K418与42CrMo异种金属激光焊接接头组织与力学性能

试验研究了额定功率为3kW的连续波Nd：YAG激光焊接热输入对激光焊接K418与42CrMo异种金属焊缝形貌的影响。通过光学显微镜、扫描电镜、能谱分析仪、硬度仪、万能试验机及X衍射对激光焊接K418与42CrMo异种金属焊缝接头组织、元素分布、相组成及接头的力学性能进行分析。结果表明，在焊接热输入恒定的条件下，高功率、高焊速的匙孔焊接比低功率、低焊速的热传导焊接更能增加焊缝熔深。通过扫描电镜在焊缝区域观察到了颗粒状物和针状物，能谱分析表明，颗粒状物Nb，Ti，Mo元素聚集，Fe，Ni元素减少；针状物Ti，Nb元素聚集。K418与42CrMo异种金属激光焊接工艺参数优化后的焊缝抗拉强度高于42CrMo母材。

低能质子注入金属靶实验中的核现象研究

在低能 ( 60～ 360keV)质子注入氘化钛 (Ti2 Hx)、钛 (Ti)、钼底衬钛箔及钼 (Mo)和不锈钢 (SS)等金属样品的实验中 ,观测到了能量分别约为 3 9、5 6和 8 4MeV的带电粒子产物。用符合望远镜和吸收片法进行粒子鉴别的结果表明 :这些带电粒子均具有α粒子特性。 3种α粒子来自质子与不同靶核发生的垒下核反应。其中 ,能量为 3 9MeV的α粒子具有很高的产额 ,其对应核反应的准激发函数曲线在 150～ 330keV能区内 ,随入射质子能量增大呈指数增长趋势。上述反应产物可能源于11N( p ,α) 12 C ,11B( p ,α) 8Be和7Li( p ,α) 4 He等核反应。但相关靶核的来源仍有待解释。利用扫描电子显微镜观测到有微球状的奇异形貌

萃取分离电感耦合等离子体原子发射光谱法测定钢中的微量稀土元素

本文采用苯甲酰苯胲(BPHA)-甲基异丁基酮(MIBK)溶剂萃取方法将钢中基体元素Fe,Ti,Mo,V等大量非稀土元素萃入有机相中,稀土元素留于水溶液中.由电感耦合等离子体原子发射光谱(ICP-AES)仪直接测定水溶液中的微量稀土元素La,Ce,Pr,Nd.Sm,Y和Gd,实验结果与推荐值基本相符,方法的回收率为96％～108％,相对标准偏差低于5％.

Effect of Carbon Addition on Microstructure and Mechanical Properties of Ti-Based Bulk Metallic Glass Forming Alloys

A kind of novel Ti-based composites was developed by introducing different amounts of carbon element to the Ti-50 Cu-23 Ni-20 Sn-7 bulk metallic glass forming alloys. The thermal stability and microstructural evolution of the composites were investigated. Room temperature compression tests reveal that the composite samples with 1% and 3% (mass fraction) carbon additions have higher fracture strength and obvious plastic strain of 2 195 MPa, 3.1% and 1 913 MPa, 1.3% respectively, compared with those of the corresponding carbon-free Ti-50 Ni-20 Cu-23 Sn-7 alloys. The deformation mechanisms of the composites with improved mechanical properties were also discussed.

Crystallographic and electrochemical characteristics of melt-spun Ti-Zr-Ni-La alloys

Ti-based icosahedral quasicrystalline phase (I-phase) exhibited excellent hydrogen storage property for special structure. Unfortunately, the application as the negative electrode material of the nickel-metal hydride batteries was limited due to the poor electrochemical kinetics. Meanwhile, rare-earth element was beneficial to the electrochemical properties of Ti, Zr-based alloy.

Crystallographic and electrochemical characteristics of Ti-Zr-Ni-Pd quasicrystalline alloys

Ti45Zr35Ni20-xPdx (x = 0, 1, 3, 5 and 7, at%) alloys were prepared by melt-spinning. The phase structure and electrochemical hydrogen storage performances of melt-spun alloys were investigated. The melt-spun alloys were icosahedral quasicrystalline phase, and the quasi-lattice constant increased with increasing x value. The maximum discharge capacity of alloy electrodes increased from 79 mAh/g (x = 0) to 148 mAh/g (x = 7). High-rate dis-chargeability and cycling stability were also enhanced with the increase of Pd content. The improvement in the electrochemical hydrogen storage characteristics may be ascribed to better electrochemical activity and oxidation resistance of Pd than that of Ni.

Crystallographic and electrochemical characteristics of melt-spun Ti-Zr-Ni-Cu alloys

Ti44Zr32Ni22Cu2 and Ti41Zr29Ni28Cu2 alloys were prepared by the melt-spinning method. The phase structure was analyzed by X-ray diffraction, and the electrochemical performances of the melt-spun alloys were investigated. The results indicated that the Ti44Zr32Ni22Cu2 alloy was composed of the icosahedral quasicrystals and amorphous phases, and the Ti41Zr29Ni28Cu2 alloy comprised icosahedral quasicrystals, amorphous, and Laves phases. The maximum discharge capacity was 141 mAh/g for the Ti44Zr32Ni22Cu2 alloy and 181 mAh/g for the Ti41Zr29Ni28Cu2 alloy, respectively. The Ti41Zr29Ni28Cu2 alloy also showed a better high-rate dischargeabifity and cycling stability. The better electrochemical properties should be ascribed to the high content of Ni, which was beneficial to the electrochemical kinetic properties and made the alloy more resistant to oxidation, as well as to the Laves phase in the Ti41Zr29Ni28Cu2 alloy, which could work as the electro-catalyst and the micro-current collector.

