Sulfonated poly(arylene-co-imide)s as water stable proton exchange membrane materials for fuel cells

A novel sulfonated poly(arylene-co-imide)s were synthesized by Ni(0) catalytic copolymerization of sodium 3-(2,5-dichlorobenzoyl)benzenesulfonate and naphthalimide dichloride monomer. The synthesized copolymers with the - SO3H group on the side-chain of polymers possessed high molecular weights revealed by their high viscosity and the formation of tough and flexible membranes. Because of the introduction of electron donating phenoxy groups into naphthalimide moieties, the hydrolysis of the imide rings was depressed. The resulting copolymers exhibited excellent water stability. The copolymer membranes display no apparently change in appearance, flexibility, and toughness after a soaking treatment in pressurized water at 140 degrees C for 250 h.

Preparation and evaluation of a proton exchange membrane based on oxidation and water stable sulfonated polyimides

A series of novel oxidation and water stable sulfonated polyimides (SPIs) were synthesized from 4,4'-binaphthyl-1,1',8,8'-tetracarboxylic dianhydride (BTDA), and wholly aromatic diamine 2,2'-bis(3-sulfobenzoyl) benzidine (2,2'-BSBB) for proton exchange membrane fuel cells. These polyimides could be cast into flexible and tough membranes from m-cresol solutions. The copolymer membranes exhibited excellent oxidative stability and mechanical properties due to their fully aromatic structure extending through the backbone and pendant groups. Moreover, all BTDA-based SPI membranes exhibited much better water stability than those based on the conventional 1,4,5,8-naphthalenecarboxylic dianhydride. The improved water stability of BTDA-based polyimides was attributed to its unique binaphthalimide structure. The SPI membranes with ion exchange capacity (IEC) of 1.36-1.90 mequiv g(-1) had proton conductivity in the range of 0.41 x 10(-1) to 1. 12 x 10(-1) S cm(-1) at 20 degrees C. The membrane with IEC value of 1.90 mequiv g(-1) displayed reasonably higher proton conductivity than Nafion((R)) 117 (0.9 x 10(-1) S cm(-1)) under the same test condition and the high conductivity of 0.184 S cm(-1) was obtained at 80 degrees C. Microscopic analyses revealed that well-dispersed hydrophilic domains contribute to better proton conducting properties. These results showed that the synthesized materials might have the potential to be applied as the proton exchange membranes for PEMFCs.

利用与经营方式对黑土团聚体水稳定性的影响

在松嫩平原典型中厚黑土区，通过对不同地点荒地和耕地、长期定位试验地的野外调查、采样分析及室内模拟实验，系统研究了荒地、耕地不同粒级团聚体的剖面结构特性及有机胶结物质含量变化规律，探讨了有机碳及无机氮添加对黑土不同粒级团聚体水稳定性的影响。阐明了黑土轻组分有机C的积累分布变化及其与团聚体水稳定性的关系。结果表明，荒地各粒级水稳性团聚体内部孔隙较多，并有根毛和菌丝体穿插；耕地则内部结构紧实，孔隙度明显低于荒地，内部很难发现根毛与菌丝体，具有压实的表面特征。耕地各粒级水稳性团聚体间有机碳含量无明显差别，而荒地则随粒级减小呈下降趋势。微粒有机C主要存在水稳性大团聚体中，其含量随粒级减少而下降，这对维持耕地黑土大团聚体的水稳定性起重要作用。不同养分供给条件下，无机氮单独添加不能维持耕地团聚体的水稳定性，有机碳和无机氮可明显增加不同粒级团聚体的水稳定性。抗分解稳定性实验表明，荒地大团聚体中的轻组分有机C含量急剧减少，大团聚体的水稳定性迅速下降。可以推断大团聚体中活性有机胶结物质减少是黑土开垦后水稳性团聚结构退化的直接原因，无机N会加速消耗黑土团聚体有机胶结物质，不利于黑土团聚体水稳定性的保持。

HEC和AAM添加剂对提高黄土集流效率的试验研究

基于西北地区黄土资源丰富、地形复杂、外源材料运输困难的实际状况 ,提出将 HEC(High Strength andWater Stability Earth Consolidator)和 AAM(Active Aluminate Mixture)材料添加剂与黄土混掺 ,以期提高其集流效率。通过室内人工降雨模拟试验 ,探讨了典型黄土与 HEC和 AAM材料添加剂分别混掺后集流效率和性能的变化过程。同时 ,对照其它几种集雨材料 ,对不同雨强、雨量及坡度下的起流历时、集流效率和材料性能进行了比较。结果表明 :黄土与 HEC和 AAM添加剂混掺后形成的黄土复合集流材料具有较强的抗拉、抗压能力 ,不同雨强和雨量等级范围均具有较高的集流效率 (>78% ) ,已达到混凝土的集流效果 ,其成本仅为混凝土的 1/ 3～ 1/ 2。

