Synthesis of different gold nanostructures by solar radiation and their SERS spectroscopy

In this article, a simple and novel photochemical synthesis of different gold nanostructures is proposed using solar radiation. This method is rapid, convenient and of low cost, and can be performed under ambient conditions. By adjusting the concentration of sodium acetate (NaAc), different morphologies of the products can be easily obtained. Without NaAc, the products obtained are mainly polyhedral gold particles; lower concentration of NaAc (0.05 and 0.1 M) accelerates the formation of flowerlike gold nanostructures; while higher concentration of NaAc (0.5 M) facilitates the formation of a variety of gold nanowires and nanobelts. It is found that the morphology change of gold nanaostructures is the result of the synergistic effect of poly(diallyl dimethylammonium) chloride (PDDA), Ac- ions, and the pH value. In addition, the different gold nanostructures thus obtained were used as substrates for surface-enhanced Raman scattering (SERS) with p-aminothiophenol (p-ATP) as the probe molecule.

Facile synthesis of platinum nanoelectrocatalyst with urchinlike morphology

A very simple and effective wet chemical route to direct synthesis of well-dispersed Pt nanoparticles with urchinlike morphology is proposed, which was carried out by simply mixing H2PtCl6 aqueous solution and poly(vinyl pyrrolidone) with the initial molar ratios of 1:3.5 kept constant at 30 degrees C for 3 days in the presence of formic acid. As-prepared urchinlike Pt nanostructures showed excellent electrocatalytic activity toward the reduction of dioxygen and oxidation of methanol and could be used as a promising nanoelectrocatalyst.

Seed-Mediated Growth of Nearly Monodisperse Palladium Nanocubes with Controllable Sizes

Nearly monodisperse Pd nanocubes with controllable sizes were synthesized through a seed-mediated growth approach. By using Pd nanocubes of 22 nm in size as seeds, the morphology of the as-grown nanostructures was fixed as single-crystalline, which enabled us to rationally tune the size of Pd nanocubes. The formation mechanism of initial 22 nm nanocubes was also discussed. The size-dependent surface plasmon resonance properties of the as-synthesized Pd nanocubes were investigated. Compared with previous methods, the yield, monodispersity, perfection of the shape formation, and the range of size control of these nanocubes are all improved.

Efficient preparation of silver nanoplates assisted by non-polar solvents

In the paper, we report an efficient method to prepare high yield (up to 97%) of silver nanoplates. Synthesis of silver nanoplates was carried Out in a binary solvent system of N,N-dimethylformamide (DMF) and toluene, in which DMF served as the reductant and polyvinylpyrrolidone (PVP) as the capping agent. By increasing the ratio of toluene to DMF to 7:6, silver nanoplates can be Successfully synthesized; otherwise other shaped nanoparticles would be the major products. The nanoplate sample was characterized by TEM, HRTEM, SAED, XRD, AFM and UV-visible spectroscopy, proving the high nanoplate purity of this sample. The influence of toluene content, other solvents, AgNO3 concentration, preparation temperature and chloride ions was also examined, which suggests that the function of nonpolar solvents in this system is to enhance the PVP coverage on silver surface and, furthermore, to facilitate the preferential adsorption of PVP on two (I I I) facets of silver nanoplates.

Polyol-Mediated Synthesis of PbS Crystals: Shape Evolution and Growth Mechanism

An interesting shape evolution of. PbS crystals, that is, from cubes to (truncated) octahedra and finally to stable star-shaped multipods with six arms along the < 100 > directions is first realized via a facile polyol-mediated reaction between lead acetate and sulfur powder in the absence of surfactants. X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), and Fourier transform infrared (FT-IR) techniques were employed to characterize the samples. We elucidate the important parameters (including reaction temperature and sulfur sources) responsible for the shape-controlled synthesis of PbS crystals.

Nanostructured CaWO4, CaWO4 : Pb2+ and CaWO4 : Tb3+ particles: Polyol-mediated synthesis and luminescent properties

Nano-submicrostructured CaWO4, CaWO4 : Pb2+ and CaWO4 : Tb3+ particles were prepared by polyol method and characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), Fourier transform infrared spectra (FT-IR), thermogravimetry-differential thermal analysis (TG-DTA), photoluminescence (PL), cathodo-luminescence (CL) spectra and PL lifetimes. The results of XRD indicate that the as-prepared samples are well crystallized with the scheelite structure of CaWO4. The FE-SEM images illustrate that CaWO4 and CaWO4 : Pb2+ and CaWO4 : Tb3+ powders are composed of spherical particles with sizes around 260, 290, and 190 nm respectively, which are the aggregates of smaller nanoparticles around 10-20 nm. Under the UV light or electron beam excitation, the CaWO4 powders exhibits a blue emission band with a maximum at about 440 nm. When the CaWO4 particles are doped with Pb2+, the intensity of luminescence is enhanced to some extent and the luminescence band maximum is red shifted to 460 nm. Tb3+-doped CaWO4 particles show the characteristic emission of Tb3+ D-5(4)-F-7(J) (J=6-3) transitions due to an energy transfer from WO42- groups to Tb3+.

Polyol-mediated synthesis of polyhedral silver clusters

Besides the spheres, polyhedral silver nanoclusters were prepared by the polyol process with 3-aminopropyl triethoxysilane (APTES). In the process, APTES acts as not only the stabilizer but also the template.

Novel synthesis of highly active Pt/C cathode electrocatalyst for direct methanol fuel cell

A 40 wt% Pt/C cathode electrocatalyst with controlled Pt particle size of similar to 2.9 nm showing better performance than commercial catalyst for direct methanol fuel cell was prepared by a polyol process with water but without using stabilizing agent.

