High-Tc superconductivity in the Er---Ba---Cu---O and related systems

ErBa2Cu3O7 and Er0.5Y0.5Ba2Cu3O7 are both high-Tc superconductors attaining zero resistance above 80 K. Preliminary studies indicate that Yb1−xYxBa2Cu3O7 also exhibits zero resistance above 77 K.

HIGH-Tc superconductivity in perovskite oxides of the Y-Ba-Cu-O system

Several biphasic compositions of the type Y3-xBa3+xCu6O14 show an onset of superconductivity in the 90-115K range, attaining zero resistance in the 70-85K range. The phase responsible for superconductivity in these compositions is a perovskite oxide of composition YBa2Cu3 O7. This oxide annealed in oxygen shows the onset of superconductivity at 120K and zero resistance at 87K. YBa2,Cu3O7 shows the highest Meissner effect of all oxide superconductors. The superconducting behaviour of the two perovskite oxides, Y0.95Ba1.95,Cu3O7 and Y1.05Ba1.95Cu3O7 show interesting features; a marked decrease in resistivity is observed from room temperature itself in the former oxide with zero resistance at 89K. Electron microscopy and infrared spectra of these oxides are briefly discussed.

High-temperature superconductivity in the 100 K region in perovskite-related oxides of the Ln-Ba-Cu-O (Ln=Y or La) system

Oxides of the Y-Ba-Cu-O system are found to show onset of superconductivity in the 100–120 K region.

Hydrothermal preparation of Ba(Ti,Zr)O3 fine powders

Fine powders consisting of aggregated submicron crystallites of Ba(Ti,Zr)O3 in the complete range of Ti/Zr ratios are prepared at 85–130°C by hydrothermal method, starting from TiO2 + ZrO2 · xH2O mixed gel and Ba(OH)2 solution. The products obtained below 110°C incorporate considerable amounts of H2O and OH− within the lattice. As-prepared BaTiO3 is cubic and converts to tetragonal phase after the heat treatment at 1200°C, accompanied by the loss of residual hydroxyl ions. TEM investgations of the growth features show a transformation of the gel to the crystallite. Ba2+ ions entering the gel produce chemical changes within the gel, followed by dehydration, resulting in a cubic perovskite phase irrespective of Ti/Zr. The sintering properties of these powders to fine-grained, high density ceramics and their dielectric properties are presented.

Hydrothermal synthesis of Ba(Ti, Sn)O3 fine powders and dielectric properties of the corresponding ceramics

Fine powders of submicron-sized crystallites of BaTiO3 were prepared at 85–130°C by the hydrothermal method, starting from TiO2.ξH2O gel and Ba(OH)2 solution. The products obtained below 110°C incorporated considerable amounts of H2O and OH− in the lattice. As-prepared BaTiO3 is cubic and converts to the tetragonal phase after heat treatment at 1200°C, accompanied by the loss of residual OH− ions. Hydrothermal reaction of SnO2.ξH2O gel with Ba(OH)2 at 150–260°C gives rise to the hydrated phase, BaSn(OH)6.3H2O, due to the amphoteric nature of SnO2.ξH2O which stabilises Sn(OH)62− anions in basic media. On heating in air or releasing the pressure in situ at 260°C, BaSn(OH)6.3H2O converts to BaSnO3 through an intermediate, BaSnO(OH)4. Solid solutions of Ba(Ti,Sn)O3 are directly formed from (TiO2 + SnO2)..ξH2O gel up to 35 mol% SnO2. At higher Sn contents, the hydrothermal products are mixtures of BaSn(OH)6.3H2O and BaTiO3, which on annealing at 1000°C result in monophasic Ba(Ti,Sn)O3. The sintering characteristics and the dielectric properties of the ceramics prepared out of these fine powders are presented. The dielectric properties of fine-grained Ba(Ti,Sn)O3 ceramics are explained on the basis of the prevailing diffuse phase transition behaviour.

TlCaBa2Cu2O7: The 1122 (90 K) superconductor in the new Tl(Ca,Ba)n+1CunO2n+3 seriesstar, open

The 1122 (n=2) member of the Tl(Ca,Ba)n+1CunO2n+3 series containing a single Tl-O layer is shown to be associated with a Tc of 90 K. This value of Tc is significantly lower than that of the 2122 phase (Tcnot, vert, similar110 K) with two Tl-O layers.

