Phase identification in a series of liquid crystalline TPP polyethers and copolyethers having highly ordered mesophase structures. 7. Phase structures in a series of copolyethers containing odd and even numbers of methylene units of different compositions

A series of liquid crystalline copolyethers have been synthesized from 1-(4-hydroxy-4'-biphenyl)-2-(4-hydroxyphenyl)propane with 1,7-dibromoheptane and 1,12-dibromododecene [coTPPs(7/12)], which represents copolyethers containing both odd and even numbers of methylene units. The molar ratio of odd to even methylene units in this series ranges from 1/9 to 9/1. The coTPPs(7/12) exhibit multiple phase transitions during cooling and heating in differential scanning calorimetry experiments. For all these thermal transitions, a small undercooling and superheating dependence is observed upon cooling and heating at different rates. Three types of phase behaviors can be classified in coTPPs(7/12) on the basis of the structural analyses by wide-angle X-ray diffraction on powder and fiber samples and by electron diffraction experiments in transmission electron microscopy. At room temperature, highly ordered smectic and smectic crystal (SC) phases are identified in coTPPs(7/12: 1/9 and 2/8), which is similar to the homopolymer TPP(m = 12). The coTPPs(7/12: 3/7, 4/6, and 5/5) possess a hexagonal columnar (Phi(H)) phase in which the molecular and columnar axes are parallel to the fiber direction and perpendicular to the hexagonal lateral packing. The coTPPs(7/12: 6/4, 7/3, and 8/2) possess a tilted hexagonal columnar (Phi(TH)) phase with a single tilt angle which increases with the increasing composition of the seven-numbered methylene units. However, in coTPP(7/12: 9/1), a Phi(TH) phase with multiple tilt angles is found. Upon heating, phase structures in most coTPPs(7/12) involving the columnar phases enter directly into the nematic (N) phase, while the coTPP(7/12: 1/9) exhibits a highly ordered smectic F (S-F) phase before it reaches the N phase. One exception is found in coTPP(7/12: 2/8), wherein the transformation from the S-F to Phi(H) occurs prior to the N phase. Combining the copolymer phase behaviors observed with the corresponding homopolymers TPP(n = 7) and TPP(m = 12), a phase diagram describing transition temperatures with respect to the composition can be constructed.

MELTING BEHAVIOR OF DRAWN POLYPROPYLENE

The melting behavior of drawn, compression-molded isotactic polypropylene has been examined in terms of the influence of drawing conditions on the observed properties. Two endothermic peaks were observed on differential scanning calorimetry (DSC) for samples when high draw ratios and high heating rates were used during DSC tests. The peak at lower temperature is influenced by draw ratio, temperature, and rate, and exhibits a strong superheating effect. The species associated with this peak can partially recrystallize into another species associated with the peak at higher temperature during DSC measurements. The position of the peak at higher temperature depends only on draw ratio. It is proposed that the double-melting peaks at lower and higher temperature result from extremely thin quasi-amorphous or crystalline layers between microfibrils and the lamellar crystals within microfibrils, respectively. (C) 1993 John Wiley & Sons, Inc.