Synthesis and photoluminescence, field emission properties of stalactite-like ZnS-ZnO composite nanostructures

Wurtzite stalactite-like quasi-one-dimensional ZnS nanoarrays with ZnO protuberances were synthesized through a thermal evaporation route. The structure and morphology of the samples are studied and the growth mechanism is discussed. X-ray diffraction (XRD) results show both the ZnS stem and the ZnO protuberances have wurtzite structure and show preferred [001] oriented growth. The photoluminescence and field emission properties have also been investigated. Room temperature photoluminescence result shows it has a strong green light emission, which has potential application for green light emitter. Experimental results also show that the stalactite arrays have a good field emission property, with turn-on field of 11.4 V/mu m, and threshold field of 16 V/mu m. The ZnO protuberances on the ZnS stem might enhance the field emission notably.

Synthesis and properties of novel random and block copolymers composed of phthalimidine- and perfluoroisopropylidene-polyarylether-sulfones

A series of novel polyarylethersulfone (AB)(n) block copolymers with different segment lengths have been synthesized by nucleophilic solution polycondensation of phenoxide-terminated and fluorine-terminated oligomers; random copolymers have been prepared over the whole composition ranges. The structures of the resultant copolymers have been confirmed by FTIR, C-13 NMR spectra and differential scanning calorimetry (DSC). Compared with two homopolymers and random copolymers, the block copolymers of this study possess excellent thermal stability (5% thermal decomposition under nitrogen atmosphere above 500 C) and high glass transition temperatures, and have a wide melt-processing temperature range. They may become a new class of mouldable high performance thermoplastics. (C) 2001 Society of Chemical Industry.

Low-temperature molten salt synthesis and characterization of CoWO4 nano-particles

CoWO4 nano-particles were successfully synthesized at a low temperature of 270 degrees C by a molten salt method, and effects of such processing parameters as holding time and salt quantity on the crystallization and development Of CoWO4 crystallites were initially studied. The products were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM). and photoluminescent spectra techniques (PL), respectively. Experimental results showed that the well-crystallized CoWO4 nano-particles with ca. 45 nm in diameter could be obtained at 270 degrees C for a holding time of 8 h with 6:1 mass ratio of the salt to CoWO4 precursor, and XRD analysis evidenced that the as-prepared sample was a pure monoclinic phase Of CoWO4 with wolframite structure. Their PL spectra revealed that the CoWO4 nano-particles displayed a very strong PL peak at 453 nm with the excitation wavelength of 230 nm, and PL properties of CoWO4 crystallites relied on their crystalline state, especially on their particle size. (C) 2009 Elsevier B.V. All rights reserved.

Mesoporous spinel MgAl2O4 prepared by in situ modification of boehmite sol particle surface: I Synthesis and characterization of the unsupported membranes

Mesoporous spinel membranes as ultrafiltration membranes were prepared through a novel sol-gel technique. By in situ modification of the sol particle surface during the sol-gel process, control of the material structure on a nanometer scale from the earliest stages of processing was realized. Nano-particles with a chocolate-nut-like morphology, i.e. spinel MgAl2O4 as a shell and gamma -Al2O3 as a core, were first revealed by HRTEM results. The formation of the spinel phase was confirmed by X-ray diffraction (XRD). N-2 adsorption-desorption results showed that the mesoporous membranes had a narrow pore size distribution. (C) 2001 Elsevier Science B.V. All rights reserved.

Influences Of Precursor Constitution And Processing Speed On Microstructure And Wear Behavior During Laser Clad Composite Coatings On Gamma-Tial Intermetallic Alloy

The effects of constitution of precursor mixed powders and scan speed on microstructure and wear properties were designed and investigated during laser clad gamma/Cr7C3/TiC composite coatings on gamma-TiAl intermetallic alloy substrates with NiCr-Cr3C2 precursor mixed powders. The results indicate that both the constitution of the precursor mixed powders and the beam scan rate have remarkable influence on microstructure and attendant hardness as well as wear resistance of the formed composite coatings. The wear mechanisms of the original TiAl alloy and laser clad composite coatings were investigated. The composite coating with an optimum compromise between constitution of NiCr-Cr3C2 precursor mixed powders as well as being processed under moderate scan speed exhibits the best wear resistance under dry sliding wear test conditions. (C) 2008 Elsevier Ltd. All rights reserved.

Synthesis and characterization of photorefractive polymer based on chemically hybridized CdS-PVK nanocomposite with a new azo chromophore

We report an organic/inorganic polymer composite based on the chemically hybridized photoconductor CdS-PVK nanocomposite doped with a new second-order optically nonlinear chromophore 1-n-butoxy-2-methyl-(4-p-nitrophenylazo)benzene (BMNPAB) and plasticizer 9-ethyl-carbazole (ECZ) to manifest a photorefractive (PR) effect. A detailed description of the synthesis and characterization of BMNPAB is presented. The poled film including PVK-10-CdS nanocomposite and BMNPAB exhibits a high second harmonic generation (SHG) coefficient of 31 pm/V The photoconductivity of PVK-CdS nanocomposite also was studied here. Two-beam coupling experiment clearly indicated an asymmetric optical energy exchange between two beams on the polymer composite at zero electrical field, and the two-beam coupling gain of 50.0 cm(-1) and diffraction efficiencv of 4.2% were obtained at 647.1 nm wavelength. (C) 2007 Elsevier Ltd. All rights reserved.

Synthesis and formation mechanism of silver nanowires by a templateless and seedless method

Silver nanowires in large quantities can be obtained through a simple method in the absence of a surfactant or polymer and without addition of external seeding nanocrystallites. A plausible mechanism was proposed to elucidate the formation mechanism of silver nanowires based on TEM studies.