Synthesis and properties of sulfonated poly[bis(benzimidazobenzisoquinolinones)] as hydrolytically and thermooxidatively stable proton conducting ionomers

Novel sulfonated poly [bis(benzimidazobenzisoquinolinones)] as hydrolytically and thermooxidatively stable electrolyte for high -temperature fuel cell applications are reported. A series of sulfonated polymers (SPBIBI-x, x refers to molar percentage of sulfonated dianhydride monomer) were synthesized from 6,6'-disulfonic-4,4'-binaphthyl-1,1',8,8'-tetracarboxylic dianhydride (SBTDA), 4,4-binaphthyl-1,1,8,8-tetracarboxylic dianhydride (BTDA), and 3,3'-diaminobenzidine. The chemical structures of those polymers as well as model compounds synthesized from SBTDA and o-phenylenediamine were confirmed by nuclear magnetic resonance (NMR) and Fourier transform infrared (FTIR).

Synthesis and properties of novel polyimides from sulfonated binaphthalene dianhydride for proton exchange membranes

A sulfonated dianhydride monomer, 6,6-disulfonic-4,4'-binaphthyl-1,1',8,8'-tetracarboxylic dianhydride (SBTDA), was successfully synthesized by direct sulfonation of the parent dianhydride, 4,4'-binaphthyl-1,1',8,8'-tetracarboxylic dianhydride (BTDA), using fuming sulfuric acid as the sulfonating reagent. A series of sulfonated homopolyimides were prepared from SBTDA and various common nonsulfonated diamines. The resulting polymer electrolytes, which contain ion conductivity sites on the deactivated positions of the aryl backbone rings, displayed high proton conductivities of 0.25-0.31 S cm(-1) at 80 degrees C. The oxidative stability test indicated that the attachment of the -SO3H groups onto the dianhydride units did not deteriorate the oxidative stability of the SPI membranes.

Novel acid-base polyimides synthesized from binaphthalene dianhydrie and triphenylamine-containing diamine as proton exchange membranes

The synthesis and characterization of novel acid-base polyimide membranes for the use in polymer electrolyte membrane fuel cell is presented in this paper. The sulfonated polyimides (SPIs) bearing basic triphenylamine groups were easily synthesized using 4,4'-binaphthyl-1,1',8,8'-tetracarboxylic dianhydride (BTDA), sulfonated diamine of 4,4'-diaminodiphenyl ether-2,2'-disulfonic acid (ODADS), and nonsulfonated diamines of 4,4'-diaminotriphenylamine (DATPA). The effects of the structure of the dianhydride and diamines on the properties of SPI membranes were evaluated through the study of membrane parameters including water sorption, proton conductivity, water stability, dimensional changes, and methanol permeability.

Synthesis and characterization of rigid-rod sulfonated polyimides bearing sulfobenzoyl side groups as proton exchange membranes

A novel wholly aromatic diamine, 2,2 '-bis(3-sulfobenzoyl)benzidine (2,2 '-BSBB), was successfully prepared by the reaction of 2,2 '-dibenzoylbenzidine (2,2 '-DBB) with fuming sulfuric acid. Copolymerization of 1,4,5,8-naphathlenetetracarboxylic dianhydride with 2,2 '-BSBB and 2,2 '-DBB generated a series of rigid-rod sulfonated polyimides. The synthesized copolymers with the -SO3H group on the side chain of polymers possessed high molecular weights revealed by their high viscosity and the formation of tough and flexible membranes. The copolymer membranes exhibited excellent oxidative stability and mechanical properties due to their fully aromatic structure extending through the backbone and pendent groups. They displayed clear anisotropic membrane swelling in water with negligibly small dimensional changes in the plane direction of the membrane. The proton conductivities of copolymer membranes increased with increasing IEC and temperature, reaching value above 1.25 x 10(-1) S/cm at 20 degrees C, which is higher than that of Nafion (R) 117 at the same measurement condition. They displayed reasonably high proton conductivity due to the higher acidity of benzoyl sulfonic acid group, the larger interchain spacing, which is available for water to occupy, taking their lower water uptake (WU) into account. Consequently, these materials proved to be promising as proton exchange membrane.

