植物根与茎输水结构的研究和功能分析

本文采用树脂复型法对裸子植物红豆杉的管胞，木本单子叶植物竹和棕榈藤木质部中各种管状分子（主要是导管和管胞）的内壁结构进行了研究;采用原子力显微镜对玉米和小麦根内皮层细胞内切向壁的表面结构进行了探索性的研究;用光学显微镜并结合荧光技术对典型的旱生、中生及水生植物根内皮层的次生加厚壁进行了比较观察;同时辅以传统的组织切片法对以上研究结果做了进一步的论证。 采用树脂复型法，不仅可观察到常规解剖法所能展示的结构，而且还可清晰地观察到管状分子间具缘纹孔对等常规方法所难以显示的三维构造，并对其各项结构参数进行了定量测量。结果表明：裸子植物管胞和竹、藤管状分子具缘纹孔的内、外口比例分别约为3:1 和1:1，其它各项结构参数均存在较大差别。此外，在云南省藤和桂竹等导管内壁上还观察到瘤层结构，瘤体直径大小为200-800纳米之间。 旱生植物内皮层细胞内切向壁的闪生加厚最为明显，水生植物的加厚程度最微弱，而中生植物则介于两类植物之间。玉米内皮层细胞内切向壁的内表面起伏不平，并具有70-90纳米的“孔状”质外体结构，其频率约为2，000个/平方微米。

Improvement and observation of immunoelectron microscopic method for the localization of frog Rana grylio virus (RGV) in infected fish cells

In this paper, to understand the roles of amorphous structures which were observed within the viromatrix of Rana grylio virus (RGV), an improved immunoelectron microscopy (IEM) method was developed to detect the localization of RGV in carp Epithelipma papulosum cyprinid (EPC) cells. Infected EPC cells were fixed with 4% paraformaldehyde-0.25% glutaraldehyde mixture, dehydrated completely, and embedded in LR White resin. This method allowed good ultrastructural preservation and specific labeling with anti-RGV antibodies. The results of IEM showed that colloidal gold mainly bound to the capsids of viral particles at the stage of viral assembly, while during the viral maturation colloidal gold bound to the envelop of virions. In addition, within the viromatrix, the amorphous structures, including dense floccules, membranous materials and tubules, also had strong colloidal gold signals, revealing that those amorphous structures were participated in RGV assembly. In contrast, no significant gold labeling signals were obtained in negative controls. The present study not only provided further evidence that amorphous structures within the viromatrix were involved in the process of RGV assembly, but also developed an improved IEM method for studying the interaction between iridovirus and host cells. (C) 2006 Elsevier Ltd. All rights reserved.

Critical serrated flow features during nanoindentation in La-based bulk metallic glasses

La57.6Al17.5(Cu,Ni)(24.9) and La64Al14(Cu,Ni)(22) bulk metallic glasses (BMGs) were prepared by copper-mould casting method. Plastic deformation behavior of the two BMGs at various loading rates was studied by nanoindentation. The results showed that the La57.6Al17.5(Cu,Ni)(24.9) BMG with a glass transition temperature of 423 K exhibited prominent serrated flow at low loading rates, whereas less pronounced serrated flow at high rates during nanoindentation. In contrast, the La64Al14(Cu,Ni)(22) BMG with a glass transition temperature of 401 K exhibited prominent serrated flow at high loading rates. The different rate dependency of serrated flow in the two La-based BMGs is related to the different glass transition temperature, and consequently the degree of viscous flow during indentation at room temperature. A smoother flow occurs in the alloy with relatively lower glass transition temperature, due to the relaxation of stress concentration.

溶液热历史对蛋白质晶体生长影响的内在原因研究

从溶液中聚集体的角度研究了溶液的热历史改变生长出的蛋白质晶体的数目和尺寸的内在原因.将在281和309 K下保存1 d的两组溶菌酶溶液按不同比例混合,加入沉淀剂生长晶体.随着高温溶液的比例增加,生长出的晶体数目减少,同时溶液中生长基元的尺寸增大.在5周内,采用动态光散射对281,293和309K三种温度下保存的溶菌酶溶液中聚集体的变化情况进行监测,发现溶液中均存在大小不同的两部分聚集体,称之为小聚集体与多聚体.前者的尺寸基本不随保存时间而变化,而后者尺寸随保存时间增加而减小,减小的速度与保存温度有关.多聚体的尺寸经过5周后和小聚集体基本相同.研究结果表明,处于无序聚集阶段的溶液的均一化程度和成核阶段生长基元的尺寸受到了溶液热历史的影响,并最终对晶体的数目产生影响.

Thermal Residual Stresses in SiCw/Al Composite

<正> The SiCw/6061Al composites were fabricated by squeeze casting method. Varia-tions of thermal residual stresses with quenching temperature, cooling manner, aging time and thethermal-cold cycle process in thin specimens,and the distributions of thermal residual stresses alongthe distances from the surface and changes with heating temperatnres in thick specimens were stud-ied by means of X-ray diffraction (XRD). The effects of residual stresses on the mierostructure, di-mensional stability and age-hardening behavior were studied by SEM, TEM observations, and tensiletest. The results showed that there existed macrostress, microstress and thermal mismatch stress inSiCw/Al compo-site,and the presence of microstress and thermal mismatch stress has no influenceon the measurement of macrostress, but the macrostress can affect the measured value of thermalmismatch stress. Thermal res dual stress induced during the composite fabrication process, will be further in-creased when the composite were subjected to the e

Investigation on the microstructure and mechanical properties of a cast Mg–6Zn–5Al–4RE alloy

Mg-6Zn-5Al-4RE (RE = Mischmetal, mass%) alloy was prepared by metal mould casting method. The microstructure and mechanical properties of the as-cast and heat-treated alloys were investigated

Effects of cerium on the microstructure and mechanical properties of Mg–20Zn–8Al alloy

Mg-20Zn-8Al-xCe(x=0-2 wt.%) alloys were prepared by metal mould casting method, the effects of Ce on the microstructure and mechanical properties of the alloys were investigated. The results showed that the dendrite as well as gram size were refined by the addition of Ce, and the best refinement was obtained in 1.39% Ce containing alloy.

