Nanofiltration membranes modified with aromatic polyamide dendrimers active layers

This thesis describes the modification of the commercial TFC-S nanofiltration membrane with shape-persistent dendritic architectures. Amphiphilic aromatic polyamide dendrimers (G1-G3) are synthesized via a divergent approach and used for membrane modification by direct percolation. The permeate samples collected from the percolation experiments are analyzed by UV-Vis spectroscopy to instantly monitor the influence of dendrimer generations on percolation behaviors and new active layer formation. The membrane structures are further characterized by Rutherford backscattering spectrometry (RBS) and atomic force microscopy (AFM) techniques, suggesting a low-level accumulation of dendrimers inside the TFC-S NF membranes and subsequent formation of an additional aramide dendrimer active layer. Thus, all the modified TFC-S membranes have a double active layer structure. A PES-PVA film is used as a control membrane showing that structural compatibility between the dendrimer and supports plays an important role in the membrane modification process. The performance of modified TFC-S membrane is evaluated on the basis of rejection abilities of a variety of water contaminants having a range of sizes and chemistry. As the water flux is inversely proportional to the thickness of the active layer, we optimize the amount of dendrimers deposited for specific contaminants to improve the solute rejection while maintaining high water flux.

Stoichiometry dependence of the evolution of the irradiated-induced defect clusters in lanthanum-doped ceria

To study the stoichiometry dependence of irradiation e ects in fluorite-type mixed oxide nuclear fuel (UPuO2), ion implantation in La doped ceria was used. Cerium dioxide single crystals with 0 mol%, 5 mol% and 25 mol% La concentration were irradiated with 1 MeV Kr ions at 800 C. In-situ transmission electron microscope (TEM) was utilized to observe the the damage process and defects created by the ion beam irradiation. Dislocation loops were observed after irradiation and were determined to be on {111} planes, but not on {220} or {200} planes. Ab substantial difference in the average size of dislocation loops for 0 %, 5% and 25% cases was observed at several doses.The growth rate of dislocation loops and the oxygen vacancy di usivity were found to be inversely correlated.