Cr4+在Al2O3多晶体中的光谱性能研究

Transparent polycrystalline Cr:Al2O3 ceramics were synthesized by conventional pressureless synthesis processing. The absorption and emission spectra of Cr:Al2O3 ceramics specimens before and after annealing were measured at room temperature. It was discovered that the emission spectra of Cr4+ in Al2O3 octahedral coordination site is in infrared wavelength range of 1100-1600 nm. The emission peak of Cr4+ is centered at 1223 nm, which is similar to that of Cr4+ in tetrahedral site. Al2O3 has smaller lattice constant, resulting in the larger crystal field strength, so there is a blue shift in the peak of Cr4+:Al2O3 ceramics compared to those of other Cr4+-doped crystals. And the emission band is much narrower with full width at half maximum Delta lambda 37 nm.

Enhancement of 1.53 mu m photoluminescence from spin-coated Er-Si-O (Er2SiO5) crystalline films by nitrogen plasma treatment

Er-Si-O (Er2SiO5) crystalline films are fabricated by the spin-coating and subsequent annealing process. The fraction of erbium is estimated to be 21.5 at% based on Rutherford backscattering measurement. X-ray diffraction pattern indicates that the Er-Si-O films are similar to Er2SiO5 compound in the crystal structure. The fine structure of room-temperature photoluminescence of Er3+-related transitions suggests that Er has a local environment similar to the Er-O-6 octahedron. Our preliminary results show that the intensity of 1.53 mu m emission is enhanced by a factor of seven after nitrogen plasma treatment by NH3 gas with subsequent post-annealing. The full-width at half-maximum of 1.53 pm emission peak increases from 7.5 to 12.9 nm compared with that of the untreated one. Nitrogen plasma treatment is assumed to tailor Er3+ local environment, increasing the oscillator strength of transitions and thus the excitation/emission cross-section. (c) 2005 Elsevier B.V. All rights reserved.

Void-like defects in annealed Czochralski silicon

Void-like defects of octahedron structure having {111} facets were observed in annealed Czochralski silicon. The amorphous coverage of SiOx and SiCx on the inner surface of the defects was identified using transmission electron microscopy and electron energy-loss spectroscopy. It is suggested that these defects are a kind of amorphous precipitate origin. A mechanism for the generation of these defects and the previously reported solid amorphous precipitates is proposed. (C) 1998 American Institute of Physics. [S0003-6951(98)02842-3].

Solvothermal synthesis of well-dispersed MF2 (M = Ca, Sr, Ba) nanocrystals and their optical properties

MF2 (M = Ca, Sr, Ba) nanocrystals (NCs) were synthesized via a solvothermal process in the presence of oleic acid and characterized by x-ray diffraction (XRD), transmission electron microscopy (TEM), Fourier transform infrared (FT-IR) spectra, UV/vis absorption spectra, photoluminescence (PL) excitation and emission spectra, and lifetimes, respectively. In the synthetic process, oleic acid as a surfactant played a crucial role in confining the growth and solubility of the MF2 NCs. The as-prepared CaF2, SrF2 and BaF2 NCs present morphologies of truncated octahedron, cube and sheet in a narrow distribution, respectively.

Fabrication and characterization of uniform Fe3O4 octahedral micro-crystals

Uniform Fe3O4 octahedral microcrystals with perfect appearance have been successfully synthesized by a Triton X100-assisted polyol process. During the polyols process for the preparation of Fe3O4 octahedra. the introduction of Triton X100 decreases significantly the needed concentration of NaOH. The results show that Fe3O4 octahedra are composed of eight triangular sheets, which are equilateral triangles. The edge size of Fe3O4 octahedron is about 4 mu m. The magnetic properties of Fe3O4 octahedral particles were evaluated on a SQUID magnetometer at room temperature.

Alternating Copolymerization of Carbon Dioxide and Propylene Oxide Catalyzed by Cobalt Schiff Base Complex

Cobalt 2,4-dinitrophenolate (complex 1) based upon a N,N,O,O-tetradentate Schiff base ligand framework was prepared. X-ray diffraction analysis confirmed that complex 1 was triclinic species with a six-coordinated central cobalt octahedron in the solid. Asymmetric alternating copolymerization of carbon dioxide (CO2) with racemic propylene oxide (rac-PO) proceeded effectively by complex 1 in conjunction with (4-dimethylamino)pyridine (DMAP), yielding a perfectly alternating and bimodal molecular weight distribution PO/CO2 poly(propylene carbonate) (PPC) with a small amount of cyclic carbonate byproducts.

