The electrical and magnetic properties of lanthanide alkaline-earth transition-metal oxides

Five Ln(2)SrMCuO(6.5) oxides (M = Co, Ln = Y and Ho; M = Fe, Ln = Y, Ho, and Dy) were synthesized, and their crystal structures, IR spectra, and physical properties were studied. They have almost the same structure and crystallize in orthorhombic systems. Below room temperature, Y2SrFeCuO6.5, a known layered oxide, shows antiferromagnetic behavior, but the four new oxides are paramagnetic. Y2SrFeCuO6.5 fits the Curie-Weiss law in the temperature range 300-100 K, but Y2SrCoCuO6.5 shows complex magnetic behavior because of the disproportion of some Co+3 to Co+2 and Co+4 The five oxides are all p-type semiconductors in the measured temperature range and have large electrical resistivities at room temperature.

STUDIES ON THE SYNTHETIC, STRUCTURAL, ELECTRICAL, AND MAGNETIC-PROPERTIES OF THE NEW LAYERED OXIDES LN(2)MCO(2)O(7) (LN=SM, GD, M=SR, BA)

Three new oxides Ln(2)MCo(2)O(7) (Ln = Sm, Gd; M = Sr, Ba) have been synthesized in solid state reaction method. The powder X-ray diffraction spectra show that they are all isostructural with Sr3Ti2O7. The electrical resistivities in the temperature range 300-1100 K show that they are all semiconductors, and a transition to metals is observed at 1053, 1053, and 573 K for Sm2SrCo2O7, Gd2SrCo2O7, and Sm2BaCo2O7, respectively. The magnetic suspectivities of Gd2SrCo2O7 in the temperature range 300-673 K fit the Curie-Weiss law well. A plateau is observed in the curves of Sm(2)MCo(2)O(7) (M = Sr, Ba) which is attributed to the configuration state change of Co(III) from low spin to high spin. (C) 1995 Academic Press, Inc.

Magnetic properties of tin-doped magnetite nanoparticles

Structural and magnetic characteristics of Fe3-xSnxO4 (x < 0.3) nanoparticles synthesized using the precipitation exchange method have been investigated by X-ray diffraction, transmission electron microscope, Mossbauer spectra, X-ray photoelectron spectroscopy and magnetization measurement. The mean particle dimension decreases from 8 to 6 nm, the lattice parameters enlarge, the saturation magnetization decreases, as well as the magnetization and the coercive field increase, with increasing tin-content. The paramagnetic property of the specimens indicates that the replacement of Fe3+ by Sn4+ on the octahedral sites of Fe3O4 causes a progressive lowering of the Curie temperature and the Curie temperatures of the materials are all lower than that of crystallite tin-doped magnetite. This striking debasing is due to the lessening of the grain size. This is the smallest size reported thus far for paramagnetic tin-doped magnetite particles. (c) 2006 Elsevier B.V. All rights reserved.

Influence of Fe3+ on perovskite oxides: La2/3Ca1/3Mn1-xFexO3

The structure and magnetoresistance properties in sintered samples of La-2/3 Ca-1/3 Mn1-x FexO3 (0 less than or equal to x less than or equal to 0.84) are studied by using Mossbauer spectroscopy, XRD and magnetic measurement. There are antiferromagnetic interactions between Fe and its nearest neighbors (Fe, Mn) when 0 less than or equal to x less than or equal to 0.67, which are important factors influencing the double-exchange between Mn3+ and Mn4+, Curie temperature, magnetic moment and GMR. It is suggested that the Mn3+(Fe3+)/Mn4+ system also consists of magnetic clusters with different sizes.

Erbium-Complex-Doped Near-Infrared Luminescent and Magnetic

A near-infrared luminescent macroporous material (PL-Macromaterial) and a near-infrared luminescent/magnetic bifunctional macroporous material (MML-Macromaterial) were synthesized by using polystyrene microspheres (PS) and Fe3O4 @polystyrene core-shell nanoparticles (Fe3O4@PS), respectively, as templates. Both the PL-Macromaterial and the M/PL-Macromaterial show the characteristic emission of the Er 3, ion. Moreover, the M/PL-Macromaterial possesses superparamagnetic properties at room temperature.

