Kinetics of acetic acid esterification with 2-ethoxyethanol over an Al-pillared clay catalyst

The Al-pillared clay catalyst obtained by exposing activated clay powder to sulfuric acid and aluminium salts and calcining in air at 373-673 K, was found to be highly active for the title reaction. The results indicated that pillared layer clay of the mixed oxide has been employed as parent catalysts for their definite structure and special properties which can be modified by the substitution of L and B acid sites cations. Solid acid catalyst of Supported aluminium was found to be highly active and selective at the 373-473 K temperature range for heterogeneous esterification. The activity is mainly attributed to the Lewis (and a considerably small number of Bronsted) acid sites whose number and strength increased due to pillaring. The water produced in the esterification can be induced by Al3+, which makes the catalyst surface to form strong B acid. Their acidities are obtained by pH measurement. If only B acid sites are > 70%, and pH < 1 in the 2-ethoxyethanol, there exists an activity of esterification. The used catalyst gave identical results with that of the fresh one. X-ray diffraction spectra show that the composition and active phase of the used catalysts are the same as the fresh ones. The kinetic study of the reaction was carried out by an integral method of analysis. The kinetic equation of surface esterification is y = 2.36x - 0.98.

Enhanced electrochemical properties of nanocomposite polymer electrolyte based on copolymer with exfoliated clays

In this present work, a polymer electrolyte based on polymer/clay nanocomposite has been developed. Montmorillonite (MMT) clay was used as the filler. due to its special size in length and thickness, and its sandwich type structure. The obtained gel polymer electrolytes have high ionic conductivity up to 2.5 mS cm(-1) with high cationic transference number (about 0.64) at room temperature. The influences of the filler on the membrane morphology. the solvent uptake, the ionic conductivity, and the cation transport number were investigated, and thus the significant contribution from the exfoliated organophilic MMT was identified.

Poly(vinylidene fluoride-hexafluoropropylene)/organo-montmorillonite clays nanocomposite lithium polymer electrolytes

Polymer-clay nanocomposite (PCN) materials were prepared by intercalation of an alkyl-ammonium ion spacing/coupling agent and a polymer between the planar layers of a swellable-layered material, such as montmorillonite (MMT). The nanocomposite lithium polymer electrolytes comprising such PCN materials and/or a dielectric solution (propylene carbonate) were prepared and discussed. The chemical composition of the nanocomposite materials was determined with X-ray diffraction (XRD) and Fourier transform infrared (FTIR) spectroscopy, which revealed that the alkyl-ammonium ion successfully intercalated the layer of MMT clay, and thus copolymer poly(vinylidene fluoride-hexafluoropropylene) entered the galleries of montmorillonite clay. Cyclic voltammetry and electrochemical impedance spectroscopy (EIS) were used to investigate the electrochemical properties of the lithium polymer electrolyte. Equivalent circuits were proposed to fit the EIS data successfully, and the significant contribution from MMT was thus identified. The resulting polymer electrolytes show high ionic conductivity up to 10(-3) S cm(-1) after felling with propylene carbonate.

Hydrogen-bonded lamellar network of pyromellitic acid pillared by 8-hydroxyquinoline

8-Hydroxyquinoline (8-q) salt of pyromellitic acid (benzene-1,2,4,5-tetracarboxylic acid, H(4)bta) forms robust lamellar structure where [H(2)bta](2-) anions build up sheets through strong hydrogen bonds in two dimensions and [H-8-q](+) cations act as pillars to afford an extended three dimensional network.

Effects of surfactant loadings on the dispersion of clays in maleated polypropylene

A series of organically modified clays (OMCs) with a surfactant loading range from 0.625 to 2.5 times the cation exchange capacity (CEC) were melt-mixed with maleated polypropylene (PPMA). Wide-angle X-ray diffraction and transmission electron microscopy results of these narrocomposites show that dispersion of clays becomes unfavorable in the PPMA matrix during melt intercalation as the surfactant loading increases in the process of modifying clays, though larger interlayer distances are obtained in their corresponding OMCs. It is even important that clays uniformly disperse at the nanoscale level in the PPMA matrix when the surfactant loadings are below the CEC, which implies that incomplete exchange of inorganic cations in the process of modifying clay benefits the dispersion of clays in the PPMA matrix.