Sulfonated polyimides bearing benzimidazole groups for proton exchange membranes

A series of sulfonated polymides containing benzimidazole groups were synthesized using 4,4'-binaphthyl-1,1',8,8'-tetracarboxylic dianhydride (BTDA), 4,4'-diaminodiphenyl ether-2,2'-disulfonic acid (ODADS) as the sulfonated diamine, and 2-(3',5-diaminophenyl)benzimidazole (a) or 6,4'-diamino-2-phenylbenzimidazole (b) as the nonsulfortated diamine. The electrolyte properties of the synthesized polyimides Ia-x, Ib-x, x refers to molar percentage of the sulfonated diamine) were investigated and compared with those of polyimides (Ic-x) from BTDA, ODADS, and m-phenylenediamine (c). All synthesized polyimides possessed high molecular weights revealed by their high viscosity, and formation of tough and flexible membranes. Polyintides with benzimidazole groups exhibited much better swelling capacity than those without benzimiclazole groups. This was attributed to the strong interchain interaction through basic benzimidazole functions and sulfonic acid groups. The sulfortated polyimides that are incorporated with 1, 1',8,8'-binaphthalimide exhibited better hydrolytic stability than that with 1,4,5,8-naphthalimide. Polyimide membranes with good water stability as well as high proton conductivity were developed. Polyimide membrane (Ia - 90), for example, did not lose mechanical properties after being soaked in boiling water for tOOO h, while its proton conductivity was still at a high level (compared to that of Nafion 117).

Mn(II)-monosubstituted polyoxometalates as candidates for contrast agents in magnetic resonance imaging

Two mono-substituted manganese polyoxometalates, K6MnSiW11O39 (MnSiW11) and K8MnP2W17O61 (MnP2W17), have been evaluated by in vivo and in vitro experiments as the candidates of potential tissue-specific contrast agents for magnetic resonance imaging (MRI). T-1-relaxivities of 12.1 mM(-1) s(-1) for MnSiW11 and 4.7 mM(-1) s(-1) for MnP2W17 (400 MHz, 25 degrees C) were higher than or similar to that of the commercial MRI contrast agent (GdDTPA). Their relaxivities in BSA and hTf solutions were also reported. After administration of MnSiW11 and MnP2W17 to Wistar rats, MR imaging showed longer and remarkable enhancement in rat liver and favorable renal excretion capability. The signal intensity increased by 74.0 +/- 4.9% for the liver during the whole imaging period (90 min) and by 67.2 +/- 5.3% for kidney within 20-70 min after injection at 40 +/- 3 mu mol kg(-1) dose for MnSiW11. MnP2W17 induced 71.5 +/- 15.1%. enhancement for the liver in 10-45 min range and 73.1 +/- 3.2% enhancement for kidney within 5-40 min after injection at 39 +/- 3 mu mol kg(-1) dose. In vitro and in vivo study showed MnSiW11 and MnP2W17 being favorable candidates as the tissue-specific contrast agents for MRI.

The gadolinium complexes with polyoxometalates as potential MRI contrast agents

The two gadolinium (Gd) polyoxometalates, K-15[Gd(BW11O39)(2)] [Gd(BW11)(2)] and K-17[Gd(CuW11O39)(2)] [Gd(CuW11)(2)] have been evaluated by in vivo and in vitro experiments as the candidates of potential tissue-specific magnetic resonance imaging (MRI) contrast agents. T-1 relaxivities of 17.12 mM(-1) . s(-1) for Gd(BW11)(2) and 19.95 mM(-1) . s(-1) for Gd(CuW11)(2) (400MHz, 25 degrees C) were much higher than that of the commercial MRI contrast agent (GdDTPA). Their relaxivities in bovine serum albumin and human serum transferrin solutions were also reported. After administration of Gd(BW11)(2) and Gd(CuW11)(2) to Wistar rats, MRI showed longer and remarkable enhancement in rat liver and favorable renal excretion capability. The signal intensity increased by 37.63 +/- 3.45% for the liver during the whole imaging period (100 min) and by 61.47 +/- 10.03% for kidney within 5-40 min after injection at 40 +/- 1-mu mol . kg(-1) dose for Gd(CuW11)(2), and Gd(BW11)(2) induced 50.44 +/- 3.51% enhancement in the liver in 5-50-min range and 61.47 +/- 10.03% enhancement for kidney within 5-40 min after injection at 39 +/- 4 mu mol . kg(-1) dose. In vitro and in vivo study showed that Gd(BW11)(2) and Gd(CuW11)(2) are favorable candidates as tissue-specific contrast agents for MRI.

Synthesis and characterization of novel sulfonated polyimides from 1,4-bis(4-aminophenoxy)-naphthyl-2,7-disulfonic acid

A novel sulfonated diamine monomer, 1,4-bis(4-aminophenoxy)-naphthyl-2,7-disulfonic acid (BAPNDS), was synthesized. A series of sulfonated polyimide copolymers were prepared from BAPNDS, 1,4,5,8-naphthalenetetracarboxylic dianhydride (NTDA) and nonsulfonated diamine 4,4'-diaminodiphenyl ether (ODA). Flexible, transparent, and mechanically strong membranes were obtained. The membranes displayed slightly anisotropic membrane swelling. The dimensional change in thickness direction was larger than that in planar. The novel SPI membranes showed higher conductivity, which was comparable or even higher than Nafion 117. Membranes exhibited methanol permeability from 0.24 x 10(-6) to 0.80 X 10(-6) cm(2)/s at room temperature, which was much lower than that of Nafion (2 x 10-6 CM2/s). The copolymers were thermally stable up to 340 degrees C. These preliminary results have proved its potential availability as proton-exchange membrane for PEMFCs or DMFCs.