Synthesis and Luminescence Properties of CdS Nanoparticles

CdS nanoparticles were successfully prepared by polyol method with PVP-K30 as a surfactant. The microstructure, size and morphology of the products were investigated in detail by XRD, TEM and SEM. The results indicate that uniform CdS nanospheres were achieved. Photoluminescence properties of the resulted nanoparticles (S1 and S3) were investigated, and the results indicate that the CdS nanoparticles could be used as a potential blue light emitting material.

Morphology-controlled synthesis of magnetites with nanoporous structures and excellent magnetic properties

Different morphological single-crystal magnetites (Fe3O4) with a nanoporous structure, which exhibit excellent magnetic properties, have been synthesized by a polyol process. Both the type of polyol and the concentration of KOH play important roles in the formation of various morphologies. Cubic, truncated-octahedral, and octahedral shapes can be prepared by changing the concentration of the KOH solution in ethylene glycol.

Facile Synthesis and Characterization of Single Crystalline Bi2S3 with Various Morphologies

Single crystalline Bi2S3 With various morphologies (wires, rods, and flowers) has been successfully prepared via a simple polyol solution process and characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), and transmission electron microscopy (TEM) techniques. The morphologies of Bi2S3 crystals are highly dependent on the experimental parameters, including the reaction temperature, reactant ratio, sulfur source, and additive. The adjustment of these parameters can lead to an obvious shape evolution of products, and the growth mechanism has been proposed.

One-Step Synthesis and Luminescent Properties of Nanocrystalline YVO4:Eu3+ powders

In this paper, nanocrystalline YVO4:Eu3+ powders have been successfully synthesized via high-temperature solution-phase synthesis process. The nanocrystalline YVO4:Eu3+ particles were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), UVNis absorption spectra and luminescence spectra, luminescence decay curve and Fourier transform infrared (FT-IR), X-ray photoelectron spectra (XPS) respectively. The as-prepared nanocrystalline YVO4:Eu3+ particles are well crystallized with ellipsoidal morphology.

Morphology control of nanoscale PbS particles in a polyol process

Nanostructured PbS with different morphologies and particle sizes have been prepared through a polyol process. Narrow size distribution for star-shaped, octahedral, tetradecanehedral, and cubic products were achieved by slowly introducing the source materials using a peristaltic pump in the presence of poly(vinylpyrrolidone) (PVP) as additive. Systematic variation of the kinetic factors, including the additive, the reaction temperature, the duration time, the ratio of source materials, the Sulfur sources, and the Pb(Ac)(2)center dot 3H(2)O concentration, reveals that the morphology depends mainly on the supersaturation degree of the free sulfur ions released from thiourea under elevated temperature.

A facile synthesis and characterization of monodisperse spherical pigment particles with a core/shell structnre

In this paper, a facile sol-gel process for producing monodisperse, spherical, and nonaggregated pigment particles with a core/shell structure is reported. Spherical silica particles (245 and 385 nm in diameter) and Cr2O3, alpha-Fe2O3, ZnCo2O4, CuFeCrO4, MgFe2O4, and CoAl2O4 pigments are selected as cores and shells, respectively. The obtained core/shell-structured pigment samples, denoted as SiO2@Cr2O3 (green), SiO2@alpha-Fe2O3 (red), SiO2@MgFe2O4 (brown), SiO2@ZnCo2O4 (dark green), SiO2@CoAl2O4 (blue), and SiO2@CuFeCrO4 (black), are well characterized by using X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), and UV-vis diffuse reflection, as well as by investigating the magnetic properties. The results of XRD and high-resolution TEM (HRTEM) demonstrate that the pigment shells crystallize well on the surface Of SiO2 Particles. The thickness of the pigment shell can be tuned by the number of coatings, to some extent. These pigment particles can be well dispersed in some solvents (such as glycol) to form relatively more stable suspensions than the commercial products.

Facile synthesis and photoluminescent properties of redispersible CeF3, CeF3 : Tb3+, and CeF3 : Tb3+/LaF3 (core/shell) nanoparticles

CeF3, CeF3:Tb3+, and CeF3:Tb3+/LaF3 (core/shell) nanoparticles were prepared by the polyol method and characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), X-ray photoelectron spectra (XPS), UV-vis absorption spectra, photoluminescence (PL) spectra, and lifetimes. The results of XRD indicate that the obtained CeF3, CeF3:Tb3+, and CeF3:Tb3+/LaF3 (core/shell) nanoparticles crystallized well at 200 degrees C in diethylene glycol (DEG) with a hexagonal structure. The TEM images illustrate that the CeF3 and CeF3:Tb3+ nanoparticles are spherical with a mean diameter of 7 nm. The growth of the LaF3 shell around the CeF3:Tb3+ core nanoparticles resulted in an increase of the average size (11 nm) of the nanopaticles as well as in a broadening of their size distribution. These nanocrystals can be well-dispersed in ethanol to form clear colloidal solutions. The colloidal solutions of CeF3 and CeF3:Tb3+ show the characteristic emission of Ce3+ 5d-4f (320 nm) and Tb3+ D-5(4)-F-7(J) (J = 6-3, with D-5(4)-F-7(5) green emission at 542 nm as the strongest one) transitions, respectively. The emission intensity and lifetime of the CeF3:Tb3+/LaF3 (core/shell) nanoparticles increased with respect to those of CeF3:Tb3+ core particles.