Synthesis and properties of novel soluble polyimides having a spirobisindane-linked dianhydride unit

A new synthetic procedure was elaborated allowing the preparation of semiaromatic dianhydride. N-Methyl protected 4-chlorophthalic anhydride was nitrated with HNO3 to produce N-methyl-4-chloro-5-nitrophthalimide (1). The aromatic nucleophilic substitution reaction between 5,5',6,6'-tetrahydroxy-3,3,3',3'-tetramethyl-1,1-spirobisindane and 1 afforded spirobisindane-linked bis(N-methylphthalimide) (2), which was hydrolyzed and subsequently dehydrated to give the corresponding dianhydride (3). The latter was polymerized with five different aromatic diamines to afford a series of aromatic polyimides. The properties of polyimides such as inherent viscosity, solubility, UV transparency and thermal stability were investigated to illustrate the contribution of the introduction of spirobisindane groups into the polyimide backbone. The resulting polyimides were readily soluble in polar solvents such as chloroform, THF and N-methyl-2-pyrrolidone. The glass-transition temperatures of these polyimides were in the range of 254-292 degrees C. The tensile strength, elongation at break, and Young's modulus of the polyimide film were 68.8-106.6 MPa, 5.9-9.8%, 1.7-2.0 GPa, respectively. The polymer films were colorless and transparent with the absorption cutoff wavelength at 286-308 nm.

Synthesis and properties of soluble polyimides based on isomeric ditrifluoromethyl substituted 1,4-bis(4-aminophenoxy)benzene

A new fluorinated diamine monomer, [1,4-bis(4-amino-3-trifluoromethylphenoxy)benzene (2)], and a known isomeric analog 1,4-bis(4-amino-2-trifluoromethylphenoxy)benzene (3) were synthesized. A series of organosoluble polyimides Ia-d and IIa were prepared from the diamines (2, 3) and dianhydrides (a-d) by a high-temperature one-step method. The effects of the trifluoromethyl substituents on the properties of polyimides were evaluated through the study of their soluble, thermal, optical, and gas permeability properties. Polyimides (Ia-d) had glass transition temperatures between 229 and 279 degrees C, and the temperatures at 5% weight loss ranged from 510 to 533 degrees C under nitrogen. These polyimides could be cast into flexible and tough membranes from DMAc solutions. The membranes had tensile strengths in the range of 137-169 MPa, tensile modulus in the range of 1.6-2.2 GPa and elongations at break from 11% to 14%. The polyimide la with trifluoromethyl groups ortho to the imide nitrogen exhibited enhanced gas permeability, solubility, transparency, and thermal stability compared with the isomeric polyimide IIa with the CF3 group meta to the imide nitrogen.

The electrochemical behavior of soluble polyimides

The effect of organic solvents on the electrochemical behavior of the soluble polyimide(PI) was studied by using cyclic voltammetry. It was found that PI can undergo electrochemical reaction in some solvents, while the electrochemical response can not be observed in other solvents. The results of IR spectra indicate that the effect of the solvents on the electrochemical behavior of PI is due to the different interactions between PI and the solvent.

Synthesis and characterization of soluble polyimides from 2,2-bis(4-aminophenyl)cycloalkane derivatives

New aromatic diamines [(1) and (2)] containing polycycloalkane structures between two benzene rings were synthesized by HCl-catalyzed condensation reaction of aniline hydrochloride and corresponding polycycloalkanone derivatives. The structures of diamines were identified by H-1-NMR, C-13-NMR, FTIR spectroscopy, and elemental analysis. The polyimides were synthesized from the obtained diamines with various aromatic dianhydrides by one-step polymerization in m-cresol. The inherent viscosities of the resulting polyimides were in the range of 0.34-1.02 dL/g. The polyimides showed good thermal stabilities and solubility. All the polymers were readily soluble in N-methyl-2-pyrrolidone, m-cresol, tetrachloroethane, etc. Some of them were soluble even in chloroform at room temperature. The glass transition temperatures were observed in the range of 323-363 degrees C, and all of the polymers were stable up to 400 degrees C under nitrogen atmosphere. (C) 1999 John Wiley & Sons, Inc.