Magnetic Mesoporous Silica Spheres for Drug Targeting and Controlled Release

Magnetically functionalized mesoporous silica spheres with different size (average diameter, A.D.) from 150 nm to 2 mu m and pore size distribution were synthesized by generating magnetic FexOy nanoparticles onto the mesoporous silica hosts using the sol-gel method. The X-ray diffraction (XRD), field emission scanning electron microscope (FESEM), N-2 adsorption/desorption results show that these composites conserved regular sphere morphology and ordered mesoporous structure after the formation of FexOy nanoparticles. XRD and X-ray photoelectron spectroscopy (XPS) analysis confirmed that the FexOy generated in these mesoporous silica hosts is mainly composed of gamma-Fe2O3. Magnetic measurements reveal that these composites with different gamma-Fe2O3 loading amounts possess super-paramagnetic properties at 300 K, and the saturation magnetization increases with increasing Fe ratio loaded.

Particle Size-Dependent Charge Ordering and Magnetic Properties in Pr0.55Ca0.45MnO3

A series of Pr0.55Ca0.45MnO3 compounds with average particle size ranging from 2000 to 30 nm have been synthesized by the sol-gel method and their charge ordering (CO) and magnetic properties are investigated. It is observed that with particle size decreasing, the CO transition is gradually suppressed and finally disappears upon particle size down to 35 nm, while the ferromagnetism (FM) emerges and exhibits a nonmonotonous variation with a maximum at 45 nm samples. The FM components in all samples never reach long-range ordering but rather only show short-range clusters. A new explanation considering the coupling between lattice, charge, and spin in the system is raised to understand the suppression of the CO state, Both the competition between the CO/AFM and FM states and the core-shell model are employed to explain the variation of the FM phase. These results may provide a deeper insight into the physics of particle size effect on the charge ordering manganite.

Structure and magnetic properties of new compounds CdYFeWO7

The solid solutions of CdYFeWO7, which are cubic pyrochlores of the type A(2)B(2)O(7), have been prepared and their structures were determined using Ab initio method. Rietveld refinement of the powder XRD data showed that CdYFeWO7 adopted cubic (Fd-3m) structure, while oxides crystallized in a defect-pyrochlore structure where both O (48f) and O'(8b) sites were partially occupied, and the frustrated cations sublattice precluded long range ordering of Fe/W in the pyrochlore structure. Charge distribution analysis also suggested incomplete occupation of different oxygen sites, thus the compound was non-stoichiometric, with the formula CdYFeW0.982O6.94, Magnetic measurements were carried out to find that Fe ions were in the high spin trivalent state. Curie Weiss paramagnetism down to similar to 5 K and the characteristic superposition between FC and ZFC suggested spin liquid rather than spin glass state.

Tunable synthesis, growth mechanism, and magnetic properties of La0.5Ba0.5MnO3

La0.5Ba0.5MnO3 products with novel flowerlike, microcube, and nanocube structures were successfully synthesized by a simple hydrothermal route by controlling the alkalinity of the reaction solutions. The synthesized products were systematically studied by X-ray powder diffraction, field-emission scanning electron microscopy, transmission electron microscopy, and energy dispersive X-ray spectroscopy. The results showed that the formation of the flowerlike structures with a layer assembly experienced a nucleation-aggregation-crystallization growth process, while the cubic structures experienced a nucleation-crystallization growth process due to the effect of different alkalinity in the reaction solutions. The higher alkalinity also led to a decrease in the size in the cubic structures. Suitable temperature and pressure were demonstrated to be crucial to the formation of the flowerlike structures by carrying out further control experiments. The measurement of the magnetic properties of three samples obtained at different alkaline conditions indicated that the size of the La0.5Ba0.5MnO3 products had an obvious influence on their properties; however, the dependence of the properties upon the morphology of the La0.5Ba0.5MnO3 products was minor.

Magnetic and electric properties of Bi(La)Sr(Ca)Mn2O6

Bi1-xLaxSrMn2O6 and BiSr1-xCaxMn2O6 are prepared by solid state reaction. They are n-type semiconductors with ferromagnetism at room temperture. When Bi is substituted partly by rare earth, a negative magnetoresistance effect is observed in the pellet of Bi1-xLaxSrMn2O6. There are semiconductor-metal transitions at 820 K in BiSrMn2O6. The transitions are attributed to the magnetic transition at high temperature. The substitution of Ca for Sr makes the transition temperature increase. However, when Bi is partly substituted by La, the solid solution does not change into metal. (C) 1996 Academic Press, Inc.

