Mixed-mode stress intensity factors for arbitrarily oriented cracks in cylindrical shells under axial pull and torsion

Results of photoelastic investigations conducted on cylindrical tubes (made of Araldite material) containing cracks oriented at 0°, 30°, 45°, 60° and 90° to the axis of the tube and subjected to axial and torsional loads are reported. The stress-intensity factors (SIFs) were determined by analysing the crack-tip stress fields. Smith and Smith's method [Engng Fracture Mech.4, 357–366 (1972)] and a new method developed by the authors by modifying Rakesh et al.'s method [Proc. 26th Congress of ISTAM, India (1981)] were employed to evaluate the mixed-mode SIFs.

ESR studies of X-irradiated strontium mixed calcium tartrate crystals

The electron spin resonance spectra of X-ray irradiated single crystals of strontium doped calcium tartrate tetrahydrate (CST) with molecular formula Ca0.88Sr0.12C4H4O6.4H(2)O grown in gels has been investigated. Only one species of free radical but with two magnetically unequivalent sites was observed at room temperature. The free radical was found to be the result of the splitting of a C-II bond adjacent to both the hydroxyl and carboxyl groups. The a factor was found to be slightly anisotropic. Couplings with two H nuclei, believed to be the proton of the OH group attached directly to the unsaturated asymmetric carbon atom and the proton attached directly to the: other asymmetric carbon atom of the molecule were observed. The principal g-values were found to be 2.0030, 2.0017, 2.0027. The principal elements of the nuclear coupling are 7.45, 6.59, 4.28 and 8.56, 7.22, 18.71 G, respectively. The radical was found to be very stable. (C) 2000 Elsevier Science Ltd. All rights reserved.

Oxide-based bifunctional oxygen electrode for rechargeable metal/air batteries

Statistical methods for optimizing the morphology of oxide-based, bifunctional oxygen electrodes for use in rechargeable metal/air batteries are examined with regard to binder composition, compaction time, and compaction load. Results show that LaNiO3 with PTFE binder in a nickel mesh envelope provides a satisfactory electrode.

Unsteady mixed convection with double diffusion over a horizontal cylinder and a sphere within a porous medium

The combined effects of the permeability of the medium, magnetic field, buoyancy forces and dissipation on the unsteady mixed convection flow over a horizontal cylinder and a sphere embedded in a porous medium have been studied. The nonlinear coupled partial differential equations with three independent variables have been solved numerically using an implicit finite-difference scheme in combination with the quasilinearization technique. The skin friction, heat transfer and mass transfer increase with the permeability of the medium, magnetic field and buoyancy parameter. The heat and mass transfer continuously decrease with the stream-wise distance, whereas the skin friction increases from zero, attains a maximum and then decreases to zero. The skin friction, heat transfer and mass transfer are significantly affected by the free stream velocity distribution. The effect of dissipation parameter is found to be more pronounced on the heat transfer than on the skin friction and mass transfer

Electronic structure of high-Tc Ba0.6K0.4BiO3 by x-ray photoelectron spectroscopy

We have investigated the electronic structure of Ba1-xKxBiO3 (0

Mixed convection along a vertical cone

An analysis is performed to study the flow and heat transfer characteristics for the case of laminar mixed convection along a vertical circular cone. A mixed-convection parameter is introduced in the formulation of the problem such that smooth transition from one convective limit to the other is possible. The transformed conservation equations of the nonsimilar boundary layers are solved by an efficient finite-difference method.

Reducibility of Ce1-xZrxO2: origin of enhanced oxygen storage capacity

We combine first-principles calculations with EXAFS studies to investigate the origin of high oxygen storage capacity in ceria-zirconia solid solution, prepared by solution combustion method. We find that nanocrystalline Ce0.5Zr0.5O2 can be reduced to Ce0.5Zr0.5O1.57 by H-2 upto 850 degrees C with an OSC of 65 cc/gm which is extremely high. Calculated local atomic-scale structure reveals the presence of long and short bonds resulting in four-fold coordination of the cations, confirmed by the EXAFS studies. Bond valence analysis of the microscopic structure and energetics is used to evaluate the strength of binding of different oxide ions and vacancies. We find the presence of strongly and weakly bound oxygens, of which the latter are responsible for the higher oxygen storage capacity in the mixed oxides than in the pure CeO2.

Low-temperature polymer precursor-based synthesis of nanocrystalline particles of lanthanum calcium manganese oxide (La0.67Ca0.33MnO3) with enhanced ferromagnetic transition temperature

We report a simple modified polymeric precursor route for the synthesis of highly crystalline and homogenous nanoparticles of lanthanum calcium manganese oxide (LCMO). The LCMO phase formation was studied by thermal analysis, x-ray powder diffraction, and infrared spectroscopy at different stages of heating. These nanocrystallites (average particle size of 30 nm) possess ferromagnetic-paramagnetic transition temperature (T-c) of 300 K, nearly 50 K higher than that of a single crystal. The Rietveld analysis of the powder x-ray diffraction data of the nanopowders reveals significant lattice contraction and reduction in unit cell anisotropy-these structural changes are correlated to the enhancement in T-c.