The electrochemical behaviour of soluble polyimides

The electrochemical behaviour of five soluble polyimides was studied in organic solution using cyclic voltammetry. The relationship between the electrochemical behaviour and the molecular structure was discussed, It was found that the colours of polyimides can be changed due to the electrochemical redox reactions.

Synthesis and characterization of soluble polyimides from 1,1-bis(4-aminophenyl)cyclohexane derivatives

A series of novel aromatic diamines (1-3) containing kinked cyclohexylidene moieties was synthesized by a reaction of excess aniline and corresponding methyl-substituted cyclohexanone derivatives. The structures of (1-3) were identifield by H-1 NMR, C-13 NMR, and FT-IR. The polymers were synthesized from the obtained diamines and various aromatic dianhydrides by the conventional polycondensation reaction followed by chemical imidization as well as high-temperature one-step polymerization. The inherent viscosities and weight-average molecular weights of the resulting polyimides were in the ranges of 0.55-1.58 dL/g and (7.4-15.2) x 10(4) g/mol, respectively. The prepared polyimides showed excellent thermal stabilities and good solubility. All polymers were readily soluble in common organic solvents such as tetrahydrofuran, chloroform, tetrachloroethane, etc., and the glass transition temperatures were observed at 290-372 degrees C.

Direct deposition and characterization of Langmuir-Blodgett monolayers of soluble polyimides

Langmuir-Blodgett (LB) monolayers of three kinds of soluble polyimides were prepared with the direct deposition method, The monolayer structures were characterized with W-vis absorption spectroscopy, the wide angle X-ray scattering method and electrochemical techniques. The polyimide molecules in the LB monolayers lie orderly on the substrate surfaces with the orientation in which the dianhydride group is normal to the substrate surface and two carbonyl oxygen groups close to the surface. Therefore, the thickness of the three kinds of polyimide LB monolayers are the same because it depends on the distance between the two carbonyl oxygen groups in the same ring. The area of monomeric units are dependent on the length of the diamine group. The model of the molecular packing proposed from the quantomechanical calculation is in good agreement with the experimental results. (C) 1997 Elsevier Science S.A.

The electrochemical behaviours of soluble polyimides

The electrochemical behaviours of three kinds of soluble polyimides were investigated for the first time. It was observed that the cyclic voltammograms(CVS) of these polyimides in nonaqueous solutions are obviously different from that of the poly-imide films casted on surfaces of glass carbon electrode(GCEs) in aqueous solutions.

Synthesis and properties of novel regioirregular polyimides from easily synthesized asymmetrical dichlorophthalimide monomers

New asymmetrical aromatic dichlorophthalimide monomers containing pendant groups (trifluoromethyl or methyl) were conveniently prepared from inexpensive and commercially available compounds. With these monomers, a new class of soluble polyimides with a regioirregular structure within the polymer backbone was obtained by the Ni(0)-catalyzed polymerization method. The structures of the polymers were confirmed by various spectroscopic techniques. The polyimides displayed better solubility and higher thermal stability than the corresponding regular polyimides. In addition, fluorinated polyimides in this study had low dielectric constants ranging from 2.52 to 2.78, low moisture absorptions of less than 0.59%, and low thermal expansion coefficients between 10.6 and 19.7 ppm/degrees C. The oxygen permeability coefficients and permeability selectivity of oxygen to nitrogen of the films were in the ranges of 2.99-4.20 barrer and 5.55-7.50, respectively. We have demonstrated that the synthetic pathway for polyimides provides a successful approach to increasing the solubility and processability of polyimides without sacrificing their thermal stability.

