Size effects on self-assembly and melting of silver-alkanethiolate on inert surfaces

Self-assembled materials produced in the reaction between alkanethiol and Ag are characterized and compared. It is revealed that the size of the Ag substrate has a significant role in the self-assembly process and determines the reaction products. Alkanethiol adsorbs on the surface of Ag continuous planar thin films and only forms self-assembled monolayers (SAMs), while the reaction between alkanethiol and Ag clusters on inert surfaces is more aggressive and generates a significantly larger amount of alkanethiolate. Two dissimilar products are yielded depending on the size of the clusters. Small Ag clusters are more likely to be converted into multilayer silver-alkanethiolate (AgSR, R = CnH2n+1) crystals, while larger Ag clusters form monolayer-protected clusters (MPCs). The AgSR crystals are initially small and can ripen into large lamellae during thermal annealing. The crystals have facets and flat terraces with extended area, and have a strong preferred orientation in parallel with the substrate surface. The MPCs move laterally upon annealing and reorganize into a single-layer network with their separation distance approximately equal to the length of an extended alkyl chain. AgSR lamellar crystals grown on inert surfaces provide an excellent platform to study the melting characteristics of crystalline lamellae of polymeric materials with the thickness in the nanometer scale. This system is also unique in that each crystal has integer number of layers – magic-number size (thickness). The size of the crystals is controlled by adjusting the amount of Ag and the annealing temperature. X-ray diffraction (XRD) and atomic force microscopy (AFM) are combined to accurately determine the size (number of layers) of the lamellar crystals. The melting characteristics are measured with nanocalorimetry and show discrete melting transitions which are attributed to the magic-number sizes of the lamellar crystals. The discrete melting temperatures are intrinsic properties of the crystals with particular sizes. Smaller lamellar crystals with less number of layers melt at lower temperatures. The melting point depression is inversely proportional to the total thickness of the lamellae – the product of the number of layers and the layer thickness.

No right to sext? A critical examination of media and legal debates about teenage girls' sexual agency in the digital age

Advances in digital photography and distribution technologies enable many people to produce and distribute images of their sex acts. When teenagers do this, the photos and videos they create can be legally classified as child pornography since the law makes no exception for youth who create sexually explicit images of themselves. The dominant discussions about teenage girls producing sexually explicit media (including sexting) are profoundly unproductive: (1) they blame teenage girls for creating private images that another person later maliciously distributed and (2) they fail to respect—or even discuss—teenagers’ rights to freedom of expression. Cell phones and the internet make producing and distributing images extremely easy, which provide widely accessible venues for both consensual sexual expression between partners and for sexual harassment. Dominant understandings view sexting as a troubling teenage trend created through the combination of camera phones and adolescent hormones and impulsivity, but this view often conflates consensual sexting between partners with the malicious distribution of a person’s private image as essentially equivalent behaviors. In this project, I ask: What is the role of assumptions about teen girls’ sexual agency in these problematic understandings of sexting that blame victims and deny teenagers’ rights? In contrast to the popular media panic about online predators and the familiar accusation that youth are wasting their leisure time by using digital media, some people champion the internet as a democratic space that offers young people the opportunity to explore identities and develop social and communication skills. Yet, when teen girls’ sexuality enters this conversation, all this debate and discussion narrows to a problematic consensus. The optimists about adolescents and technology fall silent, and the argument that media production is inherently empowering for girls does not seem to apply to a girl who produces a sexually explicit image of herself. Instead, feminist, popular, and legal commentaries assert that she is necessarily a victim: of a “sexualized” mass media, pressure from her male peers, digital technology, her brain structures or hormones, or her own low self-esteem and misplaced desire for attention. Why and how are teenage girls’ sexual choices produced as evidence of their failure or success in achieving Western liberal ideals of self-esteem, resistance, and agency? Since mass media and policy reactions to sexting have so far been overwhelmingly sexist and counter-productive, it is crucial to interrogate the concepts and assumptions that characterize mainstream understandings of sexting. I argue that the common sense that is co-produced by law and mass media underlies the problematic legal and policy responses to sexting. Analyzing a range of nonfiction texts including newspaper articles, talk shows, press releases, public service announcements, websites, legislative debates, and legal documents, I investigate gendered, racialized, age-based, and technologically determinist common sense assumptions about teenage girls’ sexual agency. I examine the consensus and continuities that exist between news, nonfiction mass media, policy, institutions, and law, and describe the limits of their debates. I find that this early 21st century post-feminist girl-power moment not only demands that girls live up to gendered sexual ideals but also insists that actively choosing to follow these norms is the only way to exercise sexual agency. This is the first study to date examining the relationship of conventional wisdom about digital media and teenage girls’ sexuality to both policy and mass media.

Self-sealing of thermal fatigue and mechanical damage in fiber-reinforced composite materials

Fiber reinforced composite tanks provide a promising method of storage for liquid oxygen and hydrogen for aerospace applications. The inherent thermal fatigue of these vessels leads to the formation of microcracks, which allow gas phase leakage across the tank walls. In this dissertation, self-healing functionality is imparted to a structural composite to effectively seal microcracks induced by both mechanical and thermal loading cycles. Two different microencapsulated healing chemistries are investigated in woven glass fiber/epoxy and uni-weave carbon fiber/epoxy composites. Self-healing of mechanically induced damage was first studied in a room temperature cured plain weave E-glass/epoxy composite with encapsulated dicyclopentadiene (DCPD) monomer and wax protected Grubbs' catalyst healing components. A controlled amount of microcracking was introduced through cyclic indentation of opposing surfaces of the composite. The resulting damage zone was proportional to the indentation load. Healing was assessed through the use of a pressure cell apparatus to detect nitrogen flow through the thickness direction of the damaged composite. Successful healing resulted in a perfect seal, with no measurable gas flow. The effect of DCPD microcapsule size (51 um and 18 um) and concentration (0 - 12.2 wt%) on the self-sealing ability was investigated. Composite specimens with 6.5 wt% 51 um capsules sealed 67% of the time, compared to 13% for the control panels without healing components. A thermally stable, dual microcapsule healing chemistry comprised of silanol terminated poly(dimethyl siloxane) plus a crosslinking agent and a tin catalyst was employed to allow higher composite processing temperatures. The microcapsules were incorporated into a satin weave E-glass fiber/epoxy composite processed at 120C to yield a glass transition temperature of 127C. Self-sealing ability after mechanical damage was assessed for different microcapsule sizes (25 um and 42 um) and concentrations (0 - 11 vol%). Incorporating 9 vol% 42 um capsules or 11 vol% 25 um capsules into the composite matrix leads to 100% of the samples sealing. The effect of microcapsule concentration on the short beam strength, storage modulus, and glass transition temperature of the composite specimens was also investigated. The thermally stable tin catalyzed poly(dimethyl siloxane) healing chemistry was then integrated into a [0/90]s uniweave carbon fiber/epoxy composite. Thermal cycling (-196C to 35C) of these specimens lead to the formation of microcracks, over time, formed a percolating crack network from one side of the composite to the other, resulting in a gas permeable specimen. Crack damage accumulation and sample permeability was monitored with number of cycles for both self-healing and traditional non-healing composites. Crack accumulation occurred at a similar rate for all sample types tested. A 63% increase in lifetime extension was achieved for the self-healing specimens over traditional non-healing composites.