Solid-state MAS NMR studies on the hydrothermal stability of the zeolite catalysts for residual oil selective catalytic cracking

By using the solid-state MAS NMR technique, the hydrothermal stabilities (under 100% steam at 1073 K) of HZSM-5 zeolites modified by lanthanum and phosphorus have been studied. They are excellent zeolite catalysts for residual oil selective catalytic cracking (RSCC) processes. It was indicated that the introduction of phosphorus to the zeolite via impregnation with orthophosphoric acid led to dealumination as well as formation of different Al species, which were well distinguished by Al-27 3Q MAS NMR. Meanwhile, the hydrothermal stabilities of the zeolites (P/HZSM-5, La-P/HZSM-5) were enhanced even after the samples were treated under severe conditions for a prolonged time. It was found that the Si-O-Al bonds were broken under hydrothermal conditions, while at the same time the phosphorous compounds would occupy the silicon sites to form (SiO)(x)Al(OP)(4 - x) species. With increasing time, more silicon sites around the tetrahedral coordinated Al in the lattice can be replaced till the aluminum is completely expelled from the framework. The existence of lanthanum can partially restrict the breaking of the Si-O-Al bonds and the replacement of the silicon sites by phosphorus, thus preventing dealumination under hydrothermal conditions. This was also proved by P-31 MAS NMR spectra. (C) 2004 Elsevier Inc. All rights reserved.

Characterization of the acid sites in dealuminated nanosized HZSM-5 zeolite with the probe molecule trimethylphosphine

The acid sites in dealuminated HZSM-5 zeolite with crystal sizes down to the nanoscale were firstly characterized by the probe molecule trimethylphosphine (TMP). As evidenced by the combination of P-31 CP/MAS NMR, Al-27 MAS and H-1 --> Al-27 CP/MAS NMR measurements, the Bronsted acid sites of both microsized and nanosized HZSM-5 could be decreased upon the dealumination of zeolitic framework after hydrothermal treatment. At the same time, the appearance of Lewis acid sites was observed. The dealuminated nanosized HZSM-5 is easier to form Lewis acid sites than microsized HZSM-5, and the type of Lewis acid sites in nanosized HSM-5 is more than one. In addition, the origin of Lewis acid sites is mainly associated with the aluminum at ca. 30 ppm, in the Al-27 MAS NMR spectra, and only a part of which in the dealuminated HZSM-5 zeolite acts as Lewis acid sites. (C) 2002 Elsevier Science B.V. All rights reserved.

On configuration of exchanged La3+ on ZSM-5: A theoretical approach to the improvement in hydrothermal stability of La-modified ZSM-5 zeolite

Density functional calculations have been employed to investigate the locating and binding of lanthanum cation, i.e., La(OH)(2)(+), on HZSM-5 zeolite. Through geometry optimization, it was determined that lanthanum ions are favorably accommodated in the two 6-T rings of the straight channels (Clusters 1 and 2, see Sec. III A for details). Cluster 1 was found to exist in prior to Cluster 2 due to the preference of Al substitution in the T11 site (Cluster 1) rather than in the T8 site (Cluster 2). Geometry-optimization of Cluster 1 containing another two lanthanide ions Nd3+ and Yb3+ was also carried out and it was found that a monotonic decrease in Ln-O bond length will take place as the atomic number increases, conforming well to the rule of lanthanide contraction. Some of the optimized parameters are comparable to the corresponding experimental values in Y zeolite, which confirms that the optimized configurations are acceptable. The average frequencies of hydroxyls attached to La3+ or Yb3+ in Cluster 1 fall at 3609.16 and 3579.76 cm(-1), respectively, with the gap of these two frequencies close to that in the sodalite cage of Y zeolite. Compared to H-form zeolite, the charges on both Al and O atoms in Ln-ZSM-5 zeolite show an obvious increase, which will undoubtedly lead to a stronger mutual interaction and hence enhance the stability of the [AlO4](-) anion. Moreover, the Ln(OH)(2)(+) seem to have thickened the zeolite framework, which can effectively retard the process of dealumination. Through the evaluation of the possibility for dimer formation, it turned out that when the exchange degree arrived to approximately 0.28, lanthanum monomers began to aggregate into dimers, and were completely converted into dimers when the exchange degree approached 0.60. (C) 2003 American Institute of Physics.

Formation of the V center on H-type zeolites with thermal treatment

The effect of thermal treatment on H-MCM-22 and H-ZSM-5 zeolites was investigated using the electron spin resonance technique. A six-line signal (denoted as A, g = 2.048, A = 22. 15 G) was detected on H-MCM-22 after He purging at high temperatures, whose intensities increased with the treating temperature. The same signal was also found on H-ZSM-5 zeolites with different crystal sizes. The paramagnetic center was identified as a V center, namely, a hole of an electron trapped on an oxygen atom bonding to a nearby aluminum atom. These signals appeared only on a dealuminated sample or a sample concomitantly with dealumination. The formation of the hole might involve an electron transferring from the lattice oxygen to a nonframework aluminum species, and the hyperfine splitting is caused by the interaction between the electron hole locating on the p orbit of oxygen and the framework aluminum bonding with the oxygen. The signal disappeared after the sample was exposed to air or oxygen at room temperature. However, the process was reversible. A new set of signals (denoted as B, g(1) = 2.008, g(2) = 2.003, g(3) = 1.9985) was observed after oxygen adsorption on the H-MCM-22 pretreated with He at 973 K or He purging at 973 K on the H-MCM-22 pretreated with oxygen at 813 K, which was attributed to the O- species.

The stability of nanosized HZSM-5 zeolite: a high-resolution solid-state NMR study

The thermal and hydrothermal stabilities of HZSM-5 zeolites with crystal sizes less than 100 nm have been studied by multinuclear solid-state NMR, combined with BET and XRD. As evidenced by Al-27 and Si-29 MAS as well as their corresponding cross-polarization/MAS NMR investigations, the thermal stability of nanosized HZSM-5 is not so good as that of microsized HZSM-5. This is due to two processes concerning dealumination and desilicification involved in the calcination of nanosized HZSM-5, while only the dealumination process is conducted in microsized HZSM-5 under the similar calcination process. The hydrothermal stability of nanosized HZSM-5 is, contrary to what was expected, not so bad as that of the microsized HZSM-5 in the course of steam treatment. The actual resistance of the hydrothermal stability to the crystal size of HZSM-5 can be ascribed to an active reconstruction of zeolitic framework through an effective filling of amorphous Si species into nanosized HZSM-5 during hydrothermal treatment. (C) 2001 Published by Elsevier Science B.V.