Synthesis and properties of novel organosoluble polyimides derived from 1,4-bis[4-(3,4-dicarboxylphenoxy)]triptycene dianhydride and various aromatic diamines

A novel triptycene-based dianhydride, 1,4-bis[4-(3,4-dicarboxylphenoxy)]triptycene dianhydride, was prepared from 4-nitro-N-methylphthalimide and potassium phenolate of 1,4-dihydroxytriptycene (1). The aromatic nucleophilic substitution reaction between 4-nitro-N-methylphthalimide and I afforded triptycene-based bis(N-methylphthalimide) (2), which hydrolyzed and subsequently dehydrated to give the corresponding dianhydride (3). A series of new polyimides containing triptycene moieties were prepared from the dianhydride monomer (3) and various diamines in in-cresol via conventional one-step polycondensation method. Most of the resulting polyimides were soluble in common organic solvents, such as chloroform, THF, DMAc and DMSO. The polyimides exhibited excellent thermal and thermo-oxidative stabilities with the onset decomposition temperature and 10% weight loss temperature ranging from 448 to 486 degrees C and 526 to 565 degrees C in nitrogen atmosphere, respectively. The glass transition temperatures of the polyimides were in the range of 221-296 degrees C. The polyimide films were found to be transparent, flexible, and tough. The films had tensile strengths, elongations at break, and tensile moduli in the ranges 95-118 MPa, 5.3-16.2%, and 1.03-1.38 GPa, respectively. Wide-angle X-ray diffraction measurements revealed that these polyimides were amorphous.

Synthesis and properties of polyimides derived from cis- and trans-1,2,3,4-cyclohexanetetracarboxylic dianhydrides

Cis-1,2,3,4-cyclohexanetetracarboxylic dianhydride (cis-1,2,3,4-CHDA) was synthesized. It was found that under such conditions as heating or boiling in acetic anhydride, cis-1,2,3,4-CHDA could be converted to its trans-isomer. The process of thermal isomerization was monitored by H-1 NMR spectra and the mechanism of conversion was proposed. Their absolute structures of cis- and trans-1,2,3,4-CHDAs were elucidated by single crystal X-ray diffraction. The polycondensations of cis- and trans-1,2,3,4-CHDAs with aromatic diamines such as 4,4'-oxydianiline (ODA), 4,4'-methylenedianiline (MDA), 4,4'-diamino-3,3'-dimethyldiphenylmethane (DMMDA), 4,4'-bis(4-aminophenoxy)benzene (TPEQ), 2,2-bis[4-(4-aminophenoxy)phenyl] propane (BAPP) were studied. It is easy to obtain higher molecular weight polyimides from trans-1,2,3,4-CHDA using conventional one-step or two-step methods. However, higher molecular weight polyimides derived from cis-1,2,3,4-CHDA could not be prepared by the usual methods (solid content ca. 10%) owing to the trend of forming cyclic oligomers.

Polyimides derived from 3,3 '-bis(N-aminophthalimide)

A novel diamine, 3,3'-bis(N-aminophthalimide) (BAPI), was prepared from 3,3'-bis(N-phenylphthalimide). Its structure was determined via IR, H-1 NMR, N-15 NMR, elemental analysis, and single-crystal X-ray diffraction analysis. A series of homo- and copolyimides were synthesized by a conventional one-step method in p-chlorophenol. The characteristic IR absorption bands of hydrazine-based imide groups were near 1780, 1750, 1350, 1100, and 730 cm(-1). The polymers showed good solubility in polar aprotic solvents and phenols at room temperature. The temperatures of 5% weight loss (T-5%) of the polyimides ranged from 495 to 530 degrees C in air. DMTA analyses indicated that the glass-transition temperatures (Tgs) of the polyimides were in the range 371-432 degrees C. These polymers had cutoff wavelengths between 350 and 400 nm. The polyimide films of 6FDA/BAPI and 4,4'-HQPDA/BAPI were colorless; other films were pale yellow or yellow.

