表面纳米化Zr的拉伸性能

利用表面机械研磨处理(SMAT)技术在Zr片状拉伸样品表面施加剧烈变形,获得超细/纳米晶粒组织的变形细化表层,其中Zr板厚度1 mm,两侧变形层厚度均为100μm.拉伸实验结果表明,表层细化组织提高了屈服强度和抗拉强度,使加工硬化能力及伸长率下降.应变速率在10~(-4)～10~(-3)s~(-1)范围时,拉伸强度随应变速率的提高而提高;应变速率增大至10~(-2)s~(-1)量级时,抗拉强度下降.扫描电镜观察显示出韧性韧窝状断裂特征.

Enhanced Plasticity of Zr-Based Bulk Metallic Glass Matrix Composite with Ductile Reinforcement

A composite material containing uniformly distributed micrometer-sized Nb particles in a Zr-based amorphous matrix was prepared by suction cast. The resulting material exhibits high fractured strength over 1550 MPa and enhanced plastic strain of about 29.7% before failure in uniaxial compression test at room temperature. Studies of the serrations on the stress-strain curves and the shear bands on the fractured samples reveal that the amplitude of the stress drop of each serration step corresponds to the extent of the propagation of a single shear band through the materials. The composite exhibits more serration steps and smaller amplitude of stress drop due to the pinning of shear band propagation by ductile Nb particles.

Microstructure of Zr-alloyed coating using pulsed laser

Coatings were synthesized by laser alloying of zirconium (Zr) particles using a pulsed Nd:YAG laser on an austenite stainless steel. The distribution of Zr is uneven, in a depth of 18 mum just below the surface of the pool. The coating consisted of duplex microstructures, i.e. metallic glass (MG) and austenite. The MG formed in Zr-contained regions, with the Zr composition ranging from 7.6 to 16.8 at.%. The formation of the MG was attributed to an increase in glass-forming ability by Zr addition.

两种Zr基块体非晶合金的变形行为

使用单轴压缩、纳米压入、界面粘结和显微观察等技术对Zr65A10Ni10-Cu15和Zr52.5Al10Ni10Cu15Be12.5合金的宏观和细观塑性变形行为进行了研究．结果表明：Be代替了部分Zr后的非晶合金的单轴压缩强度和塑性明显提高．两种合金均在低加载速率的纳米压入中表现出锯齿流变特征，在高加载速率中为连续的塑性变形，但变形行为转变的临界加载速率有明显差别．对比两种合金压痕下方塑性变形区域中剪切带形貌表明，在同样加载条件下，Zr52.5Al10Ni10Cu15Be12．5合金中形成剪切带的数量多、尺寸小、间距小，随着压入深度的增大，剪切带间距基本不变．这表明Zr65Al10Ni10Cu15合金中剪切带形成相对困难，趋向于单个剪切带的扩展，因此宏观塑性变形能力有限．而在含Be合金的塑性变形过程中剪切带容易形核，趋向于多重剪切带的同时开动，因此宏观塑性变形能力显著．两种合金塑性变形行为的差异符合自由体积模型．

Effect of Nb Content on the Microstructure and Mechanical Properties of Zr-Cu-Ni-Al-Nb Glass Forming Alloys

(Zr65Al10Ni10Cu15)(100-x) Nb-x glass forming alloys with Nb contents ranging from 0 to 15 at.% were prepared by water-cooled copper mould cast. The alloys with different Nb contents exhibited different microstructures and mechanical properties. Unlike the monolithic Zr65Al10Ni10Cu15 bulk metallic glass, only a few primary bee beta-Ti phase dendrites were found to distribute in the glassy matrix of the alloys with x = 5. For alloys with x = 10, more beta-phase dendrites forms, together with quasicrystalline particles densely distributed in the matrix of the alloys. For alloys with x = 15, the microstructure of the alloy is dominated by a high density of fully developed P-phase dendrites and the volume fraction of quasicrystalline particles significantly decreases. Room temperature compression tests showed that the alloys with x = 5 failed at 1793 MPa and exhibited an obvious plastic strain of 3.05%, while the other samples all failed in a brittle manner. The ultimate fracture strengths are 1793, 1975 and 1572 MPa for the alloys with x = 0, 10 and 15 at.% Nb, respectively.

Metallographic Analysis of Cu-Zr-Al Bulk Amorphous Alloys with Yttrium Addition

Minor yttrium addition can improve the glass-forming ability of Cu-Zr-Al ternary alloys via suppression of the growth of eutectic clusters. Yttrium addition also makes the room temperature ductility of the alloys decrease, and both the compressive strength and elastic strain limits increase slightly.

Effect of structural relaxation on deformation behaviour of Zr-based metallic glass

Structural relaxation through isothermal annealing at tempertature below glass transition is conducted on Zr46.75Ti8.25Cu7.5Ni10Be27.5 (Vitreloy-4) bulk metallic glass. Defect concentration is correlated with the annealing time t according to differential scanning calorimetry thermalgrams. The effects of structural relaxation on mechanical properties and deformation behaviour are investigated by using instrumented nanoindentation. It is found that as-cast alloy exhibits pronounced serration flow during the loading process of nanoindentation, and the size and number of serrations decrease with the annealing time. The change of the deformation behaviour with structural relaxation is explained using a free volume model.

