Metallographic Analysis of Cu-Zr-Al Bulk Amorphous Alloys with Yttrium Addition

Minor yttrium addition can improve the glass-forming ability of Cu-Zr-Al ternary alloys via suppression of the growth of eutectic clusters. Yttrium addition also makes the room temperature ductility of the alloys decrease, and both the compressive strength and elastic strain limits increase slightly.

富钇稀土-铝合金制取的研究Study on Preparation of Yttrium-Rich RE-Al Alloys

我国江西龙南稀土矿是目前世界上储量最大的富钇稀土矿、研制具有多种用途的钇（Y）-铝（Al）或富钇混合稀土（Ymm）-铝中间合金，对于开拓我国龙南稀土矿的应用领域扩大稀土合金出口具有重要意义。基于这一背景并针对目前氟化物体系制取Ymm-Al合金时存在着电解温度高，腐蚀现象严重，电效偏低等缺点，本文系统开展了在氯化物熔盐体系中电解制取Ymm-Al合金的研究工作。本工作由三部分组成：在第一部分工作中，开展了熔盐电解所需要基本原料-无水稀土氯化物制取的工艺研究。利用化学分析和结构分析手段，弄清了干法氯化过程中YmmCl_3水解的机理，提出了减弱水解的措施，即YmmCl_3先在850-900 ℃灼烧1.5 + 0.2hr，脱掉吸附水并将碱式碳酸盐转化为氧化物，增加稀土氧化物的比表面。通过条件试验得到最佳工艺条件为：采用NH_4 Cl:Ymm_2 O_3 = 14:1（摩尔比）的配料比，每次投入氯化装置的原料量为0.26 - 0.36 kg, 在400-450 ℃氯化反应激烈开始后迅速降温至400 ℃以下，待物料粘结现象消失后，再行升温氯化。出料及后期控制温在475 ± 25 ℃。经过3.8 ± 0.2hr氯化，可制得水不溶物小于1%并符合熔盐电解要求的YmmCl_3原料。此新工艺与原有干法工艺相比，流程短，装置简单，不需密闭抽真空，成本低，适于制取任何量的优质熔盐电解所需氯化稀土原料。在第二部分工作中，利用上述YmmCl_3原料，以液态铝为阴极，在氯化物体系中进行熔盐电解，通过试验得出在小型试验规模制取Ymm-Al合金的最隹工艺条件为：电解质组成（重量比）40%YmmCl_3-1%NaF-59%等摩尔的NaCl-KCl；电解温度为790 ± 5 ℃；阴极电流密为0.7 - 0.02A/cm~2；电解电量为333 ± 5库仑/克铝，制得钇铝合金中Ymm含量为10 ± 2%。添加1%的NaF可消除阴极表面生成枝状物，减少合金中夹渣和熔盐中沉渣。在电解工作中，将方差分析应用于试验数据处理，方差分析结果表明，各种试验因素对电效有明显影响，试验数据可靠，试验误差在允许范围以内。在第三部分工作中，利用线性扫描伏安法测定了在最隹电解工艺条件下Y~（3+）和Ymm在液态铝及钼电极上的析出电位。测定结果表明：Y~（3+）和Ymm~（3+）在液态铝阴极上的析出电位比在钼阴极上偏正0.2 ～ 0.8伏，氟离子的加入要比不加氟时析出电位不有同程度的负移，但考虑到氟离了具有消渣作用，加入少量氟比物添加剂对提高电效有利。

In-situ synthesis of AlN powders and composite AlN powders with yttrium addition

Using Al-Mg and Al-Mg-Y alloys as raw materials and nitrogen as gas reactants, AIN powders and composite AIN powders by in-situ synthesis method were prepared. AIN lumps prepared by the nitriding of Al-Mg and Al-Mg-Y alloys have porous microstructure, which is favorable for pulverization. They have high purity, containing 1.23 % (mass fraction) oxygen impurity, and consisted of AIN single phase . The average particle size of AIN powders is 6.78 mum. Composite AlN powders consist of AlN phases and rare, earth oxide Y2O3 phase. The distribution of particle size of AIN powders shows two peaks. In view, of packing factor, AIN powders with such size distribution can easily be sintered to high density.

The microstructure and mechanical properties of Mg-3Al-3RE alloys

The Mg-3Al-3RE alloys (RE, the cerium-rich or the yttrium-rich misch metal) were smelted in a resistance furnace under the protective flux from the Mg-RE master alloys and pure magnesium ingots. The microstructure and mechanical properties of samples prepared by steel mould casting method were investigated.

