Microstructure Study Of Laser Welding Cast Nickel-Based Superalloy K418

Experiments of laser welding cast nickel-based superalloy K418 were conducted. Microstructure of the welded seam was characterized by optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD), and energy dispersive spectrometer (EDS). Mechanical properties of the welded seam were evaluated by microhardness. The corresponding mechanisms were discussed in detail. Results show that the laser welded seam have non-equilibrium solidified microstructures consisting of Cr-Ni-Fe-C austenite solid solution dendrites as the dominant and some fine and dispersed Ni-3(Al,Ti) gamma' phase as well as little amount of MC needle carbides and particles enriched in Nb, Ti and Mo distributed in the interdendritic regions, cracks originated from the liquation of the low melting points eutectics in the HAZ grain boundary are observed, the average microhardness of the welded seam and HAZ is higher than that of the base metal due to alloy elements' redistribution of the strengthening phase gamma'. (C) 2008 Elsevier B.V. All rights reserved.

Transmission Electron Microscopy Characterization of Laser Welding Cast Ni-Based Superalloy K418 Turbo Disk And Alloy Steel 42Crmo Shaft

Microstructure characterization is important for controlling the quality of laser welding. In the present work, a detailed microstructure characterization by transmission electron microscopy was carried out on the laser welding cast Ni-based superalloy K418 turbo disk and alloy steel 42CrMo shaft and an unambiguous identification of phases in the weldment was accomplished. It was found that there are gamma-FeCrNiC austenite solid solution dendrites as the matrix, (Nb, Ti) C type MC carbides, fine and dispersed Ni-3 Al gamma' phase as well as Laves particles in the interdendritic region of the seam zone. A brief discussion was given for their existence based on both kinetic and thermodynamic principles. (c) 2007 Elsevier B.V. All rights reserved.

Research on laser welding of cast Ni-based superalloy K418 turbo disk and alloy steel 42CrMo shaft

Exploratory experiments of laser welding cast Ni-based superalloy K418 turbo disk and alloy steel 42CrMo shaft were conducted. Microstructure of the welded seam was characterized by optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD), energy-dispersive spectrometer (EDS). Mechanical properties of the welded seam were evaluated by microhardness and tensile strength testing. The corresponding mechanisms were discussed in detail. Results showed that the laser-welded seam had non-equilibrium solidified microstructures consisting of FeCr0.29Ni0.16C0.06 austenite solid solution dendrites as the dominant and some fine and dispersed Ni3Al gamma' phase and Laves particles as well as little amount of MC short stick or particle-like carbides distributed in the interdendritic regions. The average microhardness of the welded seam was relatively uniform and lower than that of the base metal due to partial dissolution and suppression of the strengthening phase gamma' to some extent. About 88.5% tensile strength of the base metal was achieved in the welded joint because of a non-full penetration welding and the fracture mechanism was a mixture of ductility and brittleness. The existence of some Laves particles in the welded seam also facilitated the initiation and propagation of the microcracks and microvoids and hence, the detrimental effects of the tensile strength of the welded joint. The present results stimulate further investigation on this field. (c) 2006 Elsevier B.V. All rights reserved.

Characteristics of deep penetration laser welding of dissimilar metal Ni-based cast superalloy K418 and alloy steel 42CrMo

Experimental trials of autogenous deep penetration welding between dissimilar cast Ni-based superalloy K418 and alloy steel 42CrMo flat plates with 5.0 mm thickness were conducted using a 3 kW continuous wave (CW) Nd:YAG laser. The influences of laser output power, welding velocity and defocusing distance on the morphology, welding depth and width as well as quality of the welded seam were investigated. Results show that full keyhole welding is not formed on both K4.18 and 42CrMo side, simultaneously, due to the relatively low output power. Partial fusion is observed on the welded seam near 42CrMo side because of the large disparity of thermal-physical and high-temperature mechanical properties of these two materials. Tile rnicrohardness of the laser-welded joint was also examined and analyzed. It is suggested that applying negative defocusing in the range of Raylei length can increase the welding depth and improve tile coupling efficiency of the laser materials interaction. (c) 2007 Elsevier Ltd. All rights reserved.