Precipitation of rutile and anatase (Tio12) fine powders and their conversion to MTiO3 (M = Ba, Sr, Ca) by the hydrothermal method

Fine powders of TiO2 (rutile) with high degree of crystallinity are formed from aqueous titanium oxychloride solution under hydrothermal conditions at 160–230°C and 15–100 kg/cm2 for 1–2 hours. The anatase phase is produced from the same medium when sulfate ion impurity is present, with Image . Both these fine powders are converted to BaTiO3, SrTiO3 or CaTiO3 when suspended in Ba(OH)2 or Sr(OH)2 solution or in an aqueous slurry of carbonate-free CaO with Image , at 180–280°C and 12–65 kg/cm2 for 4–8 hours. The resulting fine powders contain monocrystallites of the perovskite phase with 0.1–1.5 μm particle size.

Infra-red spectra of crystalline chloroacetates of Cu, Ca, Sr, Ba and Pb

The infra-red spectra of Cu, Ca, Sr, Ba and Pb chloroacetates were studied in order to investigate the effect of co-ordination on the vibration spectra of the ligand. The shifts of the symmetric and antisymmetric COO− vibrational frequencies indicate a bridged structure as the most probable one for the complexes investigated. No linear relationship between the shifts of the COO− stretching frequencies and E/r (where E is the electron excitation energy and r the ionic radius) was observed. No systematic mass effect on these COO− frequencies also could be established.

Dielectric response in pulsed laser ablated (Ba,Sr)TiO3 thin films

The dielectric response of pulsed laser ablated barium strontium titanate thin films were studied as a function of frequency and ambient temperature (from room temperature to 320 degrees C) by employing impedance spectroscopy. Combined modulus and impedance spectroscopic plots were used to study the response of the film, which in general may contain the grain, grain boundary, and the electrode/film interface as capacitive elements. The spectroscopic plots revealed that the major response was due to the grains, while contributions from the grain boundary or the electrode/film interface was negligible. Further observation from the complex impedance plot showed data points lying on a single semicircle, implying the response originated from a single capacitive element corresponding to the bulk grains. Conductivity plots against frequency at different temperatures suggested a response obeying the 'universal power law'. The value of the activation energies computed from the Arrhenius plots of both ac and dc conductivities with 1000/T were 0.97 and 1.04 eV, respectively. This was found to be in excellent agreement with published literature, and was attributed to the motion of oxygen vacancies within the bulk. (C) 2000 American Institute of Physics. [S0021-8979(00)02801-2].

On superconducting Y-Ba-Cu-O films prepared by printing on lumina substrates

This Letter attempts to examine the impact of the chemical interaction of the alumina substrate on the Y-Ba-Cu-O film deposited on it.

Crystal chemistry of a new solid solution in the BaO-Bi2O3-Nb2O5 system: Ba-5x/2-Bi(1-x)5/3Nb5O15

A solid solution of the type Ba5x/2Bi(1-x)5/3Nb5O15 has been identified in the BaO-Bi2O3-Nb2O5 system for the first time. The limits of the solid solution are within the range 0.52 <= x <= 0.80. The compositions x = 0.52, 0.60, 0.72, 0.77, 0.78, and 0.80 were synthesized by the solid-state technique from the starting materials in stoichiometric quantities. The powder X-ray patterns of all the phases in the domain indicate a structural similarity to tetragonal tungsten bronzes (TTBs). The compositions below x = 0.52 and those above x = 0.80 exhibit barium niobate and bismuth niobate impurities, respectively. Single crystals of the composition x = 0.77 were obtained by the melt cooling technique. The crystal structure of Ba3.85/2Bi1.15/3Nb5O15 (x = 0.77) was solved in the tetragonal space group P4bm (No. 100) with a = 12.4938 (14) angstrom, c = 3.9519 (2) A, V = 616.87 (10) angstrom(3), and Z = 2 and was refined to an R index of 0.034. Dielectric measurements on all the phases indicate a typical relaxor behavior with a broad phase transition at T-m approximate to 300 K.