Aging behavior and mechanical properties of Mg-Gd-Ho alloys

The Mg-8Gd-0.6Zr-xHo (x = 1, 3 and 5, mass%) alloys were prepared by casting technology, and structures, aging strengthening mechanism and mechanical properties of the alloys were investigated. The age behaviors and the mechanical properties are improved by adding Ho addition. The structures of the alloys are characterized by the present of rosette-shaped equiaxed grains. The peak hardness value of the Mg-8Gd-0.6Zr-3Ho alloy is 100 Hv, which is about 30% higher than that of Mg-8Gd-0.6Zr alloy.

The influence of mischmetal and tin on the microstructure and mechanical properties of Mg-6Zn-5Al-based alloys

The influence of the addition of mischmetal (MM) and tin (Sn) (total content of mischmetal and tin = 4 wt.%) on the microstructure, aging behavior and mechanical properties of Mg-6Zn-5Al-based alloys has been investigated. The microstructure of the as-cast alloys consists of alpha-Mg. Mg-32(Al,Zn)(49), Al2Mg5Zn2, Mg2Sn and Al2MMZn2 phases, and the morphology of these intermetallic phases varies with different MM and Sri additions.

Microstructures and mechanical properties of as-cast Mg–5Al–0.4Mn–xNd (x=0, 1, 2 and 4) alloys

Mg-5Al-0.4Mn-xNd (x=0, 1, 2 and 4wt.%) alloys were prepared by metal mould casting method. The microstructures and mechanical properties were investigated. The results demonstrated that Al11Nd3 phase was formed and mainly aggregated along the grain boundaries with the addition of Nd. Meanwhile, the grain sizes were greatly reduced with the increasing Nd content.

Effect of Y for enhanced age hardening response and mechanical properties of Mg-Ho-Y-Zr alloys

In this study, compositional dependence of age hardening characteristics and tensile properties were investigated for Mg-4Ho-xY-0.6Zr alloys (x = 0, 3 5, and 7 wt%). The result showed that with increasing Y content, the hardness of the alloys increased in the as-quenched and aged-peak conditions. Considerable age hardening response was recognized for the alloys. When the alloy containing 7% Y showed the most remarkable age hardening response at aging temperature of 250 degrees C.

Microstructure and mechanical properties of high performance Mg-Gd based alloys

The Mg-12Gd-4Y-2Nd-0.3Zn-0.6Zr (wt.%) alloy was prepared by casting technology, and the structure, age hardening behavior and mechanical properties of the alloy have been investigated. The results demonstrated that the alloy was composed of alpha-Mg matrix, a lot of dispersed Mg24RE5 (RE = Gd/Y/Nd) and Mg5RE precipitates in the as-cast and the T6 state alloys. The alloy exhibited remarkable age hardening response and excellent mechanical properties from room temperature (RT) to 300 degrees C by optimum solid solution and aging conditions. The ultimate tensile strength.

Electrolytic Deposition and Diffusion of Lithium onto Magnesium-9 Wt Pct Yttrium Bulk Alloy in Low-Temperature Molten Salt of Lithium Chloride and Potassium Chloride

The electrolytic deposition and diffusion of lithium onto bulk magnesium-9 wt pct yttrium alloy cathode in molten salt of 47 wt pct lithium chloride and 53 wt pct potassium chloride at 693 K were investigated. Results show that magnesium-yttrium-lithium ternary alloys are formed on the surface of the cathodes, and a penetration depth of 642 mu m is acquired after 2 hours of electrolysis at the cathodic current density of 0.06 A center dot cm(-2). The diffusion of lithium results in a great amount of precipitates in the lithium containing layer. These precipitates are the compound of Mg41Y5, which arrange along the grain boundaries and hinder the diffusion of lithium, and solid solution of yttrium in magnesium. The grain boundaries and the twins of the magnesium-9 wt pct yttrium substrate also have negative effects on the diffusion of lithium.

Effect of yttrium-rich misch metal on the microstructures, mechanical properties and corrosion behavior of die cast AZ91 alloy

Die cast AZ91-xYmm (x = 0-0.8 wt.%) magnesium alloys with excellent tensile properties and corrosion resistance behavior were successfully prepared by a simple addition of yttrium-rich misch metal (Ymm) to AZ91. Influences of Ymm on the microstructure, mechanical properties and corrosion behavior of AZ91 were investigated. The results showed that addition of Ymm to die cast AZ91 alloy could re. ne the microstructure including primary alpha-Mg and eutectic beta-Mg17Al12. When the content of Ymm reached 0.8 wt.% a small quantity of Al2Y phase would form. The tensile properties were improved greatly with addition of Ymm to AZ91. The creep rate of the AZ91-Ymm alloys, tested at 150 degrees C/50MPa, was one order of magnitude lower than that of AZ91. When addition of Ymm was more than 0.3 wt.%, the salt-spray corrosion resistance of AZ91-Ymm alloys could be 30-40 times of that of AZ91. The improvement of corrosion resistance with addition of Ymm was confirmed by the results of electrochemical polarization experiments. Mechanism of the improvement of mechanical properties and corrosion behavior caused by Ymm was also discussed.

