Preparation of CaTiO3 fine powders by the hydrothermal method

Fine powders consisting of 0.1–0.5 μm size crystallites of CaTiO3 are prepared at 150–200°C by the hydrothermal method starting from hydrated titania gel and reactive calcium oxide suspended as an aqueous slurry in an autoclave. The resulting high-purity CaTiO3 is characterised by TEM, X-ray powder diffraction, chemical analyses and sintering characteristics. The hydrothermally prepared CaTiO3 powders are sinterable to high-density ceramics below 1400°C. The dc conductivity behaviour of the chemically reduced ceramics is presented.

Hydrothermal preparation of Ba(Ti,Zr)O3 fine powders

Fine powders consisting of aggregated submicron crystallites of Ba(Ti,Zr)O3 in the complete range of Ti/Zr ratios are prepared at 85–130°C by hydrothermal method, starting from TiO2 + ZrO2 · xH2O mixed gel and Ba(OH)2 solution. The products obtained below 110°C incorporate considerable amounts of H2O and OH− within the lattice. As-prepared BaTiO3 is cubic and converts to tetragonal phase after the heat treatment at 1200°C, accompanied by the loss of residual hydroxyl ions. TEM investgations of the growth features show a transformation of the gel to the crystallite. Ba2+ ions entering the gel produce chemical changes within the gel, followed by dehydration, resulting in a cubic perovskite phase irrespective of Ti/Zr. The sintering properties of these powders to fine-grained, high density ceramics and their dielectric properties are presented.

Ultrafine powders of SrTiO3 from the hydrothermal preparation and their catalytic activity in the photolysis of water

Ultrafine powders of SrTiO3 are prepared at 100–150°C by the hydrothermal method, starting from TiO2·xH2O gel and Sr(OH)2 and H2O-isopropanol mixed solvent as the medium, The X-ray diffractograms of the powder show line broadening. The minimum crystallite size obtained ranges from 5 to 20nm with 20% H2O-80% C3H7OH as the reaction medium, as estimated from X-ray half-peak widths and TEM studies. The electron diffraction results indicate high concentration of lattice defects in these crystallites. The optical spectra of the particle suspensions in water show that the absorption around the band gap is considerably broadened, together with the appearance of maxima in the far ultraviolet. Aqueous suspensions of SrTiO3 powders, as such, do not produce H2 or O2 on UV irradiation. After coating with rhodium, H2 and O2 are evolved on illumination. However, the turn over number of O2 is lower than the stoichiometrically expected values from the corresponding values of H2. No correlation of the photocatalytic activity with surface area is observed. The activity of Rh-SrTiO3 slowly deteriorates with extended period of irradiation.

Wet chemical syntheses of ultrafine multicomponent ceramic powders through gel to crystallite conversion

Coarse (BOn/2)-O-n+/xH(2)O (10

A simple method for the preparation of plasma-sprayable powders based on ZrO2

Plasma-sprayable powders of calcia, magnesia and yttria-stabilized zirconia have been prepared by using polyvinyl alcohol binders. The powders have been characterized for sprayability by spray coating on steer plates previously coated with an NiAl bond coat. The suitability of these coatings for thermal barrier applications have been examined. Thermal barrier and related properties, along with phase stability and mechanical properties, have been found to be good. Failure of the thermal barrier coating has been observed to occur at the interface between the bond coat and the substrate, due to the formation of a pile-up layer consisting of Fe-Zr-Al-O compound.

Photocatalysis on Fine Powders of Perovskite Oxides

Fine powders of semiconductor oxides have been widely used as photocatalysts for many reactions. Among the various photocatalytic reactions, water splitting has been given much importance, since it is a promising chemical route for solar energy conversion. Perovskite oxides, in particular SrTiO, have been commonly used as photocatalysts because some of them can decompose H,O into H, and 0, without an external bias potential (1). In turn, this is because the conduction band (CB) edges of some of the perovskite oxides are more negative than the H+/H, energy level. Since the catalytic activity is related to the surface properties of the solids, fine powders rather than single crystals are used. Photocatalysis on fine powers can be conveniently discussed in three parts, viz. preparation, characterization and their catalytic activity. Presently, photo-decomposition of water using SrTiO, fine powders is discussed in greater detail, although other photocatalytic reactions on various perovskite oxides are also briefly dealt with.

Preparation and characterization of nanocrystalline powders of bismuth vanadate

The influence of mechanical activation on the formation of Bi2VO5.5 bismuth vanadate (BiV) phase, was investigated by ball-milling a stoichiometric mixture of bismuth oxide and vanadium pentoxide. The structural evolution of the desired BN phase, via an intermediate BiVO4,phase, was investigated using X-ray powder diffraction; (XRD), differential thermal analysis (DTA) and transmission electron microscopy (TEM). Milling for 54h. yielded monophasic gamma-BiV powders with an average crystallite size of 30 nm. The electron paramagnetic resonance (EPR) peaks associated with the V4+ ions are stronger and broader in nanocrystalline (n) BN than in the conventionally prepared microcrystalline (m) BN, suggesting theta significant portion of V5+ has been transformed to V4+ during milling. The optical bandgap of n-BiV was found to be higher than that of m-BiV. High density (97% of the theoretical density), fine-grained (average grain-size of 2 tun) ceramics with uniform grain-size distribution could be fabricated using n-BiV powders. These fine-grained ceramics exhibit improved dielectric, pyre and ferroelectric properties. (C) 1999 Elsevier Science S.A. All rights reserved.

