In situ hydrate dissociation using microwave heating: Preliminary study

In this work, we investigate the dissociation behavior of natural gas hydrate in a closed system with microwave (MW) heating and hot water heating. The hydrate was formed at temperatures of 1-4 degrees C and pressures of 4.5-5.5 MPa. It was found that the gas hydrate dissociated more rapidly with microwave than with hot water heating. The rate of hydrate dissociation increased with increasing microwave power, and it was a function of microwave power. Furthermore, the temperature of the hydrate increased linearly with time during the microwave radiation.

Reduction of NO by CH4 with microwave heating

The reduction of NO by CH4 in the presence of excess O-2 over Co/HZSM-5, Ni/HZSM-5 and Mn/HZSM-5 catalysts with microwave heating was studied. By comparing the activities of the catalysts in the microwave heating mode with that in the conventional reaction mode, it was demonstrated that microwave heating could greatly reduce the reaction temperature, and could clearly expand the temperature window of the catalysts. Especially for the Co/HZSM-5 catalyst, the maximum conversion of NO to N-2 in the conventional reaction mode was consistent with that in the microwave heating mode. However, the temperature window for the maximum conversion in the microwave heating mode was from 260 to 360degreesC instead of a temperature of 420degreesC in the conventional reaction mode. The results suggest that microwave heating has a novel effect in the reduction of NO.

Direct decomposition of NO by microwave heating over Fe/NaZSM-5

Catalytic decomposition of NO was studied over Fe/NaZSM-5 catalyst. Novel results were observed with the microwave heating mode. The conversion of NO to N-2 increased remarkably with the increasing of Fe loading. The effects of a series of reaction parameters, including reaction temperature, O-2 concentration, NO concentration, gas flow rate and H2O addition, on the productivity of N-2 have been investigated. It is shown that the catalyst exhibited good endurance to excess O-2 in the microwave heating mode. Under all reaction conditions, NO converted predominantly to N-2. The highest conversion of NO to N-2 was up to 70%. (C) 2002 Elsevier Science B.V. All rights reserved.

Synthesis of a high-permeance NaA zeolite membrane by microwave heating

Zeolite membranes with high permeance and separation factors are highly desirable for practical applications. Although, in the past, very good separation factors have been obtained, it has proved difficult to achieve a high permeance. Ken a comparative study of microwave versus conventional heating in the hydrothermal synthesis of NaA zeolite membranes is made. It is demonstrated that membranes prepared by microwave heating have not only a higher permeance but also a considerably shorter synthesis time. These observations are rationalized by examining the mechanism of membrane formation.

Synthesis of NaA zeolite membrane by microwave heating

The synthesis of NaA zeolite membrane on a porous alpha -Al2O3 support by microwave heating (MH) was investigated. The formation of a NaA zeolite membrane was drastically promoted by MH. The synthesis time was reduced from 3 h for conventional heating (CH) to 15 min for MH. Surface seeding cannot only promote the formation of NaA zeolite on the support, but also inhibit the transformation of NaA zeolite into other types of zeolites. The thickness of the NaA zeolite membrane synthesized by MH was about 4 mum, thinner than that of NaA zeolite membrane synthesized by CH. The permeance of NaA zeolite membrane synthesized by MH was four times higher than that of the NaA zeolite membrane synthesized by CH, while their permselectivities were comparable. Multi-stage synthesis resulted in the transformation of NaA zeolite into other types of zeolites, and the perfection of the as-synthesized membrane decreased.

Effect of microwave on formation/decomposition of natural gas hydrate

Natural gas hydrate (NGH) reservoirs have been considered as a substantial future clean energy resource and how to recover gas from these reservoirs feasibly and economically is very important. Microwave heating will be taken as a promising method for gas production from gas hydrates for its advantages of fast heat transfer and flexible application. In this work, we investigate the formation/decomposition behavior of natural gas hydrate with different power of microwave (2450MHZ), preliminarily analyze the impact of microwave on phase equilibrium of gas hydrate,and make calculation based on van der Waals-Platteeuw model. It is found that microwave of a certain amount of power can reduce the induction time and sub-cooling degree of NGH formation, e.g., 20W microwave power can lead to a decrease of about 3A degrees C in sub-cooling degree and the shortening of induction time from 4.5 hours to 1.3 hours. Microwave can make rapid NGH decomposition, and water from NGH decomposition accelerates the decomposition of NGH with the decomposition of NGH. Under the same pressure, microwave can increase NGH phase equilibrium temperature. Different dielectric properties of each composition of NGH may cause a distinct difference in temperature in the process of NGH decomposition. Therefore, NGH decomposition by microwave can be affected by many factors.

