Hydrothermal synthesis of the two-dimensional coordination polymer {[Fe(phen)(OH)](bta)(0.5)}(n) (phen=1,10-phenanthroline, bta=benzene-1,2,4,5-tetracaboxylate)

The title two-dimensional coordination polymer was synthesised and characterised by X-ray diffraction analysis.

Corrosion inhibition of carbon steel in tetra-n-butylammonium bromide aqueous solution by benzotriazole and Na3PO4

The corrosion inhibition behavior of benzotriazole, Na3PO4 and their mixture on carbon steel in 20 wt.% (0.628 mol l(-1)) tetra-n-butylammonium bromide aerated aqueous solution was investigated by weight-loss test, potentiodynamic polarization measurement, electrochemical impedance spectroscopy and scanning electron microscope/energy dispersive X-ray techniques. The inhibition action of BTA or SP or inhibitors mixture on the corrosion of carbon steel is mainly due to the inhibition of anodic process of corrosion. The results revealed that inhibitors mixtures have shown synergistic effects at lower concentration of inhibitors. At 2 g l(-1) BTA and 2 g l(-1) SP showed optimum enhanced inhibition compared with their individual effects.

稀土苯多酸络合物的合成及其性质的研究

苯多酸作为配体，因有多个可参与配位的羧基，因此，可以和稀土离子生成不同配比而结构特殊的化合物，同时这类化合物具有一系列有趣的性质。本论文选择1,2,4,5-苯四酸（H_4L），1,3,5-苯三酸（H_3L_I），1,2,4-苯三酸（H_3L_(II)）和1,2,3-苯三酸（H_3L_(III)）作为配体，合成了除P_m以外的十四个镧系元素和Y的络合物。对于稀土和均苯四酸的络合物，除得到了文献曾报导过的4:3组成外，还合成了一个新的系列，其组成为1:1的络合物：Ln·HL·nH_2O(Ln = La-Gd，Er，Y)和Ln·L·NH_4·nH_2O(Ln=Eu，Tb-Lu)。培养出了未见文献报导的稀土Er与均苯四酸络合物的单晶，晶体结构分析指出其组成为[ Er·L·3H_2O]·NH_4·4H_2O，中心离子和配体形成八配位络阴离子，呈畸变的四方反棱柱结构。对所合成的稀土苯多酸络合物（除稀土和1,2,3-苯三酸络合物外），进行了热分析研究，结果表明这类络合物具有很高的热稳定性，空气中，除Ce外，其分解温度均大于420 ℃。指出了络合物热分解机理，对于绝大部分稀土苯多酸络合物。分解分两步进行，第一步络合物脱水，第二步分解为氧化物。镧的苯多酸络合物其分解过程经碱式碳酸盐（LaO）_2 CO_3，最后分解为La_2O_3。络合物DTA分解峰温随稀土原子序有规律地变化，且不同的苯多酸系列络合物呈类似的变化规律，变价元素处于曲线峰谷的位置。测定Ln_4L_3·nH_2O系列络合物的脱水热及脱水和分解表观活化能。系统地研究了络合物在4000-100cm~(-1)范围内的FT-IR光谱，通过对羧基反对称和对称伸缩振动的分析，指出了络合物中羧基的可能配位形式。对组成为Ln·HL·nH_2O(Ln=La-Gd，Y)，Ln·L·NH_4·nH_2O (Ln=Tb-Lu)，LnL_I·nH_2O (Ln = La-Ho)和LnL_(II)·nH_2O (Ln=Pr-Tm)的络合物，指认了Ln-O链伸缩振动，其振动频率随稀土离子总角动量量子数呈类似“斜W”效应的变化。对于Ln_4L_3·nH_2O，LnL_I·nH_2O和LnL_(II)·nH_2O络合物，随着配体的不同，羧基反对称和对称伸缩振动频率差ΔV以ΔV_(1,3,5)BTA > ΔV_(PMA) > ΔV_(1,2,4)BTA的规律变化。研究了Eu和Tb苯多酸铬合物的萤光相对亮度及其萤光光谱，对Tb络合物，其萤光相对亮度随配体结构的变化有如下变化规律：PMA > 1,2,4 BTA≥1,2,3 BTA > 1,3,5 BTA。Tb的PMA络合物由于其发光强度较大，有可能在实际中得到应用。

Difference of ZSM-5 zeolites synthesized with various templates

ZSM-5 zeolites with similar SUM ratio were synthesized successfully using various templates (n-butylamine (BTA), ethylamine (ETA), isopropylamine (IPA), ethylenediamine (EDA), ethanol (ETL), ethanol-ammonium (ETL-AM) and no template (NT)) under hydrothermal conditions. The samples were characterized by XRD, SEM, XRF, NH3-TPD and BET surface area measurements in order to understand the template effects and the differences of the ZSM-5 samples. The synthesis of ZSM-5 with organic templates was relatively easier than those with inorganic templates and without template. SEM results revealed that ZSM-5 synthesized with different templates had different morphology and particle size. The Si/Al ratio and BET specific surface area of the sample with ethanol as template was the lowest. NH3-TPD results showed that the sample synthesized without template had fewer strong acid sites than others. n-Hexane cracking reaction was carried out over the samples to evaluate the catalytic properties. All ZSM-5 zeolites were effective in n-hexane cracking reaction, especially for the sample synthesized without template. (C) 2004 Elsevier B.V. All rights reserved.

Hydrogen-bonded lamellar network of pyromellitic acid pillared by 8-hydroxyquinoline

8-Hydroxyquinoline (8-q) salt of pyromellitic acid (benzene-1,2,4,5-tetracarboxylic acid, H(4)bta) forms robust lamellar structure where [H(2)bta](2-) anions build up sheets through strong hydrogen bonds in two dimensions and [H-8-q](+) cations act as pillars to afford an extended three dimensional network.

赣中周潭群变质脉体的微量元素及氧同位素地球化学研究

笔者等对周潭群沉积变质岩及其中脉体的微量元素、氧同位素地球化学进行了研究, 结果表明, 变质石英脉继承了其围岩的稀土元素及氧同位素地球化学特征, 表明形成石英脉的流体来源于围岩; 脉体的微量元素对Zr—Hf、U —Th、N b—Ta 和Y—Ho 与变质岩有一定的差异, 且有一定的分异, 指示脉体是流体作用的产物。变质流体通过侧向扩散作用形成了周潭群变沉积岩中的变质脉体。