Co-Cu-Al mixed oxides derived from hydrotalcite-like compound for NO reduction by CO

Various hydrotalcite based catalysts were prepared for catalytic removal of NO (NO reduction by CO). The general formula of hydrotalcite compounds (HTLc) was Co-Cu-Al-HTLc. Precalcination of these materials at 450 degrees C for NO reduction by CO, was necessary for catalytic activity. All catalysts except Co-A1 and Cu-Al have very good activity at lower temperature for NO reduction by CO. All samples were characterized by XRD and BET. The tentative reaction mechanism was also proposed.

Preparation, charactreization, and catalytic properties of Co-M-Al (M = transition metal) mixed oxides derived from hydrotalcite-like compound

Hydrotalcite-like compounds (HTLcs) CoMAlCO3, where M stands for Cr, Mn, Ni, Cu, or Fe, were synthesized by coprecipitation. After calcination at 450 degrees C, they became mixed oxides with spinel-like structure. The mixed oxides were characterized by XRD, BET, chemical analysis and the adsorption of NO. The catalytic decomposition of NO and its reduction by CO were studied over these mixed oxides. The study showed that the catalytic activity for removal of NO, was very high. The reaction mechanism is proposed and the effects of d-electrons of the transition metals on catalytic activity are elucidated.

Catalytic reduction of NO by CO with hydrotalcite derived mixed oxides

Catalysts with spinel structure derived from Hydrotalcite-like Compounds (HTLcs) containing cobalt have been investigated in NO catalytic reduction by Co. It was found that catalysts with spinel structures derived from HTLcs had obviously higher activity than that prepared from general methods. A two-step reaction was observed during the reaction curse: NO was first reduced to N2O by Co, and with the increase of temperature, the N2O was reduced to N-2. The reactivity of the catalysts studied increased with the amount of cobalt-content in the catalyst, and decreased with the calcination temperature. The crystal defect would play an important role in the reaction.

Catalysis of hydrotalcite-like compounds in liquid phase oxidation: (II) - Oxidation of p-cresol to p-hydroxybenzaldehyde

Hydrotalcite-like compounds (HTLcs): CoMAlCO3-HTLcs (M=Cu2+, Ni2+, Mn2+, Cr3+, Fe3+), were synthesized by coprecipitation and characterized with XRD and IR. The catalysis of these HTLcs and their calcined products were studied in the p-cresol oxidation, and the effects of the temperature of HTLcs calcination, the ratio of Co/Cu, different promoters, reaction temperatures and reaction times on reaction activities were investigated. It has been found that calcined HTLcs have higher activity than uncalcined samples and mechanical mixed oxides in this reaction. The best yield was obtained from the CoCuAlCO3-HTLc (Co/Cu/Al=3:1:1) calcined at 450 degrees C. A tentative reaction mechanism was also proposed. (C) 1998 Elsevier Science B.V.

Catalysis of hydrotalcite-like compounds in liquid phase oxidation: (I) phenol hydroxylation

Hydrotalcite-like compounds (HTLcs): (CuMAlCO3)-Al-II-HTLcs, where M-II=Co2+, Ni2+, Cu2+, Zn2+ and Fe2+, were synthesized by coprecipitation and characterized with XRD and IR. The catalysis of these HTLcs was studied in the phenol hydroxylation by H2O2 in liquid phase; then the effects of the ratio of Cu/Al, reaction temperature, solvent and pH of medium were investigated. It has been found that the uncalcined HTLcs have higher activities than those of calcined samples in this reaction. The catalyst CuAlCO3-HTLcs having Cu/Al=3 efficiently oxidized phenol and gave high yields of the corresponding diphenols in appropriate reaction conditions. A tentative reaction mechanism is also proposed. (C) 1998 Elsevier Science B.V.

A study of catalysis of copper-aluminium hydrotalcite-like compounds in the phenol hydroxylation

Copper-Aluminium Hydrotalcite-like compounds are synthesized by coprecipitation and characterized with XRD and IR. Catalysis of the above mentioned HTLcs are investigated in the phenol hydroxylation, good results are obtained. Meanwhile, the effects of the ratio of Cu/Al, reaction temperature, reaction medium and pH of reaction system are discussed, The reaction mechanism is also proposed.

Catalysis of copper-containing transition metal hydrotalcite-like compounds in the phenol hydroxylation with hydrogen peroxide

Hydrotalcite-like compounds containing carbonate ion as the interlayer anion were prepared by coprecipitation under low supersaturation condition by mixing an aqueous solution of metal nitrates with an aqueous solutions of NaOH and Na2CO3, at room temperature, maintaining pH = 8-10 with vigorous stirring, Following the mixing, the resulting heavy slurry was aged at 353 K for 18 h with vigorous stirring, The precipitate was then filtered, washed several times with hot distilled water and dried in air at 353 K overnight, In this way, CuMI AlCO3-HTLcs and M-I AlCO3-HTLcs were synthesized and characterized by means of XRD and IR, The catalysis of the above mentioned HTLcs were investigated in the phenol hydroxylation with H2O2. The results indicated that all of the copper-containing HTLcs had a higher catalytic activity in the reaction, However, those catalysts that did not contain copper had no catalytic activity in this reaction, This means that copper was the active center in the phenol hydroxylation. Meanwhile, the mechanism was also proposed, which could be used to explain the main reason for higher activity for CuCuAlCO3-HTLcs in the phenol hydroxylation and the effect of Mg2+, Zn2+, Co2+, Ni2+ on activity of CuMI AlCO3-HTLcs.