Microwave-assisted hydrothermal synthesis of hydroxy-sodalite zeolite membrane

A high quality pure hydroxy-sodalite zeolite membrane was successfully synthesized on an alpha-Al2O3 support by a novel microwave-assisted hydrothermal synthesis (MARS) method. Influence of synthesis conditions, such as synthesis time, synthesis procedure, etc., on the formation of hydroxy-sodalite zeolite membrane by MAHS method was studied by X-ray diffraction (XRD), scanning electron microscopy (SEM) and gas permeation measurements. The synthesis of hydroxy-sodalite zeolite membrane by MAHS method only needed 45 min and synthesis was more than 8 times faster than by the conventional hydrothermal synthesis (CHS) method. A pure hydroxy-sodalite zeolite membrane was easily synthesized by MAHS method, while a zeolite membrane, which consisted of NaX zeolite, NaA zeolite and hydroxy-sodalite zeolite, was usually synthesized by CHS method. The effect of preparation procedures had a dramatic impact on the formation of hydroxy-sodalite zeolite membrane and a single-stage synthesis procedure produced a pure hydroxy-sodalite zeolite membrane. The pure hydroxy-sodalite zeolite membrane synthesized by MARS method was found to be well inter-grown and the thickness of the membrane was 6-7 mum. Gas permeation results showed that the hydrogen/n-butane permselectivity of the hydroxy-sodalite zeolite membrane was larger than 1000. (C) 2004 Elsevier Inc. All rights reserved.

Synthesis and characterization of Eu-doped hydroxyapatite through a microwave assisted microemulsion process

Europium doped hydroxyapatite (Eu:HAp) nanosized particles with multiform morphologies have been successfully prepared via a simple microemulsion-mediated process assisted with microwave heating. The physicochemical properties of the samples were well characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray photoelectron spectra (XPS), Fourier transform infrared spectroscopy (FT-IR), photoluminescence (PL) spectra, and the kinetic decays, respectively. The results reveal that the obtained Eu:HAp particles are well assigned to the hexagonal lattice structure of the hydroxyapatite phase. Additionally, it is found that samples exhibit uniform morphologies which can be controlled by altering the pH values. Furthermore, the samples show the characteristic D-5(0)-F-7(1-4) emission lines of Eu3+ excited by UV radiation.

Salt-assisted acid hydrolysis of chitosan to oligomers under microwave irradiation

The effect of inorganic salts such as sodium chloride on the hydrolysis of chitosan in a microwave field was investigated. While it is known that microwave heating is a convenient way to obtain a wide range of products of different molecular weights only by changing the reaction time and/or the radiation power, the addition of some inorganic salts was shown to effectively accelerate the degradation of chitosan under microwave irradiation. The molecular weight of the degraded chitosan obtained by microwave irradiation was considerably lower than that obtained by traditional heating. Moreover, the molecular weight of degraded chitosan obtained by microwave irradiation assisted under the conditions of added salt was considerably lower than that obtained by microwave irradiation without added salt. Furthermore, the effect of ionic strength of the added salts was not linked with the change of molecular weight. FTIR spectral analyses demonstrated that a significantly shorter time was required to obtain a satisfactory molecular weight by the microwave irradiation-assisted inorganic salt method than by microwave irradiation without inorganic salts and conventional technology. (C) 2005 Elsevier Ltd. All rights reserved.

Preparation of low-molecular-weight and high-sulfate-content chitosans under microwave radiation and their potential antioxidant activity in vitro

In the present paper microwave radiation has been used to introduce N-sulfo and O-sulfo groups into chitosan with a thigh degree of substitution and low-molecular weight. The sulfation of chitosan was performed in microwave ovens. It was found that microwave heating is a convenient way to obtain a wide range of products of different degrees of substitution and molecular weight only by changing reaction time or/and radiation power. Moreover, microwave radiation accelerated the degradation of sulfated chitosan, and the molecular weight of sulfated chitosan was considerably lower than that obtained by traditional heating. There are no differences in the chemical structure of sulfated chitosan obtained by microwave and by conventional technology. FTIR and C-13 NMR spectral analyses demonstrated that a significantly shorter time is required to obtain a satisfactory degree of substitution and molecular weight by microwave radiation than by conventional technology. In this present paper, we also determined antioxidant activity of low-molecular-weight and high-sulfate-content chitosans (LCTS). The results showed LCTS could scavenge superoxide and hydroxyl radical. Its IC50 is 0.025 and 1.32mg/mL, respectively. It is a potential antioxidant in vitro. (C) 2004 Published by Elsevier Ltd.

