Double-template synthesis of platinum nanomaterials for oxygen reduction

Gas bubble dynamic template, a new green and promising template, can be used to prepare nanostructured materials with different shapes from electrochemical deposition processes. Different morphological platinum nanomaterials have been synthesized by the replacement reaction of the deposited copper nanomaterials which were obtained under negative potential along with H-2 evolution (dynamic template) at a glassy carbon electrode. Scanning electron microscopy, X-ray photoelectron spectroscopy, X-ray diffraction, and electrochemical methods were adopted to characterize their structures and properties. The nanomaterials platinum exhibited excellent catalytic activity toward oxygen reduction. The results demonstrated that the strategy is a simple, cost-effective, and potent method to prepare platinum nanomaterials.

Ultrasonic synthesis of silica-alumina nanomaterials with controlled mesopore distribution without using surfactants

A novel sol-gel process has been developed for the synthesis of amorphous silica-aluminas with controlled mesopore distribution without the use of organic templating agents, e.g., surfactant molecules. Ultrasonic treatment during the synthesis enables production of precursor sols with narrow particle size distribution. Atomic force microscopy analysis shows that these sol particles are spherical in shape with a narrow size distribution (i.e., 13-25 nm) and their aggregation during the gelation creates clusters containing similar sized interparticle mesopores. A nitrogen physiadsorption study indicates that the mesoporous materials containing different Si/Al ratios prepared by the new synthesis method has a large specific surface area (i.e., 587-692 m(2)/g) and similar pore sizes of 2-11 nm. Solid-state Al-27 magic angle spinning (MAS) NMR shows that most of the aluminum is located in the tetrahedral position. A transmission electron microscopy (TEM) image shows that the mesoporous silica-alumina consists of 12-25 nm spheres. Additionally, high-resolution TEM and electron diffraction indicate that some nanoparticles are characteristic of a crystal, although X-ray diffraction and Si-29 MAS NMR analysis show an amorphous material.

Spray combustion synthesis of nanocrystalline Y2O3 and its thermodynamical and morphological study

Nano Y2O3 particles with a spherical shape and narrow size distribution have been prepared by a novel spray combustion method. The experimental procedure is briefly described and the thermodynamical process of the post-heat treatment is investigated in this paper. The precursor fully crystallized when treated at as low as 400 degrees C. Prepared particles showed spherical shape and well dispersibility under different treating conditions. Narrow size distribution of particles was achieved even when the precursor was treated at 1373 K. (C) 2007 Elsevier B.V. All rights reserved.

Synthesis of novel hexagon SnO2 nanosheets in ethanol/water solution by hydrothermal process

The novel hexagon SnO2 nanosheets are successfully synthesized in ethanol/water solution by hydrothermal process. The samples are characterized by X-ray diffraction (XRD), infrared ray (IR) and transmission electron microscopy (TEM). By changing the reaction conditions, the size and the morphology can be controlled. Comparison experiments show that when the temperature increased from 140 degrees C to 180 degrees C, the edge length of the hexagon nanoparticles increases from 300-450 nm to 700-900 nm. On the other hand, by adjusting the ratios of water to ethanol from 2 to 0.5, SnO2 nanoparticles with different morphologies of triangle and sphere are obtained. When the concentration of NaOH is increased from 0.15 M to 0.30 M, a hollow ring structure can be obtained. (c) 2006 Elsevier B.V. All rights reserved.

Controlled synthesis of monodisperse nanocrystals by a two-phase approach without the separation of nucleation and growth processes

The synthesis of monodisperse nanocrystals is an important topic in the field of nanomaterials not only for practical applications, but also for scientific interest in fundamental research. In this feature article, we mainly focus on synthesis of monodisperse nanocrystals by a two-phase approach without the separation of nucleation and growth processes, and report some progress made recently in the observation and understanding of nucleation and growth of semiconductor nanocrystals. Firstly, a novel two-phase approach to monodisperse nanocrystals, which is different from the well-established synthesis models, is discussed. We demonstrate that the two-phase approach has a quite lengthy nucleation process, and can be applied to the synthesis of many kinds of binary monodisperse nanocrystals.