NOx storage-reduction over Pt/Mg-Al-O catalysts with different Mg/Al atomic ratios

A series of Pt/Mg-Al-O catalysts with different Mg/Al atomic ratios were prepared. The NOx storage capacities of these catalysts were measured by isothermal storage at 350 degreesC. It was found that the NOx storage capacity increased with increasing Mg/Al atomic ratios. The catalytic behaviors of Pt/Mg-Al-O and Pt/MgO were studied with storage-reduction cycles at 400 degreesC. Under oxidizing conditions, NOx concentration in the outlet gas gradually increased with time, which indicated the catalysts could store NOx effectively. After a switch from oxidizing conditions to reducing conditions, NOx desorption peak emerged immediately due to the incomplete reduction of stored NOx, which lowered the total NOx conversion. With increasing Mg/Al atomic ratio in the catalysts, NOx conversion increases. Pt/MgO has the highest NOx conversion because of its best activity in the reduction of NOx by C3H6. It seems that with an increasing amount of MgO in the catalysts, the self-poisoning of Pt-sites by adsorbed species during the reaction of NOx with C3H6 may be inhibited effectively.

Hydrogenation of phenol in scCO(2) over carbon nanofiber supported Rh catalyst

A catalyst of Rh nanoparticles supported on a carbon nanofiber, 5 wt.% Rh/CNF, with an average size of 2-3 nm has been prepared by a method of incipient wetness impregnation. The catalyst presented a high activity in the ring hydrogenation of phenol in a medium of supercritical CO2 (scCO(2)) at a low temperature of 323 K. The presence of compressed CO2 retards hydrogenation of cyclohexanone to cyclohexanol under the reaction conditions used, and this is beneficial for the formation of cyclohexanone, increasing the selectivity to cyclohexanone.

Catalytic reduction of NO, by CO on hydrotalcites-derived mixed oxides CoAlM and MgAlM (M = Cr, Mn, Fe, Co, Ni, Cu)

Two series of mixed oxides, CoAlM and MgAlM (M = Cr, Mn, Fe, Co, Ni, Cu), were prepared by calcining their corresponding hydrotalcite-like compounds (HTLc). The ratio of Mg: Al: M (or Co: Al: hi) was 3:1:1. The catalytic activity of all samples for the reaction of NO + CO was investigated. The results showed that the activity of CoAlM was much higher than that of MgAlM. The structure and the property of redox were characterized by XRD and H-2-TPR. The results indicated that only MgO phase was observed after calcining MgAlM hydrotalcites, and the transition metals became more stable. The spinel-like phase appeared in all of CoAlM samples after the calcination, and the transition metals were changed to be more active, and easily reduced. The activities of three series of mixed oxides CoAlCu obtained from different preparation methods, different ratio of Co:Al: Cu and at different calcination temperatures, were studied in detail for proposing the mechanism of reaction. The ability of adsorption of NO and CO were investigated respectively for supporting the mechanism.

Synthesis and catalytic properties of layered double hydroxides pillared by heteropolyoxometalate

Layered double hydroxides (LDHs) pillared with heteropolyoxometalate have been synthesized via both restructuring of hydrotalcite-like compounds and direct anion exchange under microwave field. LDHs and their derivatives are both found to be efficient for alkylation of isobutane with butene with a higher butene conversion and selectivity towards C-8(0).

Alrylation Over Layered Double Hydrotalcites Pillared by Heteropolyoxometalate Catalysts

Layered double hydroxides (LDHs) pillared with heteropolyoxo-metalate have been synthesized via both restructuring of hydrotalcite-like compounds and direct anion exchange under microwave field. LDHs and their derivatives are both found to be efficiency f

ALKYLATION OF ISOBUTANE WITH BUTENE OVER LAYERED DOUBLE HYDROXIDE PILLARED HETEROPOLYOXOMETALATE ACID-BASE CATALYSTS

[Si(W2O7)(6)](8-) pillared LDH structure hydroxides were synthesized by the method of restructuring of the thermally decomposed hydrotalcite-like compounds for Zn-Al and Mg-Al oxide systems. [P(W2O7)(6)](8-) pillared Ni-Al LDH structure hydroxide was synt

Structure and base properties of calcined hydrotalcites

Five hydrotalcites with Mg/Al molar ratio range of 3-15 were prepared. The structure and basicity of Mg-Al mixed oxides (Mg(Al)O) transformed from hydrotalcites were investigated by TPD, XPS, XRD, FT-IR and NMR techniques. The results of elemental analysis and XPS indicate that Al is enriched in the surface regions of Mg(Al)O, and its amount increases with the Mg/Al molar ratio and, the calcination temperature. Al-27-MAS-NMR results show that Al exists in two chemical environments: tetrahedral aluminium (Al(t)) and octahedral aluminium (Al(o)) in Mg(AI)O. The amount of Al(t) increases with the Mg/Al molar ratio and the calcination temperature. It is assumed that Al(t) may be mainly from the surface Al. Temperature-programmed desorption (TPD) of CO2 shows that the number of basic sites of Mg(Al)O samples increases with the Mg/Al molar ratio, and the maximum number of basic sites is obtained for hydrotalcite calcined at 773 K. Infrared spectra of adsorbed CO2 and B(OCH3)(3) reveal that there are two kinds of basic sites: weak basic OH- sites and strong basic O2- sites on the Mg(AI)O samples, the base strength depends on the Mg/Al molar ratio and calcination temperature.