Thermal properties and crystallization behavior of ultrafine fully-vulcanized powdered rubber particle toughened polypropylene

Thermal properties and crystallization-behavior of ultrafine fully-vulcanized powdered rubber (UFPR) toughened poly propylene (PP) were studied by Differential scanning calorimetry (DSC) and Wide angle X-ray diffraction (WAXD) measurements. It was found that the fraction of beta-form in the PP crystal increased at first, then sharply deceased up to zero with increasing UFPR content

Lanthanum zirconate ceramic toughened by BaTiO3 secondary phase

La2Zr2O7 (LZ) is a promising thermal barrier coating material for the high-temperature applications, which could be significantly toughened by the BaTiO3 piezoelectric phase incorporated into the matrix. The composites of xBaTiO(3)/(l-x)LZ (x=5, 10, 15, 20 vol%, LZ-x-BaTiO3) were densified by means of high-pressure sintering (HPS) under a pressure of 4.5 GPa at 1450 degrees C for 10 min, by which a high relative density above 93% could be obtained.

Brittle-ductile transition of particle toughened polymers: influence of the matrix properties

It was theoretically pointed out that the product of the yield stress and yield strain of matrix polymer that determined the brittle-ductile transition (BDT) of particle toughened polymers. For given particle and test condition, the higher the product of the yield stress and the yield strain of the matrix polymer, the smaller the critical interparticle distance (IDc) of the blends was. This was why the IDc (0.15 mum) of the polypropylene (PP)/rubber blends was smaller than that (0.30 mum) of the nylon 66/rubber blends, and the IDc of the nylon 66/rubber blends was smaller than that (0.60 mum) of the high density polyethylene (HDPE)/rubber blends.

Deformation mechanism of polystyrene toughened with sub-micrometer monodisperse rubber particles

Core-shell polybutadiene-graft-polystyrene (PB-g-PS) rubber particles with different ratios of polybutadiene to polystyrene were prepared by emulsion polymerization through grafting styrene onto polybutadiene latex. The weight ratio of polybutadiene to polystyrene ranged from 50/50 to 90/10. These core-shell rubber particles were then blended with polystyrene to prepare PS/PB-g-PS blends with a constant rubber content of 20 wt%. PB-g-PS particles with a lower PB/PS ratio (<= 570/30) form a homogeneous dispersion in the polystyrene matrix, and the Izod notched impact strength of these blends is higher than that of commercial high-impact polystyrene (HIPS). It is generally accepted that polystyrene can only be toughened effectively by 1-3 mu m rubber particles through a toughening mechanism of multiple crazings. However, the experimental results show that polystyrene can actually be toughened by monodisperse sub-micrometer rubber particles. Scanning electron micrographs of the fracture surface and stress-whitening zone of blends with a PB/PS ratio of 70/30 in PB-g-PS copolymer reveal a novel toughening mechanism of modified polystyrene, which may be shear yielding of the matrix, promoted by cavitation.

Mechanical and thermal properties of high-density polyethylene toughened with glass beads

Glass beads were used to improve the mechanical and thermal properties of high-density polyethylene (HDPE). HDPE/glass-bead blends were prepared in a Brabender-like apparatus, and this was followed by press molding. Static tensile measurements showed that the modulus of the HDPE/glass-bead blends increased considerably with increasing glass-bead content, whereas the yield stress remained roughly unchanged at first and then decreased slowly with increasing glass-bead content. Izod impact tests at room temperature revealed that the impact strength changed very slowly with increasing glass-bead content up to a critical value; thereafter, it increased sharply with increasing glass-bead content. That is, the lzod impact strength of the blends underwent a sharp transition with increasing glass-bead content. It was calculated that the critical interparticle distance for the HDPE/glass-bead blends at room temperature (25degreesC) was 2.5 mum. Scanning electron microscopy observations indicated that the high impact strength of the HDPE/glass-bead blends resulted from the deformation of the HDPE matrix. Dynamic mechanical analyses and thermogravimetric measurements implied that the heat resistance and heat stability of the blends tended to increase considerably with increasing glass-bead content.

Effect of cavitations on brittle-ductile transition of particle toughened thermoplastics

In this study, we established a correlation between cavitations volume and the brittle-ductile transition (BDT) for particle toughened thermoplastics. The brittle-ductile transition temperature (T-BD) was calculated as a function of T* and interparticle distance (ED), respectively, where T* was a parameter related to the volume of cavitations. The results showed that the smaller the cavitations volume, the higher the brittle-ductile transition temperature. The calculations correlated well with the experimental data. With respect to rubber particle, the rigid particle was too hard to be voided during deformation, thereby the TED of the blend was much higher than that of rubber particle toughened thermoplastic. This was a main reason that rubber particle could toughen thermoplastics effectively, whereas rigid particle could not.