Serrated Plastic Flow in a Zr-Based Bulk Metallic Glass During Nanoindentation

We investigate plastic deformation of Zr41.2Ti13.8Cu12.5Ni10Be22.5 bulk metallic glass using depth sensing nanoindentation. Numerous serrations in the load-displacement curves during indentation, shear bands and pile-ups around the indent were observed. The results revealed that the serrated plastic flow behaviour in this alloy depends strongly on the indentation strain rate.

Behavior of Multiple Shear Bands in Zr-Based Bulk Metallic Glass

The deformation behavior of Zr41.2Ti13.8Cu12.5Ni10Be22.5 bulk metallic glass was studied by in situ scanning electron microscopy (SEM) quasi-static uniaxial compression tests at room temperature. Multiple shear bands were observed with a large plasticity. Microscopic examination demonstrates that slipping, branching and intersecting of multiple shear bands are the main mechanisms for enhancing the plasticity of this metallic glass. Additionally, nano/micro-scale voids and cracks at the intersecting sites of shear bands and preferential etching of shear bands were observed as well. These observations demonstrated that the formation of shear bands in bulk metallic glasses is resulted mainly from local free volume coalescence.

Characterization of Plastic Flow in Two Zr-Based Bulk Metallic Glasses

Plastic deformation behaviors of Zr65Al10Ni10CU15 and Zr52.5Al10Ni10Cu15Be12.5 bulk metallic glasses (BMGs) are studied by using the depth-sensing nanoindentation, microindentation and uniaxial compression. The Be-containing BMG exhibits a significantly improved overall plastic strain compared with the Be-free alloy during compressive tests. Both BMGs show a loading-rate-dependent serrated flow during nanoindentation measurements, but the Be-containing alloy exhibits a much lower critical loading rate for the disappearance of the serration than the Be-free BMG. The shear band patterns developed during plastic deformation are investigated by microindentation technique, wherein much higher shear band density is found in the Be-containing alloy than in the Be-free alloy, indicating an easier nucleation of shear bands in the former BMG. The difference in the plastic deformation behavior of the two BMGs can be explained by a free volume model.

Microstructure and mechanical properties of a novel Zr-based bulk metallic glass composite

Zr48.5Cu46.5Al5 bulk metallic glass (BMG) composites with diameters of 3 and,4 mm were prepared through suction casting in an arc melting furnace by modulating the alloy composition around the monothetic BMG composition of the high glass forming ability. Microstructural characterization reveals that the composites contain micron-sized CuZr phase with martensite structure, as well as nano-sized Zr2Cu crystalline particles and Cu10Zr7 plate-like phase embedded in an amorphous matrix. Room temperature compression tests showed that the composites exhibited significant strain hardening and obvious plastic strain of 7.7% for 3 nun and 6.4% for 4 nun diameter samples, respectively.

Microstructure and mechanical properties of Zr-Cu-Al bulk metallic glasses

Zr49Cu46Al5 and Zr48.5Cu46.5Al5 bulk metallic glasses(BMGs) with diameter of 5 mm were prepared through water-cooled copper mold casting. The phase structures of the two alloys were identified by X-ray diffractometry(XRD). The thermal stability was examined by differential scanning calorimetry(DSC). Zr49Cu46Al5 alloy shows a glass transition temperature, T, of about 689 K, an crystallization temperature, T-x, of about 736 K. The Zr48.5Cu46.5Al5 alloy shows no obvious exothermic peak. The microstructure of the as-cast alloys was analyzed by transmission electron microscopy(TEM). The aggregations of CuZr and CuZr2 nanocrystals with grain size of about 20 nm are observed in Zr49Cu46Al5 nanocrystalline composite, while the Zr48.5Cu46.5Al5 alloy containing many CuZr martensite plates is crystallized seriously. Mechanical properties of bulk Zr49Cu46Al5 nanocrystalline composite and Zr48.5Cu46.5Al5 alloy measured by compression tests at room temperature show that the work hardening ability of Zr48.5Cu46.5Al5 alloy is larger than that of Zr48.5Cu46.5Al5 alloy.

一种新型Zr基块状非晶复合材料的显微组织与力学性能

通过在块状Zr-Cu—Al非晶合金形成能力较大的成分范围附近设计成分，利用电弧炉吸铸的方法制备了直径分别为3和4mm的Zr48.5Cu46.5Al5块状非晶复合材料．显微组织分析表明，复合材料中含有微米尺度的具有马氏体结构的CuZr相，同时还生成了在非晶基体上均匀分布的Zr2Cu纳米颗粒和Cu10Zr7片状相．室温压缩实验表明，直径为3和4mm块状非晶复合材料分别达到7．7％和6．4％的塑性变形，同时有显著的应变硬化现象．

Synthesis Of Plastic Zr-Based Bulk Metallic Glass Matrix Composites By The Copper-Mould Suction Casting And The Bridgman Solidification

Zr-based bulk metallic glass matrix composites with the composition of Zr56.2Ti13.8Nb5.0Cu6.9Ni5.6Be12.(5) were synthesized by the copper-mould suction casting and the Bridgman solidification. The composite, containing a well-developed flowery beta-Zr dendritic phase, was obtained by the Bridgman solidification with the withdrawal velocity of 0.8 mm/s and the temperature gradient of 45 K/mm, and the ultimate strength of 2050 MPa and fracture plastic strain of 14.6% of the composite were achieved, which was mainly interpreted by the homogeneous dispersion of bcc beta-Zr phase in the glass matrix. Crown Copyright (C) 2008 Published by Elsevier B.V. All rights reserved.