Trends in the stability of ternary oxides: Systems M-Pb-O (M = Ca, Sr, Ba)

Recent experimental investigations of phase equilibria and thermodynamic properties of the systems M-Pb-O, where M = Ca, Sr or Ba, indicate a regular increase in thermodynamic stability of ternary oxides, MPbO3 and M2PbO4, with increasing basicity of the oxide of the alkaline-earth metal. Number of stable interoxide compounds at 1100 K in the systems M-Pb-O (M = Mg, Ca, Sr, Ba) increases in unit increments from Mg to Ba. In this paper, experimentally determined standard Gibbs energies of formation of M2PbO4 (M = Ca, Sr, Ba) and MPbO3 (M = Sr, Ba) from their component binary monoxides and oxygen gas are combined with an estimated value for CaPbO3 to delineate systematic trends in thermodynamic stability of the ternary oxides. The trends are interpreted using concepts of tolerance factor and acid-base interactions. All the ternary oxides in these systems contain lead in the tetravalent state. The small Pb4+ ions polarize the surrounding oxygen ions and cause the formation of oxyanions which are acidic in character. Hence, the higher oxidation state of lead is stabilized in the presence of basic oxides of alkaline-earth group. A schematic subsolidus temperature-composition phase diagram is presented for the system BaO-PbO-O-2 to illustrate the change in oxidation states in binary and ternary oxides with temperature.

Microstructure related influence on the electrical properties of pulsed laser ablated (Ba, Sr)TiO3 thin films

The microstructural dependence of electrical properties of (Ba, Sr)TiO3(BST) thin films were studied from the viewpoint of dc and ac electrical properties. The films were grown using a pulsed laser deposition technique in a temperature range of 300 to 600 degrees C, inducing changes in grain size, structure, and morphology. Consequently, two different types of films were realized, of which type I, was polycrystalline, multigrained, while type II was [100] oriented possessing a densely packed fibrous microstructure. Leakage current measurements were done at elevated temperatures to provide evidence of the conduction mechanism present in these films. The results revealed a contribution from both electronic and ionic conduction. In the case of type I films, two trapping levels were identified with energies around 0.5 and 2.73 eV, which possibly originate from oxygen vacancies V-O and Ti3+ centers, respectively. These levels act as shallow and deep traps and are reflected in the current-voltage characteristics of the BST thin films. The activation energy associated with oxygen vacancy motion in this case was obtained as 1.28 eV. On the contrary, type II films showed no evidence of deep trap energy levels, while the identified activation energy associated with shallow traps was obtained as 0.38 eV. The activation energy obtained for oxygen vacancy motion in type II films was around 1.02 eV. The dc measurement results were further elucidated through ac impedance analysis, which revealed a grain boundary dominated response in type I in comparison to type II films where grain response is highlighted. A comparison of the mean relaxation time of the two films revealed three orders of magnitude higher relaxation time in the case of type I films. Due to smaller grain size in type I films the grains were considered to be completely depleted giving rise to only grain boundary response for the bulk of the film. The activation energy obtained from conductivity plots agree very well with that of dc measurements giving values 1.3 and 1.07 eV for type I and type II films, respectively. Since oxygen vacancy transport have been identified as the origin of resistance degradation in BST thin films, type I films with their higher value of activation energy for oxygen ion mobility explains the improvement in breakdown characteristics under constant high dc field stress. The role of microstructure in controlling the rate of degradation is found useful in this instance to enhance the film properties under high electric field stresses. (C) 2000 American Institute of Physics. [S0021-8979(00)00418-7].

High-temperature superconductivity in bismuth-copper oxides of the type BimMnCupOx (M=Mg, Ca, Sr, Ba, Bi)

Several oxides of the Bi m M n Cu p O x family (m=2, 3;n=2, 3, 4;p=1, 2, 3 and M=alkaline earth or Bi), possessing structures similar to the Aurivillius family of oxides, show highT c superconductivity.

Superconducting Y--Ba--Cu--O Thin Films by RF Sputtering

Thin films of Y--Ba--Cu--O have been prepared by conventional methods of RF sputtering. The films exhibit superconducting onset temperatures as high as 91K, midpoint at 80K and a zero resistance state at 35K. Critical current measurements implied critical current densities of the order of 31 A/cm exp 2 . An attempt has been made to establish the role of substrate and various deposition parameters. 7 ref.--AA.