Monte-Carlo simulation of surface crack growth rate for offshore structural steel E36-Z35

The Monte- Carlo method is used to simulate the surface fatigue crack growth rate for offshore structural steel E36-Z35, and to determine the distributions and relevance of the parameters in the Paris equation. By this method, the time and cost of fatigue crack propagation testing can be reduced. The application of the method is demonstrated by use of four sets of fatigue crack propagation data for offshore structural steel E36-Z35. A comparison of the test data with the theoretical prediction for surface crack growth rate shows the application of the simulation method to the fatigue crack propagation tests is successful.

Ice induced low temperature fatigue crack propagation in offshore structural steel A131

To investigate the low temperature fatigue crack propagation behavior of offshore structural steel A131 under random ice loading, three ice failure modes that are commonly present in the Bohai Gulf are simulated according to the vibration stress responses induced by real ice loading. The test data are processed by a universal software FCPUSL developed on the basis of the theory of fatigue crack propagation and statistics. The fundamental parameter controlling the fatigue crack propagation induced by random ice loading is determined to be the amplitude root mean square stress intensity factor K-arm. The test results are presented on the crack propagation diagram where the crack growth rate da/dN is described as the function of K-arm. It is evident that the ice failure modes have great influence on the fatigue crack propagation behavior of the steel in ice-induced vibration. However, some of the experimental phenomena and test results are hard to be physically explained at present. The work in this paper is an initial attempt to investigate the cause of collapse of offshore structures due to ice loading.

Experimental investigation on low-temperature fatigue crack propagation in offshore structural steel A131 under random sea ice loading

An apparatus of low-temperature controlling for fatigue experiments and its crack measuring system were developed and used for offshore structural steel A131 under conditions of both low temperature and random sea ice. The experimental procedures and data processing were described, and a universal random data processing software for FCP under spectrum loading was written. Many specific features of random ice-induced FCP which differed with constant amplitude FCP behaviours were proposed and temperature effect on ice-induced FCP was pointed out with an easily neglected aspect in designing for platforms in sea ice emphasized. In the end, differences of FCP behaviours between sea ice and ocean wave were presented.

Experimental investigation of Very-High-Cycle Fatigue behavior for a structural steel

Very-High-Cycle Fatigue (VHCF) test for a medium carbon structural steel (40Cr) has been performed and a stepwise S-N curve was obtained by employing cantilever-type rotary bending fatigue machine with hourglass shape specimen. The S-N curve was well explained as a combination of curves for surface-induced fracture and interior inclusion-induced fracture with fish-eye patterns. The morphology of the fish-eye pattern was illustrated in order to clarify subsurface crack initiation and propagation behavior.

Investigation of high cycle and Very-High-Cycle Fatigue behaviors for a structural steel with smooth and notched specimens

The high cycle and Very-High-Cycle Fatigue (VHCF) properties of a structural steel with smooth and notched specimens were studied by employing a rotary bending machine with frequency of 52.5 Hz. For smooth specimens, VHCF failure did occur at fatigue cycles of 7.1 x 10(8) with the related S-N curve of stepwise tendency. Scanning Electron Microscopy (SEM) was used for the observations of the fracture surfaces It shows that for smooth specimens the crack origination is surface mode in the failure regime of less than 10(7) cycles While at VHCF regime, the material failed from the nonmetallic inclusion lies in the interior of material, leading to the formation of fisheye pattern. The dimensions of crack initiation region were measured and discussed with respect to the number of cycles to failure. The mechanism analysis by means of low temperature fracture technique shows that the nonmetallic inclusion in the interior of specimen tends to debond from surrounding matrix and form a crack. The crack propagates and results to the final failure. The stress intensity factor and fatigue strength were calculated to investigate the crack initiation properties. VHCF study on the notched specimens shows that the obtained S-N curve decreases continuously. SEM analysis reveals that multiple crack origins are dominant on specimen surface and that fatigue crack tends to initiate from the surface of the specimen. Based on the fatigue tests and observations, a model of crack initiation was used to describe the transition of fatigue initiation site from subsurface to surface for smooth and notched specimens. The model reveals the influences of load, grain size, inclusion size and surface notch on the crack initiation transition. (C) 2010 Elsevier Ltd. All rights reserved

Study on corrosion simulation device for marine structural steel

A corrosion simulation device was studied using offshore long scale hanging specimens. An Ni-Cu-P steel specimen was studied by analysing its corrosion products and corrosion types. The appearance of the samples and the surface of the metallic substrate after the removal of the rust layer produced by these two methods were observed and compared after 470 days of exposure. The phase structure of the corrosion products under different marine environments were analysed and compared. It further indicated good correlation between the electrically connected hanging specimen method and the long scale hanging specimen method.

A probabilistic model for fatigue crack propagation analysis

A simple probabilistic model for predicting crack growth behavior under random loading is presented. In the model, the parameters c and m in the Paris-Erdogan Equation are taken as random variables, and their stochastic characteristic values are obtained through fatigue crack propagation tests on an offshore structural steel under constant amplitude loading. Furthermore, by using the Monte Carlo simulation technique, the fatigue crack propagation life to reach a given crack length is predicted. The tests are conducted to verify the applicability of the theoretical prediction of the fatigue crack propagation.

环境介质对40Cr结构钢高周和超高周疲劳行为的影响

选用40Cr结构钢,分别在空气、水和3.5%NaCl水溶液中进行旋转弯曲疲劳实验,研究环境介质对该结构钢高周和超高周疲劳特性的影响.结果表明,40Cr钢在水环境中的疲劳强度比在空气中明显降低;在3.5%NaCl水溶液环境中的疲劳强度比在水中低.断面观察显示,在水和3.5%NaCl水溶液中,疲劳裂纹多源萌生;在稳态扩展阶段,裂纹沿晶界扩展并存在广泛分布的沿晶二次裂纹.

