Quasicrystals, crystals and multiple twins in rapidly solidified Al-Cr-Si, Al-Mn-Si and Al-Mn-Cr-Si alloys

The coexistence of quasicrystals and rational approximant structures (RAS) has been observed in melt-spun Al80Cr14Si6, Al80Mn14Si6 and Al75Mn10Cr5Si10 alloys. The presence of a b.c.c. alpha-AlMnSi phase in Al-Mn-Si and alpha-AlMnSi(Cr) phase in Al-Mn-Cr-Si has been seen. A multiple twinning around an irrational axis of the RAS has been reported in an aggregate of fine size cubic crystallites in all three alloys. Selected area diffraction patterns show that the crystalline aggregate symmetry is linked to the icosahedral point group symmetry (m35). Various ways of expressing the twin relationship in the cubic crystalline aggregates have been discussed. The thermal stability of the icosahedral phase at high temperatures reveals that the icosahedral phase in Al-Mn-Si and Al-Mn-Cr-Si alloys transforms to alpha-AlMnSi at temperatures of 690 and 670 K, respectively. In Al-Cr-Si alloy, heating to a high temperature (615 K) leads to the transformation of the icosahedral phase into a new metastable phase having an ordered cubic structure equivalent to alpha-AlMnSi. The occurrence of multiple twinning leading to icosahedral symmetry in the as-spun Al-Cr-Si alloy is presumably due to this metastable phase. Copyright (C) 1996 Acta Metallurgica Inc.

Reactivities of aluminium and aluminium-magnesium alloy powders in polymeric composites

Polymeric compositions containing Al-Mg alloys show higher reactivities, in comparison with similar compositions containing aluminium. This is observed irrespective of the amount of oxidizer, type of oxidizer used, type of polymeric binder, and over a range of the particle sizes of the metal additive. This is evident from the higher calorimetric values obtained for compositions containing the alloy, in comparison to samples containing aluminium. Analysis of the combustion residue shows the increase in calorimetric value to be due to the greater extent of oxidation of the alloy. The interaction between the polymeric binder and the alloy was studied by coating the metal particles with the polymer by a coacervation technique. On ageing in the presence of ammonium perchlorate, cracking of the polymer coating on the alloy was noticed. This was deduced from differential thermal analysis experiments, and confirmed by scanning electron microscopic observations. The increase in stiffness of the coating, leading to cracking, has been traced to the cross-linking of the polymer by magnesium.

Differences in the glass-forming ability of rapidly solidified and mechanically alloyed Ti-Ni-Cu alloys

Melt spinning of Ti50Ni50 ? xCux (x = 10, 25, 40) alloys showed that the glass-forming ability is good for Cu-rich compositions and poor for Ni-rich compositions. The results of mechanical alloying experiments in the same system showed a reverse trend as far as the glass-forming ability is concerned. These contradictory results are explained in the light of thermodynamic and kinetic considerations. Crystallization results of the melt spun alloys are also presented.

Photocytotoxicity and DNA photocleavage activity of La(III) and Gd(III) complexes of phenanthroline bases

Lanthanide(II) complexes La(B)(acac)(3)] (1-3) and Gd(B)(acac)(3)] (4-6), where B is a N,N-donor phenanthroline base, viz., 1,10-phenanthroline (phen in 1, 4), dipyrido3,2-d:2',3'-f]quinoxaline (dpq in 2, 5) and dipyrido3,2-a:2',3'-c]phenazine (dppz in 3, 6), have been prepared and characterized. The Gd(111) complexes 4 6 are structurally characterized by single crystal X-ray crystallography. The complexes display GdO6N2 coordination with the ligands showing bidentate chelating mode of bonding. The complexes are non-electrolytic in aqueous DMF and exhibit ligand-centered absorption bands in the UV region. The dppz complexes show a band at 380 nm in DMF. The La(111) complexes are diamagnetic. The Gd(III) complexes are paramagnetic with magnetic moment that corresponds to seven unpaired electrons. The Complexes are avid binders to calf thymus DNA giving K-b values in the range of 4.7 x 10(4) 6.1 x 10(5) M-1 with a relative binding order: 3, 6 (dppz) > 2, 5 (dpq) > 1, 4 (phen). The binding data suggest DNA surface and/or groove binding nature of the complexes. The dpq and dppz complexes efficiently cleave SC DNA to its nicked circular form in UV-A light of 365 nm via formation of both singlet oxygen (O-1(2)) and hydroxyl radical (HO center dot) species. The dppz complexes 3 and 6 exhibit significant PDT effect in He La cervical cancer cells giving respective IC50 value of 460(+/- 50) and 530(+/- 30) nM in UV-A light of 365 rim, and are essentially non-toxic in dark with an IC50 value of >100 mu M. The dppz ligand alone is cytotoxic in dark and UV-A light. A significant decrease in the dark toxicity of the dppz base is observed on binding to the Ln(III) ion while retaining its photocytotoxicity.

