Fabrication and luminescence properties of Y2SiWO8 : Dy3+ phosphors via sol-gel process

(YSiWO8)-Si-2:Dy3+ phosphors were prepared through a sol-gel process. XRD and photoluminespectra were used to characterize the resulting phosphors. The results indicated that the phosphors crystallized completely at 1000 degrees C. In Y2SiWO8:Dy3+ phosphors, the Dy3+ showed its characteristic yellow emission at 483nm (F-4(9/2)-H-6(5/2)) and 575nm (F-4(9/2)-H-6(13/2)) upon excitation into 275nm.

Cure processing modeling and cure cycle simulation of epoxy-terminated poly(phenylene ether ketone). V: Estimation of temperature distribution during cure process

A numerical method to estimate temperature distribution during the cure of epoxy-terminated poly(phenylene ether ketone) (E-PEK)-based composite is suggested. The effect of the temperature distribution on the selection of cure cycle is evaluated using a suggested alternation criterion. The effect of varying heating rate and thickness on the temperature distribution, viscosity distribution and distribution of the extent of cure reaction are discussed based on the combination of the here-established temperature distribution model and the previously established curing kinetics model and chemorheological model. It is found that, for a thin composite (<=10mm) and low heating rate (<=2.5K/min), the effect of temperature distribution on cure cycle and on the processing window for pressure application can be neglected. Low heating rate is of benefit to reduce the temperature gradient. The processing window for pressure application becomes narrower with increasing thicknesses of composite sheets. The validity of the temperature distribution model and the modified processing window is evaluated through the characterization of mechanical and physical properties of E-PEK-based composite fabricated according to different temperature distribution conditions.

Oscillatory Flow Induced Hydrodynamic Forces upon a Pipeline near Erosive Sandy Seabed

An experimental study of the properties of hydrodynamic forces upon a marine pipeline is presented in this paper, in the equilibrium scour conditions for various Keulegan-Carpenter numbers and various initial relative gaps between pipeline and the erosive sandy seabed. The tests are conducted in a U-shaped oscillatory water tunnel with a sand box located at the bottom of the test section. According to the experimental results, the maximum horizontal forces on the pipelines with an initial gap to seabed will decrease to some extent due to scouring process. For engineering appliances, it seems safer to estimate wave induced forces on pipelines under the assumption that seabed is plane. However, it should be noticed that great changes would be brought to the frequency properties of lift forces because of the sandy scour beneath the pipeline, which occurs for certain KC numbers.

基于工作流的J2EE遗留系统改造

为了满足用户对软件系统内部业务过程定义的定制需求,针对流行的J2EE平台,以工作流技术为基础设计了对遗留软件系统的改造平台JSPMP。JSPMP利用工作流引擎的过程定义与任务管理能力驱动系统业务流程执行,赋予软件系统在业务过程定义方面的动态可定制性。实践证明,开发者利用此方案能够迅速改造遗留系统,满足用户多样化的过程定制需求,极大地降低了改造、定制成本。

Synthesis and luminescent properties of Lu3Ga5O12 : RE3+ (RE = Eu, Tb, and Pr) nanocrystalline phosphors via sol-gel process

Lu3Ga5O12:Eu3+, Lu3Ga5O12:Tb3+, and Lu3Ga5O12:Pr3+ phosphors were prepared through a Pechini-type sol-gel process. X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), photoluminescence, and cathodoluminescence spectra were utilized to characterize the synthesized phosphors. The XRD results reveal that the sample begins to crystallize at 800 degrees C and fully crystallined pure Lu3Ga5O12 phase can be obtained at 1000 degrees C. The FESEM image indicates that the phosphor sample is composed of aggregated rice grainlike particles with sizes around 80-120 nm.

Synthesis and Luminescent Properties of LaAlO3:RE3+ (RE = Tm, Tb) Nanocrystalline Phosphors via a Sol-Gel Process

LaAlO3:Tm3+ and LaAlO3:Tb3+ phosphors were prepared through a Pechini-type sol-gel process. X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), photoluminescence, and cathodoluminescence (CL) spectra were utilized to characterize the synthesized phosphors. The XRD results reveal that the fully crystalline pure LaAlO3 Phase can be obtained at 800 degrees C. The FE-SEM image indicates that the phosphor samples are composed of aggregated spherical particles with sizes ranging from 40 to 80 nm. Under the excitation of ultraviolet light (230 nm) and low-voltage electron beams (1-3 kV), the LaAlO3:Tm3+ and LaAlO3:Tb3+ phosphors show the characteristic emissions of Tb3+ (D-1(2)-> H-3(6,4),F-3(4) transitions) and Tm3+ (D-5(3,4)-> F-7(6,5,4,3) transitions) respectively. The CL of the LaAlO3:Tm3+ phosphors have high color purity and comparable intensity to the Y2SiO5:Ce3+ commercial product, and the CL colors of Tb3+-doped LaAlO3 phosphors can be tuned from blue to green by changing the doping concentration of Tb3+ to some extent.

Three-Dimensional Modeling of Heat Transfer and Fluid Flow in Laminar-Plasma Material Re-Melting Processing

Modeling study is performed concerning the heat transfer and fluid flow for a laminar argon plasma jet impinging normally upon a flat workpiece exposed to the ambient air. The diffusion of the air into the plasma jet is handled by using the combined-diffusion-coefficient approach. The heat flux density and jet shear stress distributions at the workpiece surface obtained from the plasma jet modeling are then used to study the re-melting process of a carbon steel workpiece. Besides the heat conduction within the workpiece, the effects of the plasma-jet inlet parameters (temperature and velocity), workpiece moving speed, Marangoni convection, natural convection etc. on the re-melting process are considered. The modeling results demonstrate that the shapes and sizes of the molten pool in the workpiece are influenced appreciably by the plasma-jet inlet parameters, workpiece moving speed and Marangoni convection. The jet shear stress manifests its effect at higher plasma-jet inlet velocities, while the natural convection effect can be ignored. The modeling results of the molten pool sizes agree reasonably with available experimental data.

Numerical study of bluff body flow structures

Our recent progress in numerical studies of bluff body flow structures and a new method for the numerical analysis of near wake flow field for high Reynolds number flow are introduced. The paper consists of three parts. In part one, the evolution of wake vortex structure and variation of forces on a flat plate in harmonic oscillatory flows and in in-line steady-harmonic combined flows are presented by an improved discrete vortex method, as the Keulegan-Carpenter number (KC) varies from 2 to 40 and ratios of U-m to U-0 are of O(10(-1)), O(10) and O(10), respectively. In part 2, a domain decomposition hybrid method, combining the finite-difference and vortex methods for numerical simulation of unsteady viscous separated flow around a bluff body, is introduced. By the new method, some high resolution numerical visualization on near wake evolution behind a circular cylinder at Re = 10(2), 10(3) and 3 x 10(3) are shown. In part 3, the mechanism and the dynamic process for the three-dimensional evolution of the Karman vortex and vortex filaments in braid regions as well as the early features of turbulent structure in the wake behind a circular cylinder are presented numerically by the vortex dynamics method.