Wood properties and processing outcomes for plantation grown African mahogany (Khaya senegalensis) trees from Clare, Queensland (18 and 20 year-old trees) and Katherine, Northern Territory (14 year-old trees).

Khaya senegalensis, African mahogany, a high-value hardwood, was introduced in the Northern Territory (NT) in the 1950s; included in various trials there and at Weipa, Q in the 1960s-1970s; planted on ex mine sites at Weipa (160 ha) until 1985; revived in farm plantings in Queensland and in trials in the NT in the 1990s; adopted for large-scale, annual planting in the Douglas-Daly region, NT from 2006 and is to have the planted area in the NT extended to at least 20,000 ha. The recent serious interest from plantation growers, including Forest Enterprises Australia Ltd (FEA), has seen the establishment of some large scale commercial plantations. FEA initiated the current study to process relatively young plantation stands from both Northern Territory and Queensland plantations to investigate the sawn wood and veneer recovery and quality from trees ranging from 14 years (NT – 36 trees) to 18-20 years (North Queensland – 31 trees). Field measures of tree size and straightness were complemented with log end splitting assessment and cross-sectional disc sample collection for laboratory wood properties measurements including colour and shrinkage. End-splitting scores assessed on sawn logs were relatively low compared to fast grown plantation eucalypts and did not impact processing negatively. Heartwood proportion in individual trees ranged from 50% up to 92 % of butt cross-sectional disc area for the visually-assessed dark coloured central heartwood and lighter coloured transition wood combined. Dark central heartwood proportion was positively related to tree size (R2 = 0.57). Chemical tests failed to assist in determining heartwood – sapwood boundary. Mean basic density of whole disc samples was 658 kg/m3 and ranged among trees from 603 to 712 kg/m3. When freshly sawn, the heartwood of African mahogany was orange-red to red. Transition wood appeared to be pinkish and the sapwood was a pale yellow colour. Once air dried the heartwood colour generally darkens to pinkish-brown or orange-brown and the effect of prolonged time and sun exposure is to darken and change the heartwood to a red-brown colour. A portable colour measurement spectrophotometer was used to objectively assess colour variation in CIE L*, a* and b* values over time with drying and exposure to sunlight. Capacity to predict standard colour values accurately after varying periods of direct sunlight exposure using results obtained on initial air-dried surfaces decreased with increasing time to sun exposure. The predictions are more accurate for L* values which represent brightness than for variation in the a* values (red spectrum). Selection of superior breeding trees for colour is likely to be based on dried samples exposed to sunlight to reliably highlight wood colour differences. A generally low ratio between tangential and radial shrinkages was found, which was reflected in a low incidence of board distortion (particularly cupping) during drying. A preliminary experiment was carried out to investigate the quality of NIR models to predict shrinkage and density. NIR spectra correlated reasonably well with radial shrinkage and air dried density. When calibration models were applied to their validation sets, radial shrinkage was predicted to an accuracy of 76% with Standard Error of Prediction of 0.21%. There was also a strong predictive power for wood density. These are encouraging results suggesting that NIR spectroscopy has good potential to be used as a non-destructive method to predict shrinkage and wood density using 12mm diameter increment core samples. Average green off saw recovery was 49.5% (range 40 to 69%) for Burdekin Agricultural College (BAC) logs and 41.9% (range 20 to 61%) for Katherine (NT) logs. These figures are about 10% higher than compared to 30-year-old Khaya study by Armstrong et al. (2007) however they are inflated as the green boards were not docked to remove wane prior to being tallied. Of the recovered sawn, dried and dressed volume from the BAC logs, based on the cambial face of boards, 27% could potentially be used for select grade, 40% for medium feature grade and 26% for high feature grades. The heart faces had a slightly higher recovery of select (30%) and medium feature (43%) grade boards with a reduction in the volume of high feature (22%) and reject (6%) grade boards. Distribution of board grades for the NT site aged 14 years followed very similar trends to those of the BAC site boards with an average (between facial and cambial face) 27% could potentially be used for select grade, 42% for medium feature grade, 26% for high feature grade and 5% reject. Relatively to some other subtropical eucalypts, there was a low incidence of borer attack. The major grade limiting defects for both medium and high feature grade boards recovered from the BAC site were knots and wane. The presence of large knots may reflect both management practices and the nature of the genetic material at the site. This stand was not managed for timber production with a very late pruning implemented at about age 12 years. The large amount of wane affected boards is indicative of logs with a large taper and the presence of significant sweep. Wane, knots and skip were the major grade limiting defects for the NT site reflecting considerable amounts of sweep with large taper as might be expected in younger trees. The green veneer recovered from billets of seven Khaya trees rotary peeled on a spindleless lathe produced a recovery of 83% of green billet volume. Dried veneer recovery ranged from 40 to 74 % per billet with an average of 64%. All of the recovered grades were suitable for use in structural ply in accordance to AS/NZ 2269: 2008. The majority of veneer sheets recovered from all billets was C grade (27%) with 20% making D grade and 13% B grade. Total dry sliced veneer recovery from the logs of the two largest logs from each location was estimated to be 41.1%. Very positive results have been recorded in this small scale study. The amount of colour development observed and the very reasonable recoveries of both sawn and veneer products, with a good representation of higher grades in the product distribution, is encouraging. The prospects for significant improvement in these results from well managed and productive stands grown for high quality timber should be high. Additionally, the study has shown the utility of non-destructive evaluation techniques for use in tree improvement programs to improve the quality of future plantations. A few trees combined several of the traits desired of individuals for a first breeding population. Fortunately, the two most promising trees (32, 19) had already been selected for breeding on external traits, and grafts of them are established in the seed orchard.

