The effect of acidity on olefin aromatization over potassium modified ZSM-5 catalysts

The transformation of olefin to aromatics over ZSM-5 catalysts with different K-loadings has been investigated both in a continuous flow fixed-bed reactor and in a pulse microreactor. Investigation of variation of olefin aromatization activity with K-loadings shows that strong acid sites are indispensable for the converting of olefin to aromatics. As intermediates of olefin aromatization process, butadiene and cyclopentene not only show much higher aromatization activity than mono-olefins, but also can be transformed into aromatics over relatively weak acid sites of K/ZSM-5. A proposal is put forward, stating that among all the steps experienced in olefins aromatization, the formation of diene or cycloolfin from mono-olefins through hydrogen transfer is the key step and can be catalyzed by strong acid sites.

Effect of acid strength distribution on conversion of FCC gasoline over a ZSM-5 zeolite catalyst

Acid strength distribution and the distribution of aromatics formed in the FCC gasoline conversion reaction on a ZSM-5 zeolite with different Na contents have been studied. With increasing Na content in the ZSM-5 zeolite, the acid sites determined by NH3-TPD technique, especially the strong acid sites, clearly decrease. When used as catalyst for the aromatization reaction, the transformation of olefins in the FCC gasoline into aromatics is governed directly by the strong acid sites on the ZSM-5 catalyst. Only under the conditions that a ZSM-5 catalyst possesses suitable strong acid sites is reaction temperature favorable for the aromatics formed.

On configuration of exchanged La3+ on ZSM-5: A theoretical approach to the improvement in hydrothermal stability of La-modified ZSM-5 zeolite

Density functional calculations have been employed to investigate the locating and binding of lanthanum cation, i.e., La(OH)(2)(+), on HZSM-5 zeolite. Through geometry optimization, it was determined that lanthanum ions are favorably accommodated in the two 6-T rings of the straight channels (Clusters 1 and 2, see Sec. III A for details). Cluster 1 was found to exist in prior to Cluster 2 due to the preference of Al substitution in the T11 site (Cluster 1) rather than in the T8 site (Cluster 2). Geometry-optimization of Cluster 1 containing another two lanthanide ions Nd3+ and Yb3+ was also carried out and it was found that a monotonic decrease in Ln-O bond length will take place as the atomic number increases, conforming well to the rule of lanthanide contraction. Some of the optimized parameters are comparable to the corresponding experimental values in Y zeolite, which confirms that the optimized configurations are acceptable. The average frequencies of hydroxyls attached to La3+ or Yb3+ in Cluster 1 fall at 3609.16 and 3579.76 cm(-1), respectively, with the gap of these two frequencies close to that in the sodalite cage of Y zeolite. Compared to H-form zeolite, the charges on both Al and O atoms in Ln-ZSM-5 zeolite show an obvious increase, which will undoubtedly lead to a stronger mutual interaction and hence enhance the stability of the [AlO4](-) anion. Moreover, the Ln(OH)(2)(+) seem to have thickened the zeolite framework, which can effectively retard the process of dealumination. Through the evaluation of the possibility for dimer formation, it turned out that when the exchange degree arrived to approximately 0.28, lanthanum monomers began to aggregate into dimers, and were completely converted into dimers when the exchange degree approached 0.60. (C) 2003 American Institute of Physics.

Enhancement on the hydrothermal stability of ZSM-5 zeolites by the cooperation effect of exchanged lanthanum and phosphoric species

It was explored by density functional calculations that exchanged La or P species exert great influence on the local Al sites as well as on the adjacent exchanged species. In partially exchanged La- or P/H-ZSM-5 zeolite, some of the Al sites will fall off from the zeolite framework even more easily than in H-form ZSM-5, consistent with our XRF experiments. However, when exchanged by both La and P species, Al at either of the two exchanged sites shows better stability compared to H-from. zeolite. La and P species will interact strongly with each other, as evidenced by the charge donation process and the shortening of P-O-1 bond length. It was just the cooperation of La and P species that enabled RSCC catalysts worked normally under severe conditions. (C) 2004 Elsevier B.V. All rights reserved.