Dissimilar autogenous full penetration welding of superalloy K418 and 42CrMo steel by a high power CWNd : YAG laser

Experiments of autogenous laser full penetration welding between dissimilar cast Ni-based superalloy K418 and alloy steel 42CrMo flat plates with 3.5 mm thickness were conducted using a 3 kW continuous wave (CW) Nd:YAG laser. The influences of laser welding velocity, flow rate of side-blow shielding gas, defocusing distance were investigated. Microstructure of the welded seam was characterized by optical microscopy (OM), scanning electron microscopy (SEM) and X-ray diffraction (XRD) and energy dispersive spectrometer (EDS). Mechanical properties of the welded seam were evaluated by microhardness and tensile strength testing. Results show that high quality full penetration laser-welded joint can be obtained by optimizing the welding velocity, flow rate of shielding gas and defocusing distance. The laser-welded seam have non-equilibrium solidified microstructures consisting of gamma-FeCr0.29Ni0.16C0.06 austenite solid solution dendrites as the dominant and very small amount of super-fine dispersed Ni3Al gamma' phase and Laves particles as well as MC needle-like carbides distributed in the interdendritic regions. Although the microhardness of the laser-welded seam was lower than that of the base metal, the strength of the joint was equal to that of the base metal and the fracture mechanism showed fine ductility. (c) 2007 Elsevier B.V. All rights reserved.

Welding of Al alloy plates using a novel high-average-power pulsed CO2 laser

A novel high-average-power pulsed CO2 laser with a unique electrode structure is presented. The operation of a 5-kW transverse-flow CO2 laser with the preionized pulse-train switched technique results in pulsation of the laser power, and the average laser power is about 5 kW. The characteristic of this technique is switching the preionized pulses into pulse trains so as to use the small preionized power (hundreds of watts) to control the large main-discharge power (tens of kilowatts). By this means, the cost and the complexity of the power supply are greatly reduced. The welding of LF2, LF21, LD2, and LY12 aluminum alloy plates has been successfully achieved using this laser. (c) 2005 Society of Photo-Optical Instrumentation Engineers.

Welding of Al alloy plates using a novel high-average-power pulsed CO2 laser

A novel high-average-power pulsed CO2 laser with a unique electrode structure is presented. The operation of a 5-kW transverse-flow CO2 laser with the preionized pulse-train switched technique results in pulsation of the laser power, and the average laser power is about 5 kW. The characteristic of this technique is switching the preionized pulses into pulse trains so as to use the small preionized power (hundreds of watts) to control the large main-discharge power (tens of kilowatts). By this means, the cost and the complexity of the power supply are greatly reduced. The welding of LF2, LF21, LD2, and LY12 aluminum alloy plates has been successfully achieved using this laser. (c) 2005 Society of Photo-Optical Instrumentation Engineers.

K418与42CrMo异种金属的激光穿透焊接

实验研究了连续波Nd：YAG激光焊接速度、侧吹保护气流量和离焦量等参量对激光穿透焊接K418和42CrMo焊缝成形的影响。结果表明，K418与42CrMo激光穿透焊接有X形和T形两种典型的焊缝形貌，且焊缝形貌是不对称的。随着焊接速度的提高，焊接线能量降低，焊缝尺寸变小，且焊缝上部尺寸变化比下部尺寸变化慢，焊缝形貌由X形过渡到T形。当离焦量在瑞利长度范围内时，焊缝正面宽度变化很小；当离焦量超出瑞利长度范围时，在足够高的激光功率密度下，焊缝正面宽度快速增加。在激光功率为3kW，侧吹保护气角度为35°条件下，通过优化焊接速度、侧吹保护气流量和离焦量等参量可以得到最佳焊缝质量。

K418高温合金和42CrMo合金钢的激光焊接

进行了K418高温合金和42CrMo钢的激光焊接实验，分别采用OM、SEM、XRD和EDS等手段分析了焊缝的金相组织和物相组成，评价了焊缝的显微硬度和拉伸强度。结果表明：焊缝主要由树枝状非平衡凝固的FeCrNiC（力固溶体组成，此外，还有少量细小、弥散的Ni_3Al（γ′）相、Laves颗粒和少量MC碳化物分布在树枝晶间区域。由于主要强化相γ′在激光辐照后的部分溶解和随后快速凝固的抑制作用，焊缝的硬度虽分布较均匀但低于母材。由于没有获得穿透的焊接接头，焊接接头的强度约只有母材的88．5％，焊缝的断裂机制是塑性和脆性断裂的混合机制。由于在焊缝中存在一些Laves颗粒，这促进了微裂纹和微孔的形成和扩展，降低了焊接接头的抗拉强度。