Soil properties and crop yields in a dryland Vertisol sown with cotton-based crop rotations

Information on the effects of growing cotton (Gossypium hirsutum L.)-based crop rotations on soil quality of dryland Vertisols is sparse. The objective of this study was to quantify the effects of growing cereal and leguminous crops in rotation with dryland cotton on physical and chemical properties of a grey Vertisol near Warra, SE Queensland, Australia. The experimental treatments, selected after consultations with local cotton growers, were continuous cotton (T1), cotton-sorghum (Sorghum bicolor (L.) Moench.) (T2), cotton-wheat (Triticum aestivum L.) double cropped (T3), cotton-chickpea (Cicer arietinum L.) double cropped followed by wheat (T4) and cotton-wheat (T5). From 1993 to 1996 land preparation was by chisel ploughing to about 0.2 m followed by two to four cultivations with a Gyral tyne cultivator. Thereafter all crops were sown with zero tillage except for cultivation with a chisel plough to about 0.07-0.1 m after cotton picking to control heliothis moth pupae. Soil was sampled from 1996 to 2004 and physical (air-filled porosity of oven-dried soil, an indicator of soil compaction; plastic limit; linear shrinkage; dispersion index) and chemical (pH in 0.01 M CaCl2, organic carbon, exchangeable Ca, Mg, K and Na contents) properties measured. Crop rotation affected soil properties only with respect to exchangeable Na content and air-filled porosity. In the surface 0.15 m during 2000 and 2001 lowest air-filled porosity occurred with T1 (average of 34.6 m3/100 m3) and the highest with T3 (average of 38.9 m3/100 m3). Air-filled porosity decreased in the same depth between 1997 and 1998 from 45.0 to 36.1 m3/100 m3, presumably due to smearing and compaction caused by shallow cultivation in wet soil. In the subsoil, T1 and T2 frequently had lower air-filled porosity values in comparison with T3, T4 and T5, particularly during the early stages of the experiment, although values under T1 increased subsequently. In general, compaction was less under rotations which included a wheat crop (T3, T4, T5). For example, average air-filled porosity (in m3/100 m3) in the 0.15-0.30 m depth from 1996 to 1999 was 19.8 with both T1 and T2, and 21.2 with T3, 21.1 with T4 and 21.5 with T5. From 2000 to 2004, average air-filled porosity (in m3/100 m3) in the same depth was 21.3 with T1, 19.0 with T2, 19.8 with T3, 20.0 with T4 and 20.5 with T5. The rotation which included chickpea (T4) resulted in the lowest exchangeable Na content, although differences among rotations were small. Where only a cereal crop with a fibrous root system was sown in rotation with cotton (T2, T3, T5) linear shrinkage in the 0.45-0.60 m depth was lower than in rotations, which included tap-rooted crops such as chickpea (T4) or continuous cotton (T1). Dispersion index and organic carbon decreased, and plastic limit increased with time. Soil organic carbon stocks decreased at a rate of 1.2 Mg/ha/year. Lowest average cotton lint yield occurred with T2 (0.54 Mg/ha) and highest wheat yield with T3 (2.8 Mg/ha). Rotations which include a wheat crop are more likely to result in better soil structure and cotton lint yield than cotton-sorghum or continuous cotton.

Sap properties and alk(en)ylresorcinol concentrations in Australian-grown mangoes.

Physical and chemical properties of sap and sap concentrations of constitutive alk(en)ylresorcinols were determined in several varieties of mango grown in different locations in Queensland, Australia, over two consecutive cropping seasons. Sap weight from individual fruit, sap pH, percentage of non-aqueous sap and concentrations of constitutive alk(en)ylresorcinols (5-n-heptadecenylresorcinol and 5-n-pentadecylresorcinol) in sap varied significantly among the varieties. 'Calypso', 'Keitt', 'Kensington Pride' and 'Celebration' had the greatest proportion of non-aqueous sap, whereas 'Nam Doc Mai' had the least. The highest concentrations of 5-n-heptadecenylresorcinol were found in the sap of 'Kensington Pride', and the lowest in 'Honey Gold' and 'Nam Doc Mai'. Highest concentrations of 5-n-pentadecylresorcinol were found in sap of 'Calypso' and 'Celebration', and the lowest levels were in 'Honey Gold' and 'Nam Doc Mai'. There was a direct relationship between the percentage of non-aqueous sap and the concentrations of alk(en)ylresorcinols (r(2) = 0.77 for 5-n-heptadecenylresorcinol, and r(2) = 0.87 for 5-n-pentadecylresorcinol). The alk(en)ylresorcinols were distributed mainly in the upper non-aqueous phase of 'Kensington Pride' sap. Growing location also had significant effects on the composition of mango sap but the effects appeared to be related to differences in maturity. Sap removal is necessary to prevent sapburn, but considerable quantities of alk(en)ylresorcinols that assist in protecting the harvested fruit from anthracnose disease are also removed.