Preparation of a ZrO2–Al2O3 nanocomposite by high-pressure sintering of spray-pyrolyzed powders

ZrO2–Al2O3 powders were synthesized by spray pyrolysis. These powders were sintered at 1 GPa in the temperature range of 700–1100 °C. The microstructural evolution and densification are reported in this paper. The application of 1 Gpa pressure lowers the crystallization temperature from ∼850 to <700 °C. Similarly, the transformation temperature under 1 GPa pressure for γ → α–Al2O3 reduces from ∼1100 to 700–800 °C range, and that for t → m ZrO2 reduces from ∼1050 to 700–800 °C range. It was possible to obtain highly dense nanocrystalline ZrO2–Al2O3 composite at temperatures as low as 700 °C. The effect of high pressure on nucleation and transformation of phases is discussed.

Preparation of lamellar and hexagonal forms of mesoporous silica and zirconiaby the neutral amine route: lamellar-hexagonal transformation in the solid state

The chain length of the surfactant and the solvent composition are two of the factors that determine whether the lamellar or the hexagonal form of mesoporous SiO2 (or ZrO2) is formed by the neutral amine route; a lamellar-hexagonal transformation occurs on removal of the amine from the former.

Preparation of Hexafluorodisilane and Reactions of Hexafluorodisilane and Hexachlorodisilane with Sulfur Trioxide

Hexafluorodisilane has been prepared by the fluorination of hexachlorodisilane or hexabromodisilane by potassium fluoride in boiling acetonitrile, in yields approximating 45 and 60% respectively. Hexafluorodisilane has been characterised by infrared spectral data, vapour density measurements and analytical data. Both hexafluorodisilane and hexachlorodisilane are found to react with sulfur trioxide when heated to 400°C for 12 h. The products of reaction are silicon tetrafluoride, silica and sulfur dioxide with hexafluorodisilane while hexachlorodisilane in addition gives rise to hexachlorodisiloxane.

A new synthetic procedure for the preparation of pyridinium tetrafluoroborate and hexafluorosilicate

Pyridinium tetrafluoroborate (C5H5NHBF4) and pyridinium hexafluorosilicate [(C5H5NH)2SiF6] have been prepared in good yields and high purity by the reaction of pyridinium poly(hydrogen fluoride) with oxides and acids of boron and silicon respectively. The salts have been characterised by melting points, IR, 1H and 19F NMR spectroscopy and chemical analysis.

An elegant direct route for the preparation of pyridinium, ammonium and alkali metal hexafluorotitanates (IV)

Pyridinium hexafluorotitanate (IV) has been prepared by a one step procedure. Addition of titanium tetrachloride to pyridinium poly(hydrogen fluoride) yields nearly quantitative amounts of pyridinium hexafluorotitanate(IV). Making use of pyridinium hexafluorotitanate as precursor, ammonium and alkali metal (Na, K, Rb, and Cs) hexafluorotitanates have been prepared in good yields. These salts have been characterised by IR, N.M.R. (1H, 13C and 19F), X-ray powder diffraction data and chemical analysis.

Preparation and catalytic studies of palladium nanoparticles stabilized by dendritic phosphine ligand-functionalized silica

Silica is a prominently utilized heterogeneous metal catalyst support. Functionalization of the silica with poly(ether imine) based dendritic phosphine ligand was conducted, in order to assess the efficacy of the dendritic phosphine in reactions facilitated by a silica supported metal catalyst. The phosphinated poly(ether imine) (PETIM) dendritic ligand was bound covalently to the functionalized silica. For this purpose, the phosphinated dendritic ligand containing an amine at the focal point was synthesized initially. Complexation of the dendritic phosphine functionalized silica with Pd(COD)Cl-2 yielded Pd(II) complex, which was reduced subsequently to Pd(0), by conditioning with EtOH. The Pd metal nanoparticle thus formed was characterized by physical methods, and the spherical nanoparticles were found to have >85% size distribution between 2 nm and 4 nm. The metal nanoparticle was tested as a hydrogenation catalyst of olefins. The catalyst could be recovered and recycled more than 10 times, without a loss in the catalytic efficiency.

Synthesis and Characterisation of Metal Hydrazine Nitrate, Azide and Perchlorate Complexes

Metal hydrazine nitrate complexes of the type M(N2H4)Nn (NO3)2 where M = Mg, n = 2; M = Mn, Fe, Co, Ni, Zn and Cd and n = 3; metal dihydrazine azide complexes of the type M(N2H4)2 (N3)2 where M = Mg, Co, Ni and Zn; and Mg(N2H4)2 (C1O4)2 have been prepared by dissolving the respective metal powders in the solution of corresponding ammonium salts (NO3, N3 and C1O4) in hydrazine hydrate. These hydrazine complexes were also prepared by the conventional method involving the addition of alcoholic hydrazine hydrate to the aqueous solution of metal salts. The hydrazine complexes have been characterised by chemical analysis, infrared spectra and differential thermal analysis (DTA). Impact sensitivities of hydrazine complexes were determined by the drop weight method. The reactivity of these hydrazine complexes does not change with the method of preparation.