Synthesis and properties of novel sulfonated polyimides containing binaphthyl groups as proton-exchange membranes for fuel cells

A novel sulfonated diamine monomer, 2,2'-bis(p-aminophenoxy)-1,1'-binaphthyl-6,6'-disulfonic acid (BNDADS), was synthesized. A series of sulfonated polyimide copolymers containing 30-80 mol % BNDADS as a hydrophilic component were prepared. The copolymers showed excellent solubility and good film-forming capability. Atomic force microscopy phase images clearly showed hydrophilic/hydrophobic microphase separation. The relationship between the proton conductivity and degree of sulfonation was examined. The sulfonated polyimide copolymer with 60 mol % BNDADS showed higher proton conductivity (0.0945-0.161 S/cm) at 20-80 degrees C in liquid water. The membranes exhibited methanol permeability from 9 x 10(-8) to 5 X 10(-7) cm(2)/s at 20 degrees C, which was much lower than that of Nafion (2 x 10(-6) cm(2)/s). The copolymers were thermally stable up to 300 degrees C. The sulfonated polyimide copolymers with 30-60 mol % BNDADS showed reasonable mechanical strength; for example, the maximum tensile strength at break of the sulfonated polyimide copolymer with 40 mol % BNDADS was 80.6 MPa under high moisture conditions. The optimum concentration of BNDADS was found to be 60 mol % from the viewpoint of proton conductivity, methanol permeability, and membrane stability.

Sulfonated poly(arylene-co-naphthalimide)s synthesized by copolymerization of primarily sulfonated monomer and fluorinated naphthalimide dichlorides as novel polymers for proton exchange membranes

A novel sulfonated aromatic dichloride monomer was successfully prepared by the reaction of 2, 5-dichlorobenzophenone with fuming sulfuric acid. Copolymerization of this monomer in the form of sodium salt (1) with N-(4-chloro-2-trifluoromethylphenyl)-5-chloro-1,8-naphthalimide (2) or bis(N-(4-chloro-2-trifluoromethylphenyl)1,4,5,8-naphthalimide (3) generated two series of novel poly(arylene-co-naphthalimide) s I-x and II-x where x represents the content of the sulfonated monomer. The synthesized copolymers with the -SO3H group in the side chains possessed high molecular weights revealed by their high viscosity and the formation of tough and flexible membranes. The copolymers exhibited excellent stability toward water and oxidation due to the introduction of the hydrophobic CF3 groups. The sulfonated copolyimides that incorporated with 1,8-naphthalimide (I-x) exhibited better hydrolytic and oxidative stabilities than those with 1,4,5,8-naphthalimide. Copolymer I-50 membrane endured for more than 83 h in Fenton's reagent at room temperature. The mechanical properties of I-50 membrane kept almost unchanged after immersing membrane in boiling water for 196 h. The proton conductivities of copolymer films increased with increasing IEC and temperature, reaching values above 6.8 x 10(-1) S/cm at 80 degrees C.

Comparison between GdDTPA and two gadolinium polyoxometalates as potential MRI contrast agents

Two gadolinium polyoxometalates, Gd2P2W18O62 and K-15[(GdO)(3)(PW9O34)(2)], have been evaluated by in vivo as well as in vitro experiments as the candidates of tissue-specific magnetic resonance imaging (MRI) contrast agents. T-1-relaxivities of 28.4 mM(-1)-s(-1) for Gd2P2W18O62 and 11.2 mM(-1)-s(-1) for K-15[(GdO)(3)(PW9O34)(2)] (400 MHz, 25 degreesC) were higher than that of the commercial MRI contrast agent (GdDTPA). Their relaxivities in bovine serum albumin and human serum transferrin were also reported. The favorable liver-specific contrast enhancement and renal excretion capability in in vivo MRI with Sprague-Dawley rats after i.v. administration of K-15[(GdO)(3)(PW9O34)(2)] was demonstrated. In vivo and in vitro assay showed that K-15[(GdO)(3)(PW9O34)(2)] is a promising liver-specific MRI contrast agent. However, Gd2P2W18O62 did not show the favorable quality in vivo as expected from its high relaxivity in vitro, which was attributed to low bioavailability, indicating that it is of limited value as tissue-specific MRI contrast agent.