Fast formation of NaA zeolite membrane in the microwave field

NaA zeolite membrane was successfully synthesized on the porous alpha-Al2O3 support by microwave heating. The synthesis of NaA zeolite membrane in the microwave field only needs 15 min and the synthesis time is 10 times shorter than that by conventional heating. SEM characterization indicates that the zeolite crystals in the NaA zeolite membrane synthesized by microwave heating are uniform in size; the membrane thickness is about 4 mu m and is thinner than that of the NaA zeolite membrane synthesized by conventional heating. Gas permeation studies indicate that the permeances of the NaA zeolite membrane synthesized by microwave heating are 3-4 times higher than those of the NaA zeolite membrane synthesized by conventional heating, while their permselectivities are comparable.

Synthesis of zeolite NaA membranes with high permeance under microwave radiation on mesoporous-layer-modified macroporous substrates for gas separation

This article reported the NaA zeolite membranes with high permeance synthesized with microwave heating method under different conditions: (1) on a macroporous substrate in gel, (11) on a mesoporous/macroporous (top-mesoporous-layer-modified macroporous) substrate in gel, and (111) on a mesoporous/macroporous substrate in sol. In general, the H-2 permeance of the NaA membranes by microwave heating in gel was usually at the level of 10(-6) mol s(-1) m(-2) Pa-1, much higher than that by the conventional hydrothermal synthesis. At similar H-2/C3H8 permselectivity. On the substrate modified mesoporous top layer, the H-2 permeance of the NaA membranes by microwave heating in gel or sol was further enhanced, while maintaining comparable H-2/C3H8 permselectivity, due to the prevention of penetration of the reagent into the pores of the macroporous substrate. Meanwhile, the synthesis took less time in sol than in gel on the mesoporous/macroporous substrate. The NaA membranes synthesized in sol had larger permeance than those in gel and underwent transformation in shorter time. The permeation of C3H8 suggested that there existed unwanted intercrystalline pores or defects in the membranes. © 2005 Elsevier B.V. All rights reserved.

Rapid synthesis of hexagon-shaped gold nanoplates by microwave assistant method

The microwave (MW)-based thermal process was applied to the preparation of hexagon-shaped gold nanoplates. The fort-nation of gold nanoplates occurs rapidly in a single step, carried out by directly heating a reaction mixture of HAuCl4 with sodium citrate in an MW reactor. And the gold nanoplates were characterized by UV-visible spectroscopy, X-ray diffraction (XRD) and transmission electron microscopy (TEM). The experimental results indicated that the sizes and morphologies of the gold nanomaterials strongly depend both on the heating methods and molar ratio of HAuCl4 to sodium citrate in the initial reaction mixture. At the molar ratio 5 : 4 (HAuCl4 to sodium citrate), hexagonal nanoplates with large Au (111) crystallographic facet were preferentially synthesized by the MW assistant method.

Microwave-assisted synthesis of high-molecular-weight poly(ether imide)s by phase-transfer catalysis

A facile and rapid polycondensation reaction of disodium bisphenol A with bis(chlorophthalimide)s was preformed with a domestic microwave oven in o-dichlorobenzene by phase-transfer catalysis. The polymerization reactions, in comparison with conventional heating polycondensation, proceeded rapidly and were completed within 25 min. The polymerizations gave the corresponding poly(ether imide)s with inherent viscosities of 0.55-0.92 dL g(-1). The effects of various factors on the polymerization, such as the amount of the catalyst, the reaction time, and the microwave power were studied. The properties of the polymers were briefly characterized.

Effect of Cold Rolling Ratio and Heating Rate of Batch Annealing on Textures of Micro-Carbon Steel Sheet

在四辊冷轧试验机和Gleeble-1500试验机上进行了热轧微碳钢板的冷轧和退火试验。用D/max-RC衍射仪测量了试样的,/”层织构,并用Roe软件进行了ODF分析。研究表明,所研究的热轧微碳深冲板压下率约为75%,退火升温速度为20-40℃/h时,试样为{111}织构特征；压下率较大(80%)时,退火织构为较弱的{111}组分。无论{111}织构还是非{111}织构都是在形核阶段开始形成,在晶粒长大优先长大,受到定向形核和选择生长双重机制的作用。