One-Step Synthesis of Folic Acid Protected Gold Nanoparticles and Their Receptor-Mediated Intracellular Uptake

We report here a facile method to obtain folic acid (FA)-protected gold nanoparticles (Au NPs) by heating an aqueous solution of HAuCl4/FA in which FA acts as both the reducing and stabilizing agent. The successful formation of FA-protected Au NPs is demonstrated by UV/Vis spectroscopy, transmission electron microscopy (TEM), selected-area electron diffraction (SAED), X-ray photoelectron spectroscopy (XPS), and Fourier transform infrared spectroscopy (FTIR). ne intracellular uptake of these nanoparticles is facilitated by HeLa cells overexpressing the folate reporter, which itself is significantly inhibited by free FA in a competitive assay as quantified by inductively coupled plasma mass spectroscopy (ICP-MS). This simple one-step approach affords a new perspective for creating functional nanomaterials, and the resulting biocompatible, functional Au NPs may find some prospective applications in various biomedical fields.

Rapid synthesis of hexagon-shaped gold nanoplates by microwave assistant method

The microwave (MW)-based thermal process was applied to the preparation of hexagon-shaped gold nanoplates. The fort-nation of gold nanoplates occurs rapidly in a single step, carried out by directly heating a reaction mixture of HAuCl4 with sodium citrate in an MW reactor. And the gold nanoplates were characterized by UV-visible spectroscopy, X-ray diffraction (XRD) and transmission electron microscopy (TEM). The experimental results indicated that the sizes and morphologies of the gold nanomaterials strongly depend both on the heating methods and molar ratio of HAuCl4 to sodium citrate in the initial reaction mixture. At the molar ratio 5 : 4 (HAuCl4 to sodium citrate), hexagonal nanoplates with large Au (111) crystallographic facet were preferentially synthesized by the MW assistant method.

Templateless synthesis of catalysts with narrow mesoporous distribution

In this study, amorphous silica-alumina nanomaterials with narrow mesoporous distribution can be obtained by two novel sol-gel processes, without the use of any templates. The results of our experiments show that the preparation method has a great influence on the precursor sol structure as well as the specific surface area and mesopore volume of the final product, but has no effect on the pore size distribution.

Effects of Graphitization on the Synthesis of Ultrafine Diamond by Explosive Detonation

金刚石的石墨化对于炸药爆轰过程中金刚石的产出率有重要的影响。对碳相图进行了讨论,提出采用金刚石2石墨的动力学平衡线来评价炸药爆轰过程中金刚石的石墨化。通过数值模拟,对炸药爆轰过程中金刚石的石墨化进行了分析和讨论。

Morphological Evolution During Synthesis of New AlPO4 Center dot H2O Crystal

A new crystal of aluminophosphate, AIPO(4)(.)H(2)O, is synthesized from two-batch aqueous solution under hydrothermal conditions. Three types of the crystal habits, i.e. the tetragonal double pyramid, the tetragonal prism and the plate-type tetragonal prism, are found from batch-A solution. Two types of the crystal habits, i.e. the hexagonal pyramid and the strip-type tetragonal prism, are found from batch-B solution. The change of crystal morphology is originated from the fluctuation of the synthesis conditions, such as the supersaturation, the temperature and the impurity content. It causes change of the step energies, the defect density and the step roughness, and further, change of the growth rates. Since the crystal morphology is sensitive to the mass transport mechanism, the crystal habits could be changed under the microgravity.

