A new class of high T-g and organosoluble polynaphthalimides

A new class of soluble six-membered ring polynaphthalimides (PNIs) was synthesized from asymmetrical fluorinated naphthalenesubstituted monomers. All the resulting PNIs were easily soluble in many organic solvents, such as N-methyl-2-pyrrolidinone (NMP), N,N-dimethylacetamide (DMAc), dimethyl sulfoxide (DMSO). and chloroform. They also showed good thermal stability with glass transition temperature of 340-386 degrees C, 10% weight loss temperature in excess of 529 degrees C. Polyimide 3c could be solution-cast into tough and flexible film. The film had a tensile strength, elongation at break, and Young's modulus of about 117.6 Wa, 23.6%, and 1.77 GPa, respectively. The gas permeation property of the film of 3c was investigated with oxygen permeability coefficient (PO2 = 3.99) and permeability selectivity coefficient of oxygen to nitrogen (P-O2/P-N2 = 5.27). Therefore, these materials are expected to be a good alternative to PIs based on five-membered rings with applications in gas separation membranes.

Preparation and characteristic of a new class of silica/polyimide nanocomposites

A new class of silica/polyimide nanocomposites was successfully prepared by the sol-gel reaction, tetraethoxysilane, (TEOS), was hydrolyzed by the water released from imidization at low and high temperature. Silica particles with diameter of around 30-50 nm were observed in the hybrid films by scanning electron microscopy. The flame retardance, decomposition temperature and glass transition temperature of the film increased with increasing silica content. The tensile strength increased slightly while the elongation at break of the films decreased with increasing silica content. (C) 2002 Kluwer Academic Publishers.