Direct synthesis and intense luminescence of Y2O3 : Eu nanophosphors by complexation combustion

In this paper, we report the synthesis of high-luminance Y2O3:Eu nanocrystal through a citrate-nitrate complexation combustion method at a low temperature of 200-280 degrees C. The as-combusted Y2O3:Eu phosphors are almost equiaxed crystallites with an average size of 30-40 run, and have an intense red luminescence. The present fuel-deficient method suggests that by control of the ratio of citric acid to nitrates, it is valuable for the fabrication of Y2O3 nanoparticles without heat treatment. This process should be applicable to a wide range of nanocrystal oxides.

Sol-gel combustion synthesis and luminescent properties of nanocrystalline YAG : Eu3+ phosphors

EU3+ -doped Y3Al5O12 (YAG:Eu3+) phosphors were synthesized by a facile sol-gel combustion method. In this process, citric acid traps the constituent cations and reduces the diffusion length of the precursors. YAG phase is obtained through sintering at 900 degrees C for 2h. There were no intermediate phases such as YAlO3 (YAP) and Y4Al2O9 (YAM) observed. The charge transfer band of nanocrystalline phosphors shows a shift toward the high-energy side, compared with that of amorphous ones due to lower covalency of Eu-O bond for nanocrystalline phosphors. The higher concentration quenching in YAG:EU3+ nanophosphors may be caused by the confinement effect on resonant energy transfer of nanocrystalline. It also indicates that the sol-gel combustion synthesis method provides a good distribution of Eu3+ activators in YAG host. (c) 2005 Elsevier B.V. All rights reserved.

Sol-gel combustion synthesis and luminescence Of Y4Al2O9 : Eu3+ nanocrystal

Y4Al2O9:EU3+ phosphor was synthesized through a sol-gel combustion method. The Y4Al2O9 phase can form through sintering at 800 degrees C. This temperature is much lower than that required via the solid state reaction method. The average grain size of the phosphor was about 30 run. Compared with the amorphous phosphor, the charge transfer band of crystalline phosphor shows a blue shift. The emission Of Y4Al2O9:Eu3+ indicates the existence of two luminescent centers, in agreement with the crystal structure of Y4Al2O9. Higher doping concentration could be realized in Y4Al2O9 nanocrystal host lattice. This indicates that the sol-gel combustion synthesis method can increase emission intensity and quenching concentration due to a good distribution of EU3+ activators in Y4Al2O9 host. (c) 2005 Elsevier B.V. All rights reserved.

Synthesis and magnetic properties of Ni-doped zinc oxide powders

Polycrystalline Zn1-xNixO diluted magnetic semiconductors have been successfully synthesized by an auto-combustion method. X-ray diffraction measurements indicated that the 5 at% Ni-cloped ZnO had the pure wurtzite structure. Refinements of cell parameters from powder diffraction data revealed that the cell parameters of Zn0.95Ni0.05O were a little bit larger than ZnO. Transmission electron microscopy observation showed that the as-synthesized powders were of the size similar to 60 nm. Magnetic investigations showed that the nanocystalline Zn0.95Ni0.05O possessed room temperature ferromagnetisin with the saturation magnetic moment of 0.1 emu/g (0.29 mu(B)/Ni2+). (c) 2005 Elsevier B.V. All rights reserved.

Synthesis and characterization of room-temperature ferromagnetism in Fe- and Ni-co-doped In2O3

Observation of room-temperature ferromagnetisin in Fe- and Ni-co-doped In2O3 samples (In0.9Fe0.1-xNix)(2)O-3 (0 <= x <= 0.1) prepared by citric acid sol-gel auto-igniting method is reported. All of the samples with intermediate x values are ferromagnetic at roomtemperature. The highest saturation magnetization (0.453 mu B/Fe + Ni ions) moment is reached in the sample with x = 0.04. The highest solubility of Fe and Ni ions in the In2O3 lattice is around 10 and 4 at%, respectively. The 10 at% Fe-doped sample is found to be weakly ferromagnetic, while the 10at% Ni-doped sample is paramagnetic. Extensive structure including Extended X-ray absorption fine structure (EXAFS), magnetic and magneto-transport including Hall effects studies on the samples indicate the observed ferromagnetism is intrinsic rather than from the secondary impurity phases. (c) 2007 Elsevier Ltd. All rights reserved.

Synthesis and characterizations of Al-doped Zn0.95Ni0.05O nanocrystals

Nanocrystalline Zn0.95-xNi0.05AlxO (x = 0.01, 0.02, 0.05 and 0.10) diluted magnetic semiconductors have been synthesized by an autocombustion method. X-ray absorption spectroscopy, high-resolution transmission electron microscopy, energy-dispersive spectrometry and Ni 2p core-level photoemission spectroscopy analyses revealed that some of the nickel ions were substituted for Zn2+ into the ZnO matrix while others gave birth to NiO nanoclusters embedded in the ZnO particles. The Zn0.95Ni0.05O sample showed no enhancement of room-temperature ferromagnetism after Al doping. (C) 2007 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Synthesis and luminescence characterization of cerium doped Lu2O3-Y2O3-La2O3 solid solution transparent ceramics

Ce3+:( Lu0.7Y0.25La0.05)(2)O-3 transparent ceramics were fabricated with nanopowders and sintered in H-2 atmosphere. The spectral properties of Ce3+:( Lu0.7Y0.25La0.05)(2)O-3 transparent ceramics were investigated and the luminescence of Ce3+ in the solid solution of Lu2O3, Y2O3 and La2O3 has been found. The ceramics has high density of 8.10g/cm(3) and short fluorescence lifetimes of 7.15 ns and 26.92 ns. It is expected to be a good fast response high temperature inorganic scintillating materials. (C) 2008 Optical Society of America.