syntactic foam reinforced with E-glass fibers in the form of chopped strands were studied. Whereas the compressive strength decreased in samples exposed to water vapor, the saline or seawater immersed samples showed increase when compared to the dry sample. The decrease in strength in the vapor-exposed case is ascribed to higher absorption of water and to debonding and damaged features for interfaces. The enhancement of strength values for the samples immersed in saltish media is traced to the larger size of the chloride ion and resultant changes in the stress state around the fiber-bearing regions. Recourse to an analysis of scanning electron microscopic pictures of the compression-failed samples is taken to explain the observed trends.

Time Evolution of the Microstructure of VO2(B) Films Deposited on Glass by MOCVD

Thin films of VO2(B), a metastable polymorph of vanadium dioxide, have been grown on glass by low-pressure metalorganic chemical vapor deposition (MOCVD). The films grown for 90 minutes have atypical microstructure, comprising micrometer-sized, island-like entities made up of numerous small, single-crystalline platelets (≅1 μm) emerging orthogonally from larger ones at the center. Microstructure evolution as a function of deposition time has been examined by X-ray diffraction, scanning electron microscopy, and transmission electron microscopy. The metastable VO2(B) transforms to the stable rutile (R) phase at 550°C in inert ambient, which on cooling convert reversibly to M phase. Electron microscopy shows that annealing leads to the disintegration of the VO2(B) platelets into small crystallites of the rutile phase VO2(R), although the platelet morphology is retained. The magnitude of the jump in resistance at the semiconductor-to-metal, VO2(M)→VO2(R) phase transition depends on the arrangement of polycrystalline platelets in the films.

Structural Relaxation and Crystallization in a Pd40Cu30Ni10P20 Bulk Metallic Glass

The stability of a Pd40Cu30Ni10P20 bulk metallic glass (BMG) against structural relaxation is investigated by isothermal and isochronal annealing heat treatments below and above its glass transition temperature, Tg, for varying periods. Differential scanning calorimetry (DSC) of the annealed samples shows an excess endotherm at Tg, irrespective of the annealing temperature. This recovery peak evolves exponentially with annealing time and is due to the destruction of anneal-induced compositional short range ordering. The alloy exhibits a high resistance to crystallization on annealing below Tg and complex Pd- and Ni-phosphides evolve on annealing above Tg.