An investigation on ion solvation and ion association in a gel-type solid state polymer electrolyte

Ion salvation and ion association in polytriethylene glycol dimethacrylate (PTREGD)-LiClO4 gel-type polymer electrolytes were investigated. It was found that the fraction of solute existing as single ions (alpha(i)) decreases and that of triple ions (alpha(i)) increases linearly with increasing LiClO4 concentration, while for ion pairs, as the salt concentration increases, its fraction (alpha(p)) increases first and then falls down. The findings can be rationalized by the fact that the ionic conductance of the polymer electrolyte may be mainly contributed by triple ions and higher ionic aggregates with unequal numbers of positive and negative charges in the salt concentration range of practical significance, i.e. in the range of 0.5-1.5 mol/l. The temperature dependence of these fractions was also examined. In the case of tetraethylene glycol as the solvent, alpha(i) and alpha(p) increase as the temperature is raised, but alpha(t) decreases as the temperature increases from 25 degrees C to 85 degrees C. It seems that the increase of alpha(i) and alpha(p) results from the redissociation of triple ions at higher temperature, The same changing trend of those fractions is also observed when PEG(400) is used as the solvent.

Tunneling magnetoresistance in (Ga,Mn)As/Al-O/CoFeB hybrid structures

Tunneling magnetoresistance (TMR) in Ga(0.9)2Mn(0.08)As/Al-O/Co40Fe40B20 trilayer hybrid structure as a function of temperature from 10 to 50 K with magnetic field vertical bar H vertical bar <= 2000 Oe has been studied. TMR ratio of 1.6% at low fields at 10 K was achieved with the applied current of 1 mu A. The behavior of junction resistance was well explained by the tunneling resistance across the barrier. Strong bias dependences of magnetoresistance and junction resistance were presented. (C) 2009 American Institute of Physics. [DOI: 10.1063/1.3068418]

Synthesis and electrical properties of new solid state. Electrolyte materials Ce5.2RE0.8MoO15-delta

A series of solid state electrolytes, Ce-5.2 RE0.8 MoO15-delta (RE = Y, La, Sm, Gd, Dy, Ho, Er), were synthesized by sol-gel method. Their structures and electrical conductivities were characterized by X-ray Diffraction (XRD), Raman and X-ray Photoelectron Spectroscopy (XPS) and AC impedance spectroscopy, respectively. The results show that the concentrations of oxygen vacancy increased with increasing x and their conductivity were improved. And the cell parameters increase as the radius of RE3+ increases. Because the ionic radius of doped Dy3+ (0.0908 nm) is closed to that of Ce4+ (0.0920 nm), their oxide has minimal cell elastic straining between RE3+ and oxygen vacancy, and the system has the least association enthalpy, thus the oxide Ce-5.2 Dy-0.8 MoO15-delta exhibits a higher conductivity (7.02 x 10(-3) S/cm) and lower activation energy (1.056 eV) compared to the other doped compounds.

Study of ion solvation and ion association in polymer gel electrolyte with polyethylene oxide-co-polypropylene oxide as a plasticizer

Using a molal conductance method, ion solvation and ion association in polytriethylene glycol dimethacrylate (PTREGD)-LiClO4 gel electrolytes with amorphous ethylene oxide-co-propylene oxide (EO-co-PO, <(M)over bar (n)>, = 1750) as the plasticizer were investigated. It was found that the fraction of solute existing as single ions (alpha(i)) and ion pairs (alpha(p)) decreases, while that of triple ions (alpha(t)) increases linearly with increasing salt concentration. The dependence of these fractions on molecular weight of plasticizer was also examined. It was shown that alpha(i) and alpha(t) increase and alpha(p) decreases with increasing molecular weight. The result of temperature dependence of these fractions was very interesting: when the temperature is lower than 55 degrees C, alpha(i) increases while alpha(p) and alpha(t) decrease with increasing temperature; however, when the temperature is higher than 55 degrees C, the reverse is true.