Preparation and electrical-magnetic properties of polyaniline doped with ionic ferrocenesulfonic acid

Conducting polyamline with electrical conductivity of 2.34 x 10(-1) S cm(-1) was obtained using ferrocenesulfonic acid as dopant. After the ferrocenesulfonic acid was oxidized with FeCl3, though the electrical conductivity of the doped polyaniline decreased by 1-2 orders of magnitude, the magnetic susceptibility (chi) increased with the increase of the oxidation degree of ferrocenesulfonic acid. EPR spectra showed not only a signal with a g value of around 2, but also a so-called half-field signal with a g value of about 4 even at room temperature. Coexistence of ferromagnetic intrachain interactions and antiferromagnetic interchain interactions in the materials has been suggested.

Effect of partial site occupation on the magnetic properties of Nd2Fe17-xSix by supercell calculation

The magnetic properties of the Nd2Fe17-xSix intermetallic compounds are studied by means of spin-polarized supercell calculations in which the selected sites of substitution are close to the situations in real samples. It is shown that the average Fe moment increases with x and saturates near x = 3. This correlates quite well with the experimental dependence of Te on x. The difference between supercell and unit cell calculations are pointed out and the influence of Si atoms on the density of states of the nearby Fe atoms is emphasized. (C) 1997 American Institute of Physics.

Electronic and magnetic properties of YBa2Fe3O8 from a first-principles study

The electronic and magnetic properties of YBa2Fe3O8 have been systematically investigated within the framework of density-functional theory using the standard generalized gradient approximation (GGA) as well as the GGA plus Hubbard U(GGA + U) method. The GGA results show that the G-type antiferromagnetic (AFM) state is preferred among the considered magnetic configurations. The striking ionic character is shown for Y and Ba atoms while very strong hybridization is found between Fe 3d and O 2p orbitals

Structure and magnetic properties of new compounds CdYFeWO7

The solid solutions of CdYFeWO7, which are cubic pyrochlores of the type A(2)B(2)O(7), have been prepared and their structures were determined using Ab initio method. Rietveld refinement of the powder XRD data showed that CdYFeWO7 adopted cubic (Fd-3m) structure, while oxides crystallized in a defect-pyrochlore structure where both O (48f) and O'(8b) sites were partially occupied, and the frustrated cations sublattice precluded long range ordering of Fe/W in the pyrochlore structure. Charge distribution analysis also suggested incomplete occupation of different oxygen sites, thus the compound was non-stoichiometric, with the formula CdYFeW0.982O6.94, Magnetic measurements were carried out to find that Fe ions were in the high spin trivalent state. Curie Weiss paramagnetism down to similar to 5 K and the characteristic superposition between FC and ZFC suggested spin liquid rather than spin glass state.

Tunable synthesis, growth mechanism, and magnetic properties of La0.5Ba0.5MnO3

La0.5Ba0.5MnO3 products with novel flowerlike, microcube, and nanocube structures were successfully synthesized by a simple hydrothermal route by controlling the alkalinity of the reaction solutions. The synthesized products were systematically studied by X-ray powder diffraction, field-emission scanning electron microscopy, transmission electron microscopy, and energy dispersive X-ray spectroscopy. The results showed that the formation of the flowerlike structures with a layer assembly experienced a nucleation-aggregation-crystallization growth process, while the cubic structures experienced a nucleation-crystallization growth process due to the effect of different alkalinity in the reaction solutions. The higher alkalinity also led to a decrease in the size in the cubic structures. Suitable temperature and pressure were demonstrated to be crucial to the formation of the flowerlike structures by carrying out further control experiments. The measurement of the magnetic properties of three samples obtained at different alkaline conditions indicated that the size of the La0.5Ba0.5MnO3 products had an obvious influence on their properties; however, the dependence of the properties upon the morphology of the La0.5Ba0.5MnO3 products was minor.

Microstructure and Magnetic Properties of Nd60Al10Fe20Co10 Glass-forming Alloy

The microstructural variations of the Nd60Al10Fe20CO10 melt-spun ribbons and the as-cast rod were studied by high resolution transmission electron microscopy (HRTEM), x-ray diffraction (XRD) and differential scanning calorimetry. Nano-clusters in glassy m

Magnetic properties and magnetic domain structure of bulk glass forming Nd60Al10Fe20Co10 alloy

The transition from hard to soft magnetic behaviour with increasing quenching rate is shown for Nd60WAl10Fe20Co10 melt-spun ribbons with different thickness. Microstructure and magnetic domain structure of ribbons were studied by magnetic force microscopy (MFM). Particle sizes < 5 nm decreasing gradually with increasing quenching rate were deduced from topographic images which differ from large-scale magnetic domains with a periodicity of about 350 nm in all ribbons irrespective the coercivity. This indicates that the magnetic properties of the alloy are governed by interaction of small magnetic particles. It is concluded that the presence of short-range-ordered structures with a local ordering similar to the Al metastable Nd-Fe binary phase is responsible for the hard magnetic properties in samples subjected to relatively low quenching rate.

Phase Evolution and its Effect on Magnetic Properties of Nd60Al10Fe20Co10 Bulk Metallic Glass

The thermal stability of nanocrystalline clusters, the phase evolution, and their effects on magnetic Propertieswere studied for as-cast Nd60Al10Fe20Co10 alloy using differential scanning calorimetry curves, x-ray diffraction patterns, scanning electron microscopy, and high-resolution transition electron microscopy. Thermomagnetic curves and hysteresis loops of the bulk metallic glass were measured during the annealing process. The high thermostability of the hardmagnetic properties of the samples observed is attributed to the stability of the nanocrystalline clusters upon annealing, while the slight enhancement in the magnetization is due to the precipitation of some Nd-rich metastable phases. The mechanism of thermostability of the nanocrystalline clusters and the formation of the metastable phases are discussed.