Electron microscopy and diffraction of ordering in Ni---W alloys

Electron microscopy and diffraction studies of ordering in stoichiometric Ni-20%W and off-stoichiometric Ni-15%W alloys have been carried out. The specimens of Ni-20%W were first disordered at 1398 K for 4 h and then quenched rapidly into water. Short range order (SRO) spots were observed at {1 1/2 0}* positions. Two hitherto unknown metastable phases: D-2h(25)-Ni2W and DO22-Ni3W were observed in the diffraction patterns. Long range order (LRO) transformations were studied at 1103 and 1213 K. Kinetics and mechanism of transformations have been identified. Ni-15%W specimens were solution treated at 1523 K for 1 h followed by quenching in water. SRO spots similar to those found in Ni-20%W were observed in this alloy as well. The transition to LRO was studied at 1093 K. Distinct Ni4W precipitates could be observed after 5 h of annealing at this temperature. After 100 h of annealing precipitates were found to grow into faceted shape coherent with the disordered matrix. After prolonged annealing for over 150 h the Ni4W precipitates began to lose coherency by the generation of misfit dislocations. The microstructural observations have been compared for the stoichiometric and off-stoichiometric alloys.

The influence of pH on the corrosion of medium strength aerospace alloys 8090, 2091 and 2014

The influence of pH on the corrosion behaviour of two aluminium-lithium-copper-magnesium-zirconium (8090 and 2091) alloys was studied and compared with a standard aircraft alloy, 2014 (Al-4.4% Cu) and 99.9% pure Al. In constant exposure and potentiodynamic polarization studies conducted in 3.5% NaCl solution having different pH values, all the alloys exhibited high corrosion rates in acidic and alkaline environments, with a minimum in less hostile environments close to neutral pH. The pitting potentials for aluminium-lithium alloys were slightly lower than those for 2014 and pure Al. The effect of pH on the passive current density was also less for aluminium-lithium alloys.

On the decomposition of ? phase in some rapidly quenched titanium-eutectoid alloys

The decomposition of the beta phase in rapidly quenched Ti-2.8 at. pet Co, Ti-5.4 at. pet Ni, Ti-4.5 at. pet, and 5.5 at. pet Cu alloys has been investigated by electron microscopy. During rapid quenching, two competitive phase transformations, namely martensitic and eutectoid transformation, have occurred, and the region of eutectoid transformation is extended due to the high cooling rates involved. The beta phase decomposed into nonlamellar eutectoid product (bainite) having a globular morphology in Ti-2.8 pet Co and Ti-4.5 pet Cu (hypoeutectoid) alloys. In the near-eutectoid Ti-5.5 pet Cu alloy, the decomposition occurred by a lamellar (pearlite) type, whereas in Ti-5.4 pct Ni (hypereutectoid), both morphologies were observed. The interfaces between the proeutectoid alpha and the intermetallic compound in the nonlamellar type as well as between the proeutectoid alpha and the pearlite were often found to be partially coherent. These findings are in agreement with the Lee and Aaronson model proposed recently for the evolution of bainite and pearlite structures during the solid-state transformations of some titanium-eutectoid alloys. The evolution of the Ti2Cu phase during rapid quenching involved the formation of a metastable phase closely related to an ''omega-type'' phase before the equilibrium phase formed. Further, the lamellar intermetallic compound Ti2Cu was found to evolve by a sympathetic nucleation process. Evidence is established for the sympathetic nucleation of the proeutectoid alpha crystals formed during rapid quenching.

