Synthesis of ZnO Nanoneedles on Flexible Polymer Substrates at Room Temperature by Activated Reactive Evaporation

ZnO nanoneedles were successfully deposited on flexible polymer substrates at room temperature by activated reactive evaporation. Neither a catalyst nor a template was employed in this synthesis. These synthesized needles measured 500 - 600 nm in length and its diameter varied from 30 - 15 nm from the base to the tip. The single-crystalline nature of the nanoneedle was observed by high-resolution transmission electron microscopy studies. The Raman studies on these nanoneedles had shown that they are oxygen deficient in nature. A possible growth mechanism has been proposed here, in which the nanoneedles nucleate and grow in the gas phase by vapor-solid mechanism.

Fabrication and mechanisms of densification of ZrB2-based ultra high temperature ceramics by reactive hot pressing

Dense ZrB2-SiC (25-30 vol%) composites have been produced by reactive hot pressing using stoichiometric Zr, B4C, C and Si powder mixtures with and without Ni addition at 40 MPa, 1600 degrees C for 60 min. Nickel, a common additive to promote densification, is shown not to be essential; the presence of an ultra-fine microstructure containing a transient plastic ZrC phase is suggested to play a key role at low temperatures, while a transient liquid phase may be responsible at temperatures above 1350 degrees C. Hot Pressing of non-stoichiometric mixture of Zr, B4C and Si at 40 MPa, 1600 degrees C for 30 min resulted in ZrB2-ZrCx-SiC (15 vol%) composites of similar to 98% RD.

Soft matter lithium salt electrolytes: ion conduction and application to rechargeable batteries

Soft matter provides diverse opportunities for the development of electrolytes for all solid state lithium batteries. Here we review soft matter solid electrolytes for lithium batteriesthat are primarily obtained starting from liquid electrolytic systems. This concept of solid electrolyte synthesis from liquid is significantly different from prevalent approaches. The novelty of our approach is discussed in the light of various fundamental issues and in relation to its application to rechargeable lithium batteries.

Influence of Temperature and High Electric Field on Power Consumption by Piezoelectric Actuated Integrated Structure

The influence of electric field and temperature on power consumption of piezoelectric actuated integrated structure is studied by using a single degree of freedom mass-spring-damper system model coupled with a piezoactuator. The material lead zirconate titanate, is considered as it is capable of producing relatively high strains (e.g., 3000 mu epsilon). Actuators are often subject to high electric fields to increase the induced strain produced, resulting in field dependant piezoelectric coefficient d(31), dielectric coefficient epsilon(33) and dissipation factor delta. Piezostructures are also likely to be used across a wide range of temperatures in aerospace and undersea operations. Again, the piezoelectric properties can vary with temperature. Recent experimental studies by physics researchers have looked at the effect of high electric field and temperature on piezoelectric properties. These properties are used together with an impedance based power consumption model. Results show that including the nonlinear variation of dielectric permittivity and dissipation factor with electric field is important. Temperature dependence of the dielectric constant also should be considered.

Preparation temperature effect on the synthesis of various carbon nanostructures

Various carbon nanostructures (CNs) have been prepared by a simple deposition technique based on the pyrolysis of a new carbon source material tetrahydrofuran (THF) mixed with ferrocene using quartz tube reactor in the temperature range 700-1100 degrees C. A detailed study of how the synthesis parameter such as growth temperature affects the morphology of the carbon nanostructures is presented. The obtained CNs are investigated by scanning electron microscope (SEM), X-ray diffraction (XRD), electron dispersive scattering (EDS)thermogravimetry analysis (TGA), Raman and transmission electron microscope (TEM). It is observed that at 700 degrees C. normal CNTs are formed. Iron filled multi-walled carbon nanotubes (MWCNTs) and carbon nanoribbons (CNRs) are formed at 950 degrees C. Magnetic characterization of iron filled MWCNTs and CNRs studied at 300 K by superconducting quantum interference device (SQUID) reveals that these nanostructures have an enhanced coercivity (Hc = 1049 Oe) higher than that of bulk Fe. The large shape anisotropy of MWCNTs, which act on the encapsulated material (Fe), is attributed for the contribution of the higher coercivity. Coiled carbon nanotubes (CCNTs) were obtained as main products in large quantities at temperature 1100 degrees C.

