InGaN/GaN p-i-n Photodiodes Fabricated with Mg-Doped p-InGaN Layer

Mg-doped p-InGaN layers with In composition of about 10% are grown by metalorganic chemical vapor deposition (MOCVD). The effect of the annealing temperature on the p-type behavior of Mg-doped InGaN is studied. It is found that the hole concentration in p-InGaN increases with a rising annealing temperature in the range of 600 850 C, while the hole mobility remains nearly unchanged until the annealing temperature increases up to 750 C, after which it decreases. On the basis of conductive p-type InGaN growth, the p-In0.1Ga0.9N/i-In0.1Ga0.9N/n-GaN junction structure is grown and fabricated into photodiodes. The spectral responsivity of the InGaN/GaN p-i-n photodiodes shows that the peak responsivity at zero bias is in the wavelength range 350-400 nm.

快速退火对SiGe/Si多量子阱p-i-n光电二极管的影响（英文）

利用光电流谱，结合X射线双晶衍射研究了快速退火对Si_(1-x)Ge/Si多量子阱p-i-n光电二极管的影响。由于应变SiGe的部分弛豫和Si-Ge互扩散，退火后的二极管的截止波长有显著的减小。但是，在750-850℃范围内，波长蓝移量随着退火温度的增加而变化缓慢，而样品的光电流强度却随温度是先减弱而后又增强，这可能主要是由于在不同温度退火过程中失配位错的产生和点缺陷的减小造成的。