Studies on the synthetic, structural, electrical and magnetic properties of Ln(n)MCo(n)O(3n+1) (Ln=Sm, Gd; M=Sr, Ba; n=1,2)

Three new oxides Sm2SrCo2O7, Sm2BaCo2O7 and Gd2SrCo2O7 have been synthesized successfully by solid state reaction mathod. The X-Ray diffraction spectra show that they are all isostructural with Sr3Ti2O7, and Ln(2)SrCo(2)O(7)(Ln=Sm,Gd) crystallized in tetragonal system, Sm2BaCo2O7 in orthrhombic system. The Co-O bonds in CoO2 planes of Ln(2)SrCo(2)O(7) are shorter than those of LnSrCoO(4)(Ln=Sm, Gd), and so their delectrons are more delocalized and their electrical resistivities are smaller. The electrical resistivities versus temperature in the range 300 similar to 1100K showed that the five brides show the characters of weakly localized systems. In the lower temperature range, the magnetic behaviors of Gd2SrCo2O7 and GdSrCoO4 fit Curie-Weiss law well, and the magnetic exchange reaction in CoO2 sublattices of Gd2SrCo2O7 is ferromagnetic, but that of GdSrCoO4 is antiferromagnetic. The other three oxides with Sm3+ showed complex magnetic behaviors which is perhaps related with the complexity of Sm3+.

PREPARATION STRUCTURE AND PHYSICAL-PROPERTIES OF NEW SILVER LANTHANIDE MOLYBDENUM OXIDES [AGLNMO(2)O(8)(LN=LA-ND AND SM)]

We present the synthesis of AgLnMo(2)O(8) compounds with Ln = La-Nd and Sm. These compounds represent a scheelite-type structure characterized by MoO4- tetrahedrons. IR spectra show five absorption peaks in the region of 1000-400cm(-1), around 800cm(-1) and 400cm(-1), which correspond to the modes of the tetrahedral MoO42- groups. All of AgLnMo(2)O(8) (Ln = La-Nd and Sm) oxides are dielectric materials at room temperature. The temperature dependence of the magnetic susceptibility ofAgLnMo(2)O(8) (Ln = Ce-Nd and Sm) shows Curie-Weiss law behavior from 100K to 300K. This indicates that both Ce and Pr exist in +3 oxidation state in AgLnMo(2)O(8). For AgLaMo2O8, diamagnetic properties are found as expected.

THE SYNTHESIS AND PHYSICAL-PROPERTIES OF THE NEW LAYERED LANTHANIDE ALKALINE-EARTH COBALT OXIDES [LN2MCO2O7 (LN=SM,GD M=SR,BA)]

Three new oxides Sm2SrCo2O7, Sm2BaCo2O7 and Gd2SrCo2O7 have been successfully synthesized by a solid state reaction method.The X - Ray diffraction spectra show that they are all isostructural with Sr8Ti 2O7, Ln2SrCo2O7(Ln=Sm, Gd) crystallized in the tetra

INFLUENCE OF THE SUBSTITUTION OF Y BY IN ON THE STRUCTURE AND MAGNETIC PROPERTY OF Y2CU2O5

In2CuO5 is isostructural to Y2Cu2O5 both in its crystal and magnetic structure. In and Y can be substituted by each other in any ratio to make new compounds Y2-xInxCu2O5 (x = 0-2) which were identified by XRD and IR spectrum. The structural change in Y2-x

MAGNETIC-PROPERTIES OF LANTHANUM MANGANITE AND VALENCE EQUILIBRIA OF MANGANESE

The paramagnetic susceptibility of lanthanum manganite has been measured over a wide temperature range (100-1073 K). On the basis of the thermodynamic equilibria between the various manganese ions with different valence and spin states and the magnetic interactions between the various manganese ions, a semiempirical formula has been proposed to calculate the paramagnetic susceptibilities of lanthanum manganite at different temperatures. The results indicate that most of the discrepancies between the calculated and experimental reciprocal susceptibilities of lanthanum manganite are less than 10% and that the relative contents of the various manganese ions in lanthanum manganite vary with temperature. The relative content of the trivalent manganese ion with a high spin state is dominant over the whole temperature range, while be relative content of the tetravalent manganese ion with a high spin state decreases monotonously with increasing temperature. At 300 K the calculated relative content of the tetravalent manganese ion in lanthanum manganite is about 34%, which is in good agreement with the experimental result (30%). There are some divalent manganese ions present in lanthanum manganite from low temperature to high temperature. The ratio of the relative contents of the tetravalent and divalent manganese ions in the compound varies with temperature. Above 750 K the relative content of the tetravalent manganese ion is less than that of the divalent manganese ion. The variation in the electrical resistivity of lanthanum manganite with temperature has also been interpreted reasonably.