Optimization of hot workability of an Al-Mg-Si alloy using processing maps

The hot workability of an Al-Mg-Si alloy has been studied by conducting constant strain-rate compression tests. The temperature range and strain-rate regime selected for the present study were 300-550 degrees C and 0.001-1 s(-1), respectively. On the basis of true stress data, the strain-rate sensitivity values were calculated and used for establishing processing maps following the dynamic materials model. These maps delineate characteristic domains of different dissipative mechanisms. Two domains of dynamic recrystallization (DRX) have been identified which are associated with the peak efficiency of power dissipation (34%) and complete reconstitution of as-cast microstructure. As a result, optimum hot ductility is achieved in the DRX domains. The strain rates at which DRX domains occur are determined by the second-phase particles such as Mg2Si precipitates and intermetallic compounds. The alloy also exhibits microstructural instability in the form of localized plastic deformation in the temperature range 300-350 degrees C and at strain rate 1 s(-1).

Low-temperature magnetoresistance of ?-phase FexNi80-xCr20 alloys near the critical composition for ferromagnetism

We present a comprehensive study of magnetoresistance (MR) of the crystalline pseudobinary ?-phase Fe alloy series FexNi80-xCr20 (50?x?66). This alloy series shows exotic magnetic phases as the composition (x) is varied. It has a critical composition for ferromagnetism at x=xc?59�60. MR was measured in the temperature range 1.7�110 K and up to a field of 7 T. The observed MR was small and the change was ?1%. The temperature dependence of MR was found to contain a positive and a negative contribution. The positive term was found to be ?H2 and it dominates at high field and high temperatures. We explain this as a manifestation of Kohler�s rule. The negative MR was found to have a quadratic dependence on magnetization M. The magnitude of the negative MR reaches a maximum as x?xc.

Mechanism of seizure of aluminium-silicon alloys dry sliding against steel

A steel ball was slid on aluminium-silicon alloys at different temperatures. After the coefficient of friction had been measured, the surface shear stress was deconvoluted using a two-term model of friction. The ratio of surface shear stress to bulk hardness was calculated as a function of temperature, silicon content and alloying additions. These results are qualitatively similar to those recorded for pre-seizure specimens slid against an En24 disc in a pin-on-disc machine. This similarity, when viewed in the context of the phenomenon of bulk shear, provides a model for seizure of these alloys.

Nanoscale Ag–Pd and Cu–Pd alloys

Nanoparticles of Ag-Pd and Gu-Pd alloys with diameters in the 5-40 nm range have been prepared over the entire range of compositions, by employing the heterogeneous reaction of dry methanol or ethanol with intimate mixtures of AgNO3+PdOx and CuOx+PdOx, respectively. The nanoscale alloys have been characterized by energy-dispersive Xray (EDX) analysis, transmission electron microscopy (TEM) and X-ray diffraction (XRD). All the alloy particles possess the fee structure and can be obtained in bulk quantities.