Magnetic Properties of Mn-Implanted n-Type Ge

Mn+ ions were implanted into n-type Ge(111) single crystal at room temperature at an energy of 100 keV with a dose of 3 x 1016 cm-2. Subsequent annealing was performed on the samples at 400 °C and 600 °C in a flowing nitrogen atmosphere. The magnetic properties of the samples have been investigated by alternating gradient magnetometer at room temperature. The compositional properties of the annealed samples were studied by Auger electron spectroscopy and the structural properties were analyzed by X-ray diffraction measurements. Magnetization measurements reveal room-temperature ferromagnetism for the annealed samples. The magnetic analysis supported by compositional and structural properties indicates that forming the diluted magnetic semiconductor (DMS) MnxGe1-x after annealing may account for the ferromagnetic behavior in the annealed samples.

Structural and magnetic properties of insulating Zn1-xCoxO thin films

Cobalt-doped ZnO (Zn1-xCoxO) thin films were fabricated by reactive magnetron cosputtering. The processing conditions were carefully designed to avoid the occurrence of Co precipitations. The films are c-axis oriented, and the solubility limit of Co in ZnO is less than 17%, determined by x-ray diffraction. X-ray photoemission spectroscopy measurements show Co ions have a chemical valance of 2+. In this paper, hysteresis loops were clearly observed for Zn1-xCoxO films at room temperature. The coercive field, as well as saturation magnetization per Co atom, decreases with increasing Co content, within the range of 0.07

Magnetic properties of sintered sm2fe17ny magnets

Sintered magnets of Sm2Fe17Ny nitrides, with a density of 6.0-7.4 g/cm3, have been prepared by using an explosion technique. Both crystalline structure and the magnetic properties of Sm2Fe17Ny nitrides were retained in the process. The sintered magnet had a remanence B(r)=0.83 T, an intrinsic coercivity mu(0i)H(c)=0.57 T and an energy product (BH)max=88 kJ/m3. The temperature dependence of coercivity and remanence were also measured. The temperature coefficients alpha of remanence and beta of coercivity are -0.076%/degrees-C and -0.51%/degrees-C, respectively.

Synthesis and magnetic properties of Ni-doped zinc oxide powders

Polycrystalline Zn1-xNixO diluted magnetic semiconductors have been successfully synthesized by an auto-combustion method. X-ray diffraction measurements indicated that the 5 at% Ni-cloped ZnO had the pure wurtzite structure. Refinements of cell parameters from powder diffraction data revealed that the cell parameters of Zn0.95Ni0.05O were a little bit larger than ZnO. Transmission electron microscopy observation showed that the as-synthesized powders were of the size similar to 60 nm. Magnetic investigations showed that the nanocystalline Zn0.95Ni0.05O possessed room temperature ferromagnetisin with the saturation magnetic moment of 0.1 emu/g (0.29 mu(B)/Ni2+). (c) 2005 Elsevier B.V. All rights reserved.

Structure and magnetic properties of CoNiP nanowire arrays embedded in AAO template

Ternary CoNiP nanowire (NW) arrays have been synthesized by electrochemical deposition inside the nanochannels of anodic aluminum oxide (AAO) template. The CoNiP NWs deposited at room temperature present soft magnetic properties, with both parallel and perpendicular coercivities less than 500 Oe. In contrast, as the electrolyte temperature (T-elc) increases from 323 to 343 K, the NWs exhibit hard magnetic properties with coercivities in the range of 1000-2500 Oe. This dramatic increase in coercivities can be attributed to the domain wall pinning that is related to the formation of Ni and Co nanocrystallites and the increase of P content. The parallel coercivity (i.e. the applied field perpendicular to the membrane surface) maximum as high as 2500 Oe with squareness ratio up to 0.8 is achieved at the electrolyte temperature of 328 K. It has been demonstrated that the parallel coercivity of CoNiP NWs can be tuned in a wide range of 200-2500 Oe by controlling the electrolyte temperature, providing an easy way to control magnetic properties and thereby for their integration with magnetic-micro-electromechanical systems (MEMS). (C) 2008 Elsevier B.V. All rights reserved.

Influence of Si doping on magnetic properties of (Ga,Mn)As

We have systematically investigated the magnetic properties of Si-doped (Ga,Mn)As films. When the Si content is low, both Curie temperature (T-C) and carrier density (p) decrease compared with undoped (Ga,Mn)As, whereas a monotonic increase of T-C and p is observed with further increase in the doping content of Si. We discuss the possible mechanism for the changes obtained by different Si doping contents and attribute the results to a competition between the existence of Si-Ga (Si substitutes for Ga site) that acts as a donor and Si-I (Si interstitials) which is in favor of the improvement of ferromagnetism. (C) 2008 Elsevier B.V. All rights reserved.

First-principles study of the electronic structures and magnetic properties of 3d transition metal-doped anatase TiO2

We study the electronic structures and magnetic properties of the anatase TiO2 doped with 3d transition metals (V, Cr, Mn, Fe, Co, Ni), using first-principles total energy calculations based on density functional theory (DFT). Using a molecular-orbital bonding model, the electronic structures of the doped anatase TiO2 are well understood. A band coupling model based on d-d level repulsions between the dopant ions is proposed to understand the chemical trend of the magnetic ordering. Ferromagnetism is found to be stabilized in the V-, Cr-, and Co-doped samples if there are no other carrier native defects or dopants. The ferromagnetism in the Cr- and Co-doped samples may be weakened by the donor defects. In the Mn-, and Fe-doped samples, the ferromagnetism can be enhanced by the acceptor and donor defects, respectively.