Synthesis of isotactic polystyrene with a rare-earth catalyst

Polymerization of styrene with the neodymium phosphonate Nd(P-507)/H2O/Al(i-Bu)(3) catalytic system has been examined. The polymer obtained was separated into a soluble and an insoluble fraction by 2-butanone extraction. C-13-NMR spectra indicate that the insoluble fraction is isotactic polystyrene and the soluble one is syndiotactic-rich atactic polystyrene. The polymerization features are described and discussed. The optimum conditions for the polymerization are as follows: [Nd] = (3.5-5.0) x 10(-2) mol/L; [styrene] = 5 mol/L; [Al]/[Nd] = 6-8 mol/mol; [H2O]/[Al] = 0.05-0.08 mol/mol; polymerization temperature around 70 degrees C. The percent yield of isotactic polystyrene (TY) is markedly affected by catalyst aging temperature. With increase of the aging temperature from 40 to 70 degrees C, TY increases from 9% to 48%. Using AlEt3 and Al(i-Bu)(2)H instead of Al(i-Bu)(3) decreases the yield of isotactic polystyrene. Different neodymium compounds give the following activity order: Nd(P-507)(3) > Nd(P-204)(3) > Nd(OPri)(3) > NdCl3 + C2HF5OH > Nd(naph)(3). With Nd(naph)(3) as catalyst, only atactic polystyrene is obtained. (C) 1998 John Wiley & Sons, Inc.

Mechanical properties and miscibility of polyethersulfone phenoxy blends

The blends of polyethersulfone and phenoxy were prepared by melt mixing in a Brabender-like apparatus. The specimens for measurements were made by compression molding and then were water-quenched at room temperature under pressure. The tensile strength, tensile modulus, elongation at break and yield, density, thermal analysis, and dynamic mechanical properties were each measured. The dependence of tensile strength, tensile modulus, elongation at break and yield, and density on composition was obtained. The relationship between tensile modulus and elongation at break and yield and speed of the crosshead at different weight ratios of the blends is shown. The effects of composition and miscibility on the mechanical properties are discussed. (C) 1996 John Wiley & Sons, Inc.