Wood properties and knot occlusion of plantation grown Eucalyptus dunnii and Corymbia citriodora subsp. variegata in a pruning and thinning experiment.

A 2 × 2 factorial combination of thinned or unthinned, and pruned or unpruned 11-year-old Eucalyptus dunnii (DWG) and 12-year-old Corymbia citriodora subsp. variegata (CCV) was destructively sampled to provide 60 trees in total per species. Two 1.4 m long billets were cut from each tree and were rotary veneered in a spindleless lathe down to a 45 mm diameter core to expose knots which were classified as either alive, partially occluded or fully occluded. Non-destructive evaluation of a wider range of thinning treatments available in these trials was undertaken with Pilodyn and Fakopp tools. Disc samples were also taken for basic density and modulus of elasticity. Differences between treatments for all wood property assessments were generally small and not significantly different.Thinning and pruning had little effect on the stem diameter growth required to achieve occlusion, therefore occlusion would be more rapid after thinning due to more rapid stem diameter growth. The difference between the treatments of greatest management interest, thinned and pruned (T&P) and unthinned and unpruned (UT&UP) were small. The production of higher value clear wood produced after all knots had occluded, measured as the average stem diameter growth over occlusion of the three outermost knots, was approximately 2 centimetres diameter. Two of the treatments can be ruled out as viable management alternatives: (i) the effect of thinning without pruning (T&UP) is clear, leading to a large inner core of stem wood containing knots (large knotty core diameter) and (ii) pruning without thinning (UT&P) results in a small knotty core diameter, however the tree and therefore log diameters are also small.

Characterisation of wood properties and transverse anatomy for vacuum drying modelling of commercially important Australian hardwood species.

Characterisation and investigation of a number of key wood properties, critical for further modelling work, has been achieved. The key results were: • Morphological characterisation, in terms of fibre cell wall thickness and porosity, was completed. A clear difference in fibre porosity, size, wall thickness and orientation was evident between species. Results were consistent with published data for other species. • Viscoelastic properties of wood were shown to differ greatly between species and in the radial and tangential directions, largely due to anatomical and chemical variations. Consistent with published data, the radial direction shows higher stiffness, internal friction and glass transition temperature than the tangential directions. The loss of stiffness over the measured temperature range was greater in the tangential direction than the radial direction. Due to time dependant molecular relaxation, the storage modulus and glass transition temperature decreased with decreasing test frequency, approaching an asymptotic limit. Thus the viscoelastic properties measured at lower frequencies are more representative of static material. • Dynamic interactions between relative humidity, moisture content and shrinkage of four Australian hardwood timbers can be accurately monitored on micro-samples using a specialised experimental device developed by AgroParisTech – ENGREF. The device generated shrinkage data that varied between species but were consistent (repeatable) within a species. Collapse shrinkage was clearly evident with this method for Eucalyptus obliqua, but not with other species, consistent with industrial seasoning experience. To characterise the wood-water relations of this species, free of collapse, thinner sample sections (in the R-T plane) should be used.

Construction timbers in Queensland. Book 1 and Book 2: Properties and specifications for satisfactory performance of construction timbers in Queensland. Class 1 and Class 10 buildings (houses, carports, garages, greenhouses and sheds). 2013 edition.

This publication lists the more important wood properties of commercial timbers used for construction in Queensland. It also provides requirements and conditions of use for these timbers to provide appropriate design service life in various construction applications. The correct specification of timber considers a range of timber properties including, but not limited to, stress grade; durability class; moisture content and insect resistance. For the specification of timber sizes and spans, relevant Australian Standards and design manuals should be consulted—e.g. Australian Standard AS 1684 series Residential timber—framed construction parts 2 and 3 (Standards Australia 2006a;b.) Book 1 explains the terms used; with reference to nomenclature; origin and timber properties presented under specific column headings in the schedules (Book 2). It also explains target design life; applications and decay hazard zones; presented in the Book 2 Schedules. Book 2 consists of reference tables; presented as schedules A; B and C: • Schedule A contains commercial mixtures of unidentified timbers and of some Australian and imported softwoods. Index numbers 1–10 • Schedule B contains Australian-grown timber species; including both natural forests and plantations. Index numbers 11–493 • Schedule C contains timbers imported into Australia from overseas. Index numbers 494–606 Each schedule has two parts presenting data in tables. • Part 1: Nomenclature, origin and properties of imported timber species • Part 2: Approved uses for commercial mixtures of imported timber species The recommendations made in this publication assume that good building practice will be carried out.