Dissolved oxygen and O-2 flux across the water-air interface of the Changjiang Estuary in May 2003

The field observation of this study was carried out in the Changjiang Estuary from May 19 to 26,2003, just a few days before the Three Gorges Dam began to store water. A total of 29 stations, including 2 anchor stations, were distributed through almost the whole salinity gradient Based on the data gained from these stations, the biogeochemical characteristics of dissolved oxygen (DO) were examined. Spatial distribution of DO concentrations showed the pattern that it increased in a downriver direction. DO concentration generally varied within a narrow range of 733-8.10 mg l(-1) in the freshwater region and the west part of the mixed water region, and after that it increased rapidly. In vertical direction, the differences in DO concentrations between surface and 2 m above the bottom were big at the stations with water depths exceeding 20 m; DO concentration up to 14.88 mg l(-1) was recorded at the sea surface, while at 2 m above the bottom its concentration was only about 4 mg l(-1). The fluctuation in DO concentrations was small during a period of 48 h in the mixed water region and 2 m above the bottom of the seawater region; while it was large during the same period in the seawater region for surface and 5 m below the surface layer, and a maximum variation from 8.77 to 12.66 mg l(-1) in 4 h was recorded. Oxygen fluxes also showed a marked spatio-temporal variation. As a whole, the freshwater region and mixed water region were an oxygen sink while the seawater region was a source. Relationships between dissolved oxygen and some biogeochemical parameters which could markedly influence its spatio-temporal distribution were discussed in this paper. (C) 2008 Elsevier B.V. All rights reserved.

Partial oxidation of ethane to syngas in an oxygen-permeable membrane reactor

A perovskite-type oxide of Ba0.5Sr0.5Co0.8Fe0.2O3-delta (BSCFO) with mixed electronic and oxygen ionic conductivity at high temperatures was used as an oxygen-permeable membrane. A tubular membrane of BSCFO made by extrusion method has been used in the membrane reactor to exclusively transport oxygen for the partial oxidation of ethane (POE) to syngas with catalyst of LiLaNiO/gamma-Al2O3 at temperatures of 800-900 degreesC. After only 30 min POE reaction in the membrane reactor, the oxygen permeation flux reached at 8.2 ml cm(-2) min(-1). After that, the oxygen permeation flux increased slowly and it took 12 h to reach at 11.0 ml cm(-2) min(-1). SEM and EDS analysis showed that Sr and Ba segregations occurred on the used membrane surface exposed to air while Co slightly enriched on the membrane surface exposed to ethane. The oxygen permeation flux increased with increasing of concentration of C2H6, which was attributed to increasing of the driving force resulting from the more reducing conditions produced with an increase of concentration of C2H6 in the feed gas. The tubular membrane reactor was successfully operated for POE reaction at 875 degreesC for more than 100 h without failure, with ethane conversion of similar to 100%, CO selectivity of >91% and oxygen permeation fluxes of 10-11 ml cm(-2) min(-1). (C) 2002 Elsevier Science B.V. All rights reserved.

Perovskite-type B-site Bi-doped ceramic membranes for oxygen separation

Novel mixed conducting oxides, B-site Bi-doped perovskites were exploited and synthesized. Cubic perovskite structures were formed for BaBi0.2COyFe0.8-yO3-delta (y less than or equal to 0.4) and BaBixCo0.2Fe0.8-xP3-delta (x=0.1-0.5) The materials exhibited considerable high oxygen permeability at high temperature. The oxygen permeation flux of BaBi0.2Co0.35Fe0.45O3-delta membrane reached about 0.77 x 10(-6) mol/cm(2) s under an air/helium oxygen partial pressure gradient at 900 degrees C, which was much higher than that of other bismuth-contained mixed conducting membranes. The permeation fluxes of the materials increased with the increase of cobalt content, but no apparent simple relationship was found with the bismuth content. The materials also demonstrated excellent reversibility of oxygen adsorption and desorption. Stable time-related oxygen permeation fluxes were found for BaBi0.2CO0.35Fe0.45O3-delta and BaBi0.3Co0.2Fe0.5O3-delta a membranes at 875 degrees C.

Synthesis and characterization of gallium-based perovskite-type dense membrane with oxygen semipermeability

La0.15Sr0.85Ga0.3Fe0.7O3-delta (LSGFO) and La0.15Sr0.85Co0.3Fe0.7O3-delta (LSCFO) mixed oxygen-ion and electron conducting oxides were synthesized by using a combined EDTA and citrate complexing method, and the corresponding dense membranes were fabricated. The properties of the oxide powders and membranes were characterized with combined SEM, XRD, H-2-TPR, O-2-TPD techniques, mechanical strength and oxygen permeation measurement. The results showed that LSGFO had much higher thermochemical stability than LSCFO due to the higher valence stability of Ga3+. After the temperature-programmed reduction by 5% H-2 in Ar from 20 degreesC to 1020 degreesC, the basic perovskite structure of LSGFO was successfully preserved. LSGFO also favors the oxygen vacancy formation better than LSCFO. Oxygen permeation measurement demonstrated that LSGFO had higher oxygen permeation flux than LSCFO, but they had similar activation energy for oxygen transportation, with a value of 110 and 117 kJ . mol(-1), respectively The difference in oxygen permeation fluxes was correlated with the difference in oxygen vacancy concentrations for the two materials.