Polyimides from isomeric diphenylthioether dianhydrides

3,3',4,4'-Diphenylthioether dianhydride (4,4'-TDPA), 2,3,3',4'-diphenylthioether dianhydride (3,4'-TDPA), and 2,2',3,3-diphenylthioether dianhydride (3,3'TDPA) were synthesized from 3-chlorophthalic anhydride and 4-chlorophthalic anhydride. A series of polyimides derived from the isomeric diphenylthioether dianhydrides with several diamines were prepared. The properties, such as the solubility, thermal and mechanical behavior, dynamic mechanical behavior, wide-angle X-ray diffraction, and permeability to some gases, were compared among the isomeric polyimides. Both 3,3'-TDPA- and 3,4-TDPA-based polyimides had good solubility in polar aprotic solvents and phenols. The 5% weight loss temperatures of all the obtained polyimides was near 500 degrees C in nitrogen. The glass-transition temperatures decreased according to the order of the polyimides based on 3,3'-TDPA, 3,4'-TDPA, and 4,4'-TDPA. The 3,4'-TDPA-based polyimides had the best permeability and lowest permselectivity, whereas the 4,4'-TDPA-based polyimides had the highest permselectivity and the lowest permeability of the three isomers. Furthermore, the rheological properties of thermoplastic polyimide resins based on the isomeric dipbenylthioether dianhydrides were investigated, and they showed that polyimide 3,4'-TDPA/4,4-oxydianiline had the lowest melt viscosity among the isomers; this indicated that the melt processibility had been greatly improved.

Novel polyimides derived from 2,3,3 ',4 '-benzophenonetetracarboxylic dianhydride

A series of polyimides (PIs) based on 2,3,3',4'-benzophenonetetracarboxylic dianhydride (2,3,3',4'-BTDA) and 3,3',4,4'-BTDA were prepared by the conventional two-step process. The properties of the 2,3,3',4'-BTDA based polyimides were compared with those of polyimides prepared from 3,3',4,4'-BTDA. It was found that PIs from 2,3,3,4'-BTDA have higher glass transition temperature and better solubility without sacrificing their thermal properties. Furthermore the theological properties of PMR-15 type polyimide resins based on 2,3,3',4'-BTDA showed lower melt viscosity and wider melt flow region (flow window) compared with those from 3,3',4,4'-BTDA. The structure-property relations resulted from isomerism were discussed.

Polyimides from isomeric oxydiphthalic anhydrides

2,2',3,3'-Oxydiphthalic dianhydride (2,2',3,3'-ODPA) and 2,3,3',4'-ODPA were synthesized from 3-chlorophthalic anhydride with 2,3-xylenol and 3,4-xylenol, respectively. Their structures were determined via single-crystal X-ray diffraction. A series of polyimides derived from isomeric ODPAs with several diamines were prepared in dimethylacetamide (DMAc) with the conventional two-step method. Matrix-assisted laser desorption/ionization time-of-flight spectra showed that the polymerization of 2,2',3,3'-ODPA with 4,4'-oxydianiline (ODA) has a greater trend to form cyclic oligomers than that of 2,3,3',4'-ODPA. Both 2,2',3,3'-ODPA and 2,3,3',4'-ODPA based polyimides have good solubility in polar aprotic solvents such as DMAc, dimethylformamide, and N-methylpyrrolidone. The 5% weight-loss temperatures of all polyimides were obtained near 500 degreesC in air. Their glass-transition temperatures measured by dynamic mechanical thermal analysis or differential scanning calorimetry decreased according to the order of polyimides on the basis of 2,2',3,3'-ODPA, 2,3,3',4'-ODPA, and 3,3',4,4'-ODPA. The wide-angle X-ray diffraction of all polyimide films from isomeric ODPAs and ODA showed some certain extent of crystallization after stretching. Rheological properties revealed that polyimide (2,3,3',4'-ODPA/ODA) has a comparatively lower melt viscosity than its isomers, which indicated its better melt processability.