Active site structure of NO decomposition on perovskite(-like) oxides: An investigation from experiment and density functional theory

Active site structure for NO decomposition carried out on perovskite-like oxides were discussed based on the N-2 yield measured from LaSrNi1-x,AlxO4 with different B-site cations and from La2-ySryCuO4 with different crystal phases. Results show that the active site contains two oxygen vacancies, two transition metals, and one lattice-oxygen, with the oxygen vacancy locating on the apex of MO6 octahedron, and the lattice oxygen locating between the two transition metals (i.e., M-O-M plane). Density functional theory (DFT) analysis to the structure shows that this new active site is the most active structure for NO adsorbing, and hence, for NO decomposition. The similar trend of the relative energies that are required for the formation of oxygen vacancies with f form (calculated from DFT), the amount of oxygen vacancies, and the activities (N-2 yield) certifies this result further.

Rare earth metal complexes bearing thiophene-amido ligand: Synthesis and structural characterization

2,6-Diisopropyl-N-(2-thienylmethyl) aniline ( H2L) has been prepared, which reacted with equimolar rare earth metal tris( alkyl)s, Ln( CH2SiMe3)(3)( THF)(2), afforded rare earth metal mono( alkyl) complexes, LLn(CH2SiMe3)(THF)(3) ( 1: Ln = Lu; 2: Ln = Y). In this process, H2L was deprotonated by one metal alkyl species followed by intramolecular C-H activation of the thiophene ring to generate dianionic species L2- with the release of two tetramethylsilane. The resulting L2- combined with three THF molecules and an alkyl unit coordinates to Y3+ and Lu3+ ions, respectively, in a rare N,C-bidentate mode, to generate distorted octahedron geometry ligand core. Whereas, with treatment of H2L with equimolar Sc(CH2SiMe3)(3)( THF)(2), a heteroleptic complex ( HL)( L) Sc( THF) ( 3) was isolated as the main product, where the dianionic L2- species bonds to Sc3+ via chelating N, C atoms whilst the monoanionic HL connects to Sc3+ in an S,N-bidentate mode. All complexes 1-3 have been characterized by NMR spectroscopy and X-ray diffraction analysis.

Structural determination of a new phase of monoclinic BaTb2Mn2O7

A new phase of monoclinic BaTb2Mn2O7 with extra superlattice lines in addition to the usual orthorhombic X-ray diffraction patterns was prepared and a Rietveld refinement was applied to analyze the crystal structure using X-ray powder diffraction data at room temperature. The refined lattice parameters were a = 0.54918(8) nm, b = 2.0149(5) nm, c = 0.54922(9) nm, and beta = 90.62degrees with the space group A2/m (no. 12). The MnO6 oxygen octahedron has distortion and tilts around a-axis by about 7degrees each other in the reverse direction.

Phase behavior of BaLn(2)Mn(2)O(7) (Ln = rare earth) with a layered perovskite structure

Many phases appear in BaLn(2)Mn(2)O(7) family (Ln = rare earth) belonging to one of the Ruddlesden-Popper type compounds, depending upon the experimental conditions such as heating conditions when prepared and composition. Some of these phases were characterized by powder X-ray diffraction method using Rietveld analysis. These phases have only a little difference in crystal structure which has fundamentally K2NiF4 type structure, although the X-ray diffraction patterns are clearly different: a little deformation or tilting of the oxygen octahedron surrounding a central manganese ion composing the main frame of this structure induce these different diffraction patterns. Phase behavior of these compounds, mainly the detailed relation between various phases in BaTb2Mn2O7, was refined including the data of high temperature X-ray diffractometry.

Phase transition of BaNd2Mn2O7

Phase transition of BaNd2Mn2O7 from orthorhombic (space group Fmmm) to tetragonal phase (I4/mmm) was studied by high temperature powder X-ray diffractometry and Rietveld analysis. The transition temperature was identified at 523 K, which is almost the same transition temperature as the compounds with other rare earth ions in this BaLn(2)Mn(2)O(7) family (Ln=Sm and Eu) with Fmmm space group. During the transition an oxygen octahedron of each phase changes a little its form, in which four oxygen atoms perpendicular to C-axis make a rectangle and a square for orthorhombic and tetragonal phases, respectively. Manganese ion is not on the center of the quadrilateral consisting of these four oxygen ions, but a little apart from the center along c-axis in both phases.