Microstructures and mechanical properties of Mg-8Gd-0.6Zr-xNd (x=0, 1, 2 and 3 mass%) alloys

Mg-8Gd-0.6Zr-xNd (x = 0, 1, 2 and 3 mass%) alloys were prepared by metal mould casting method, and the microstructures, age hardening responses and mechanical properties have been investigated. The microhardness of the as-cast alloys is increased with increasing Nd content. The age hardening behavior and mechanical properties are enhanced significantly by adding Nd element. The peak ageing hardness of the Mg-8Gd-0.6Zr-3Nd alloy is 103, it is about 1.3 times more than that of the Mg-8Gd-0.6Zr alloy. The aged Mg-8Gd-0.6Zr-3Nd alloy exhibits maximum ultimate tensile strength and yield strength, and the values are 271 and 205 MPa at room temperature, 205 MPa and 150 MPa at 250 degrees C, respectively. Which are about 2 times higher than those of Mg-8Gd-0.6Zr alloy. The improved hardness and strength are mainly attributed to the fine dispersiveness Of Mg5RE and Mg12RE precipitates in the alloy.

Solvent extraction of scandium(III), yttrium(III), lanthanum(III) and gadolinium(III) using Cyanex 302 in heptane from hydrochloric acid solutions

The extractions of the selected rare earths (Sc, Y, La and Gd) from hydrochloric acid solutions have been investigated using bis(2,4,4-trimethylpentyl)-mono thiophosphinic acid (Cyanex 302, HL) in heptane as an extractant. The results demonstrate that the extractions of rare earths occur via the following reaction: Sc(OH)(2+) + 2[(HL)(2)]((O)) double left right arrow [Sc(OH)L-2 (.) 2(HL)]((O)) + 2H(+) Y3+ + 3[(HL)(2)]((O)) double left right arrow [Y(HL2)(3)]((O)) + 3H(+) La(OH)(2)(+) + 3[(HL)(2)](O) double left right arrow [La(OH)(2)L (.) 5(HL)]((O)) + H+ Gd(OH)(2+) + 3[(HL)(2)]((O)) double left right arrow [Gd(OH)L-2 (.) 4(HL)]((O)) + 2H(+) The pH(1/2) values and equilibrium constants of the extracted complexes have been deduced by taking into account the aqueous phase complexation of the metal ion with hydroxyl ligands and plausible complexes extracted into the organic phase. According to the pH(1/2) values, it is possible to realize mutual separation among Sc(III), Y(III), La(III) and Gd(III) with Cyanex 302 by controlling aqueous acidity.

Selective separation of yttrium by CA-100 in the presence of a complexing agent

The selective separation of Y from yttrium solution containing small heavy rare earth (HRE) impurities (Ho, Er, Tm, Yb, Lu) by liquid-liquid extraction using CA-100 in the presence of a water-soluble complexing agent of ethylenediaminetetraacetic acid (EDTA) was experimentally studied at 298K. Experiments were carried Out in two feeds, Feed-I: [RE](f) = 4.94 x 10(-3) M, Y = 98.5%, HRE (Ho, Er, Tm, Yb, Lu) = 1.5%; Feed-II: [RE](f) = 4.94 x 10(-3) M, Y = 99.9%, HRE (Ho, Er, Tm, Yb, Lu) = 0.1%, as a function of equilibrium pH (pH(eq)), the concentration ratio of [EDTA]:[HRE impurities]. It was shown that the extraction of HRE in the presence of EDTA was suppressed when compared to that of Y because of the masking effect, while the selective extraction of Y was enhanced and the separation factors increased to maximum at appropriate condition for Feed-I: Y/Ho = 1.53, Y/Er = 3.09, Y/Tm = 5.61, Y/Yb = 12.04, Y/Lu = 27.51 at pH 4.37 and [EDTA]:[HRE impurities] = 4: 1, for Feed-II: Y/Ho = 1.32, Y/Er = 1.91, Y/Tm = 2.00, Y/Yb = 3.05, Y/Lu = 3.33 at pH 4.42 and [EDTA]: [HRE impurities] = 8:1. The separation and purification of Y by this method was discussed.