XPS Study on the Interaction between Layers and Pillars of Layered Double Hydroxides Pillared with Heteroplyanion (II)

Layered double hydroxides (LDHs) pillared with heteropolyanions have been measured using XPS, IR, XRD spertra, and the interaction between layers and pillars discussed, The mechanism of pillars has been further discussed by XPS spectra.

Synthesis and catalytic properties of layered double hydroxides pillared by heteropolyoxometalate

Layered double hydroxides (LDHs) pillared with heteropolyoxometalate have been synthesized via both restructuring of hydrotalcite-like compounds and direct anion exchange under microwave field. LDHs and their derivatives are both found to be efficient for alkylation of isobutane with butene with a higher butene conversion and selectivity towards C-8(0).

Alrylation Over Layered Double Hydrotalcites Pillared by Heteropolyoxometalate Catalysts

Layered double hydroxides (LDHs) pillared with heteropolyoxo-metalate have been synthesized via both restructuring of hydrotalcite-like compounds and direct anion exchange under microwave field. LDHs and their derivatives are both found to be efficiency f

ALKYLATION OF ISOBUTANE WITH BUTENE OVER LAYERED DOUBLE HYDROXIDE PILLARED HETEROPOLYOXOMETALATE ACID-BASE CATALYSTS

[Si(W2O7)(6)](8-) pillared LDH structure hydroxides were synthesized by the method of restructuring of the thermally decomposed hydrotalcite-like compounds for Zn-Al and Mg-Al oxide systems. [P(W2O7)(6)](8-) pillared Ni-Al LDH structure hydroxide was synt

Flocculation and removal of the brown tide organism, Aureococcus anophagefferens (Chrysophyceae), using clays

Previous attempts to remove the brown tide organism, Aureococcus anophagefferens, through flocculation with clays have been unsuccessful, in spite of adopting concentrations and dispersal protocols that yielded excellent cell removal efficiency (RE>90%) with other species, so a study was planned to improve cell removal. Four modifications in clay preparation and dispersal were explored: 1) varying the salinity of the clay suspension; 2) mixing of the clay-cell suspension after clay addition; 3) varying of concentration of the initial clay stock; 4) pulsed loading of the clay slurry. The effect of salinity was dependent on the clay mineral type: phosphatic clay (IMC-P2) had a higher RE than kaolinite (H-DP) when seawater was used to disperse the clay, but H-DP removed cells more efficiently when suspended in distilled water prior to application. Mixing after dispersal approximately doubled RE for both clays compared to when the slurry was layered over the culture surface. Lowering the concentration of clay stock and pulsing the clay loading increased RE, regardless of mineral type. However, this increase was more apparent for clays dispersed in seawater than in distilled water. In general, application procedures that decrease the rate of self-aggregation among the clay particles and increase the collision frequency between clay particles and A. anophagefferens achieve higher cell removal efficiency. These empirical studies demonstrated that clays might be an important control option for the brown tide organism, given the proper attention to preparation, dispersal methods, environmental impacts, and the hydrodynamic properties of the system being treated. Implications for the treatment of brown tides in the field are discussed.

Studies on two coordination polymers [M(mu(4)-pz25dc)](n) (M = Cd or Zn, pz25dc=pyrazine-2,5-dicarboxylato) with three-dimensional pillared-layer three-nodal framework: Synthesis, structural characterization, strong optical non-linearities and optical limiting properties

Two isomorphous new candidates [M(mu(4)-pz25dc)](n) (M = Cd, 1; Zn, 2; pz25dc = pyrazine-2,5-dicarboxylato)for nonlinear optical (NLO) materials have been synthesized hydrothermally and characterized crystallographically as pillared-layer three-nodal frameworks with one four-connected metal nodes and two crystallographically different four-connected ligand nodes. Their optical non-linearities are measured by the Z-Scan technique with an 8 ns pulsed laser at 532 nm. These two coordination polymers both exhibit strong NLO absorptive abilities [alpha(2) = (63 +/- 6) x 10 (12) mW (1) 1, ( 46 +/- 6) x 10 (11) mW (1) 2] and effective self-focusing performance [n(2) = (67 +/- 5) x 10 (18) 1, (13 +/- 3) x 10 (18) m(2) W (1) 2] in 1.02 x 10 (4) 1 and 1.05 x 10 (4) mol dm (3) 2 DMF solution separately. The values of the limiting threshold are also measured from the optical limiting experimental data. The heavy atom effect plays important role in the enhancement of optical non-linearities and optical limiting properties. (C) 2009 Elsevier B. V. All rights reserved.