Cu2+-induced room temperature hydrogen release from ammonia borane

Mechanical stirring of ammonia borane with CuCl2 in the solid state resulted in the release of hydrogen at room temperature through the intermediacy of [NH4](+)[BCl4](-).

Temperature independent mixing rules to correlate the solubilities of antibiotics and anti-inflammatory drugs in SCCO2

The accurate experimental determination of the solubilities of antibiotics and anti-inflammatory drugs in supercritical fluids (SCFs) and correlations are essential for the development of supercritical technologies for the pharmaceuticals industry. In this work, the solubilities of penicillinG, penicillinV, flurbiprofen, ketoprofen, naproxen, ibuprofen, aspirin and diflunisal in supercritical carbon dioxide (SCCO2) were correlated using Peng-Robinson equation of state (PR EOS) with the modified Kwak and Mansoori mixing rules (mKM) and with Bartle model. The ability of mKM rules was compared against the conventional mixing rules of van der Waals in correlating the solubilities. In the present model, vapor pressure was considered as an adjustable parameter along with binary interactions parameters. In the proposed model, the constants used in the mixing rule, and vapor pressure expression coefficients are temperature independent. The optimization of these constants with experimental data gives binary interaction parameters along with vapor pressure correlations. Sublimation enthalpies were estimated with both the models compared with literature reported experimental values.

Transition from radiatively inefficient to cooling dominated phase in two temperature accretion disks around black holes

We investigate the transition of a radiatively inefficient phase of a viscous two temperature accreting flow to a cooling dominated phase and vice versa around black holes. Based on a global sub-Keplerian accretion disk model in steady state, including explicit cooling processes self-consistently, we show that general advective accretion flow passes through various phases during its infall towards a black hole. Bremsstrahlung, synchrotron and inverse Comptonization of soft photons are considered as possible cooling mechanisms. Hence the flow governs a much lower electron temperature similar to 10(8) - 10(9.5) K compared to the hot protons of temperature similar to 10(10.2) - 10(11.8) K in the range of the accretion rate in Eddington units 0.01 less than or simiar to (M) over dot less than or similar to 100. Therefore, the solutions may potentially explain the hard X-rays and the gamma-rays emitted from AGNs and X-ray binaries. We finally compare the solutions for two different regimes of viscosity and conclude that a weakly viscous flow is expected to be cooling dominated compared to its highly viscous counterpart which is radiatively inefficient. The flow is successfully able to reproduce the observed minosities of the under-fed AGNs and quasars (e.g. Sgr A*), ultra-luminous X-ray sources (e.g. SS433), as well as the highly luminous AGNs and ultra-luminous quasars (e.g. PKS 0743-67) at different combinations of the mass accretion rate and ratio of specific heats.

Two temperature viscous accretion flows around rotating black holes: Description of under-fed systems to ultra-luminous X-ray sources

We discuss two temperature accretion disk flows around rotating black holes. As we know that to explain observed hard X-rays the choice of Keplerian angular momentum profile is not unique, we consider the sub-Keplerian regime of the disk. Without any strict knowledge of the magnetic field structure, we assume the cooling mechanism is dominated by bremsstrahlung process. We show that in a range of Shakura-Sunyaev viscosity parameter 0.2 greater than or similar to alpha greater than or similar to 0.0005, flow behavior varies widely, particularly by means of the size of disk, efficiency of cooling and corresponding temperatures of ions and electrons. We also show that the disk around a rotating black hole is hotter compared to that around a Schwarzschild black hole, rendering a larger difference between ion and electron temperatures in the former case. With all the theoretical solutions in hand, finally we reproduce the observed luminosities (L) of two extreme cases-the under-fed AGNs and quasars (e.g. Sgr A') with L greater than or similar to 10(33) erg/s to ultra-luminous X-ray sources with L similar to 10(41) erg/s, at different combinations of mass accretion rate, ratio of specific heats, Shakura-Sunyaev viscosity parameter and Kerr parameter, and conclude that Sgr A' may be an intermediate spinning black hole.