K418与42CrMo异种金属激光焊接接头组织与力学性能

试验研究了额定功率为3kW的连续波Nd：YAG激光焊接热输入对激光焊接K418与42CrMo异种金属焊缝形貌的影响。通过光学显微镜、扫描电镜、能谱分析仪、硬度仪、万能试验机及X衍射对激光焊接K418与42CrMo异种金属焊缝接头组织、元素分布、相组成及接头的力学性能进行分析。结果表明，在焊接热输入恒定的条件下，高功率、高焊速的匙孔焊接比低功率、低焊速的热传导焊接更能增加焊缝熔深。通过扫描电镜在焊缝区域观察到了颗粒状物和针状物，能谱分析表明，颗粒状物Nb，Ti，Mo元素聚集，Fe，Ni元素减少；针状物Ti，Nb元素聚集。K418与42CrMo异种金属激光焊接工艺参数优化后的焊缝抗拉强度高于42CrMo母材。

K418与42CrMo异种金属激光深熔焊接

研究了连续波Nd:YAG激光焊接功率、速度、离焦量和侧吹保护气流量对激光深熔焊接K418与42CrMo异种金属焊缝形貌、焊缝熔深的影响,讨论了焊缝区热裂纹产生机制.结果表明,额定功率为3 kW的Nd:YAG激光深熔焊接K418与42CrMo异种金属,由于它们的物理化学性质的差异,焊缝靠近42CrMo侧易出现未熔合;激光光斑向42CrMo侧偏移可以减少焊缝靠近42CrMo侧未熔合量;通过优化侧吹保护气流量和离焦量可以增加熔深.由于K418液态金属的流动性差,导致焊缝靠近K418侧对流传热不充分,使焊缝靠近K418侧熔合线呈现锯齿形.焊缝区热裂纹的产生主要是由于焊缝区元素偏析形成的低熔物导致.

异种金属激光焊接关键问题研究

现代工程结构要求对异种金属材料进行焊接.激光焊接具有密度高、焊缝深宽比大、热影响区窄以及变形小等特点,成为异种金属材料焊接的有效方法.异种金属激光焊接过程包含多种效应,机制复杂.比如,材料性能差异对焊缝微观组织与宏观性能的影响;焊接熔池的形成、演化机制;熔池凝固过程焊接缺陷及残余应力形成等.围绕异种金属激光焊接过程中的关键问题,国内外开展了诸多研究工作,对此进行了全面阐述.在此基础上,指出异种金属材料激光焊接研究中的不足及发展方向.

42CrMo激光焊焊缝组织

42CrMo合金钢C含量高、合金元素含量多、淬硬倾向大,焊接性能差。激光焊接具有功率密度高、焊接变形小等优点,适合焊接传统工艺难焊的同种或异种金属。通过额定功率为3kW的Nd∶YAG固体激光器焊接42CrMo,采用光学显微镜(OM)、扫描电镜(SEM)、X衍射、硬度仪分析了焊缝区域组织、成分和硬度变化。研究结果表明:焊缝区域组织为马氏体,热影响完全淬火区的组织为马氏体+贝氏体组织,热影响不完全淬火区的组织为贝氏体。从焊缝正面到焊缝背面的硬度分布表明:由于焊缝正面有保护气体的作用提高了焊缝正面熔池的冷却速度,使焊缝背面的硬度低于焊缝正面的硬度。

激光焊接技术与航空制造

激光焊接能够实现多种类型材料的连接,而且具有许多其他熔焊工艺无法比拟的优越性,未来航空工业将是激光焊接技术应用的一个重要领域。

一种并联激光焊接机器人的机构设计与运动学分析

提出了一种3分支5自由度的并联激光焊接机器人,通过3个分支共同作用,使整机具备了5个自由度的空间加工能力.针对激光焊接,通过分析该机器人的结构特性,建立了其正反解运动学模型,通过解析法求解该模型并进行了计算仿真.最后,对机器人进行激光拼焊实验,仿真数据和实验结果表明,本文研究的并联机器人机构适用于实际的高速、高精度激光焊接。