Plate-shaped transformation products in zirconium-base alloys

Plate-shaped products resulting from martensitic, diffusional, and mixed mode transformations in zirconium-base alloys are compared. in the present study. These alloys are particularly suitable for the comparison in view of the fact that the lattice correspondence between the parent beta (bcc) and the product alpha (hcp) or gamma-hydride (fct) phases are remarkably similar for different types of transformations. Crystallographic features such as orientation relations, habit planes, and interface structures associated with these transformations have been compared:, with a view toward examining whether the transformation mechanisms have characteristic imprints on these experimental observables. Martensites exhibiting dislocated lath, internally twinned plate, and self-accommodating three-plate cluster morphologies have been encountered in Zr-2.5Nb alloy. Habit planes corresponding to all these morphologies have been found to be consistent with the predictions based on the invariant plane strain (IFS) criterion. Different morphologies have been found to reflect the manner in which the neighboring martensite variants are assembled. Lattice-invariant shears (LISs) for all these cases have been identified to be either {10 (1) over bar 1}(alpha) ((1) over bar 123)(alpha) slip or twinning on (10 (1) over bar 1)(alpha) planes. Widmanstatten alpha precipitates, forming in a step-quenching treatment, have been shown to have a lath morphology, the alpha/beta interface being decorated with a periodic array of (c + a) dislocations at a spacing of 8 to 10 nm. The line vectors of these dislocations are nearly parallel to the invariant lines. The alpha precipitates, forming in the retained beta phase on aging, exhibit an internally twinned structure with a zigzag habit plane. Average habit planes for the morphologies have been found to lie near the {103}(beta) - {113}(beta) poles, which are close to the specific variant of the {112}(beta) plane, which transforms into a prismatic plane of the type {1 (1) over bar 00}(alpha). The crystallography of the formation of the gamma-hydride phase (fct) from both the alpha and beta phases is seen to match the IFS predictions. While the beta-gamma transformation can be treated approximately as a simple shear on the basal plane involving a change in the stacking sequence, the alpha-gamma transformation call be conceptually broken into a alpha --> beta transformation following the Burgers correspondence and the simple beta-gamma shear process. The active eutectoid decomposition in the Zr-Cu system, beta --> alpha + beta', has been described in terms of cooperative growth of the alpha phase from the beta phase through the Burgers correspondence and of the partially ordered beta' (structurally similar to the equilibrium Zr2Cu phase) through an ordering process. Similarities and differences in crystallographic features of these transformations have been discussed. and the importance of the invariant line vector in deciding the geometry of the corresponding habit planes has been pointed out.

Synthesis of nanodispersed phases during rapid solidification and crystallization of glasses in Ti75Ni25 alloys

The formation of the metallic glass and crystalline phases and related microstructures and the decomposition behavior of rapidly solidified Ti75Ni25 alloys obtained under different processing conditions have been investigated in detail. The competition between glass transition and nucleation of beta-Ti during rapid solidification leads to the possibility of synthesizing the nanocomposites of beta-Ti and glass. Additionally, it is shown that the presence of a small amount of Si also promotes simultaneous nucleation of fine Ti2Ni intermetallic compound. Thermodynamic calculation of the metastable phase diagram indicates the presence of a metastable eutectic reaction between alpha-Ti and Ti2Ni. Evidence of this reaction at lower cooling rates has been presented. On heating, the glass decomposes through this reaction. Finally, on the basis of understanding of the microstructural evolution during decomposition, a new approach has been adopted to synthesize a nanodispersed composite of alpha-Ti in the crystalline Ti2Ni matrix with a narrow size distribution by controlling the devitrification heat treatment of the metallic glass.

Synthesis of nanostructured titanium alloys

The synthesis of nanostructured materials is a critical step in the development elf these novel materials. The basic principles involved in the production of nanocrystals and nanocomposites by rapid solidification are dealt with. An analysis of the various factors influencing the final grain size of the nanocrystals achieved during mechanical alloying has been presented. The devitrification of amorphous phase formed during rapid solidification processing and mechanical alloying provides an alternative and attractive route. Examples of the synthesis of nanostructured materials using these three different routes are drawn from our work on titanium alloys.

Reversibility of Mg/Mg2+ couple in a gel polymer electrolyte

Investigations on solid state rechargeable magnesium batteries are considered important similar to lithium batteries. In view of negligible hazards and less reactivity of the magnesium, in comparison with lithium, studies on rechargeable magnesium batteries are expected to have a wide scope in future. Solid polymer electrolytes, which conduct Mg2+ ions and reversibility of a Mg/Mg2+ couple are essential components of the studies. In the present investigations, the existence of reversibility of a Mg/Mg2+ couple in a gel polymer electrolyte (GPE) medium is established for the first time in literature. Results obtained by electrochemical impedance spectroscopy and cyclic voltammetry on Mg/GPE/Mg, SS/GPE/SS symmetrical cells show evidence for the reversibility. (C) 1999 Elsevier Science Ltd. All rights reserved.