Preparation of W-Al-Mo ternary alloys by mechanical alloying

Single phase WxAl(50)Mo(50)-X (X=40, 30, 20 and 10) powders have been synthesized directly by mechanical alloying (MA). The structural evolutions during MA and subsequent as-milled powders by annealing at 1400 degrees C have been analyzed using X-ray diffraction (XRD). Different from the Mo50Al50 alloy, W40Al50Mo10 and W30Al50Mo20 alloys were stable at 1400 degrees C under vacuum. The results of high-pressure sintering indicated that the microhardnesses of two compositions, namely W40Al50Mo10 and W30Al50Mo20 alloys have higher values compared with W50Al50 alloy.

Effect of Nb Content on the Microstructure and Mechanical Properties of Zr-Cu-Ni-Al-Nb Glass Forming Alloys

(Zr65Al10Ni10Cu15)(100-x) Nb-x glass forming alloys with Nb contents ranging from 0 to 15 at.% were prepared by water-cooled copper mould cast. The alloys with different Nb contents exhibited different microstructures and mechanical properties. Unlike the monolithic Zr65Al10Ni10Cu15 bulk metallic glass, only a few primary bee beta-Ti phase dendrites were found to distribute in the glassy matrix of the alloys with x = 5. For alloys with x = 10, more beta-phase dendrites forms, together with quasicrystalline particles densely distributed in the matrix of the alloys. For alloys with x = 15, the microstructure of the alloy is dominated by a high density of fully developed P-phase dendrites and the volume fraction of quasicrystalline particles significantly decreases. Room temperature compression tests showed that the alloys with x = 5 failed at 1793 MPa and exhibited an obvious plastic strain of 3.05%, while the other samples all failed in a brittle manner. The ultimate fracture strengths are 1793, 1975 and 1572 MPa for the alloys with x = 0, 10 and 15 at.% Nb, respectively.

Structure and electrochemical characteristics of melted composite Ti0.10Zr0.15V0.35Cr0.10Ni0.30-LaNi5 hydrogen storage alloys

The structure and electrochemical characteristics of melted composite Ti0.10Zr0.15V0.35Cr0.10Ni0.30+x% LaNi5 (x=0, 1, 5 and 10) hydrogen storage alloys have been investigated systematically. XRD shows that the matrix phase structure of V-based solid solution phase with a BCC structure and C14 Laves phase with hexagonal structure is not changed after adding LaNi5 alloy. However, the amount of the secondary phase increases with increasing LaNi5 content. Field emission scanning electron microscopy-energy dispersive spectroscopy (FESEM-EDS) shows that the C14 Laves phase contains more Zr and the white lard phase has a composition close to (Zr, Ti)(V, Cr, Ni, La)(2).

Structures and electrochemical characteristics of Ti0.26Zr0.07V0.24Mn0.1Ni0.33Mox (x=0-0.1) hydrogen storage alloys

Microstructures and electrochemical properties of Ti0.26Zr0.07V0.21Mn0.1Ni0.33Mox (x=0,0.025,0.05,0.075, 0.10) electrode alloys have been investigated. The results of XRD analysis show that the alloys are mainly composed of V-based solid solution phase with body centered cubic (bcc) structure and C14 Laves phase with hexagonal structure. The addition of Mo element can imp ove the activation characteristics, maximum discharge capacity and cyclic durability for the electrode alloys

Electrochemical hydrogen storage in (Ti1-xVx)(2)Ni (x=0.05-0.3) alloys comprising icosahedral quasicrystalline phase

For (Ti1-xVx)(2)Ni (x = 0.05,0.1,0.15,0.2 and 0.3) ribbons, synthesized by arc-melting and subsequent melt-spinning techniques, an icosahedral quasicrystalline phase was present, either in the amorphous matrix or together with the stable Ti2Ni-type phase. With increasing x values, the maximum discharge capacity of the alloy electrodes increased until reached 271.3 mAh/g when x = 0.3. The cycling capacity retention rates for these electrodes were approximately 80% after a preliminary test of 30 consecutive cycles of charging and discharging.

Electrochemical Hydrogen Storage in Ti1.6V0.4Ni1-xCox Icosahedral Quasicrystalline Alloys

The discovery of the icosahedral phase (i-phase) in rapidly quenched Ti1.6V0.4Ni1-xCox (x=0.02-01) alloys is described herein. The i-phase occurs in a similar amount relative to the coexisting beta Ti phase. The electron diffraction patterns show the distinct spot anisotropy, indicating that the i-phase is metastable. The electrochemical hydrogen storage performance of these five alloy electrodes are also reported herein. The hydrogen desorption of nonelectrochemical recombination in the cyclic voltammetric (CV) response exhibits the demand for electrocatalytic activity improvement.