Microwave irradiation-assisted method for the deposition of adherent oxide films on semiconducting and dielectric substrates

We report a method for the deposition of thin films and thick coatings of metal oxides through the liquid medium, involving the micro waveirradiation of a solution of a metal-organic complex in a suitable dielectric solvent. The process is a combination of sol-gel and dip-coating methods, wherein coatings can be obtained on nonconducting and semiconducting substrates, within a few minutes. Thin films of nanostructured ZnO (wurtzite) have been obtained on Si(100), glass and polymer substrates, the nanostructure determined by process parameters The coatings are strongly adherent and uniform over 15 mm x 15 mm, the growth rate similar to 0.25 mu m/min Coatings of nanocrystalline Fe2O3 and Ga2O3 have also been obtained The method is scalable to larger substrates, and is promising as a low temperature technique for coating dielectric substrates, including flexible polymers. (C) 2010 Elsevier B.V. All rights reserved.

Darcian mixed convection plumes along vertical adiabatic surfaces in a saturated porous medium

The mixed convection flow due to a line thermal source embedded at the leading edge of an adiabatic vertical plane surface immersed in a saturated porous medium has been studied. Both weakly and strongly buoyant plume regimes have been considered. The cases of buoyancy assisting and buoyancy opposing flow conditions have been incorporated in the analysis. The results are presented for the entire range of buoyancy parameter from the pure forced convection (xgr=0) to the pure free convection (xgr rarr infin@#@) regimes. For buoyancy-assisting flow, the wall temperature and the velocity at the wall increase as the plume strength increases. However, they all decrease as the free-stream velocity increases. For buoyancyopposing flow, the temperature at the wall increases as the strength of the plume increases but velocity at the wall decreases.

PVA-SSA-HPA Mixed-Matrix-Membrane Electrolytes for DMFCs

Stabilized forms of heteropolyacids (HPAs), namely phosphomolybdic acid (PMA), phosphotungstic acid (PTA), and silicotungstic acid (STA), are incorporated into poly (vinyl alcohol) (PVA) cross-linked with sulfosuccinic acid (SSA) to form mixed-matrix membranes for application in direct methanol fuel cells (DMFCs). Bridging SSA between PVA molecules not only strengthens the network but also facilitates proton conduction in HPAs. The mixed-matrix membranes are characterized for their mechanical stability, sorption capability, ion-exchange capacity, and wetting in conjunction with their proton conductivity, methanol permeability, and DMFC performance. Methanol-release kinetics is studied ex situ by volume-localized NMR spectroscopy (employing point-resolved spectroscopy'') with the results clearly demonstrating that the incorporation of certain inorganic fillers in PVA-SSA viz., STA and PTA, retards the methanol-release kinetics under osmotic drag compared to Nafion, although PVA-SSA itself exhibits a still lower methanol permeability. The methanol crossover rate for PVA-SSA-HPA-bridged-mixed-matrix membranes decreases dramatically with increasing current density rendering higher DMFC performance in relation to a DMFC using a pristine PVA-SSA membrane. A peak power density of 150 mW/cm(2) at a load current density of 500 mA/cm(2) is achieved for the DMFC using a PVA-SSA-STA-bridged-mixed-matrix-membrane electrolyte. (C) 2010 The Electrochemical Society. [DOI: 10.1149/1.3465653] All rights reserved.

Electron microscopic investigation of high-temperature oxide superconductors

Electron microscopic investigations have been carried out on superconducting YBa2Cu3 O7−δ, NdBa2Cu3 O7−δ and related oxides. All these orthorhombic oxides exhibit twin domains. Based on high resolution electron microscopy, it is shown that there is no significant change in the structure across the twins. Oxides of the La2−x Sr x (Ba x )CuO4 system do not show twins, but exhibit other types of defects. Twins appear to be characteristic of only the orthorhombic 123 structures.

Evidence for double valence fluctuation in metallic oxides of lead

The possible role of double valence fluctuation in both lead and oxide ions with reference to metallization in oxides of lead is examined by x-ray-photoemission spectroscopy, ultraviolet-photoemission spectroscopy (UPS), and 207Pb NMR studies. The double valence fluctuations may be viewed as Pb4++2O2-⇄Pb2+O22-. While the insulating oxides PbO, Pb3O4, and Sr2PbO4 show a single oxide ion, O2- characterized by O(1s) at 529.7 eV, the insulating peroxide BaO2 is characterized by the ion O22- with a single O(1s) at 533 eV. The metallic PbO2, BaPbO3, BaBiPbO3, and SrPbO3 showed the occurrence of both O2- and O22- ions. The valence band in these compounds has also been studied by UPS, and clear evidence for the coexistence of O2- and O22- is seen in PbO2. A simultaneous study of 207Pb NMR suggests that the Pb ion could also exist in mixed-valence states. Qualitative arguments are presented to rationalize the existence of such mixed valences of the anion in metal oxides in general and their role in superconductivity.