Stabilization of Cu-7 clusters in azide networks: syntheses, structures and magnetic behaviour

Two new azide bridged copper(II) coordination polymer compounds, Cu-7(N-3)(14)(C3H10N2)(C4H13N3)]n (I) and Cu-7(N-3)(14)(C3H10N2)(C5H15N3)(2)](n) (II) where C3H10N2 = 1,2-diaminopropane (1,2-DAP); C4H13N3 = di-ethylenetriamine (DETA); C5H15N3 = N-2-aminoethyl-1,3-propanediamine (AEDAP)] were prepared by employing a room temperature diffusion technique involving three layers. Single crystal studies reveal that both compounds I and II, have similar connectivity forming Cu7 clusters through end-on (EO) bonding of the azide. The Cu-7 clusters are connected through end-to-end (EE) connectivity of the azides forming three-dimensional structures. Magnetic studies confirmed the ferromagnetic interactions within the Cu-7 units and revealed the occurrence of concomitant ferro- and antiferro-magnetic interactions between these clusters. As a result I behaves as a weak-ferromagnet with T-C = 10 K.

Three-dimensional plotted hydroxyapatite scaffolds with predefined architecture: comparison of stabilization by alginate cross-linking versus sintering

Scaffolds for bone tissue engineering are essentially characterized by porous three-dimensional structures with interconnected pores to facilitate the exchange of nutrients and removal of waste products from cells, thereby promoting cell proliferation in such engineered scaffolds. Although hydroxyapatite is widely being considered for bone tissue engineering applications due to its occurrence in the natural extracellular matrix of this tissue, limited reports are available on additive manufacturing of hydroxyapatite-based materials. In this perspective, hydroxyapatite-based three-dimensional porous scaffolds with two different binders (maltodextrin and sodium alginate) were fabricated using the extrusion method of three-dimensional plotting and the results were compared in reference to the structural properties of scaffolds processed via chemical stabilization and sintering routes, respectively. With the optimal processing conditions regarding to pH and viscosity of binder-loaded hydroxyapatite pastes, scaffolds with parallelepiped porous architecture having up to 74% porosity were fabricated. Interestingly, sintering of the as-plotted hydroxyapatite-sodium alginate (cross-linked with CaCl2 solution) scaffolds led to the formation of chlorapatite (Ca9.54P5.98O23.8Cl1.60(OH)(2.74)). Both the sintered scaffolds displayed progressive deformation and delayed fracture under compressive loading, with hydroxyapatite-alginate scaffolds exhibiting a higher compressive strength (9.5 +/- 0.5MPa) than hydroxyapatite-maltodextrin scaffolds (7.0 +/- 0.6MPa). The difference in properties is explained in terms of the phase assemblage and microstructure.

Stabilization of a Tetrahedral (Mn5+O4) Chromophore in Ternary Barium Oxides as a Strategy toward Development of New Turquoise/Green-Colored Pigments

An experimental investigation of the stabilization of the turquoise-colored chrornophore (Mn5+O4) in various oxide hosts, viz., A(3)(VO4)(2) (A = Ba, Sr, Ca), YVO4, and Ba2MO4 (M = Ti, Si), has been carried out. The results reveal that substitution of Mn5+O4 occurs in Ba-3(VO4)(2) forming the entire solid solution series Ba-3(V1-x MnxO4)(2) (0 < x <= 1.0), while with the corresponding strontium derivative, only up to about 10% of Mn5+O4 substitution is possible. Ca-3(VO4)(2) and YVO4 do not stabilize Mn5+O4 at all. With Ba2MO4 (M = Ti, Si), we could prepare only partially substituted materials, Ba2M1-xMn5+O4+x/2 for x up to 0.15, that are turquoise-colored. We rationalize the results that a large stabilization of the O 2p-valence band states occurs in the presence of the electropositive barium that renders the Mn5+ oxidation state accessible in oxoanion compounds containing PO43-, VO43-, etc. By way of proof-of-concept, we synthesized new turquoise-colored Mn5+O4 materials, Ba-5(BO3)(MnO4)(2)Cl and Ba-5(BO3)(PO4)(MnO4)Cl, based on the apatite-Ba-5(PO4)(3)Cl-structure.