Adhesive strength of new thermal barrier coatings of rare earth zirconates

La2Zr2O7 (LZ) and La-2(Zr0.7Ce0.3)(2)O-7 (LZ7C3) as novel candidate materials for thermal barrier coatings (TBCs) were prepared by electron beam-physical vapor deposition (EB-PVD). The adhesive strength of the as-deposited LZ and LZ7C3 coatings were evaluated by transverse scratch test. Meanwhile, the factors affecting the critical load value were also investigated. The critical load value of LZ7C3 coating is larger than that of LZ coating, whereas both values of these two coatings are lower than that of the traditional coating material, i.e. 8 wt% yttria stabilized zirconia (8YSZ). The micro-cracks formed in the scratch channel can partially release the stress in the coating and then enhance the adhesive strength of the coating. The width of the scratch channel and the surface spallation after transverse scratch test are effective factors to evaluate the adhesive strength of LZ and LZ7C3 coatings.

THE YELLOW-TO-BLUE INTENSITY RATION (Y/B) OF DY-3+ EMISSION

Various borates, vanadates, niobates, antimonates, titanates, zirconates and CaS doped with Dy3+ were prepared. Factors which have an effect on the yellow-to-blue intensity ratio (Y/B) of Dy3+ emission are reported. Y/B increases with decreasing Z/r or electronegativity of the next-neighbour element M in the complex oxides Dy-O-M. The greater the degree of covalency between Dy3+ and O2-, the greater Y/B is. When Dy3+ is located at a site with an inverse centre and high symmetry, Dy3+ displays no luminescence. It seems that Y/B of Dy3+ located at a site deviated from an inverse centre is greater than that of Dy3+ located at a site without an inverse centre. Y/B does not vary much with the variation in concentration of Dy3+ when Dy3+ is substituted for an element with the same valency, but it does depend on the concentration of Dy3+ when Dy3+ is substituted for an element with a different valency in the matrix, because defects are formed in this case.