In Situ Synthesis Of Nanocrystalline Intermetallic Layer During Surface Plastic Deformation Of Zirconium

By means of a surface plastic deformation method a nanocrystalline (NC) intermetallic compound was in situ synthesized on the surface layer of bulk zirconium (Zr). Hardened steel shots (composition: 1.0C, 1.5Cr, base Fe in wt.%) were used to conduct repetitive and multidirectional peening on the surface layer of Zr. The microstructure evolution of the surface layer was investigated by X-ray diffraction and scanning and transmission electron microscopy observations. The NC intermetallic layer of about 25 gm thick was observed and confirmed by concentration profiles of Zr, Fe and Cr, and was found to consist of the Fe100-xCrx compound with an average grain size of 22 nm. The NC surface layer exhibited an extremely high average hardness of 10.2 GPa. The Zr base immediately next to the compound/Zr interface has a grain size of similar to 250 nm, and a hardness of similar to 3.4 GPa. The Fe100-xCrx layer was found to securely adhere to the Zr base. (c) 2007 Elsevier B.V All rights reserved.

Synthesis of thick Ni66Cr5Mo4Zr6P15B4 amorphous alloy coating and large glass-forming ability by laser cladding

A thick amorphous alloy (a-alloy) coating was synthesized by laser cladding. The a-alloy had a multicomponent chemistry, i.e., Ni66Cr5MO4Zr6P15B4 (in atom%). The maximum thickness of the coating is 0.8 mm. The a-alloy coating had large glass-forming ability (GFA) with wide supercooled liquid region (SLR) ranging from 52 to 61 K through the coating. The reason for high GFA in the a-alloy coating was discussed. (C) 2002 Published by Elsevier Science B.V.

In Situ Synthesis of Nanocrystalline Intermetallic Compound Layer During Surface Mechanical Attrition Treatment of Zirconium

The surface mechanical attrition treatment (SMAT) technique was developed to synthesize a nanocrystalline (NC) layer on the surface of metallic materials for upgrading their overall properties and performance. In this paper, by means of SMAT to a pure zirconium plate at the room temperature, repetitive multidirectional peening of steel shots (composition (wt%): 1C, 1.5Cr, base Fe) severely deformed the surface layer. A NC surface layer consisting of the intermetallic compound FeCr was fabricated on the surface of the zirconium. The microstructure characterization of the surface layer was performed by using X-ray diffraction analysis, optical microscopy, scanning and transmission electron microscopy observations. The NC surface layer was about 25 mu m thick and consisted of the intermetallic compound FeCr with an average grain size of 25 +/- 10 nm. The deformation-induced fast diffusion of Fe and Cr from the steel shots into Zr occurred during SMAT, leading to the formation of intermetallic compound. In addition, the NC surface layer exhibited an ultrahigh nanohardness of 10.2 GPa.

Synthesis Of Plastic Zr-Based Bulk Metallic Glass Matrix Composites By The Copper-Mould Suction Casting And The Bridgman Solidification

Zr-based bulk metallic glass matrix composites with the composition of Zr56.2Ti13.8Nb5.0Cu6.9Ni5.6Be12.(5) were synthesized by the copper-mould suction casting and the Bridgman solidification. The composite, containing a well-developed flowery beta-Zr dendritic phase, was obtained by the Bridgman solidification with the withdrawal velocity of 0.8 mm/s and the temperature gradient of 45 K/mm, and the ultimate strength of 2050 MPa and fracture plastic strain of 14.6% of the composite were achieved, which was mainly interpreted by the homogeneous dispersion of bcc beta-Zr phase in the glass matrix. Crown Copyright (C) 2008 Published by Elsevier B.V. All rights reserved.

Time domain synthesis of electro-optical birefringent system for optical waveform generation

In this paper is described a novel technique for producing an electro-optical intensity synthesizer which can generate different periodic time domain waveforms through only sine or cosine wave applied-voltages. The synthesizer presented here consists of a series of stages between two polarizers, with each stage consisting of an electro-optic element and a compensator. Every electro-optical element has the same applied-voltage function but different azimuth angles and ratios between the longitudinal and transverse lengths. The main principle is the synthesis of an electro-optic effect and a polarization interference effect in the time domain. This technique is based on an expanded Fourier positive-direction searching algorithm, which can not only simplify the calculation process but also produces many choices of structural parameters for different waveforms generation. A three-stage synthesis of an electro-optical birefringent system for continuous square waveform is undertaken to prove the principle.