Improvement of low-field magnetoresistance and Curie temperature in the hole doping of double perovskites Sr2FeMoO6 polycrystals

Polycrystalline Sr2FeMoO6 compounds with most vacancies at normal Fe sites were fabricated through Mo hole doping; its effect is similar to Fe3+ by our estimation. Sharp increase of magnetoconductance at low field was evidence of spin-polarized tunneling between the grains. The room temperature low-field magnetoresistivity at optimal doping x=0.03 is 8.5% in 3000 Oe and increases to 11.4% in 1 T associated with soft magnetic behaviors; furthermore it exhibits a ferromagnetic Curie temperature of 450 K, connected with hole doping effect. The improved magnetoresistivity behavior was related to Curie temperature.

钙钛矿过渡金属氧化物电、磁性质的理论研究

钙钛矿过渡金属氧化物已有大量实验和理论研究。本论文采用一般梯度近似（GGA）和GGA+U（U表示原位的库仑相互作用）下的第一性原理密度函数方法研究了双层，四层和含氧空位的钙钛矿过渡金属氧化物的晶体结构、电子结构以及电、磁性质。 从对双层钙钛矿Sr2FeMoO6和Sr2CoMoO6的研究，我们发现Sr2FeMoO6的四方相比立方相稳定，而且两种结构下它都显半金属特性；对于Sr2CoMoO6，原位的库仑相互作用决定了它的半导体性质。此外，我们还研究了实验上备受争议的Ba2YIrO6和Ba2LaIrO6在立方 Fm-3m, 菱形 R-3和单斜 P21/n三种结构下的相对稳定性。结果表明第一性原理与半经验的键价模型得到的结论相同，即Ba2YIrO6和Ba2LaIrO6的最稳定结构分别是单斜 P21/n和菱形R-3。 不同Mn-O-Mn角度下YBaMn2O5的电子结构和磁结构的计算结果表明，当Mn-O-Mn 角度处于实验所测的157.8o时，G-型反铁磁结构比A-型稳定，与实验结果相符。随着角度的增加，大约在170出现了磁结构转变。当角度大于170时，A型反铁磁结构比G型稳定，即YBaMn2O5从G型过渡到A型。此外，我们还研究了YBaMn2O5在不同磁结构以及不同角度下的导电性。 通过对四层钙钛矿化合物CaCu3M4O12 （M是3d过渡金属离子：Ti, V, Cr, Mn, Fe, Co）的能带结构计算研究了M离子的电子构型对其磁结构和导电性的影响。结果表明随着M电子数的增加，该系列化合物磁结构为：在CaCu3Ti4O12（Ti4+：d0）中Cu-Cu为反铁磁性耦合，即该物质为反铁磁体；在CaCu3M4O12 (M= V4+：d1, Cr4+：d2, Mn4+：d3, Fe4+：d4；dn，0

Structural and magnetic properties of Sr2Fe1−xGaxMoO6 (0≤x≤0.25)

We have investigated the structure, magnetization and magnetoresistance (MR) of the double perovskite compounds Sr2Fe1−xGaxMoO6 (0≤x≤0.25). Rietveld refinement results show that the anti-site defects (ASDs) concentration increases with x, giving rise to highly disordered samples at the B/B positions, for the highest doping levels. The evolution of bond lengths and ions oxidation states could be understood by the distribution of trivalent Ga ions at the B/B positions, which leads to the formation of more disorder structure. The saturation magnetization and Curie temperature decreased with the Ga content increases in the samples, and their origin was found that the cations disorder for the Ga-doped compounds is annihilating double exchange mechanism due to the presence of significant amounts of Fe and Ga cations on the B site. The low-field magnetoresistance of Sr2FeMoO6 (SFMO) can be greatly enhanced by replacing the Fe by the nonmagnetic Ga ion up to a temperature of 300 K,since Ga ions may act as a barrier for electron transport along the chain in the ferromagnetic segregation and weaken the ferromagnetic exchange.

An investigation of low-field magnetoresistance in the double perovskites Sr2Fe1-xZnxMoO6, x=0, 0.05, 0.15 and 0.25

The electrical, magnetic and transport properties of Zn doped polycrystalline samples of Sr2Fe1-xZnxMoO6 ( x = 0, 0.05, 0.15 and 0.25) with the double perovskite structure have been investigated. The subtle replacement of Fe3+ ions by Zn2+ ions facilitates the formation of a more ordered structure, while further substitution leads to disordered structure because of the presence of a striped phase. Analysis of the x-ray powder diffraction patterns based on Rietveld analysis indicates that the replacement of Fe3+ by Zn2+ ions favours the formation of Mo6+ ions. The spin-glass behaviour can be explained on the basis of the competition between the antiferromagnetic superexchange and the ferromagnetic double-exchange interaction. The low-field magnetoresistance was moderately enhanced at x = 0.05, and its origin was found to be the competition between the decrease of the concentration of the itinerant electrons and the weaker antiferromagnetic superexchange in the antiphase boundaries. An almost linear negative magnetoresistance in moderate field has been observed for x = 0.25. A possible double-exchange mechanism is proposed for elucidating the observations; it also suggests a coexistence of (Fe3+, Mo5+) and (Zn2+, Mo6+) valence pairs.

Structure and properties of the ordered double perovskites Sr2MWO6 (M = Co, Ni) by sol-gel route

The single-phase double perovskites Sr2MWO6 (M=Co, Ni) were prepared by sol-gel method. Crystal Structure, magnetic properties and the morphology of Sr2CoWO6 and Sr2NiWO6 were investigated. X-ray powder diffraction (XRD) analysis shows single phase structure for Sr2MWO6 (M=Co, Ni) without any traces of impurities and the crystal structure of all the samples belongs to the tetragonal I4/m space group. SEM image for Sr2MWO6 (M=Co, Ni) indicate that the grains are homogeneous and connect each other very well. The Neel temperature for Sr2CoWO6 and Sr2NiWO6 are 23 K and 59 K, respectively. Magnetic measurements showed that the magnetic moment in these double perovskites originates mainly from the interactions between Ni ions and Co ions.

Competition between band filling and steric effect in ordered double perovskites Sr2-xLaxMnMoO6

The ordered double perovskites, Sr2-xLaxMnMoO6, were prepared by sol-gel reaction. Structural, magnetic, and electrical properties were investigated for a series of ordered double perovskites Sr2-xLaxMnMoO6(0 <= x <= 1). The compounds have a monoclinic structure (space group P2(1)/n) and the cell volume expands monotonically with La doping. The T-C and the magnetic moment rise and the cusp-like transition temperature below which the magnetic frustration occurs shifts to high temperature as x increases. With La doping, electrical resistivity of Sr2-xLaxMnMoO6 decreases only at low doping levels (x <= 0.2); while at high doping levels (0.8 <= x <= 1), electrical resistivity tends to increase greatly. The results suggest that the competition between band filling effect and steric effect coexists in the whole doping range, and the formation of ferrimagnetic interactions is not simply at the expense of antiferromagnetic interactions.