Photochemical synthesis, properties and X-ray crystal structure of tetrabutylammonium dodecamolybdophosphate heteropoly blue

The title heteropoly blue, (Bu4N)(6)H-10 [(PMo11MoO40)-Mo-VI-O-V](4) . H2O has been photochemically synthesized and characterized with elemental analysis, solid diffusion reflectance electronic spectra, CV, ESR, XPS, IR spectra, conductivity measurement and X-ray single crystal analysis. The crystallographic data for C96H218Mo48N6O169P4 are as follows: M-r = 8889.76, triclinic, P (1) over bar, a = 1.4142 (3) nm, b = 2.6027 (5) nm, c = 2.6403(5) nm, alpha = 113.96(3)degrees, beta = 90.05(3)degrees, gamma = 105.71(3)degrees, V = 8.481 (3) nm(3), Z = 1, D-c = 1.741 g/cm(3), F (000) = 4264, mu = 1.798 mm(-1). The X-ray crystal structure analysis reveals that there Is one independent molecule in the unit cell of the title heteropoly blue which contains four mixed-valence heteropoly anions, six tetrabutylammonium cations and one water molecule. Its molecular structure possesses a centrosymmetrical arrangement in the unit cell. The phosphorus atom is In the crystallographic inversion center of the heteropoly anion and the eight oxygen atoms surrounding central phosphorus atom comprise of a distorted hexahedron. Heteropolyanion has two equal sets of PO4 tetrahedron. The PO4 tetrahedron and the MoO6 octahedron in the polyanion are greatly distorted.

High-pressure and-temperature synthesis and characterization of mixed valence perovskite oxides LaTi1-xMgxO3

Perovskite oxides LaTi1-xMgxO3 (x = 0.25, 0.5) were synthesized using high-pressure and-temperature method. LaTi0.75Mg0.25O3 is a new compound. This new synthesis route has some advantages. XRD analysis showed that the x = 0.25 sample belongs to cubic perovskite-type structure and the a = 0.5 sample belongs to orthorhombic perovskite-type structure. EPR measurement indicated that Ti ions were in mixed valence state of +3 and +4. IR measurement indicated that the vibration frequency and width of BO6 octahedron stretching vibration absorption band decreases with the increasing of x. The valence state of Ti ions can be altered by high-pressure and-temperature. (C) 2000 Elsevier Science S.A. All rights reserved.

Synthesis and structure of a novel mononuclear tungsten (VI) citrato complex, (NH4)(3)[Li(H2O)(3)WO3(C6H4O7)]

The first mononuclear tungsten-citrato complex, (NH4)(3)[Li(H2O)(3)WO3(C6H4O7)] (1) has been prepared by the reaction of ammonium tetrathio tungstate and lithium citrate in CH3OH - H2O solution at pH 8.2. There are two crystallographically independent anions in the asymmetric crystallographic unit. The crystal structure of the title compound (triclinic, space group P (1) over bar, a = 6.901(1), b = 15.136(3), c = 16.107(3) Angstrom, alpha = 75.85(3), beta = 89.89(3), gamma = 89.97(3), V = 1631.4(6) Angstrom (3), R = 0.068, R-w = 0.1674 for 3878 reflections with I > 2 sigma (1)), reveals that in the compound a tungsten atom is coordinated to a fully deprotonated citrate as a tridentate ligand and three terminal oxygen atoms to form a distorted coordination octahedron.

Hydrothermal synthesis and structural characterization of a mixed-valence molybdenum (IV,VI) arsenate (III): Ni(H2NCH2CH2NH2)(3)[((MoO6)-O-IV)(Mo6O18)-O-VI((As3O3)-O-III)(2)]H2O

A novel mixed-valence molybdenum(IV, VI) arsenate(III), Ni(H2NCH2CH2NH2)(3)[((MoO6)-O-IV)(Mo6O18)-O-VI((As3O3)-O-III)(2)]H2O, hydrothermally synthesized and characterized by single-crystal X-ray diffraction and thermogravimetric analysis. The polyanion cage derives from the Anderson structure, in which the central octahedron was filled up by molybdenum(IV) and it was capped on both sides by a novel As3O63- cyclo-triarsenate(III). The title compound had a high catalytic activity for the oxidation of benzaldehyde to benzoic acid using H2O2 as oxidant in a liquid-solid biphase system. (C) 1999 Elsevier Science B.V. All rights reserved.