结构钢中绝热剪切带形成与扩展的光学观测与数值模拟

绝热剪切带(Adiabatic Shear Band,ASB)是许多金属材料在冲击载荷作用下发生破坏的主要原因之一,它是近年来冲击动力学和损伤力学研究的前沿和热点.相关的理论研究主要针对一维剪切条件,分析应力、应变、剪切速度、材料热物理和力学性能、初始缺陷大小之间的关系,得到一个由多个物理量组合而成的量来判别材料出现剪切带的难易.ASB的实验主要利用Hopkinson压杆、扭杆、压剪炮等加载技术,研究钛合金、钨合金、高强结构钢等材料的剪切带特征,包括局部温度和变形分布、剪切带出现的阈值等.但是,对剪切带演化过程的在位观察及其动态实时演化的研究还较少见,妨碍了人们对由于剪切局部化而导致的材料破坏机理的深入认识.针对45钢,在Hopkinson压杆上,开展了不同冲击加载条件下剪切带演化过程的在位观察及可视化研究.利用自行设计的高分辨力的光学观测系统和基于数字相关理论的图像处理软件,捕捉了单一试样在冲击加载条件下ASB逐渐形成和扩展的过程.同时,利用LS-DYNA商业程序对试样的冲击压缩过程进行了数值模拟,所得主要结果与实验观测基本一致.

Investigation on Laser Cladding MOSi2 Powder on Steel

The feasibility of the fabrication of coatings for elevated-temperature structural applications by laser cladding MoSi2 powder on steel was investigated. A dense and crack-free fine coating, well-bonded with the substrate has been obtained by this technique. This coating consists of FeMoSi, Fe2Si and a small amount of Mo5Si3 due to dilution of the substrate in the coating. The microstruelure of the coating is characterized of typical fine dendrites. The dendrites are composed of FeMoSi primary phase, and the interdendritic areas are two eutectic phases of FeMoSi and Fe2Si. The hardness of the coating reaches 845 Hv(0.5), 3.7 times larger than that of the steel substrate (180Hv(0.5)).

Characterization of a Laser-Discrete Quenched Steel Substrate/Chromium System by Dissolving Coatings

A laser-discrete quenched steel (LDQS) substrate/as-deposited chromium (top high-contraction (HC) and underlying low-contraction (LC) chromium) system was investigated by dissolving coatings in order to reveal the mechanism that the service life of the coated parts is largely improved using the hybrid technique of laser pre-quenching plus chromium post-depositing. It was found that the surface characteristics of the substrate, LC and HC chromium layer can be simultaneously revealed owing to the dissolution edge effect of chromium coatings. Moreover, the periodical gradient morphologies of the LDQS substrate are clearly shown: the surfaces of laser transformation-hardened regions are rather smooth; a lot of fine micro-holes exist in the transition zones; there are many micro-dimples in the original substrate. Furthermore, the novel method of dissolving coatings with sharp interfaces may be used to reveal the structural features of a substrate/coating system, explore the effect of the substrate on the initial microstructure and morphologies of coatings, and check the quality of the coated-parts.

Mechanical Properties And Constitutive Relationships Of 30Crmnsia Steel Heated At High Rate

In this paper, the mechanical behavior of 30CrMnSiA steel after heating at a high rate are investigated experimentally and theoretically, including a detailed discussion of the effects of strain rate and temperature. Two constitutive models are presented to describe the mechanical response of this material after heating at a high rate, and verified by experimental results. (C) 2007 Elsevier B.V. All rights reserved.

The plastic instability behaviour of laser-textured steel sheet

As the production of a new technique that can offer both good formability and high image clarity for texturing metal sheet, laser-textured sheet has attracted the attention of many manufacturers and users. Among the many subjects to be studied, plastic instability behaviour of the laser-textured sheet is one of most important to understand its ability in extending material ductility and to appropriately control this technique. Experimental investigations are carried out in this paper to study the macroscopic behaviour and microstructural mechanism of the laser-textured sheet, and comparison is made with the normal sheet taken from the same coil of metal sheet. It is demonstrated that, the difference in the behaviour of plastic instability obviously shows tendency to delay strain localization and the onset of thickness necking. Shear banding and internal void damage are spread to a much wider region in the sheet being laser-textured. The prestrained microcraters enforced on the surface of the textured sheet act as hardening spots, which are likely to share out deformation and inhibit the increasing rate of voiding, and eventually favouring the ductility of the material used.

Microstructure of shear localization in low-carbon ferrite pearlite steel

A study has been made of the microstructure of the thermally assisted band in a low carbon ferrite-pearlite steel, resulting from high speed torsional testing with an average strain rate of about 1500 s−1. Metallographic examination showed that there are several fine shear bands distributed over a deformed region (the gauge length of the specimen). The width of these bands is estimated to be of the order of magnitude of 50 μm, and the spacing between them is roughly about 100 μm. Detailed scanning electron microscopy studies indicate that damage of the microstructure within the band is very apparent, as evidenced by microcrack initiation and coalescence along the shear deformation band. However, there is no evidence that the material in the band had become microcrystalline or non-crystalline.

Mechanical properties and constitutive relationships of 30CrMnSiA steel heated at high rate

In this paper, the mechanical behavior of 30CrMnSiA steel after heating at a high rate are investigated experimentally and theoretically, including a detailed discussion of the effects of strain rate and temperature. Two constitutive models are presented to describe the mechanical response of this material after heating at a high rate, and verified by experimental results. (C) 2007 Elsevier B.V. All rights reserved.