The microstructure and mechanical properties of Mg-3Al-3RE alloys

The Mg-3Al-3RE alloys (RE, the cerium-rich or the yttrium-rich misch metal) were smelted in a resistance furnace under the protective flux from the Mg-RE master alloys and pure magnesium ingots. The microstructure and mechanical properties of samples prepared by steel mould casting method were investigated.

Glass formation ability and mechanical properties of Ti40Cu40Zr10Ni10 alloy

Melt-spun ribbon and bulk samples in cylindrical rod form with diameter ranging from 2 mm to 4 mm of Ti40Cu40Zr10Ni10 alloy were prepared by melt-spinning technique and copper mould casting method, respectively. The microstructure, thermal stability and mechanical properties of the bulk samples were investigated. A completely glassy single phase is formed in the 2 mm rod sample. Increasing the diameter of the rod samples resulted in the formation of CuTi crystalline phase in the 3 mm and 4 mm rod samples.

Microstructures and mechanical properties of as-cast Mg–5Al–0.4Mn–xNd (x=0, 1, 2 and 4) alloys

Mg-5Al-0.4Mn-xNd (x=0, 1, 2 and 4wt.%) alloys were prepared by metal mould casting method. The microstructures and mechanical properties were investigated. The results demonstrated that Al11Nd3 phase was formed and mainly aggregated along the grain boundaries with the addition of Nd. Meanwhile, the grain sizes were greatly reduced with the increasing Nd content.

Near-infrared polymer light-emitting diodes based on infrared dye doped poly(N-vinylcarbazole) film

Infrared light-emitting diodes possess potential applications in optical communication and safety detection. in this paper, we fabricated near-infrared light-emitting diodes possess potential applications in optical communication and safety detection. in this paper, we fabricated near-infrared polymer light-emitting diode employing a commercial near-infrared (NIR) organic dye as an emissive dopant dispersed within poly(N-vinylcarbazole) (PVK) by spin-casting method. The used device structure was indium tin oxide/3,4-polyethylene-dioxythiophene-polystyrene sulfonate/PVK: NIR dye/Al.

Microstructure and mechanical properties of Mg-4Al-4Nd-0.5Zn-0.3Mn alloy

Mg-4Al-4Nd-0.5Zn-0.3Mn alloy was prepared by metal mould casting method. Microstructure, aging behavior, mechanical properties and fracture morphology of the alloy were investigated. The results showed that alpha-Mg, Al-11 Nd-3, Al2Nd and Mg-32(Al,Zn)(49) phases were the main phases of the as-cast alloy. And the long rod-like Al-11 Nd-3 phase was decomposed to granular Al2Nd through T6 heat treatment. The tensile strength was also enhanced by T6 treatment. The yield strength was increased by 17% and 21% at RT and 150 degrees C, respectively. It was mainly because that the precipitates were refined through T6 treatment and this became more benefit to hinder dislocations slipping.

Preparation and characterization of As-cast and hot-rolled Mg-3Al-0.5Mn-0.5Zn-1MM alloy

Mg-3Al-0.5Mn-0.5Zn-1MM alloy was prepared by metal mould casting method. The as-cast ingot was homogenized and then hot-rolled at 673 K with total thickness reduction of 65%. Microstructure and mechanical properties of the as-cast and hot-rolled samples were investigated. The results showed that the as-cast sample mainly consisted of alpha-Mg, beta-Mg17Al12, Al10Ce2Mn7, and Al11RE3 (RE = La and Ce) phases. The average grain size of the sample homogenized at 673 K was about 240 gm, and it was greatly refined to about 7 mu m by dynamic recrystallization for the hot-rolled sample.

MICROSTRUCTURE AND MECHANICAL PROPERTIES OF TI-BASED METALLIC GLASS MATRIX COMPOSITES

Ti40Cu40Ni10Zr10-xScx (x = 0.5 and 1, at%) alloys were prepared by copper mould casting method. Microstructures of the phi 3 mm rod alloys were investigated by XRD and SEM. The results showed that the phi 3 mm rods were glassy matrix with TiCu crystalline phase. Mechanical properties were studied by compressive test. Ti40Cu40Ni10Zr9Sc1 alloy exhibited good compressive strength over 2200 MPa and superior compressive deformation is about 7.9%.

High proton conductive advanced hybrid membrane based on sulfonated Si-SBA-15

Composite membranes based on Sulfonated poly(ether ether ketone) (SPEEK) and sulfonated organically modified Si-SBA-15 (S-SBA-15) were investigated with the purpose of increasing the proton conductivity. The novelty of the composite membranes was attributed to two special structures and different ion exchange capacities (IEC) of S-SBA-15 fillers, which were embedded in membranes. The typical hexagonal channels array of S-SBA-15 was confirmed by XRD and TEM. The regular vermiculate and amorphous structures of the inorganic fillers were proved by SEM. Composite membranes were prepared through common solvent casting method. SEM images indicated that the inorganic filler with regular structure dispersed homogeneously in the composite membranes, but the amorphous filler caused an agglomeration phenomenon at the same loading content.