Toughened blend of polycarbonate and epoxidized ethylene propylene diene rubber

A super-tough polycarbonate (PC) blend was obtained by using epoxidized ethylene propylene diene (eEPDM) rubber as modifier. The notched Izod impact strength of PC/eEPDM (96/4) blend shows a great improvement, with a value about 25 times of that of pure PC. Finely and homogeneously dispersed rubber particles (0.2-0.8 mu m) in the PC matrix indicated good adhesion between the eEPDM rubber phase and the PC matrix. (C) 1997 Elsevier Science Ltd.

Morphologies and mechanical properties of epoxy resins toughened by hydroxyl-terminated butadiene-acrylonitrile copolymer

The morphologies and mechanical properties of epoxy resins toughened by hydroxyl-terminated butadiene-acrylonitrile copolymer (HTBN) and cured with hexahydrophthalic anhydride were studied, The results show that the level of HTBN in epoxy resin, content of acrylonitrile in HTBN and curing temperature influence the morphology and then influence the mechanical properties of cured epoxy resin.

Toughened poly(butylene terephthalate) by epoxided ethylene-propylene-diene-rubber

Blends of poly (butylene terephthalate) (PBT) and epoxided ethylene-propylene-diene terpolymer (EEPDM) were prepared. Their mechanical properties and morphology were studied by Izod impact test machine and scanning electronic microscope respectively, It was found that the notched Izod impact strength of blend PBT/EEPDM was as about 23 times as that of pure PET and about 10 times as that of blend PBT/EPDM at room temperature, The dispersed rubber particles were much smaller and the phase boundary was more blurred in blend PBT/EEPDM than in blend PBT/EPDM. The toughness of blend PBT/EEPDM was much more better than that of blend PET and PBT/EPDM, which was in good agreement with the difference between their morphologies.

无机刚性粒子增韧聚乙烯、聚丙烯的结构与性能研究

众所周知，聚乙烯、聚丙烯因其良好的加工性能及价格相对低廉而得到了广泛应用，但刚性和韧性的不足限制了它们在工程领域的应用。因此，提高聚乙烯、聚丙烯的刚性和韧性就成为高分子科学界和工程界一重要研究课题。本论文尝试用玻璃珠增韧聚云烯、聚丙烯，并系统研究体系的结构和性能，得到的主要结果有：1．成功实现了玻璃珠对高密度聚乙烯的增韧。在刚性、热稳定性显著提高的同时，玻璃珠增韧的高密度聚乙烯仍保持着很高的低温缺口冲击强度（-10℃，玻璃珠含量48wt％时，冲击强度为16KJ/m2）。2．得到了玻璃珠增韧高密度聚乙烯在脆韧转变点临界粒子间距（IDc）与温度的关系。这是第一条无机刚性粒子增韧热塑性聚合物体系的工Dc与温度的关系曲线。结果表明与弹性体增韧热塑性聚合物体系类似，工Dc随温度的升高而非线性增大。3．虽然没能在低温和常温下实现玻璃珠对聚丙烯的增韧，但是在较高的温度下仍发现了玻璃珠对聚丙烯有明显的增韧效果，且体系的脆韧转变温度随玻璃珠含量的增加而降低。4．用偏光显微镜（PLM）成功跟踪了所用聚丙烯p晶转变为仪晶的全过程。结果表明β晶能重结晶成以晶，重结晶生成的以晶熔点要比最初生成的a晶高五度左右。5．当聚丙烯存在两种晶型（a和β）时，实验发现聚丙烯／玻璃珠共混体系出现模量随玻璃珠含量增加先下降后上升的反常现象。进一步研究结果揭示该反常现象是玻璃珠填充和提高β晶形成能力二者竞争的结果6. 实验发现聚丙烯的β晶含量与添加玻璃珠的尺寸、含量及热处理温度有关。同样玻璃珠含量下粒子尺寸小有利于β晶的生成；对一定组成的共混物，存在一个最佳β晶形成温度。

Toughening effects of poly(butylene terephthalate) with blocked isocyanate-functionalized poly(ethylene octene)

BACKGROUND: Blocked isocyanate-functionalized polyolefins have great potential for use in semicrystalline polymer blends to obtain toughened polymers. In this study, poly(butylene terephthalate) (PBT) was blended with allyl N-[2-methyl-4-(2-oxohexahydroazepine-1 -carboxamido)phenyl] carbamate-functionalized poly(ethylene octene) (POE-g-AMPC).RESULTS: New peaks at 2272 and 1720 cm(-1), corresponding to the stretching vibrations of NCO and the carbonyl of NH-CO-N, respectively, in AMPC, appeared in the infrared spectrum of POE-g-AMPC. Both rheological and X-ray photoelectron spectroscopy results indicated a new copolymer was formed in the reactive blends. Compared to uncompatibilized PBT/POE blends, smaller dispersed particle sizes with narrower distribution were found in the compatibilized PBT/POE-g-AMPC blends. There was a marked increase in impact strength by about 10-fold over that of PBT/POE blends with the same rubber content and almost 30-fold higher than that of pure PBT when the POE-g-AMPC content was 25 wt%.