Synthesis, characterization and chemical vapor deposition of transition metal di(tert-butyl)amido compounds

Although the transition metal chemistry of many dialkylamido ligands has been well studied, the chemistry of the bulky di(tert-butyl)amido ligand has been largely overlooked. The di(tert-butyl)amido ligand is well suited for synthesizing transition metal compounds with low coordination numbers; such compounds may exhibit interesting structural, physical, and chemical properties. Di(tert-butyl)amido complexes of transition metals are expected to exhibit high volatilities and low decomposition temperatures, thus making them well suited for the chemical vapor deposition of metals and metal nitrides. Treatment of MnBr₂(THF)₂, FeI₂, CoBr₂(DME), or NiBr₂(DME) with two equivalents of LiN(t-Bu)2 in benzene affords the two-coordinate complex M[N(t-Bu)₂]₂, where M is Mn, Fe, Co, or Ni. Crystallographic studies show that the M-N distances decrease across the series: 1.9365 (Mn), 1.8790 (Fe), 1.845 (Co), 1.798 Å (Ni). The N-M- N angles are very close to linear for Mn and Fe (179.30 and 179.45°, respectively), but bent for Co and Ni (159.2 and 160.90°, respectively). As expected, the d⁵ Mn complex has a magnetic moment of 5.53 μΒ that is very close to the spin only value. The EPR spectrum is nearly axial with a low E/D ratio of 0.014. The d⁶ Fe compound has a room temperature magnetic moment of 5.55 μΒ indicative of a large orbital angular momentum contribution. It does not exhibit a Jahn-Teller distortion despite the expected doubly degenerate ground state. Applied field Mössbauer spectroscopy shows that the effective internal hyperfine field is unusually large, Hint = 105 T. The magnetic moments of Co[N(t-Bu)₂]₂ and Ni[N(t-Bu)₂]₂ are 5.24 and 3.02 μΒ respectively. Both are EPR silent at 4.2 K. Treatment of TiCl₄ with three equivalents of LiN(t-Bu)2 in pentane affords the briding imido compound Ti₂[μ-N(t-Bu)]₂Cl₂[N(t-Bu)₂]₂ via a dealkylation reaction. Rotation around the bis(tert-butyl)amido groups is hindered, with activation parameters of ΔH‡ = 12.8 ± 0.6 kcal mol-1 and ΔS‡ = -8 ± 2 cal K-1 ·mol-1, as evidenced by variable temperature 1H NMR spectroscopy. Treatment of TiCl₄ with two equivalents of HN(t-Bu)₂ affords Ti₂Cl₆[N(t-Bu)₂]₂. This complex shows a close-contact of 2.634(3) Å between Ti and the carbon atom of one of the CH₃ substituents on the tert-butyl groups. Theoretical considerations and detailed structural comparisons suggest this interaction is not agostic in nature, but rather is a consequence of interligand repulsions. Treatment of NiI₂(PPh3)₂ and PdCl₂(PPh₃)₂ with LiN(t-Bu)₂in benzene affords Ni[N(t-Bu)₂](PPh₃)I and Pd₃(μ₂-NBut₂)2(μ₂-PPh₂)Ph(PPh₃) respectively. The compound Ni[N(t-Bu)₂](PPh₃)I has distorted T-shape in geometry, whereas Pd₃(μ₂-NBut₂)₂(μ₂-PPh₂)Ph(PPh₃) contains a triangular palladium core. Manganese nitride films were grown from Mn[N(t-Bu)₂]₂ in the presence of anhydrous ammonia. The growth rate was several nanometers per minute even at the remarkably low temperature of 80⁰C. As grown, the films are carbon- and oxygen-free, and have a columnar morphology. The spacings between the columns become smaller and the films become smoother as the growth temperature is increased. The composition of the films is consistent with a stoichiometry of Mn₅N₂.

Mossbauer scattering studies with the isotopes Os186, Os188, Eu153 and Pr1410

U of I Only

Influence of applied uniaxial stress upon the ultraviolet absorption bands in KBr and KI

The influence of uniaxial stress upon three types of imperfections occurring in the alkali halide crystal lattice has been investigated. The imperfections are the interstitial atom, the interstitial ion, and the negative ion vacancy. The interstitial atom, or H center, is a paraelastic defect which assumes a preferential crystal orientation in the field of an external mechanical stress. From the results of the reorientation kinetics - studies, it was possible to show that H centers are not stable in the KBr crystal lattice above 2SoK. At temperatures higher than 2SoK, the H centers are transformed into two new paraelastic defects, H(ii) and H(iii), possessing the same optical absorption band as the H center but differing both from the H' center and from each other in their reorientation kinetics. A study of the wavelength dependence of the H, H(ii), and VI (Na+) centers s~owed the 'existence of three similar-polarized transitions for each of these defects. One of these transitions, located at 230 run for all of the defects studied, was determined to be too high in energy to be explained by the simple X2 - level scheme. In addition, a comparison of various properties of the four defects indicates that the last three can be described as perturbed H centers. Dichroism measurements, performed as a function of temperature and wavelengt, h on the 230-nm I band in KBr, showed this band to be a composite of a band at 234 nm due to the I center and a band at 230 nm attributed to the H center. The I center dichroism was isolated and was observed under various experimental conditions. The results of these observations are consistent with a body-centered model for the I center in which the I-center absorption band is attributed to the excitation of a p-like electron on the interstitial Br- ion. Similar measurements were also perfonned on the a band in KI. The a-band dichroism measurements were found to be consistent with an electronic transition from an s-like ground state to a p-like excited state, indicating that the a center is best described as a quasi-molecule.