Difference of ZSM-5 zeolites synthesized with various templates

ZSM-5 zeolites with similar SUM ratio were synthesized successfully using various templates (n-butylamine (BTA), ethylamine (ETA), isopropylamine (IPA), ethylenediamine (EDA), ethanol (ETL), ethanol-ammonium (ETL-AM) and no template (NT)) under hydrothermal conditions. The samples were characterized by XRD, SEM, XRF, NH3-TPD and BET surface area measurements in order to understand the template effects and the differences of the ZSM-5 samples. The synthesis of ZSM-5 with organic templates was relatively easier than those with inorganic templates and without template. SEM results revealed that ZSM-5 synthesized with different templates had different morphology and particle size. The Si/Al ratio and BET specific surface area of the sample with ethanol as template was the lowest. NH3-TPD results showed that the sample synthesized without template had fewer strong acid sites than others. n-Hexane cracking reaction was carried out over the samples to evaluate the catalytic properties. All ZSM-5 zeolites were effective in n-hexane cracking reaction, especially for the sample synthesized without template. (C) 2004 Elsevier B.V. All rights reserved.

On the selectively catalytic reduction of NOx with methane over Ag-ZSM-5 catalysts

The catalytic performance of silver-modified ZSM-5 catalysts in the selectively catalytic reduction (SCR) of NOx with methane was investigated. NO was selectively reduced by CH4 to N-2 in the presence of excess O-2, and the catalytic activity depended on both the activation of CH4 and the adsorption properties of NOx. Silver incorporated in ZSM-5 zeolite activated CH4 at low temperatures and lowered the "light-off" temperature for the CH4-SCR of NOx. Temperature-programmed (TP) spectroscopy studies depicted that surface nitrosyl species directly decomposed to N-2 in the absence of O-2. CH4 could not effectively reduce surface nitrosyl species, but might facilitate the direct decomposition of NO through the removal of surface oxygen. Surface nitrates were formed in NO and O-2 coexisting system and could be effectively reduced by CR4 to nitrogen. The priority of surface nitrates to O-2 in the reaction with CH4 clearly demonstrated that CH4 selectively and preferentially reduced the surface nitrate species to N-2 in the excess of oxygen. (C) 2002 Elsevier Science B.V. All rights reserved.

Ag-ZSM-5 catalyst for the catalytic decomposition of NO

The catalytic decomposition of NO over Ag-ZSM-5 catalyst prepared by ion-exchange was investigated. The exchanged silver in the zeolite was reduced and it collected in the course of the reaction to form silver particles of about 20 nm. The catalytic reaction induced a pronounced restructuring of the Ag particles through preferential formation of the (111) facets. These facets were shown to hind a tightly bound oxygen species (O-gamma). The O-gamma species occupies the active sites for NO adsorption resulting in catalyst deactivation. It could be removed by appropriate reducing agents, such as CO, to recover the active sites at elevated temperatures.

The study of Ti doped ZSM-5 particles and cavities inside them

The TEM study of titanium-containing ZSM-5 zeolite before and after hydrothermal treatment was performed. The use of different TEM techniques, such as conventional TEM, HRTEM and EDX-line scans provides important information about the microscopic structure of the zeolite catalyst consisting from several phases. The hydrothermal treatment of zeolite powder leads to strong changes in the morphology of the constituting particles. They are characterized by a homogeneous structure before hydrothermal treatment while the occurrence of holes after thermal treatment was observed, These changes lead to the enrichment of zeolite with titanium which obviously enhance its catalytic activity. Some of the titanium surplus precipitates as TiO2 anatase nanoparticles within the holes. (C) 2001 Elsevier Science B.V. All rights reserved.

Butene catalytic cracking to propene and ethene over potassium modified ZSM-5 catalysts

Catalytic cracking of butene over potassium modified ZSM-5 catalysts was carried out in a fixed-bed microreactor. By increasing the K loading on the ZSM-5, butene conversion and ethene selectivity decreased almost linearly, while propene selectivity increased first, then passed through a maximum (about 50% selectivity) with the addition of ca. 0.7-1.0% K, and then decreased slowly with further increasing of the K loading. The reaction conditions were 620 degrees C, WHSV 3.5 h(-1), 0.1 MPa 1-butene partial pressure and 1 h of time on stream. Both by potassium modification of the ZSM-5 zeolite and by N(2) addition in the butene feed could enhance the selectivity towards propene effectively, but the catalyst stability did not show any improvement. On the other hand, addition of water to the butene feed could not only increase the butene conversion, but also improve the stability of the 0.7%K/ZSM-5 catalyst due to the effective removal of the coke formed, as demonstrated by the TPO spectra. XRD results indicated that the ZSM-5 structure of the 0.07% K/ZSM-5 catalyst was not destroyed even under this serious condition of adding water at 620 degrees C.