Preparation and properties of microporous membrane from poly(vinylidene fluoride-co-tetrafluoroethylene) (F2.4) for membrane distillation

Flat-sheet microporous membranes from F2.4 for membrane distillation (MD) were prepared by phase inversion process. Dimethylacetamide (DMAC) and LiClO(4)(.)3H(2)O/trimethyl phosphate (TMP) were, respectively, used as solvent and pore-forming additives. The effects of casting solution composition, exposure time prior to coagulation and temperature of precipitation bath on F2.4 membrane structure were investigated. The morphology of resultant porous membrane was observed by scanning electron microcopy. Some natures of F2.4 porous membrane after drying in air, such as mechanical properties and hydrophobicity, were exhibited and compared with poly(vinylidene fluoride) (PVDF) membrane prepared by the same ways. Stress-at-break and strength stress of F2.4 microporous membrane are higher than that of PVDF membrane, and elongation percentage of F2.4 membrane at break is about eight-fold as great as that of PVDF membrane. Contact angle of F2.4 microporous membrane to water (86.6 +/- 0.51degrees) was also larger than that of PVDF mernbrane (80.0 +/- 0.78degrees). MD experiment was carried out using a direct contact membrane distillation (DCMD) configuration as final test to permeate performance of resultant microporous membrane.

XPS STUDIES ON RADIATION-INDUCED STRUCTURAL-CHANGES IN THE COPOLYMER OF TETRAFLUOROETHYLENE AND ETHYLENE

In this work, the radiation-induced structural changes in the copolymer of tetrafluoroethylene and ethylene (F-40) were studied by X-ray photoelectron spectroscopy (XPS). During irradiation, some CF2 groups in the polymer were found to have been converted into carbon structures that bonded indirectly with fluorine atoms.

STUDIES ON RADIATION-INDUCED LOSS OF WEIGHT OF A COPOLYMER OF TETRAFLUOROETHYLENE AND HEXAFLUOROPROPYLENE

The radiation-induced loss of weight of F-46 was found to be proportional to irradiation dose and affected markedly by irradiation temperature.

XPS STUDY OF RADIATION CROSS-LINKED COPOLYMER OF TETRAFLUOROETHYLENE WITH HEXAFLUOROPROPYLENE

In this work the radiation-induced structural changes in F-46 were studied by XPS. In carbon-1s spectra of a highly crosslinked F-46 sheet, the slight increase observed in relative area under the peak due to CF3 was explained by the radiation-induced scission of polymer chains. The peak at 287.6 eV appearing in the spectra caused by ionizing radiation was attributed to carbon structures without primary fluorine substituents, in both branching and unsaturated structures, while that at 289.3 eV was assigned to = CF groups in mid-chain double bonds.

Super-hydrophobicity of silica nanoparticles modified with vinyl groups

Super-hydrophobic films with vinyl-modified silica nanoparticles (V-SiOx-NPs) were successfully prepared. The rough surface, which was composed of microstructures of disordered V-SiOx-NPs and nanostructures on the surface of V-SiOx-NPs, rather than the chemical composition devoted to the super-hydrophobicity of film. The relationship between contact angle and diameter of V-SiOx-NPs was then investigated. The sessile contact angles (CA) of films with 150-1600nm V-SiOx-NPs were around 166 regardless the diameter, while the film with 85 nm V-SiOx-NPs had the lowest CA of about 158. The packing manner of V-SiOx-NPs determined the air fraction on the surface and then the CA.

Weak epitaxy growth affording high-mobility thin films of disk-like organic semiconductors

Thin films of phthalocyanine compounds show weak epitaxial growth on a monodomain film of a rod-like molecule (see figure). The resulting organic electronic devices exhibit high charge carrier mobilities close to those of the single-crystal devices.

Low-density polyethylene superhydrophobic surface by control of its crystallization behavior

A simple and inexpensive method for forming a low-density polyethylene (LDPE) superhydrophobic surface by controlling the crystallization behavior of LDPE by adjusting the crystallization time and nucleation rate has been proposed. The resulting porous surface, with hierarchical micro- and nanostructures on the beautiful floral designs, has a water contact angle of 173.0degrees +/- 2.5degrees.

Preliminary research on microporous membrane from F2.4 for membrane distillation

An asymmetric hydrophobic microporous membrane from the copolymer of tetrafluoroethylene and vinyliden fluoride (F2.4) has been fabricated by phase inversion process. Some characteristics, such as mechanical properties and hydrophobicity, have been examined and compared with polyvinylidenefluoride (PVDF) membrane. Experimental data exhibit F2.4 membrane excellent mechanical properties and hydrophobicity. F2.4 microporous membrane was approximately 6-8 times as high as PVDF membrane in stretching strain and extension ratio at break, and contact angle to distilled water of the fore (88.5degrees) was larger than the latter (80.0degrees), too. The results from membrane distillation (MD) process were well agreed with the fundamental laws of membrane distillation.