Investigation of laser-induced damage on multi-layer dielectric gratings

We investigate mechanisms of laser induced damage thresholds (LIDTs) of multi-layer dielectric gratings (AIDG,). It is found that the laser damage thresholds of MDGs and unstructured dielectric multi-layer coatings (the substrate of MDG) are 3.15J/cm(2) and 9.32 J/cm(2), respectively, at 1064nm (12ns) with the Littrow angle 51.2 degrees and the TEM00 mode. The laser-induced damage mechanism of multi-layer dielectric is presented with the analysis of the following factors: The dominant factor is the pollution on the corrugated surface, which is induced by the complex manufacture process of multi-layer dielectric gratings; another is the electric field distribution along the corrugated surface. The third reason is due to the reduction in stoichiometry of oxide films, resulting from the manufacture process of etching.

Influence of Inter-Fiber Spacing and Interfacial Adhesion on Failure of Multi-Fiber Model Composites: Experiment and Numerical Analysis

The uniaxial tension experiments on glass-fiber-reinforced epoxy matrix composites reveal that the fragmentations of fibers display vertically aligned fracture, clustered fracture, coordinated fracture, and random fracture with the increase of inter-fiber spacing. The finite element analysis indicates that the fragmentations of fibers displaying different phenomena are due to the stress concentration as well as the inherent randomness of fiber defects, which is the dominant factor. The experimental results show that matrices adjacent to the fiber breakpoints all exhibit birefringent-whitening patterns for the composites with different interfacial adhesion strengths. The larger the extent of the interfacial debonding, the less the domain of the birefringent-whitening patterns. The numerical analysis indicates that the orientation of the matrix adjacent to a fiber breakpoint is caused by the interfacial shear stress, resulting in the birefringent-whitening patterns. The area of shear stress concentrations decides on the domain of the birefringent-whitening patterns.

Polypropylene as a carbon source for the synthesis of multi-walled carbon nanotubes via catalytic combustion

Multi-walled carbon nanotubes (MWCNTs) were efficiently synthesized by catalytic combustion of polypropylene (PP) using nickel compounds (such as Ni2O3, NiO, Ni(OH)(2) and NiCO3 (.) 2Ni(OH)(2)) as catalysts in the presence of organic-modified montmorillonite (OMMT) at 630-830 degrees C. Morphologies of the sample undergoing different combustion times were observed to investigate actual process producing MWCNTs by this method. The obtained MWCNTs were characterized by X-ray diffraction (XRD), transmission electron microscope and Raman spectroscopy. The yield of MWCNTs was affected by the composition of PP mixtures with OMMT and nickel compounds and the combustion temperature. The proton acidic sites from the degraded OMMT layers due to the Hoffman reaction of the modifiers at high temperature played an important role in the catalytic degradation of PP to supply carbon sources that are easy to be catalyzed by nickel catalyst for the growth of MWCNTs. The XRD measurements demonstrated that the nickel compounds were in situ reduced into the Ni(0) state with the aid of hydrogen gas and/or hydrocarbons in the degradation products of PP, and the Ni(O) was really the active site for the growth of MWCNTs. The combination of nickel compounds with OMMT was a key factor to efficiently synthesize MWCNTs via catalytic combustion of PP.