Structural, electrical, and optical properties of InAsxSb1-x epitaxial films grown by liquid-phase epitaxy

The InAsxSb1-x films were grown on (100) GaSb substrates by liquid-phase epitaxy, and their structural, electrical, and optical properties were investigated. The high-resolution x-ray diffraction results reveal that the single crystalline InAsxSb1-x films with a midrange composition are epitaxially grown on the GaSb substrates. Temperature dependence of the Hall mobility was theoretically modeled by considering several predominant scattering mechanisms. The results indicate that ionized impurity and dislocation scatterings dominate at low temperatures, while polar optical phonon scattering is important at room temperature (RT). Furthermore, the InAsxSb1-x films with the higher As composition exhibit the better crystalline quality and the higher mobility. The InAs0.35Sb0.65 film exhibits a Hall mobility of 4.62x10(4) cm(2) V-1 s(-1). The cutoff wavelength of photoresponse is extended to about 12 mu m with a maximum responsivity of 0.21 V/W at RT, showing great potential for RT long-wavelength infrared detection. (C) 2008 American Institute of Physics. [DOI: 10.1063/1.2989116]

Influence of growth temperature on structural and magnetic characterization of (In, Cr)As quantum dots

(In, Cr)As ferromagnetic semiconductor quantum dots (QDs) were grown by molecular beam epitaxy on GaAs (001) substrates. The growth temperature effects on structure and magnetism of the QDs were investigated systematically. The Cr(2+)3d(4) states and quantum confined effect are assumed to play an important role in the room-temperature ferromagnetism of (In, Cr)As QDs. (C) 2009 Elsevier B.V. All rights reserved.

Effect of Annealing on Structural and Magnetic Properties of a Thick (Ga,Mn)As Layer

We investigate effects of annealing on magnetic properties of a thick (Ga,Mn)As layer, and find a dramatic increase of the Curie temperature from 65 to 115 K by postgrowth annealing for a 500-nm (Ga,Mn)As layer. Auger electron spectroscopy measurements suggest that the increase of the Curie temperature is mainly due to diffusion of Mn interstitial to the free surface. The double-crystal x-ray diffraction patterns show that the lattice constant of (Ga,Mn)As decreases with increasing annealing temperature. As a result, the annealing induced reduction of the lattice constant is mainly attributed to removal of Mn interstitial.