Electrical characterization of amorphous silicon MIS-based structures for HIT solar cell applications

A complete electrical characterization of hydrogenated amorphous silicon layers (a-Si:H) deposited on crystalline silicon (c-Si) substrates by electron cyclotron resonance chemical vapor deposition (ECR-CVD) was carried out. These structures are of interest for photovoltaic applications. Different growth temperatures between 30 and 200 °C were used. A rapid thermal annealing in forming gas atmosphere at 200 °C during 10 min was applied after the metallization process. The evolution of interfacial state density with the deposition temperature indicates a better interface passivation at higher growth temperatures. However, in these cases, an important contribution of slow states is detected as well. Thus, using intermediate growth temperatures (100–150 °C) might be the best choice.

Thermal stability study of AlGaN/GaN MOS-HEMTs using Gd2O3 as gate dielectric

Thermal stability of AlGaN/GaN MOS-HEMTs and -diodes using Gd_(2)O_(3) are investigated by means of different thermal cycles and storage tests up to 500ºC for one week. IV DC and pulsed characteristics of the devices before and after the processes are evaluated and compared with conventional HEMTs. Results show that the devices with Gd_(2)O_(3) dielectric layer have lower leakage current and a more stable behavior during thermal treatment processes compared with conventional devices. In fact, an excellent on/off ratio of about 108 and a stable V_(t) is observed after storage at high temperature. The beneficial effects of Gd_(2)O_(3) on trapping effects of MOS-HEMTs are also dis-cussed.