Multicarrier conduction and Boltzmann transport analysis of heavy hole mobility in HgCdTe near room temperature

Magnetotransport measurements in pulsed fields up to 15 T have been performed on mercury cadmium telluride (Hg1-xCdxTe, x similar to 0.2) bulk as well as liquid phase epitaxially grown samples to obtain the resistivity and conductivity tensors in the temperature range 220-300 K. Mobilities and densities of various carriers participating in conduction have been extracted using both conventional multicarrier fitting (MCF) and mobility spectrum analysis. The fits to experimental data, particularly at the highest magnetic fields, were substantially improved when MCF is applied to minimize errors simultaneously on both resistivity and conductivity tensors. The semiclassical Boltzmann transport equation has been solved without using adjustable parameters by incorporating the following scattering mechanisms to fit the mobility: ionized impurity, polar and nonpolar optical phonons, acoustic deformation potential, and alloy disorder. Compared to previous estimates based on the relaxation time approximation with outscattering only, polar optical scattering and ionized impurity scattering limited mobilities are shown to be larger due to the correct incorporation of the inscattering term taking into account the overlap integrals in the valence band.

Temperature dependent structural properties of nanocrystalline SnS structures

This letter explores the structural behavior of nanocrystalline tin mono sulfide (SnS) structures with respect to temperature (100-600 K). These studies emphasize that the structural properties of SnS nanocrystalline structures depend on the surrounding temperature. The lattice parameters of SnS nanocrystals slightly varied like their microstructures with the increase of temperature. These changes strongly influence the optical properties of SnS nanostructures. On the other hand, the structures exhibited higher strain (similar to 0.44%) than that of microstructured (0.3%) and bulk (0.12%) counterparts. The observed results are discussed under the light of existing concepts and reported.

Temperature and Stress Controlled Surface Manipulation in Ni-Al Nano-Layers

In the present paper the effects of temperature and high strain rate loading on the formation of various surface patterns in Ni-Al nano-layers are discussed. Effects of boundary conditions on the B2 -> BCT phase transformation in the nano-layer are also discussed. This study is aimed at developing several interesting patterned surface structures in Ni-Al nanolayer by controlling the phase transformation temperature and mechanical loading.

Room temperature metathesis of aryl isocyanates and aromatic aldehydes catalyzed by group(IV) metal alkoxides: An experimental and computational study

Aromatic aldehydes and aryl isocyanates do not react at room temperature. However, we have shown for the first time that in the presence of catalytic amounts of group(IV) n-butoxide, they undergo metathesis at room temperature to produce imines with the extrusion of carbon dioxide. The mechanism of action has been investigated by a study of stoichiometric reactions. The insertion of aryl isocyanates into the metal n-butoxide occurs very rapidly. Reaction of the insertion product with the aldehyde is responsible for the metathesis. Among the n-butoxides of group(IV) metals, Ti((OBu)-Bu-n)(4) (8aTi) was found to be more efficient than Zr((OBu)-Bu-n)(4) (8aZr) and Hf((OBu)-Bu-n)(4) (8aHf) in carrying out metathesis. The surprisingly large difference in the metathetic activity of these alkoxides has been probed computationally using model complexes Ti(OMe)(4) (8bTi), Zr(OMe)(4) (8bZr) and Hf(OMe)(4) (8bHf) at the B3LYP/LANL2DZ level of theory. These studies indicate that the insertion product formed by Zr and Hf are extremely stable compared to that formed by Ti. This makes subsequent reaction of Zr and Hf complexes unfavorable.

High-temperature heat capacity and heat content of CaCu3Ti4O12 (CCTO)

The isobaric heat capacity of CaCu3Ti4O12 (CCTO) was measured from 300 to 1100 K using differential scanning calorimetry (DSC). The results were verified using drop calorimetric measurement of enthalpy increment (H-T - H-298.15) at T= 973 and 1073 K. The samples were dropped from room temperature into a calorimeter maintained at high temperature. The results show small negative deviation from Neumann-Kopp rule. The enthalpy and entropy increments are computed as a function of temperature and compared with values available in the literature. The results obtained in this study are consistent with available information on enthalpy and Gibbs energy of formation of CCTO.

Controlled Growth of ZnO Tetrapods: Influence of Temperature and Temperature Gradient

Though it has been established that ZnO tetrapods can be synthesized by heating Zn in air, it is advantageous to grow tetrapods with legs of different morphologies with different lengths. Here, we report the large scale synthesis of ZnO tetrapods by heating Zn in air ambient. The parameters that control the diameter, length, and morphology of tetrapods are identified. It is shown that the morphology and dimensions of the tetrapods depend not only on the vaporization temperature but also on the temperature gradient of the furnace. The controlled synthesis procedure and the key parameters that influence the morphology are discussed.